CN109280249A - A kind of friendly packaging material and preparation method for high-intensitive environment - Google Patents
A kind of friendly packaging material and preparation method for high-intensitive environment Download PDFInfo
- Publication number
- CN109280249A CN109280249A CN201811174235.7A CN201811174235A CN109280249A CN 109280249 A CN109280249 A CN 109280249A CN 201811174235 A CN201811174235 A CN 201811174235A CN 109280249 A CN109280249 A CN 109280249A
- Authority
- CN
- China
- Prior art keywords
- parts
- packaging material
- friendly packaging
- environment
- intensitive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of friendly packaging material and preparation method for high-intensitive environment, the raw material including following parts by weight: 40-65 parts of high-strength polyethylene resin, 10-20 parts of acrylic resin, 10-20 parts of bamboo charcoal fiber, 30-40 parts of starch, 10-15 parts of glass fibre, 30-50 parts of wear-resisting carbon ash, 30-50 parts of chlorinated scoline, 1-3 parts of antioxidant, 1-3 parts of stabilizer, 1-3 parts of plasticizer, 1-3 parts of toughener, 1-3 parts of anti-aging agent, 15-20 parts of fire retardant；Preparation method, comprising the following steps: each component is added sequentially in agitating device, mixing time is at least 30min, waits and is sufficiently stirred after completion, melting extrusion in double screw extruder is added mixture into, then by composite material blow molding.Solve that current packaging material intensity is low, the problem of patience difference, and also the packaging adopts the environment-protecting and non-poisonous evil of lotus, can be degraded, and the substance after degradation is environmentally friendly harmless, and manufacturing cost is low, good in economic efficiency.
Description
Technical field
The present invention relates to field of packaging material, specially a kind of friendly packaging material for high-intensitive environment and
Preparation method.
Background technique
For packaging material using very universal in daily life and production, various industries have different need to packaging material
Ask, the purpose of packaging be protection commodity it is injury-free, be readily transported, store and consumer carry, it is beautiful and generous on this basis,
Be conducive to the sale of commodity.
According to different operating environments to the difference of packaging demand, to packaging material in the environment of high-strength working
The requirement of the performances such as wear-resistant, anti-oxidant can be higher, while should also ensure that the degradability of packaging material, but existing packet
Package material is generally unable to satisfy to be used under high-intensitive environment, and performance is unable to satisfy requirement.
Summary of the invention
The present invention provides a kind of friendly packet for high-intensitive environment aiming at deficiencies of the prior art
Package material and preparation method, component ratio of the invention is reasonable, has high intensity by the packaging material that the ratio is produced
The characteristics of high tenacity, is suitble to carry out operation under high-intensitive environment, solves that current packaging material intensity is low, and patience difference is asked
Topic, and the packaging adopts the environment-protecting and non-poisonous evil of lotus, can be degraded, and the substance after degradation is environmentally friendly harmless, and manufacturing cost is low,
It is good in economic efficiency.
The present invention additionally provides a kind of close friend for high-intensitive environment aiming at deficiencies of the prior art
The preparation method of type packaging material, preparation method is simple, low in cost, and shaping speed is fast, is able to carry out large batch of push away
Wide production, practical value are high.
To achieve the above object, invention provides the following technical solutions:
A kind of friendly packaging material for high-intensitive environment, the raw material including following parts by weight: high-strength polyethylene
It is 40-65 parts of resin, 10-20 parts of acrylic resin, 10-20 parts of bamboo charcoal fiber, 30-40 parts of starch, 10-15 parts of glass fibre, resistance to
Grind 30-50 parts of carbon ash, 30-50 parts of chlorinated scoline, 1-3 parts of antioxidant, 1-3 parts of stabilizer, 1-3 parts of plasticizer, toughener
1-3 parts, 1-3 parts of anti-aging agent, 15-20 parts of fire retardant.
