CN109263263A - A kind of technique forming stone pattern effect on film - Google Patents
A kind of technique forming stone pattern effect on film Download PDFInfo
- Publication number
- CN109263263A CN109263263A CN201811223932.7A CN201811223932A CN109263263A CN 109263263 A CN109263263 A CN 109263263A CN 201811223932 A CN201811223932 A CN 201811223932A CN 109263263 A CN109263263 A CN 109263263A
- Authority
- CN
- China
- Prior art keywords
- film
- glue
- stone pattern
- pattern effect
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to molding production technical field, more particularly to it is a kind of on film form stone pattern effect technique, should on film form stone pattern effect technique include: include: step 1, stock；Step 2 prints white-substrate ink；Step 3 is toasted for the first time；Step 4 prints the solid of AB glue；Step 5, second of baking；Step 6, colour mixture；Step 7, oil pressure molding；Step 8, punching；The technique that stone pattern effect is formed on film can mold nature stone pattern effect, not only being able to satisfy plane effect but also being able to achieve straight flange and inner wall has stone pattern effect, and the molding stone pattern of institute has good wear-resisting property, and film is adhered well on silica gel.This forms the technique of stone pattern effect on film, has simple process, and production cost is low, and can be suitable for the characteristics of being mass produced.
Description
Technical field
The present invention relates to molding production technical fields, more particularly to a kind of technique for forming stone pattern effect on film.
Background technique
Application of the silica gel in electronic accessory parts field is extremely wide and well known, by mold oil pressure or is molded into
Various electronic components or peripheral product is made in type.
Currently, the general production technology of silica gel product in the market are as follows: by silica gel and mill base colour mixture, be placed in Die Oil and be pressed into
Type then carries out polishing etc. obtaining product, but this method come out effect and color it is relatively simple, it is difficult to meet client's
Demand, especially current oil pressure moulding process, it is difficult to form stone pattern effect.Even if stone pattern can be formed using printing technology
Effect, still, printing technology can only meet plane effect but and straight flange and inner wall cannot be achieved with stone pattern effect, in addition print work
The wear-resisting property for the stone pattern that skill is formed is poor, therefore, needs to seek new technical solution.
Summary of the invention
It is an object of the invention to provide one kind aiming at the deficiencies in the prior art and form stone pattern effect on film
The technique of fruit, the technique that stone pattern effect should be formed on film can mold nature stone pattern effect, not only be able to satisfy plane effect
It fruit and is able to achieve straight flange and inner wall there is stone pattern effect, and the molding stone pattern of institute has good wear-resisting property.
In order to achieve the above objectives, the present invention is achieved through the following technical solutions.
There is provided it is a kind of on film form stone pattern effect technique, it the following steps are included:
Step 1, stock: taking two different colors of mill base to carry out colour mixture with AB glue respectively, is formed two different colors of
AB glue；
Step 2 prints white-substrate ink: carrying out printing white ink to the reverse side of film；
Step 3 is toasted for the first time: the film for printing white ink to step 2 carries out baking and curing；
Step 4 prints the solid of AB glue: the film that step 3 is cured is sent to printing machine, to the front of film
Print the solid of AB glue；
Step 5, second toasts: the film of the solid of the AB glue printed to step 4 carries out baking and curing；
Step 6, colour mixture: the two different colors of AB glue that step 1 is obtained mixes by a certain percentage, and rotation is stirred
It mixes, so that two kinds of colors are mutually mixed clearly forms flow liner, the AB glue mixed；
Step 7, oil pressure molding: the AB glue that step 6 is mixed is applied to one that film printing has the solid of AB glue
Then face carries out oil pressure molding, obtain the film with stone pattern effect；
Punching: the step 7 oil pressure molding film with stone pattern effect is cut into the product of corresponding specification by step 8.
It further include step 9, rubberizing paper: the product that step 8 is obtained is in its white-substrate ink face paste in above-mentioned technical proposal
Sized paper, the protective film in stone pattern effect face paste.
In above-mentioned technical proposal, in the step 2, print white-substrate ink: using automatic volume print machine to the reverse side of film into
Row printing white ink, is rolled up print machine in printing automatically and is carried out driving to printing zone with the speed of 25cm/s~35cm/s.
In above-mentioned technical proposal, in the step 3, toasts for the first time: printing the film of white ink to step 2,
Baking and curing is carried out using infrared drying line, drying temperature is 90 DEG C~110 DEG C, and drying time is 10min~20min.
In above-mentioned technical proposal, in the step 4, print the solid of AB glue: the film that step 3 is cured transmits
To printing machine, to the solid of the front printing AB glue of film, when printing the solid of AB glue with 25cm/s~35cm/s's
Speed carries out driving to printing zone.
