CN109181333A - A kind of high-intensity wood plastic material and preparation method thereof - Google Patents
A kind of high-intensity wood plastic material and preparation method thereof Download PDFInfo
- Publication number
- CN109181333A CN109181333A CN201810770157.0A CN201810770157A CN109181333A CN 109181333 A CN109181333 A CN 109181333A CN 201810770157 A CN201810770157 A CN 201810770157A CN 109181333 A CN109181333 A CN 109181333A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- wood plastic
- plastic material
- intensity wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high-intensity wood plastic materials, it is made of the raw material of following parts by weight: 38 parts of Poplar Powder, 1.5 parts of tea tree ethereal oil, 18 parts of bagasse, useless 3 parts of red soil of the quarrel of industry, 12 parts of chestnut shell powder, 26 parts of sweet potato rattan powder, 18 parts of bamboo powder, 25 parts of waste and old polyethylene material, 24 parts of polypropylene, 23 parts of polyvinyl chloride, 5 parts of calcium carbonate crystal whisker, 4 parts of plastic-steel fabric, 3 parts of calcite in powder, 3 parts of leather powder, 1.8 parts of nano-titanium dioxide, 0.9 part of antimony oxide, 0.4 part of expansible graphite, 3 parts of o-phthalic acid dibutyl ester, 4 parts of turmeric alcohol, 3 parts of phenolic resin, 4 parts of polyethylene wax, 4 parts of titan yellow.The material is economic and environment-friendly, can make full use of discarded timber and plastics, reduce environmental pollution；By the way that calcium carbonate crystal whisker, plastic-steel fabric is added, breaking strength and tensile strength are increased, by the way that tea tree ethereal oil and turmeric alcohol is added, enhances anti-microbial property.
Description
Technical field
The present invention relates to Wood-plastic material fields, and in particular to a kind of high-intensity wood plastic material and preparation method thereof.
Background technique
Wood plastic composite (WPC) be by thermoplastic with wood-fibred or plant fiber are compound is prepared, the material
The double grading of timber and plastics is had both, thermal expansion, water imbibition are smaller than timber, good stability of the dimension, and wear-resisting property is good, produce
Product can be recycled.In order to further increase the market value of wood plastic composite, a kind of high-intensity wood plastic how is provided
New material and preparation method thereof is also an important research direction.
Summary of the invention
It is an object of the invention to: a kind of high-intensity wood plastic material and preparation method thereof is provided.
To achieve the goals above, the invention provides the following technical scheme:
A kind of high-intensity wood plastic material, the raw material including following parts by weight:
30-40 parts of Poplar Powder, 1-3 parts of tea tree ethereal oil, 10-20 parts of bagasse, industry useless quarrel red soil 1-4 parts, chestnut shell powder 8-
15 parts, 20-27 parts of sweet potato rattan powder, 15-20 parts of bamboo powder, 18-28 parts of waste and old polyethylene material, 20-25 parts of polypropylene, polyvinyl chloride
20-25 parts, 3-6 parts of calcium carbonate crystal whisker, 2-5 parts of plastic-steel fabric, 1-4 parts of calcite in powder, 1-4 parts of leather powder, nano-titanium dioxide
1-3 parts, 0.5-1 parts of antimony oxide, 0.1-0.5 parts of expansible graphite, 1-4 parts of o-phthalic acid dibutyl ester, turmeric alcohol 2-5
Part, 1-4 parts of phenolic resin, 2-5 parts of polyethylene wax.
Preferably, a kind of high-intensity wood plastic material further includes 2-5 parts of titan yellow.
Preferably, a kind of high-intensity wood plastic material, is made of the raw material of following parts by weight:
Useless quarrel 2 parts of the red soil, 9 parts of chestnut shell powder, sweet potato rattan powder of 32 parts of Poplar Powder, 2 parts of tea tree ethereal oil, 15 parts of bagasse, industry
22 parts, 17 parts of bamboo powder, 20 parts of waste and old polyethylene material, 21 parts of polypropylene, 21 parts of polyvinyl chloride, 4 parts of calcium carbonate crystal whisker, plastic-steel fabric
3 parts, 2 parts of calcite in powder, 2 parts of leather powder, 2 parts of nano-titanium dioxide, 0.6 part of antimony oxide, 0.2 part of expansible graphite, neighbour
2 parts of phthalic acid dibutyl ester, 3 parts of turmeric alcohol, 2 parts of phenolic resin, 3 parts of polyethylene wax, 3 parts of titan yellow.
