CN109264979A - A kind of method for glass preparation having silver coating - Google Patents
A kind of method for glass preparation having silver coating Download PDFInfo
- Publication number
- CN109264979A CN109264979A CN201811434669.6A CN201811434669A CN109264979A CN 109264979 A CN109264979 A CN 109264979A CN 201811434669 A CN201811434669 A CN 201811434669A CN 109264979 A CN109264979 A CN 109264979A
- Authority
- CN
- China
- Prior art keywords
- glass
- coating
- preparation
- weight percent
- surface modification
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of method for glass preparation for having silver coating, which includes the following steps: the preparation Step 1: Glass Surface Modification agent;Step 2: Glass Surface Modification;Step 3: cement base coating preparation;And Step 4: prepared by cementitious coating.The invention has the following beneficial effects: use Si (OH)4、Al(OH)3With Fe (OH)3Mixed sols carries out surface to glass and is modified, and improves the binding force of cementitious coating and glass;It using brushing method combination cement conservation curing process, can be firmly combined in the silver color inorganic gel coating material that glass surface is prepared, coating with glass, structure is cellular, and uneven, can generate the matt imitation stone decorative effect of silver color;Preparation process is simple, and cost prepares silver color glass lower than glass glazings technique;Coating is inorganic material, and aging phenomenon is not present compared with organic film material height in hardness.
Description
[technical field]
The present invention relates to building decoration materials preparation technical field more particularly to a kind of glass preparation sides for having silver coating
Method.
[background technique]
Silver color plate glass, because its special metallochrome decorative effect is widely used in the blocking material of city's interior trim
And wall surface decorative plate.At present there are two types of the conventional process methods of preparation silver color plate glass:
One is surface of plate glass is sprayed at using dedicated silver color fluorocarbon resin glass lacquer, on surface after paint curing
Silver coating, this method simple process and low cost are formed, but the coating of glass surface is organic matter, the low resistance to ag(e)ing of hardness
Can be poor, easy in use to be scratched and fallen off, normal service life is also no more than 10 years, under the conditions of intensive ultraviolet very
To less than 5 years.
Another kind is will to contain low softening point glass powder, silver pigment by the method for silk-screen printing or inkjet printing and have
The extraordinary glaze of machine aided agent is printed in glass surface, is then sintered glass by steel process, during the sintering process, has
Silver pigment is firmly adhered to glass surface by machine aided agent volatilization, low softening point glass melting, the silver color which prepares
Glass surface has the silver color glass glazings of one layer of high rigidity, and glaze layer service life is identical as plate glass matrix.
But in tempering sintering process, on the one hand, silver pigment has slight oxidative phenomena, the coloration of silver color glaze layer
It is partially dark, influence decorative effect;On the other hand, the organic additive in glaze can crack volatilization, there is certain pollution to environment.In addition
The silver color decorative layer of the glass surface either prepared using organic coating or glass glazings technique, surface smoothness is very
Height, reflecting rate is very big, both techniques can not all prepare the silver color decorative layer of matt, cannot generate the bumps on imitation stone surface
Sandstone sense effect.
[summary of the invention]
The present invention provides a kind of method for glass preparation for having silver coating, and preparation process is simple, at low cost, the glass of preparation
Glass has the silver color decorative layer of dumb light, and long service life.