In above-mentioned technical proposal, in the step 5, second is toasted: the solid of the AB glue printed to step 4
Film carries out baking and curing using infrared drying line, and drying temperature is 90 DEG C~110 DEG C, and drying time is 10min~20min.
In above-mentioned technical proposal, in the step 6, colour mixture: the two different colors of AB glue that step 1 is obtained is by 8
~12:1 is mixed, Stirring, so that two kinds of colors are mutually mixed clearly forms flow liner, the AB glue mixed.
In above-mentioned technical proposal, in the step 7, the molding temperature of oil pressure is 100 DEG C~120 DEG C, the oil pressure
The molding time is 1min~4min.
Beneficial effects of the present invention:
(1) a kind of technique that stone pattern effect is formed on film provided by the invention, comprising: step 1, stock；Step
Two, print white-substrate ink；Step 3 is toasted for the first time；Step 4 prints the solid of AB glue；Step 5, second of baking；
Step 6, colour mixture；Step 7, oil pressure molding；Step 8, punching；The technique that stone pattern effect is formed on film can form
Nature stone pattern effect out, being not only able to satisfy plane effect but also being able to achieve straight flange and inner wall has stone pattern effect, and is formed
Stone pattern there is good wear-resisting property, and film is adhered well on silica gel.
(2) a kind of technique that stone pattern effect is formed on film provided by the invention, realizes and carries out silica gel on film
Oil pressure forms the pattern of stone pattern effect, forms the patterning process of nature flowing in whole layer of silica gel, has only intervened in advance and thought
The default floral designs wanted, that is, be previously determined floral designs position and rough shape, but AB glue mobility when because of oil pressure
Uncertain factor so that formed pattern effect be similar to nature evolution so which form a kind of combination certainty with
The decalcomania of uncertainty design, therefore a kind of natural stone pattern effect is formd, pattern is unique, exquisiteness is enriched, into
And the silica gel material with natural stone pattern effect more naturally true to nature is obtained, and can be used for various electronic accessory parts or periphery
Product.
(3) a kind of technique that stone pattern effect is formed on film provided by the invention, has simple process, production cost
It is low, and the characteristics of being mass produced can be suitable for.
Specific embodiment
In order to which the technical problems, technical solutions and beneficial effects solved by the present invention is more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only used to explain
The present invention is not intended to limit the present invention.
Embodiment 1.
The present embodiment it is a kind of on film form stone pattern effect technique, it the following steps are included:
Step 1, stock: taking two different colors of mill base to carry out colour mixture with AB glue respectively, is formed two different colors of
AB glue；
Step 2 prints white-substrate ink: carrying out printing white ink to the reverse side of film using automatic volume print machine, is printing
Shi Zidong volumes of print machine carries out driving to printing zone with the speed of 30cm/s；
Step 3 is toasted for the first time: printing the film of white ink to step 2, dried using infrared drying line
Solidification, drying temperature are 100 DEG C, drying time 15min；
Step 4 prints the solid of AB glue: the film that step 3 is cured is sent to printing machine, to the front of film
The solid for printing AB glue carries out driving to printing zone with the speed of 30cm/s when printing the solid of AB glue；
Step 5, second toasts: the film of the solid of the AB glue printed to step 4, using infrared drying line into
Row baking and curing, drying temperature are 100 DEG C, drying time 15min；
Step 6, colour mixture: the two different colors of AB glue that step 1 is obtained is mixed by 10:1, Stirring,
So that two kinds of colors are mutually mixed clearly forms flow liner, the AB glue mixed；
Step 7, oil pressure molding: the AB glue that step 6 is mixed is applied to one that film printing has the solid of AB glue
Then face carries out oil pressure molding, obtain the film with stone pattern effect；In the present embodiment, the molding temperature of oil pressure is 110 DEG C,
The oil pressure molding time is 2min；
Punching: the step 7 oil pressure molding film with stone pattern effect is cut into the product of corresponding specification by step 8.
Embodiment 2.
The present embodiment it is a kind of on film form stone pattern effect technique, it the following steps are included:
Step 1, stock: taking two different colors of mill base to carry out colour mixture with AB glue respectively, is formed two different colors of
AB glue；
Step 2 prints white-substrate ink: carrying out printing white ink to the reverse side of film using automatic volume print machine, is printing
Shi Zidong volumes of print machine carries out driving to printing zone with the speed of 25cm/s；
Step 3 is toasted for the first time: printing the film of white ink to step 2, dried using infrared drying line
Solidification, drying temperature are 90 DEG C, drying time 20min；
Step 4 prints the solid of AB glue: the film that step 3 is cured is sent to printing machine, to the front of film
The solid for printing AB glue carries out driving to printing zone with the speed of 25cm/s when printing the solid of AB glue；
Step 5, second toasts: the film of the solid of the AB glue printed to step 4, using infrared drying line into
Row baking and curing, drying temperature are 90 DEG C, drying time 20min；
Step 6, colour mixture: the two different colors of AB glue that step 1 is obtained is mixed by 8:1, and Stirring makes
Two kinds of colors clearly mutually mix form flow liner, the AB glue mixed；
Step 7, oil pressure molding: the AB glue that step 6 is mixed is applied to one that film printing has the solid of AB glue
Then face carries out oil pressure molding, obtain the film with stone pattern effect；In the present embodiment, the molding temperature of oil pressure is 100 DEG C,
The oil pressure molding time is 4min；
Punching: the step 7 oil pressure molding film with stone pattern effect is cut into the product of corresponding specification by step 8；
Step 9, rubberizing paper: the product that step 8 is obtained is in its white-substrate ink face paste sized paper, in stone pattern effect face paste
Upper protective film.