Preferably, a kind of high-intensity wood plastic material, is made of the raw material of following parts by weight:
Useless quarrel 3 parts of the red soil, 12 parts of chestnut shell powder, sweet potato rattan of 38 parts of Poplar Powder, 1.5 parts of tea tree ethereal oil, 18 parts of bagasse, industry
26 parts of powder, 18 parts of bamboo powder, 25 parts of waste and old polyethylene material, 24 parts of polypropylene, 23 parts of polyvinyl chloride, 5 parts of calcium carbonate crystal whisker, plastic-steel are fine
Tie up 4 parts, 3 parts of calcite in powder, 3 parts of leather powder, 1.8 parts of nano-titanium dioxide, 0.9 part of antimony oxide, expansible graphite 0.4
Part, 3 parts of o-phthalic acid dibutyl ester, 4 parts of turmeric alcohol, 3 parts of phenolic resin, 4 parts of polyethylene wax, 4 parts of titan yellow.
A kind of preparation method of high-intensity wood plastic material, the specific steps are as follows:
(1) all raw materials are put into pressure cooker HIGH PRESSURE TREATMENT 1-3 hours, pressure 5-10MPa, is taken out, place into-
50 DEG C of freezers freeze 1-3 hour, take out, and place into drying in dryer, and drying temperature is 70-80 DEG C, and moisture content is not after drying
Greater than 3%；
(2) 10-20min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 200-210 DEG C, then through supercooling
Water is cooled and shaped.
Preferably, the time of step (1) mesohigh processing is 1.4 hours, pressure 7MPa, and cooling time is 2 hours, is dried
Dry temperature is 75 DEG C.
Preferably, mixing time is 16min in step (2).
Preferably, extrusion temperature is 201 DEG C in step (3).
The beneficial effects of the present invention are: Wood-plastic material production is simple, economic and environment-friendly, can make full use of discarded timber
And plastics, it reduces environmental pollution；By the way that calcium carbonate crystal whisker, plastic-steel fabric simultaneously is added, the breaking strength and drawing of material are increased
Intensity is stretched, by the way that tea tree ethereal oil and turmeric alcohol is added, anti-microbial property is enhanced, is worthy to be popularized.
Specific embodiment
Embodiment 1
A kind of high-intensity wood plastic material, is made of the raw material of following parts by weight:
Useless quarrel 1 part of the red soil, 8 parts of chestnut shell powder, sweet potato rattan powder of 30 parts of Poplar Powder, 1 part of tea tree ethereal oil, 10 parts of bagasse, industry
20 parts, 15 parts of bamboo powder, 18 parts of waste and old polyethylene material, 20 parts of polypropylene, 20 parts of polyvinyl chloride, 3 parts of calcium carbonate crystal whisker, plastic-steel fabric
2 parts, 1 part of calcite in powder, 1 part of leather powder, 1 part of nano-titanium dioxide, 0.5 part of antimony oxide, 0.1 part of expansible graphite, neighbour
1 part of phthalic acid dibutyl ester, 2 parts of turmeric alcohol, 1 part of phenolic resin, 2 parts of polyethylene wax, 2 parts of titan yellow.
The preparation method of above-mentioned high-intensity wood plastic material, the specific steps are as follows:
(1) all raw materials are put into pressure cooker HIGH PRESSURE TREATMENT 1-3 hours, pressure 5-10MPa, is taken out, place into-
50 DEG C of freezers freeze 1-3 hour, take out, and place into drying in dryer, and drying temperature is 70-80 DEG C, and moisture content is not after drying
Greater than 3%；
(2) 10-20min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 200-210 DEG C, then through supercooling
Water is cooled and shaped.