In order to solve the above technical problems, The technical solution adopted by the invention is as follows:
A kind of method for glass preparation having silver coating, which is characterized in that the preparation method includes the following steps:
Step 1: the preparation of Glass Surface Modification agent: by formula rate weigh a certain amount of silica solution and Aluminum sol and
FeCl3Solution pours into same container then under conditions of 6000 revs/min, stirs 1-2 hours at room temperature, adds boron
Sour powder continues to stir, and after boric acid is completely dissolved, adds waterglass, stirs 20-30 under conditions of 6000 revs/min
After minute, stop stirring, obtain mixed solution, then mixed solution is fitted into closed container, obtains Glass Surface Modification agent;
Step 2: Glass Surface Modification: by glass immersion in n-butanol, carrying out ultrasonic cleaning 5- with the frequency of 2000Hz
It after 10 clocks, is dried at room temperature for 1-2 hours, the Glass Surface Modification agent prepared by step 1, which is added to nozzle diameter, is
0.2-0.3mm and operating pressure are to spray the Glass Surface Modification agent air pressure in the air pressure spray gun of 0.8-1.2MPa
Rifle even application after the glass after spraying is then dried at room temperature for 20-24 hours, is put into glass tempering furnace to glass surface
In, in air atmosphere, glass temperature is kept the temperature 3-4 minutes, then by glass from room temperature to 650-680 DEG C in 5-6 minutes
Glass is come out of the stove, and is cooled down at room temperature, and the modified tempered glass in surface is obtained;
Step 3: cement base coating preparation: weighing the pure water, silica flour, aluminium powder, chlorination of certain mass by formula rate amount
The poly- second two of molecular weight 2000 is added in magnesium, polyethylene glycol and 525 cement under conditions of 400 revs/min into weighed pure water
Alcohol sequentially adds weighed magnesium chloride, aluminium powder and cement, stirs under conditions of 600 revs/min after stirring 20-30 minutes
After 0.5-1 hours, silica flour is added and stir 20-30 minutes under conditions of 600 revs/min again, acquisition cement base coating;
Step 4: prepared by cementitious coating: the cement base coating prepared by step 3 uniformly being brushed and is prepared in step 2
The modified tempered glass in surface on, tempered glass of the coating layer thickness control after 0.3-0.5mm, brushing lies against steam curing
In slot, after being conserved 4-6 hours at 80 DEG C, lies against room temperature indoor environment 7-10 days and obtained after carrying out complete aquation gelling reaction
There is the glass of silver coating.
Preferably, in step 1, the formula of the Glass Surface Modification agent includes: weight percent 10-15% and mould
The waterglass that number is 2.8, the silica solution that weight percent 50-60% and solid content are 10%, weight percent 10-20% and solid
The aluminum solutions that content is 15%, weight percent 10-15% and the FeCl that pH value is 1, concentration is 2mol/L3Solution, Yi Jichong
Measure the boric acid of percentage 2-3%.
Preferably, in step 3, the formula of the cement base coating includes: 525 water of weight percent 40-45%
Mud, the polyethylene glycol of weight percent 1-2% and molecular weight 2000, the magnesium chloride of weight percent 5-7%, weight percent
The aluminium powder of 10-15% and particle diameter less than 50 microns, weight percent 10-15% and diameter 0.5-2mm silica flour, with
And the pure water of weight percent 20-30%.
Preferably, in step 4, the cement base coating is uniformly brushed using the method manually brushed in the tempering
On glass.
Preferably, the glass is plate glass.
The invention has the following beneficial effects:
1, using Si (OH)4、Al(OH)3With Fe (OH)3Mixed sols carries out surface to glass and is modified, and collosol coating passes through
Tempering processing after, can and glass formed Si-O-Si and Al-O-Si key, can firmly be adhered to glass surface, when cementitious coating into
When row hydration process, the Al of the high activity of glass surface2O3And Fe2O3Nano particle can form aluminic acid dicalcium and iron with 525 cement
The inorganic glues condensate such as sour dicalcium, improves the binding force of cementitious coating and glass;
2, it using brushing method combination cement conservation curing process, can be applied in the silver color inorganic gel that glass surface is prepared
Layer material, coating are firmly combined with glass, and structure is cellular, and uneven, can generate the matt imitation stone dress of silver color
Adorn effect;
3, preparation process is simple, and cost prepares silver color glass lower than glass glazings technique;
4, coating is inorganic material, and aging phenomenon is not present compared with organic film material height in hardness.
[Detailed description of the invention]
To describe the technical solutions in the embodiments of the present invention more clearly, make required in being described below to embodiment
Attached drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for
For those of ordinary skill in the art, without creative efforts, it can also be obtained according to these attached drawings other
Attached drawing, in which:
Fig. 1 is the combination interface shape appearance figure of silver coating and glass;
Fig. 2 is the microstructure of glass surface silver coating.
