CN109266028A - A kind of fragrant Wood-plastic material and preparation method thereof - Google Patents
A kind of fragrant Wood-plastic material and preparation method thereof Download PDFInfo
- Publication number
- CN109266028A CN109266028A CN201810771238.2A CN201810771238A CN109266028A CN 109266028 A CN109266028 A CN 109266028A CN 201810771238 A CN201810771238 A CN 201810771238A CN 109266028 A CN109266028 A CN 109266028A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- wood
- plastic material
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of fragrant Wood-plastic materials, it is made of the raw material of following parts by weight: 27 parts of persimmon wood powder, 3 parts of lavender oil, 17 parts of highland barley stalk, 12 parts of chestnut shell powder, 17 parts of luffa vine powder, 2 parts of glass fiber powder, 12 parts of bamboo powder, 22 parts of waste and old packaging bag plastic pellet, 22 parts of polypropylene, 22 parts of polyvinyl chloride, 4 parts of calcium silicates of nanometer, 3 parts of catechin, 2 parts of mica powder, 2 parts of medical stone powder, 2 parts of magnesium hydroxide, 0.6 part of antimony oxide, 0.2 part of nano-graphene, 2 parts of o-phthalic acid dibutyl ester, 3 parts of rouge of polyethylene glycol distearyl acid, 2 parts of phenolic resin, 3 parts of polyethylene wax, 4 parts of iron oxide blue.The Wood-plastic material is economic and environment-friendly, can make full use of discarded timber and plastics；Compactness is good, and mechanical property is good, extremely durable；Flame-proof antibiotic effect is good, also with the fragrance of lavender, increases the surcharge of Wood-plastic material.
Description
Technical field
The present invention relates to Wood-plastic material fields, and in particular to a kind of fragrant Wood-plastic material and preparation method thereof.
Background technique
Wood plastic composite (WPC) be by thermoplastic with wood-fibred or plant fiber are compound is prepared, the material
The double grading of timber and plastics is had both, thermal expansion, water imbibition are smaller than timber, good stability of the dimension, wearability and anti-impact
Performance height is hit, product can be recycled.In order to further increase the surcharge of wood plastic composite, how one kind is provided
Fragrant Wood-plastic material and preparation method thereof is also an important research direction.
Summary of the invention
It is an object of the invention to: a kind of fragrant Wood-plastic material and preparation method thereof is provided.
To achieve the goals above, the invention provides the following technical scheme:
A kind of fragrant Wood-plastic material, the raw material including following parts by weight:
25-35 parts of persimmon wood powder, 2-4 parts of lavender oil, 15-25 parts of highland barley stalk, 10-20 parts of chestnut shell powder, sponge gourd
15-20 parts of rattan powder, 1-4 parts of glass fiber powder, 10-16 parts of bamboo powder, 20-30 parts of waste and old packaging bag plastic pellet, polypropylene 20-25
Part, 20-25 parts of polyvinyl chloride, 3-6 parts of nanometer calcium silicates, 2-5 parts of catechin, 1-4 parts of mica powder, 1-4 parts of medical stone powder, hydrogen-oxygen
Change magnesium 1-3 parts, 0.5-1 parts of antimony oxide, 0.1-0.5 parts of nano-graphene, 1-4 parts of o-phthalic acid dibutyl ester, poly- second two
2-5 parts of alcohol distearyl acid rouge, 1-4 parts of phenolic resin, 2-5 parts of polyethylene wax.
Preferably, a kind of fragrant Wood-plastic material further includes 3-6 parts of iron oxide blue.
Preferably, a kind of fragrant Wood-plastic material, is made of the raw material of following parts by weight:
27 parts of persimmon wood powder, 3 parts of lavender oil, 17 parts of highland barley stalk, 12 parts of chestnut shell powder, 17 parts of luffa vine powder, glass
2 parts of glass fiber powder, 12 parts of bamboo powder, 22 parts of waste and old packaging bag plastic pellet, 22 parts of polypropylene, 22 part, nanometer calcium silicates 4 of polyvinyl chloride
Part, 3 parts of catechin, 2 parts of mica powder, 2 parts of medical stone powder, 2 parts of magnesium hydroxide, 0.6 part of antimony oxide, nano-graphene 0.2
Part, 2 parts of o-phthalic acid dibutyl ester, 3 parts of polyethylene glycol distearyl acid rouge, 2 parts of phenolic resin, 3 parts of polyethylene wax, iron oxide blue
4 parts.