Embodiment 3.
The present embodiment it is a kind of on film form stone pattern effect technique, it the following steps are included:
Step 1, stock: taking two different colors of mill base to carry out colour mixture with AB glue respectively, is formed two different colors of
AB glue；
Step 2 prints white-substrate ink: carrying out printing white ink to the reverse side of film using automatic volume print machine, is printing
Shi Zidong volumes of print machine carries out driving to printing zone with the speed of 35cm/s；
Step 3 is toasted for the first time: printing the film of white ink to step 2, dried using infrared drying line
Solidification, drying temperature are 110 DEG C, drying time 10min；
Step 4 prints the solid of AB glue: the film that step 3 is cured is sent to printing machine, to the front of film
The solid for printing AB glue carries out driving to printing zone with the speed of 35cm/s when printing the solid of AB glue；
Step 5, second toasts: the film of the solid of the AB glue printed to step 4, using infrared drying line into
Row baking and curing, drying temperature are 110 DEG C, drying time 10min；
Step 6, colour mixture: the two different colors of AB glue that step 1 is obtained is mixed by 12:1, Stirring,
So that two kinds of colors are mutually mixed clearly forms flow liner, the AB glue mixed；
Step 7, oil pressure molding: the AB glue that step 6 is mixed is applied to one that film printing has the solid of AB glue
Then face carries out oil pressure molding, obtain the film with stone pattern effect；In the present embodiment, the molding temperature of oil pressure is 120 DEG C,
The oil pressure molding time is 1min；
Punching: the step 7 oil pressure molding film with stone pattern effect is cut into the product of corresponding specification by step 8；
Step 9, rubberizing paper: the product that step 8 is obtained is in its white-substrate ink face paste sized paper, in stone pattern effect face paste
Upper protective film.
Embodiment 4.
The present embodiment it is a kind of on film form stone pattern effect technique, it the following steps are included:
Step 1, stock: taking two different colors of mill base to carry out colour mixture with AB glue respectively, is formed two different colors of
AB glue；
Step 2 prints white-substrate ink: carrying out printing white ink to the reverse side of film using automatic volume print machine, is printing
Shi Zidong volumes of print machine carries out driving to printing zone with the speed of 28cm/s；
Step 3 is toasted for the first time: printing the film of white ink to step 2, dried using infrared drying line
Solidification, drying temperature are 95 DEG C, drying time 18min；
Step 4 prints the solid of AB glue: the film that step 3 is cured is sent to printing machine, to the front of film
The solid for printing AB glue carries out driving to printing zone with the speed of 28cm/s when printing the solid of AB glue；
Step 5, second toasts: the film of the solid of the AB glue printed to step 4, using infrared drying line into
Row baking and curing, drying temperature are 95 DEG C, drying time 18min；
Step 6, colour mixture: the two different colors of AB glue that step 1 is obtained is mixed by 9:1, and Stirring makes
Two kinds of colors clearly mutually mix form flow liner, the AB glue mixed；
Step 7, oil pressure molding: the AB glue that step 6 is mixed is applied to one that film printing has the solid of AB glue
Then face carries out oil pressure molding, obtain the film with stone pattern effect；In the present embodiment, the molding temperature of oil pressure is 105 DEG C,
The oil pressure molding time is 3min；
Punching: the step 7 oil pressure molding film with stone pattern effect is cut into the product of corresponding specification by step 8；
Step 9, rubberizing paper: the product that step 8 is obtained is in its white-substrate ink face paste sized paper, in stone pattern effect face paste
Upper protective film.
Embodiment 5.