[specific embodiment]
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that the described embodiments are merely a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts all other
Embodiment shall fall within the protection scope of the present invention.
The present invention provides a kind of method for glass preparation for having silver coating, which is characterized in that the preparation method includes such as
Lower step:
Step 1: the preparation of Glass Surface Modification agent: by formula rate weigh a certain amount of silica solution and Aluminum sol and
FeCl3Solution pours into same container then under conditions of 6000 revs/min, stirs 1-2 hours at room temperature, adds boron
Sour powder continues to stir, and after boric acid is completely dissolved, adds waterglass, stirs 20-30 under conditions of 6000 revs/min
After minute, stop stirring, obtain mixed solution, then mixed solution is fitted into closed container, obtains Glass Surface Modification agent;
In step 1, the formula of the Glass Surface Modification agent includes: weight percent 10-15% and modulus is 2.8
Waterglass, the silica solution that weight percent 50-60% and solid content are 10%, weight percent 10-20% and solid content is
15% aluminum solutions, weight percent 10-15% and the FeCl that pH value is 1, concentration is 2mol/L3Solution and weight percent
Boric acid than 2-3%.
Specifically, first mixing a certain amount of silica solution, Aluminum sol and FeCl3 solution under conditions of high-speed stirred, examine
Consider the stability of silica solution and Aluminum sol, the silica solution and Aluminum sol of technical grade are acidity, and adding pH value is 1, and concentration is
The FeCl3 solution of 2mol/L, mixed solution are still acidity, and it is molten can to obtain stable silica solution, Aluminum sol and FeCl3 mixing
Liquid, then appropriate boric acid is added in acidic mixed solution, boric acid can be dissolved in mixed solution, be eventually adding suitable modulus and be
The pH value of 2.8 waterglass, mixed solution increases, FeCl3Hydrolysis is formed Fe (OH)3Colloidal sol, by the addition for controlling waterglass
Amount, can get stable Si (OH)4、Al(OH)3With Fe (OH)3Mixed solution.
Step 2: Glass Surface Modification: by glass immersion in n-butanol, carrying out ultrasonic cleaning 5- with the frequency of 2000Hz
It after 10 clocks, is dried at room temperature for 1-2 hours, the Glass Surface Modification agent prepared by step 1, which is added to nozzle diameter, is
0.2-0.3mm and operating pressure be in the air pressure spray gun of 0.8-1.2MPa, the Glass Surface Modification agent air pressure is sprayed
Rifle even application after the glass after spraying is then dried at room temperature for 20-24 hours, is put into glass tempering furnace to glass surface
In, in air atmosphere, glass temperature is kept the temperature 3-4 minutes, then by glass from room temperature to 650-680 DEG C in 5-6 minutes
Glass is come out of the stove, and is cooled down at room temperature, and the modified tempered glass in surface is obtained;
Specifically, surface has a large amount of-OH key after glass removes oil drying in n-butanol, be conducive to step 1 preparation
Glass Surface Modification agent in glass surface homogeneous film formation.After glass after spraying is dried at room temperature for 20-24 hours, surface
Sol pellicle desiccation becomes gel layer, and the waterglass in Glass Surface Modification agent plays the role of temporary adhesive, will coagulate
Si (OH) in glue film4、Al(OH)3With Fe (OH)3Particle is firmly adhered to glass surface, facilitates subsequent technological operation.
Si (OH) in the tempering heat treatment process of glass, in gel film4、Al(OH)3With Fe (OH)3Particle further loses knot
Structure water becomes unformed SiO2、Al2O3And Fe2O3Particle, since there are a large amount of oxygen-octahedrons in glass, so tempering
Part SiO in treatment process, in gel layer2、Al2O3Can and glass formed Si-O-Si and Al-O-Si key improve film layer and
The binding force of glass.There are a certain amount of Na in film layer simultaneously2SiO3And B2O3, they will form low in tempering treatment process
Softening point glass, is filled in SiO2、Al2O3And Fe2O3Between particle, three kinds of particles are firmly bonded together, it can be effective
Prevent film layer from cracking.