Preferably, 50 parts of the high-strength polyethylene resin, 15 parts of acrylic resin, 15 parts of bamboo charcoal fiber, starch 35
Part, 12 parts of glass fibre, wear-resisting carbon grey 40 parts, 40 parts of chlorinated scoline, 2 parts of antioxidant, 2 parts of heat stabilizer, plasticizer 1
Part, 2 parts of toughener, 2 parts of anti-aging agent, 15 parts of fire retardant.
Preferably, the plasticizer is epoxy aliphatic acid methyl ester or dibutyl phthalate.
Preferably, the antioxidant is alkyl diphenylamine or tributyl 2-acetylcitrate.
Preferably, the stabilizer is di-n-butyltin dilaurate or calcium-zinc composite stabilizing agent.
Preferably, the toughener is epoxy aliphatic acid methyl ester or polypropylene glycerol aether.
Preferably, the fire retardant is decabromodiphenyl oxide or brominated polyethylene.
Preferably, the starch is corn flour.
A kind of preparation method of the friendly packaging material for high-intensitive environment, comprising the following steps: by each component according to
Secondary to be added in agitating device, mixing time is at least 30min, waits and is sufficiently stirred after completion, adds mixture into double spiral shells
Melting extrusion in bar extruder, then by composite material blow molding.
Preferably, the revolving speed of the twin-screw is 130-200r/min, and melting temperature is 80-11 DEG C.
Compared with prior art, advantageous effect of the invention is:
1, component ratio of the invention is reasonable, has high-intensity and high-tenacity by the packaging material that the ratio is produced
Feature is suitble to carry out operation under high-intensitive environment, solves that current packaging material intensity is low, the problem of patience difference, and
The packaging adopts the environment-protecting and non-poisonous evil of lotus, can be degraded, and the substance after degradation is environmentally friendly harmless, and manufacturing cost is low, economy effect
Benefit is good.
2, the present invention has the characteristics that wear-resistant, resistance to buffering, good flame retardation effect, increases the service life of packaging material,
It reduces costs, use is safer and more reliable.
3, of the invention preparation method is simple, low in cost, and shaping speed is fast, is able to carry out large batch of popularization life
It produces, practical value is high.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
A kind of friendly packaging material for high-intensitive environment, the raw material including following parts by weight: high-strength polyethylene
It is 40-65 parts of resin, 10-20 parts of acrylic resin, 10-20 parts of bamboo charcoal fiber, 30-40 parts of starch, 10-15 parts of glass fibre, resistance to
Grind 30-50 parts of carbon ash, 30-50 parts of chlorinated scoline, 1-3 parts of antioxidant, 1-3 parts of stabilizer, 1-3 parts of plasticizer, toughener
1-3 parts, 1-3 parts of anti-aging agent, 15-20 parts of fire retardant.
Preferably, 50 parts of the high-strength polyethylene resin, 15 parts of acrylic resin, 15 parts of bamboo charcoal fiber, starch 35
Part, 12 parts of glass fibre, wear-resisting carbon grey 40 parts, 40 parts of chlorinated scoline, 2 parts of antioxidant, 2 parts of heat stabilizer, plasticizer 1
Part, 2 parts of toughener, 2 parts of anti-aging agent, 15 parts of fire retardant.
Preferably, the plasticizer is epoxy aliphatic acid methyl ester or dibutyl phthalate.The antioxidant is alkyl
Diphenylamines or tributyl 2-acetylcitrate.The stabilizer is di-n-butyltin dilaurate or calcium-zinc composite stabilizing agent.It is described
Toughener is epoxy aliphatic acid methyl ester or polypropylene glycerol aether.The fire retardant is decabromodiphenyl oxide or brominated polyethylene.Institute
Stating starch is corn flour.
Component ratio of the invention is reasonable, has the spy of high-intensity and high-tenacity by the packaging material that the ratio is produced
Point is suitble to carry out operation under high-intensitive environment, solves that current packaging material intensity is low, the problem of patience difference, and this
Packaging adopts the environment-protecting and non-poisonous evil of lotus, can be degraded, the substance after degradation is environmentally friendly harmless, and manufacturing cost is low, economic benefit
It is good.Have the characteristics that wear-resistant, resistance to buffering, good flame retardation effect, increases the service life of packaging material, reduce costs, make
With safer and more reliable.