Embodiment 2
A kind of high-intensity wood plastic material, is made of the raw material of following parts by weight:
Useless quarrel 2 parts of the red soil, 9 parts of chestnut shell powder, sweet potato rattan powder of 32 parts of Poplar Powder, 2 parts of tea tree ethereal oil, 15 parts of bagasse, industry
22 parts, 17 parts of bamboo powder, 20 parts of waste and old polyethylene material, 21 parts of polypropylene, 21 parts of polyvinyl chloride, 4 parts of calcium carbonate crystal whisker, plastic-steel fabric
3 parts, 2 parts of calcite in powder, 2 parts of leather powder, 2 parts of nano-titanium dioxide, 0.6 part of antimony oxide, 0.2 part of expansible graphite, neighbour
2 parts of phthalic acid dibutyl ester, 3 parts of turmeric alcohol, 2 parts of phenolic resin, 3 parts of polyethylene wax, 3 parts of titan yellow.
The preparation method of above-mentioned high-intensity wood plastic material, the specific steps are as follows:
(1) all raw materials are put into pressure cooker HIGH PRESSURE TREATMENT 1-3 hours, pressure 5-10MPa, is taken out, place into-
50 DEG C of freezers freeze 1-3 hour, take out, and place into drying in dryer, and drying temperature is 70-80 DEG C, and moisture content is not after drying
Greater than 3%；
(2) 10-20min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 200-210 DEG C, then through supercooling
Water is cooled and shaped.
Embodiment 3
A kind of high-intensity wood plastic material, is made of the raw material of following parts by weight:
Useless quarrel 3 parts of the red soil, 12 parts of chestnut shell powder, sweet potato rattan of 38 parts of Poplar Powder, 1.5 parts of tea tree ethereal oil, 18 parts of bagasse, industry
26 parts of powder, 18 parts of bamboo powder, 25 parts of waste and old polyethylene material, 24 parts of polypropylene, 23 parts of polyvinyl chloride, 5 parts of calcium carbonate crystal whisker, plastic-steel are fine
Tie up 4 parts, 3 parts of calcite in powder, 3 parts of leather powder, 1.8 parts of nano-titanium dioxide, 0.9 part of antimony oxide, expansible graphite 0.4
Part, 3 parts of o-phthalic acid dibutyl ester, 4 parts of turmeric alcohol, 3 parts of phenolic resin, 4 parts of polyethylene wax, 4 parts of titan yellow.
The preparation method of above-mentioned high-intensity wood plastic material, the specific steps are as follows:
(1) all raw materials are put into pressure cooker HIGH PRESSURE TREATMENT 1-3 hours, pressure 5-10MPa, is taken out, place into-
50 DEG C of freezers freeze 1-3 hour, take out, and place into drying in dryer, and drying temperature is 70-80 DEG C, and moisture content is not after drying
Greater than 3%；
(2) 10-20min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 200-210 DEG C, then through supercooling
Water is cooled and shaped.
Embodiment 4
A kind of high-intensity wood plastic material, is made of the raw material of following parts by weight:
Useless quarrel 4 parts of the red soil, 15 parts of chestnut shell powder, sweet potato rattan powder of 40 parts of Poplar Powder, 3 parts of tea tree ethereal oil, 20 parts of bagasse, industry
27 parts, 20 parts of bamboo powder, 28 parts of waste and old polyethylene material, polipropene 25 part, 25 parts of polyvinyl chloride, 6 parts of calcium carbonate crystal whisker, plastic-steel fabric
5 parts, 4 parts of calcite in powder, 4 parts of leather powder, 3 parts of nano-titanium dioxide, 1 part of antimony oxide, 0.5 part of expansible graphite, adjacent benzene
4 parts of dioctyl phthalate dibutyl ester, 5 parts of turmeric alcohol, 4 parts of phenolic resin, 5 parts of polyethylene wax, 5 parts of titan yellow.
The preparation method of above-mentioned high-intensity wood plastic material, the specific steps are as follows:
(1) all raw materials are put into HIGH PRESSURE TREATMENT 1.4 hours in pressure cooker, pressure 7MPa takes out, places into -50
DEG C freezer freezes 2 hours, takes out, and places into drying in dryer, and drying temperature is 75 DEG C, and moisture content is not more than 3% after drying；
(2) 16min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 201 DEG C, then cold through supercooled water
But it forms.