Step 3: cement base coating preparation: weighing the pure water, silica flour, aluminium powder, chlorination of certain mass by formula rate amount
The poly- second two of molecular weight 2000 is added in magnesium, polyethylene glycol and 525 cement under conditions of 400 revs/min into weighed pure water
Alcohol sequentially adds weighed magnesium chloride, aluminium powder and cement, stirs under conditions of 600 revs/min after stirring 20-30 minutes
After 0.5-1 hours, silica flour is added and stir 20-30 minutes under conditions of 600 revs/min again, acquisition cement base coating;
In step 3, the formula of the cement base coating includes: 525 cement of weight percent 40-45%, weight hundred
Point than 1-2% and the polyethylene glycol of molecular weight 2000, the magnesium chloride of weight percent 5-7%, weight percent 10-15% and
The silica flour and weight percent of grain aluminium powder of the diameter less than 50 microns, weight percent 10-15% and diameter in 0.5-2mm
Pure water than 20-30%.
Specifically, the polyethylene glycol of a certain amount of molecular weight 2000 is first added in pure water, magnesium chloride, aluminium are then added
Powder and 525 cement.In the suspension, polyethylene glycol can be adsorbed in the surface of aluminium powder and 525 cement, generate steric hindrance effect
It answers, improves the suspension of aluminium powder and cement powder.Magnesium chloride meeting partial hydrolysis in suspension, generates Mg (OH)2Micelle, Mg (OH)2
Micelle can be adsorbed in aluminium powder surface, after coating after aquation gelling during, Mg (OH)2It will form inorganic coagulation material (5Mg
(OH)2·MgCL2·8H2O), for the cementitious material in gelatinization, the relatively strong basicity environment of generation can make Al powder Surface Creation
A small amount of Al (OH)3, Al (OH)3Again with Mg (OH)2Cementitious material reaction, dehydration form Al-O-Mg key.Surface has a certain amount of
The Al powder of magnalium cementitious material can be soaked by the calcium silicates cementitious material that the hydrolysis of 525 cement generates well, improve 525 water
Cementability of the mud to aluminium powder.Silver pigment is mainly played the role of in the addition of aluminium powder in cement base coating.Big granularity silica flour
Addition form rough decorative effect mainly after cementitious coating solidification on surface, generate sandstone mechanism effect.
Step 4: prepared by cementitious coating: the cement base coating prepared by step 3 uniformly being brushed and is prepared in step 2
The modified tempered glass in surface on, tempered glass of the coating layer thickness control after 0.3-0.5mm, brushing lies against steam curing
In slot, after being conserved 4-6 hours at 80 DEG C, lies against room temperature indoor environment 7-10 days and obtained after carrying out complete aquation gelling reaction
There is the glass of silver coating.
Specifically, cement base paint brush is applied on the modified tempered glass in surface, is brushed using the method manually brushed
Tempered glass afterwards is lain against in steam curing slot, and 525 cement start to generate aquation gelatification at this time, because of tempered glass table
There is the Al of a large amount of high activity in face2O3And Fe2O3Nano particle, in the hydration process of inorganic coating, part Al2O3And Fe2O3?
The Ca (OH) that grain can be generated with hydrated cementitious2Aluminic acid dicalcium and dicalcium ferrite are generated, cementitious coating and glass can be effectively improved
Binding force, obtaining surface has the glass of silver coating, and the glass is plate glass.
It is now detailed to a kind of method for glass preparation progress for having silver coating provided by the invention with specific embodiment
Explanation.
