CN109263386A - Extraordinary anti-stain connection with production of structures technique - Google Patents
Extraordinary anti-stain connection with production of structures technique Download PDFInfo
- Publication number
- CN109263386A CN109263386A CN201811252714.6A CN201811252714A CN109263386A CN 109263386 A CN109263386 A CN 109263386A CN 201811252714 A CN201811252714 A CN 201811252714A CN 109263386 A CN109263386 A CN 109263386A
- Authority
- CN
- China
- Prior art keywords
- texture
- stain
- production
- connection
- angle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of extraordinary anti-stain connection with production of structures technique, include following steps: (1) forming texture particle in die surface, it designs between 3mm-5mm at the angle R of texture particle, texture particle is two layers, first layer texture granular size is between 0.5mm-10mm, and the second layer texture granular size is between 0.3mm-0.5mm；The angle R of two layer texture particles is the re-entrant angle between 3-5mm.(2) die surface is corroded using chemical medicinal liquid, total depth controls between 45 μm -50 μm；(3) luminosity adjustment is carried out to die surface, surface luminous intensity is 6-8 °.Specific texture is formed in mold by using present invention process, the product molded has good scoring resistance energy in routine use, scratch resistant is not in bright trace, greatly promotes the aesthetics of product, and residual stains are not easy after long-time use on texture, it is easy to clean.
Description
Technical field
The present invention relates to die surface machining field technologies, refer in particular to a kind of extraordinary anti-stain connection with production of structures work
Skill.
Background technique
In order to make product reach the purpose of beauty, the surface of current many products forms textured, is forming these
When the product of belt surface texture, need to design corresponding texture in mold.However, due to grain design meeting in current mold
The product for causing existing surface textured, easily scratches in routine use, is easy to produce scuffing, bright trace occurs, influences beauty
It sees, is easy residual stains, and difficult cleaning in grain surface after long-time use.
Summary of the invention
In view of this, in view of the deficiencies of the prior art, the present invention aims to provide a kind of extraordinary anti-stains
Connection with production of structures technique, can effectively solve the textured product in existing surface has not anti-stain not scratch resistant.
To achieve the above object, the present invention is using following technical solution:
A kind of special type anti-stain connection with production of structures technique, includes following steps:
(1) texture particle being formed in die surface, the angle R of texture particle is designed between 3mm-5mm, and texture particle is two layers,
First layer texture granular size is between 0.5mm-10mm, and the second layer texture granular size is between 0.3mm-0.5mm；
(2) die surface is corroded using chemical medicinal liquid, total depth controls between 45 μm -50 μm；
(3) luminosity adjustment is carried out to die surface, surface luminous intensity is 6-8 °.
As a preferred embodiment, in the step (1), the angle R of two layer texture particles is the re-entrant angle between 3-5mm.
As a preferred embodiment, the luminosity adjustment uses bead and aluminium oxide to mix according to mass ratio for 6:1 and sprays
Sand.
As a preferred embodiment, the bead is 150# bead, which is 220# aluminium oxide.
The present invention has obvious advantages and beneficial effects compared with the existing technology, specifically, by above-mentioned technical proposal
Known to:
Specific texture is formed in mold by using present invention process, the product molded has in routine use
There is good scoring resistance energy, scratch resistant is not in bright trace, greatly promotes the aesthetics of product, and after long-time use
Residual stains are not easy on texture, it is easy to clean.
Specific embodiment
Present invention discloses a kind of extraordinary anti-stain connection with production of structures techniques, include following steps:
(1) texture particle being formed in die surface, the angle R of texture particle is designed between 3mm-5mm, and texture particle is two layers,
First layer texture granular size is between 0.5mm-10mm, and the second layer texture granular size is between 0.3mm-0.5mm.In this reality
It applies in example, the angle R of two layer texture particles is the re-entrant angle between 3-5mm.
(2) die surface is corroded using chemical medicinal liquid, total depth controls between 45 μm -50 μm.
(3) luminosity adjustment is carried out to die surface, surface luminous intensity is 6-8 °.In the present embodiment, the luminosity adjustment is adopted
It according to mass ratio is 6:1 mixing sandblasting with bead and aluminium oxide, also, the bead is 150# bead, the aluminium oxide
For 220# aluminium oxide.
By using the mold shaped article of above-mentioned technique production, product surface after molding forms anti-stain texture, surveys
When examination, after the dirts such as ink are sprinkled upon product surface, if being rinsed at once with clear water, dirt is immediately removed, if after dirt is solid
It cleans again, only needs dirt can be completely removed in bath with brush brush, will not leave behind any mark, it will not scratching products
Surface texture.So that the surface of product achievees the effect that anti-stain, anti scuffing.
Design focal point of the invention is: forming specific texture in mold by using present invention process, forms
Product out, has good scoring resistance energy in routine use, and scratch resistant is not in bright trace, greatly promotes product
Aesthetics, and residual stains are not easy on texture after long-time use, it is easy to clean.
The above described is only a preferred embodiment of the present invention, be not intended to limit the scope of the present invention,
Therefore any subtle modifications, equivalent variations and modifications to the above embodiments according to the technical essence of the invention, still
Belong in the range of technical solution of the present invention.
Claims (4)
1. a kind of special type anti-stain connection with production of structures technique, it is characterised in that: include following steps:
(1) texture particle being formed in die surface, the angle R of texture particle is designed between 3mm-5mm, and texture particle is two layers,
First layer texture granular size is between 0.5mm-10mm, and the second layer texture granular size is between 0.3mm-0.5mm；
(2) die surface is corroded using chemical medicinal liquid, total depth controls between 45 μm -50 μm；
(3) luminosity adjustment is carried out to die surface, surface luminous intensity is 6-8 °.
2. special type anti-stain connection with production of structures technique according to claim 1, it is characterised in that: in the step (1), two layers
The angle R of texture particle is the re-entrant angle between 3-5mm.
3. special type anti-stain connection with production of structures technique according to claim 1, it is characterised in that: the luminosity adjustment uses glass
Glass pearl and aluminium oxide are 6:1 mixing sandblasting according to mass ratio.
4. special type anti-stain connection with production of structures technique according to claim 1, it is characterised in that: the bead is 150# glass
Glass pearl, the aluminium oxide are 220# aluminium oxide.