Preferably, a kind of fragrant Wood-plastic material, is made of the raw material of following parts by weight:
30 parts of persimmon wood powder, 2.5 parts of lavender oil, 22 parts of highland barley stalk, 18 parts of chestnut shell powder, 18 parts of luffa vine powder,
3 parts of glass fiber powder, 14 parts of bamboo powder, 28 parts of waste and old packaging bag plastic pellet, 23 parts of polypropylene, 24 part, nanometer silicic acid of polyvinyl chloride
5 parts of calcium, 4 parts of catechin, 3 parts of mica powder, 3 parts of medical stone powder, 1.5 parts of magnesium hydroxide, 0.8 part of antimony oxide, nano-graphite
0.4 part of alkene, 3 parts of o-phthalic acid dibutyl ester, 4 parts of polyethylene glycol distearyl acid rouge, 3 parts of phenolic resin, 4 parts of polyethylene wax, oxygen
Change 5 parts of barba hispanica.
A kind of preparation method of fragrant Wood-plastic material, the specific steps are as follows:
(1) all raw materials are put into pressure cooker HIGH PRESSURE TREATMENT 1-3 hours, pressure 5-10MPa, is taken out, place into-
50 DEG C of freezers freeze 1-3 hour, take out, and place into drying in dryer, and drying temperature is 70-80 DEG C, and moisture content is not after drying
Greater than 3%；
(2) 10-15min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 190-200 DEG C, then through supercooling
Water is cooled and shaped.
Preferably, the time of step (1) mesohigh processing is 1.8 hours, pressure 7MPa, and cooling time is 2 hours, is dried
Dry temperature is 76 DEG C.
Preferably, mixing time is 14min in step (2).
Preferably, extrusion temperature is 191 DEG C in step (3).
The beneficial effects of the present invention are: Wood-plastic material production is simple, economic and environment-friendly, can make full use of discarded timber
And plastics, it reduces environmental pollution；Compactness is good, and mechanical property is good, extremely durable；Meanwhile flame-proof antibiotic effect is good, also has and smokes
The fragrance of clothing grass, increases the surcharge of Wood-plastic material.
Specific embodiment
Embodiment 1
A kind of fragrant Wood-plastic material, is made of the raw material of following parts by weight:
25 parts of persimmon wood powder, 2 parts of lavender oil, 15 parts of highland barley stalk, 10 parts of chestnut shell powder, 15 parts of luffa vine powder, glass
1 part of glass fiber powder, 10 parts of bamboo powder, 20 parts of waste and old packaging bag plastic pellet, 20 parts of polypropylene, 20 part, nanometer calcium silicates 3 of polyvinyl chloride
Part, 2 parts of catechin, 1 part of mica powder, 1 part of medical stone powder, 1 part of magnesium hydroxide, 0.5 part of antimony oxide, nano-graphene 0.1
Part, 1 part of o-phthalic acid dibutyl ester, 2 parts of polyethylene glycol distearyl acid rouge, 1 part of phenolic resin, 2 parts of polyethylene wax, iron oxide blue
3 parts.
The preparation method of above-mentioned fragrant Wood-plastic material, the specific steps are as follows:
(1) all raw materials are put into HIGH PRESSURE TREATMENT 1.8 hours in pressure cooker, pressure 7MPa takes out, places into -50
DEG C freezer freezes 2 hours, takes out, and places into drying in dryer, and drying temperature is 76 DEG C, and moisture content is not more than 3% after drying；
(2) 14min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 191 DEG C, then cold through supercooled water
But it forms.