Embodiment 1
The present invention provides a kind of method for glass preparation for having silver coating, which is characterized in that the preparation method includes such as
Lower step:
Step 1: the preparation of Glass Surface Modification agent: by formula rate weigh a certain amount of silica solution and Aluminum sol and
FeCl3Solution pours into same container then under conditions of 6000 revs/min, stirs 1.5 hours at room temperature, adds boron
Sour powder continues to stir, and after boric acid is completely dissolved, adds waterglass, stirs 30 minutes under conditions of 6000 revs/min
Afterwards, stop stirring, obtain mixed solution, then mixed solution is fitted into closed container, obtain Glass Surface Modification agent;
In step 1, the formula of the Glass Surface Modification agent includes: the water that weight percent 10% and modulus are 2.8
The aluminium that the silica solution that glass, weight percent 55% and solid content are 10%, weight percent 20% and solid content are 15% is molten
Liquid, weight percent 12% and the FeCl that pH value is 1, concentration is 2mol/L3The boric acid of solution and weight percent 3%.
Step 2: Glass Surface Modification: by glass immersion in n-butanol, carrying out ultrasonic cleaning 10 with the frequency of 2000Hz
Zhong Hou is dried at room temperature for 2 hours, and it is 0.3mm that the Glass Surface Modification agent prepared by step 1, which is added to nozzle diameter,
And operating pressure be 1.2MPa air pressure spray gun in, the Glass Surface Modification agent is arrived with the air pressure spray gun even application
Glass surface is put into glass tempering furnace after the glass after spraying is then dried at room temperature for 20 hours, in air atmosphere
Under, by glass temperature from room temperature to 680 DEG C in 6 minutes, 3 minutes are kept the temperature, then glass is come out of the stove, is cooled down at room temperature,
Obtain the modified tempered glass in surface;
Step 3: cement base coating preparation: weighing the pure water, silica flour, aluminium powder, chlorination of certain mass by formula rate amount
The poly- second two of molecular weight 2000 is added in magnesium, polyethylene glycol and 525 cement under conditions of 400 revs/min into weighed pure water
Alcohol sequentially adds weighed magnesium chloride, aluminium powder and cement after stirring 30 minutes, and it is small that 1 is stirred under conditions of 600 revs/min
Shi Hou is added silica flour and stir 30 minutes under conditions of 600 revs/min again, acquisition cement base coating;
In step 3, the formula of the cement base coating includes: 525 cement of weight percent 45%, weight percent
Than 2% and the polyethylene glycol of molecular weight 2000, the magnesium chloride of weight percent 7%, weight percent 10-15% and particle diameter
Aluminium powder less than 50 microns, weight percent 15% and diameter 0.5-2mm silica flour and weight percent 21% it is pure
Water.
Step 4: prepared by cementitious coating: the cement base coating prepared by step 3 uniformly being brushed and is prepared in step 2
The modified tempered glass in surface on, tempered glass of the coating layer thickness control after 0.4mm, brushing lies against steam curing slot
In, after conserving 6 hours at 80 DEG C, lying against to obtain after carrying out within room temperature indoor environment 7 days complete aquation gelling reaction has silver color
The glass of coating.
A kind of glass for the method for glass preparation preparation for having silver coating that embodiment 1 provides, silver coating and glass
The combination interface pattern of glass is as shown in Figure 1.The microstructure of the silver coating of glass surface is as shown in Figure 2.
The invention has the following beneficial effects:
1, using Si (OH)4、Al(OH)3With Fe (OH)3Mixed sols carries out surface to glass and is modified, and collosol coating passes through
Tempering processing after, can and glass formed Si-O-Si and Al-O-Si key, can firmly be adhered to glass surface, when cementitious coating into
When row hydration process, the Al of the high activity of glass surface2O3And Fe2O3Nano particle can form aluminic acid dicalcium and iron with 525 cement
The inorganic glues condensate such as sour dicalcium, improves the binding force of cementitious coating and glass;
2, it using brushing method combination cement conservation curing process, can be applied in the silver color inorganic gel that glass surface is prepared
Layer material, coating are firmly combined with glass, and structure is cellular, and uneven, can generate the matt imitation stone dress of silver color
Adorn effect;
3, preparation process is simple, and cost prepares silver color glass lower than glass glazings technique;
4, coating is inorganic material, and aging phenomenon is not present compared with organic film material height in hardness.