Of the invention preparation method is simple, low in cost, and shaping speed is fast, is able to carry out large batch of popularization life
It produces, practical value is high.
A kind of preparation method of the friendly packaging material for high-intensitive environment, comprising the following steps: by each component according to
Secondary to be added in agitating device, mixing time is at least 30min, waits and is sufficiently stirred after completion, adds mixture into double spiral shells
Melting extrusion in bar extruder, then by composite material blow molding.The revolving speed of the twin-screw is 130-200r/min, melting
Temperature is 80-11 DEG C.
Of the invention preparation method is simple, low in cost, and shaping speed is fast, is able to carry out large batch of popularization life
It produces, practical value is high.
Obviously, various changes and modifications can be made to the invention without departing from essence of the invention by those skilled in the art
Mind and range.In this way, if these modifications and changes of the present invention belongs to the range of the claims in the present invention and its equivalent technologies
Within, then the present invention is also intended to include these modifications and variations.
Claims (10)
1. a kind of friendly packaging material for high-intensitive environment, it is characterised in that: the raw material including following parts by weight: high-strength
Spend polyvinyl resin 40-65 parts, 10-20 parts of acrylic resin, 10-20 parts of bamboo charcoal fiber, 30-40 parts of starch, glass fibre 10-
15 parts, 30-50 parts of wear-resisting carbon ash, 30-50 parts of chlorinated scoline, 1-3 parts of antioxidant, 1-3 parts of stabilizer, 1-3 parts of plasticizer,
1-3 parts of toughener, 1-3 parts of anti-aging agent, 15-20 parts of fire retardant.
2. a kind of friendly packaging material for high-intensitive environment as described in claim 1, it is characterised in that: described high-strength
Spend 50 parts of polyvinyl resin, 15 parts of acrylic resin, 15 parts of bamboo charcoal fiber, 35 parts of starch, 12 parts of glass fibre, wear-resisting carbon ash 40
It is part, 40 parts of chlorinated scoline, 2 parts of antioxidant, 2 parts of heat stabilizer, 1 part of plasticizer, 2 parts of toughener, 2 parts of anti-aging agent, fire-retardant
15 parts of agent.
3. a kind of friendly packaging material for high-intensitive environment as described in claim 1, it is characterised in that: the plasticising
Agent is epoxy aliphatic acid methyl ester or dibutyl phthalate.
4. a kind of friendly packaging material for high-intensitive environment as described in claim 1, it is characterised in that: the antioxygen
Agent is alkyl diphenylamine or tributyl 2-acetylcitrate.
5. a kind of friendly packaging material for high-intensitive environment as described in claim 1, it is characterised in that: the stabilization
Agent is di-n-butyltin dilaurate or calcium-zinc composite stabilizing agent.
6. a kind of friendly packaging material for high-intensitive environment as described in claim 1, it is characterised in that: the toughening
Agent is epoxy aliphatic acid methyl ester or polypropylene glycerol aether.
7. a kind of friendly packaging material for high-intensitive environment as described in claim 1, it is characterised in that: described fire-retardant
Agent is decabromodiphenyl oxide or brominated polyethylene.
8. a kind of friendly packaging material for high-intensitive environment as described in claim 1, it is characterised in that: the starch
For corn flour.
9. such as a kind of described in any item friendly packaging materials for high-intensitive environment of claim 1-8, preparation method,
It is characterized by comprising following steps: each component being added sequentially in agitating device, mixing time is at least 30min, waits and fills
After dividing stirring to complete, melting extrusion in double screw extruder is added mixture into, then by composite material blow molding.
10. a kind of preparation method of the friendly packaging material for high-intensitive environment as claimed in claim 9, feature exist
In: the revolving speed of the twin-screw is 130-200r/min, and melting temperature is 80-11 DEG C.