Embodiment 2
A kind of fragrant Wood-plastic material, is made of the raw material of following parts by weight:
27 parts of persimmon wood powder, 3 parts of lavender oil, 17 parts of highland barley stalk, 12 parts of chestnut shell powder, 17 parts of luffa vine powder, glass
2 parts of glass fiber powder, 12 parts of bamboo powder, 22 parts of waste and old packaging bag plastic pellet, 22 parts of polypropylene, 22 part, nanometer calcium silicates 4 of polyvinyl chloride
Part, 3 parts of catechin, 2 parts of mica powder, 2 parts of medical stone powder, 2 parts of magnesium hydroxide, 0.6 part of antimony oxide, nano-graphene 0.2
Part, 2 parts of o-phthalic acid dibutyl ester, 3 parts of polyethylene glycol distearyl acid rouge, 2 parts of phenolic resin, 3 parts of polyethylene wax, iron oxide blue
4 parts.
The preparation method of above-mentioned fragrant Wood-plastic material, the specific steps are as follows:
(1) all raw materials are put into HIGH PRESSURE TREATMENT 1.8 hours in pressure cooker, pressure 7MPa takes out, places into -50
DEG C freezer freezes 2 hours, takes out, and places into drying in dryer, and drying temperature is 76 DEG C, and moisture content is not more than 3% after drying；
(2) 14min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 191 DEG C, then cold through supercooled water
But it forms.
Embodiment 3
A kind of fragrant Wood-plastic material, is made of the raw material of following parts by weight:
30 parts of persimmon wood powder, 2.5 parts of lavender oil, 22 parts of highland barley stalk, 18 parts of chestnut shell powder, 18 parts of luffa vine powder,
3 parts of glass fiber powder, 14 parts of bamboo powder, 28 parts of waste and old packaging bag plastic pellet, 23 parts of polypropylene, 24 part, nanometer silicic acid of polyvinyl chloride
5 parts of calcium, 4 parts of catechin, 3 parts of mica powder, 3 parts of medical stone powder, 1.5 parts of magnesium hydroxide, 0.8 part of antimony oxide, nano-graphite
0.4 part of alkene, 3 parts of o-phthalic acid dibutyl ester, 4 parts of polyethylene glycol distearyl acid rouge, 3 parts of phenolic resin, 4 parts of polyethylene wax, oxygen
Change 5 parts of barba hispanica.
The preparation method of above-mentioned fragrant Wood-plastic material, the specific steps are as follows:
(1) all raw materials are put into HIGH PRESSURE TREATMENT 1.8 hours in pressure cooker, pressure 7MPa takes out, places into -50
DEG C freezer freezes 2 hours, takes out, and places into drying in dryer, and drying temperature is 76 DEG C, and moisture content is not more than 3% after drying；
(2) 14min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 191 DEG C, then cold through supercooled water
But it forms.
Embodiment 4
A kind of fragrant Wood-plastic material, is made of the raw material of following parts by weight:
35 parts of persimmon wood powder, 4 parts of lavender oil, 25 parts of highland barley stalk, 20 parts of chestnut shell powder, 20 parts of luffa vine powder, glass
4 parts of glass fiber powder, 16 parts of bamboo powder, 30 parts of waste and old packaging bag plastic pellet, polipropene 25 part, 25 part, nanometer calcium silicates 6 of polyvinyl chloride
Part, 5 parts of catechin, 4 parts of mica powder, 4 parts of medical stone powder, 3 parts of magnesium hydroxide, 1 part of antimony oxide, 0.5 part of nano-graphene,
4 parts of o-phthalic acid dibutyl ester, 5 parts of polyethylene glycol distearyl acid rouge, 4 parts of phenolic resin, 5 parts of polyethylene wax, iron oxide blue 6
Part.
(1) all raw materials are put into HIGH PRESSURE TREATMENT 1.8 hours in pressure cooker, pressure 7MPa takes out, places into -50
DEG C freezer freezes 2 hours, takes out, and places into drying in dryer, and drying temperature is 76 DEG C, and moisture content is not more than 3% after drying；
(2) 14min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 191 DEG C, then cold through supercooled water
But it forms.