The present embodiment it is a kind of on film form stone pattern effect technique, it the following steps are included:
Step 1, stock: taking two different colors of mill base to carry out colour mixture with AB glue respectively, is formed two different colors of
AB glue；
Step 2 prints white-substrate ink: carrying out printing white ink to the reverse side of film using automatic volume print machine, is printing
Shi Zidong volumes of print machine carries out driving to printing zone with the speed of 33cm/s；
Step 3 is toasted for the first time: printing the film of white ink to step 2, dried using infrared drying line
Solidification, drying temperature are 105 DEG C, drying time 12min；
Step 4 prints the solid of AB glue: the film that step 3 is cured is sent to printing machine, to the front of film
The solid for printing AB glue carries out driving to printing zone with the speed of 33cm/s when printing the solid of AB glue；
Step 5, second toasts: the film of the solid of the AB glue printed to step 4, using infrared drying line into
Row baking and curing, drying temperature are 105 DEG C, drying time 12min；
Step 6, colour mixture: the two different colors of AB glue that step 1 is obtained is mixed by 11:1, Stirring,
So that two kinds of colors are mutually mixed clearly forms flow liner, the AB glue mixed；
Step 7, oil pressure molding: the AB glue that step 6 is mixed is applied to one that film printing has the solid of AB glue
Then face carries out oil pressure molding, obtain the film with stone pattern effect；In the present embodiment, the molding temperature of oil pressure is 115 DEG C,
The oil pressure molding time is 1.5min；
Punching: the step 7 oil pressure molding film with stone pattern effect is cut into the product of corresponding specification by step 8；
Step 9, rubberizing paper: the product that step 8 is obtained is in its white-substrate ink face paste sized paper, in stone pattern effect face paste
Upper protective film.
Finally it should be noted that the above examples are only used to illustrate the technical scheme of the present invention rather than protects to the present invention
The limitation of range, although the invention is described in detail with reference to the preferred embodiments, those skilled in the art should be managed
Solution, can with modification or equivalent replacement of the technical solution of the present invention are made, without departing from technical solution of the present invention essence and
Range.
Claims (8)
1. it is a kind of on film form stone pattern effect technique, it is characterised in that: it the following steps are included:
Stock: step 1 takes two different colors of mill base to carry out colour mixture with AB glue respectively, forms two different colors of AB
Glue；
Step 2 prints white-substrate ink: carrying out printing white ink to the reverse side of film；
Step 3 is toasted for the first time: the film for printing white ink to step 2 carries out baking and curing；
Step 4 prints the solid of AB glue: the film that step 3 is cured is sent to printing machine, prints to the front of film
The solid of AB glue；
Step 5, second toasts: the film of the solid of the AB glue printed to step 4 carries out baking and curing；
Step 6, colour mixture: the two different colors of AB glue that step 1 is obtained mixes by a certain percentage, Stirring,
So that two kinds of colors are mutually mixed clearly forms flow liner, the AB glue mixed；
Step 7, oil pressure molding: the AB glue that step 6 is mixed is applied to the one side that film printing has the solid of AB glue, so
Oil pressure molding is carried out afterwards, obtains the film with stone pattern effect；
Punching: the step 7 oil pressure molding film with stone pattern effect is cut into the product of corresponding specification by step 8.
2. a kind of technique for forming stone pattern effect on film according to claim 1, it is characterised in that: further include step
Nine, rubberizing paper: the product that step 8 is obtained is in its white-substrate ink face paste sized paper, the protective film in stone pattern effect face paste.
3. a kind of technique for forming stone pattern effect on film according to claim 1, it is characterised in that: the step 2
In, it prints white-substrate ink: printing white ink being carried out to the reverse side of film using automatic volume print machine, rolls up print machine automatically in printing
It carries out driving to printing zone with the speed of 25cm/s~35cm/s.
4. a kind of technique for forming stone pattern effect on film according to claim 1, it is characterised in that: the step 3
In, it toasts for the first time: printing the film of white ink to step 2, carry out baking and curing, drying temperature using infrared drying line
Degree is 90 DEG C~110 DEG C, and drying time is 10min~20min.
5. a kind of technique for forming stone pattern effect on film according to claim 1, it is characterised in that: the step 4
In, print the solid of AB glue: the film that step 3 is cured is sent to printing machine, prints connecing for AB glue to the front of film
Agent, print AB glue solid when carry out driving to printing zone with the speed of 25cm/s~35cm/s.
6. a kind of technique for forming stone pattern effect on film according to claim 1, it is characterised in that: the step 5
In, second toasts: the film of the solid of the AB glue printed to step 4 carries out baking and curing using infrared drying line,
Drying temperature is 90 DEG C~110 DEG C, and drying time is 10min~20min.
7. a kind of technique for forming stone pattern effect on film according to claim 1, it is characterised in that: the step 6
In, colour mixture: the two different colors of AB glue that step 1 is obtained is mixed by 8~12:1, Stirring, so that two kinds of face
Color mutually mixes clearly and forms flow liner, the AB glue mixed.
8. a kind of technique for forming stone pattern effect on film according to claim 1, it is characterised in that: the step 7
In, the molding temperature of oil pressure is 100 DEG C~120 DEG C, and the oil pressure molding time is 1min~4min.