Although the embodiments of the present invention have been disclosed as above, but it is not restricted to listed fortune in specification and embodiment
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily real
Now other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is not limited to
Specific details and the legend herein shown with description.
Claims (5)
1. a kind of method for glass preparation for having silver coating, which is characterized in that the preparation method includes the following steps:
Step 1: the preparation of Glass Surface Modification agent: weighing a certain amount of silica solution and Aluminum sol and FeCl by formula rate3It is molten
Liquid pours into same container then under conditions of 6000 revs/min, stirs 1-2 hours at room temperature, adds boric acid powder,
Continue to stir, after boric acid is completely dissolved, adds waterglass, after being stirred 20-30 minutes under conditions of 6000 revs/min,
Stop stirring, obtain mixed solution, then mixed solution is fitted into closed container, obtains Glass Surface Modification agent;
Step 2: Glass Surface Modification: by glass immersion in n-butanol, carrying out ultrasonic cleaning 5-10 clock with the frequency of 2000Hz
Afterwards, it is dried at room temperature for 1-2 hours, it is 0.2- that the Glass Surface Modification agent prepared by step 1, which is added to nozzle diameter,
0.3mm and operating pressure be in the air pressure spray gun of 0.8-1.2MPa, the Glass Surface Modification agent is equal with the air pressure spray gun
It is even to spray to glass surface, after the glass after spraying is then dried at room temperature for 20-24 hours, it is put into glass tempering furnace,
In air atmosphere, in 5-6 minutes by glass temperature from room temperature to 650-680 DEG C, 3-4 minutes are kept the temperature, then by glass
It comes out of the stove, cools down at room temperature, obtain the modified tempered glass in surface;
Step 3: cement base coating preparation: by formula rate amount weigh the pure water of certain mass, silica flour, aluminium powder, magnesium chloride,
The polyethylene glycol of molecular weight 2000 is added in polyethylene glycol and 525 cement under conditions of 400 revs/min into weighed pure water,
After stirring 20-30 minutes, weighed magnesium chloride, aluminium powder and cement are sequentially added, is stirred under conditions of 600 revs/min
After 0.5-1 hours, silica flour is added and stir 20-30 minutes under conditions of 600 revs/min again, acquisition cement base coating;
Step 4: prepared by cementitious coating: the cement base coating prepared by step 3 is uniformly brushed the table in step 2 preparation
On the modified tempered glass in face, tempered glass of the coating layer thickness control after 0.3-0.5mm, brushing lies against steam curing slot
In, after conserving 4-6 hours at 80 DEG C, lying against room temperature indoor environment 7-10 days after carrying out complete aquation gelling reaction is had
The glass of silver coating.
2. a kind of method for glass preparation for having silver coating as described in claim 1, which is characterized in that in step 1, institute
State the waterglass that formula includes: weight percent 10-15% and modulus is 2.8 of Glass Surface Modification agent, weight percent 50-
60% and solid content be 10% silica solution, the aluminum solutions that weight percent 10-20% and solid content are 15%, weight percent
The FeCl that 10-15% and pH value are 1, concentration is 2mol/L3The boric acid of solution and weight percent 2-3%.
3. a kind of method for glass preparation for having silver coating as claimed in claim 1 or 2, which is characterized in that in step 3,
The formula of the cement base coating includes: 525 cement of weight percent 40-45%, weight percent 1-2% and molecular weight
2000 polyethylene glycol, the magnesium chloride of weight percent 5-7%, weight percent 10-15% and particle diameter are less than 50 microns
Aluminium powder, weight percent 10-15% and diameter is in the silica flour of 0.5-2mm and the pure water of weight percent 20-30%.
4. a kind of method for glass preparation for having silver coating as described in claim 1, which is characterized in that in step 4, institute
Cement base coating is stated uniformly to brush on the tempered glass using the method manually brushed.
5. a kind of method for glass preparation for having silver coating as described in claim 1, which is characterized in that the glass is plate
Glass.