Claims (8)
1. a kind of fragrant Wood-plastic material, which is characterized in that the raw material including following parts by weight:
25-35 parts of persimmon wood powder, 2-4 parts of lavender oil, 15-25 parts of highland barley stalk, 10-20 parts of chestnut shell powder, luffa vine powder
15-20 parts, it is 1-4 parts of glass fiber powder, 10-16 parts of bamboo powder, 20-30 parts of waste and old packaging bag plastic pellet, 20-25 parts of polypropylene, poly-
20-25 parts of vinyl chloride, 3-6 parts of nanometer calcium silicates, 2-5 parts of catechin, 1-4 parts of mica powder, 1-4 parts of medical stone powder, magnesium hydroxide
1-3 parts, 0.5-1 parts of antimony oxide, 0.1-0.5 parts of nano-graphene, 1-4 parts of o-phthalic acid dibutyl ester, polyethylene glycol two
2-5 parts of stearate, 1-4 parts of phenolic resin, 2-5 parts of polyethylene wax.
2. the fragrant Wood-plastic material of one kind according to claim 1, which is characterized in that further include iron oxide blue 3-
6 parts.
3. the fragrant Wood-plastic material of one kind according to claim 2, which is characterized in that using following parts by weight
Raw material is made:
27 parts of persimmon wood powder, 3 parts of lavender oil, 17 parts of highland barley stalk, 12 parts of chestnut shell powder, 17 parts of luffa vine powder, glass fibers
Tie up 2 parts of powder, 12 parts of bamboo powder, 22 parts of waste and old packaging bag plastic pellet, 22 parts of polypropylene, 4 parts of 22 part, nanometer calcium silicates of polyvinyl chloride,
3 parts of catechin, 2 parts of mica powder, 2 parts of medical stone powder, 2 parts of magnesium hydroxide, 0.6 part of antimony oxide, 0.2 part of nano-graphene,
2 parts of o-phthalic acid dibutyl ester, 3 parts of polyethylene glycol distearyl acid rouge, 2 parts of phenolic resin, 3 parts of polyethylene wax, iron oxide blue 4
Part.
4. the fragrant Wood-plastic material of one kind according to claim 2, which is characterized in that using following parts by weight
Raw material is made:
30 parts of persimmon wood powder, 2.5 parts of lavender oil, 22 parts of highland barley stalk, 18 parts of chestnut shell powder, 18 parts of luffa vine powder, glass
3 parts of fiber powder, 14 parts of bamboo powder, 28 parts of waste and old packaging bag plastic pellet, 23 parts of polypropylene, 24 part, nanometer calcium silicates 5 of polyvinyl chloride
Part, 4 parts of catechin, 3 parts of mica powder, 3 parts of medical stone powder, 1.5 parts of magnesium hydroxide, 0.8 part of antimony oxide, nano-graphene
0.4 part, 3 parts of o-phthalic acid dibutyl ester, 4 parts of polyethylene glycol distearyl acid rouge, 3 parts of phenolic resin, 4 parts of polyethylene wax, oxidation
5 parts of barba hispanica.
5. a kind of preparation method of fragrant Wood-plastic material, it is characterised in that: specific step is as follows:
(1) all raw materials are put into pressure cooker HIGH PRESSURE TREATMENT 1-3 hours, pressure 5-10MPa, takes out, places into -50 DEG C
Freezer freezes 1-3 hours, takes out, and places into drying in dryer, and drying temperature is 70-80 DEG C, and moisture content is not more than after drying
3%；
(2) 10-15min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 190-200 DEG C, then cold through supercooled water
But it forms.
6. the preparation method of the fragrant Wood-plastic material of one kind according to claim 5, it is characterised in that: step
(1) time of mesohigh processing is 1.8 hours, pressure 7MPa, and cooling time is 2 hours, and drying temperature is 76 DEG C.
7. the preparation method of the fragrant Wood-plastic material of one kind according to claim 5, it is characterised in that: step
(2) mixing time is 14min in.
8. the preparation method of the fragrant Wood-plastic material of one kind according to claim 5, it is characterised in that: step
(3) extrusion temperature is 191 DEG C in.