Claims (8)
1. a kind of high-intensity wood plastic material, it is characterised in that: the raw material including following parts by weight:
Useless red soil 1-4 parts of the quarrel of 30-40 parts of Poplar Powder, 1-3 parts of tea tree ethereal oil, 10-20 parts of bagasse, industry, 8-15 parts of chestnut shell powder,
20-27 parts of sweet potato rattan powder, 15-20 parts of bamboo powder, 18-28 parts of waste and old polyethylene material, 20-25 parts of polypropylene, polyvinyl chloride 20-25
Part, 3-6 parts of calcium carbonate crystal whisker, 2-5 parts of plastic-steel fabric, 1-4 parts of calcite in powder, 1-4 parts of leather powder, 1-3 parts of nano-titanium dioxide,
0.5-1 parts of antimony oxide, 0.1-0.5 parts of expansible graphite, 1-4 parts of o-phthalic acid dibutyl ester, 2-5 parts of turmeric alcohol, phenol
1-4 parts of urea formaldehyde, 2-5 parts of polyethylene wax.
2. a kind of high-intensity wood plastic material according to claim 1, it is characterised in that: further include 2-5 parts of titan yellow.
3. a kind of high-intensity wood plastic material according to claim 2, it is characterised in that: using the raw material of following parts by weight
It is made:
Useless 2 parts of the red soil of quarrel of 32 parts of Poplar Powder, 2 parts of tea tree ethereal oil, 15 parts of bagasse, industry, 9 parts of chestnut shell powder, 22 parts of sweet potato rattan powder,
17 parts of bamboo powder, 20 parts of waste and old polyethylene material, 21 parts of polypropylene, 21 parts of polyvinyl chloride, 4 parts of calcium carbonate crystal whisker, 3 parts of plastic-steel fabric,
2 parts of calcite in powder, 2 parts of leather powder, 2 parts of nano-titanium dioxide, 0.6 part of antimony oxide, 0.2 part of expansible graphite, adjacent benzene two
2 parts of formic acid dibutyl ester, 3 parts of turmeric alcohol, 2 parts of phenolic resin, 3 parts of polyethylene wax, 3 parts of titan yellow.
4. a kind of high-intensity wood plastic material according to claim 2, it is characterised in that: using the raw material of following parts by weight
It is made:
Useless quarrel 3 parts of the red soil, 12 parts of chestnut shell powder, sweet potato rattan powder 26 of 38 parts of Poplar Powder, 1.5 parts of tea tree ethereal oil, 18 parts of bagasse, industry
Part, 18 parts of bamboo powder, 25 parts of waste and old polyethylene material, 24 parts of polypropylene, 23 parts of polyvinyl chloride, 5 parts of calcium carbonate crystal whisker, plastic-steel fabric 4
Part, 3 parts of calcite in powder, 3 parts of leather powder, 1.8 parts of nano-titanium dioxide, 0.9 part of antimony oxide, 0.4 part of expansible graphite, neighbour
3 parts of phthalic acid dibutyl ester, 4 parts of turmeric alcohol, 3 parts of phenolic resin, 4 parts of polyethylene wax, 4 parts of titan yellow.
5. a kind of preparation method of high-intensity wood plastic material, which is characterized in that specific step is as follows:
(1) all raw materials are put into pressure cooker HIGH PRESSURE TREATMENT 1-3 hours, pressure 5-10MPa, takes out, places into -50 DEG C
Freezer freezes 1-3 hours, takes out, and places into drying in dryer, and drying temperature is 70-80 DEG C, and moisture content is not more than after drying
3%；
(2) 10-20min will be stirred in raw material investment blender after drying, is allowed to dispersion without agglomeration；
(3) raw material after stirring is squeezed out by double screw extruder, and extrusion temperature is 200-210 DEG C, then cold through supercooled water
But it forms.
6. a kind of preparation method of high-intensity wood plastic material according to claim 5, it is characterised in that: in step (1)
The time of HIGH PRESSURE TREATMENT is 1.4 hours, pressure 7MPa, and cooling time is 2 hours, and drying temperature is 75 DEG C.
7. a kind of preparation method of high-intensity wood plastic material according to claim 5, it is characterised in that: in step (2)
Mixing time is 16min.
8. a kind of preparation method of high-intensity wood plastic material according to claim 5, it is characterised in that: in step (3)
Extrusion temperature is 201 DEG C.