CN109262374A - A kind of die casting surface drawing process - Google Patents
A kind of die casting surface drawing process Download PDFInfo
- Publication number
- CN109262374A CN109262374A CN201710699408.6A CN201710699408A CN109262374A CN 109262374 A CN109262374 A CN 109262374A CN 201710699408 A CN201710699408 A CN 201710699408A CN 109262374 A CN109262374 A CN 109262374A
- Authority
- CN
- China
- Prior art keywords
- die casting
- plated film
- drawing process
- casting surface
- process according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of process for treating surface, in particular disclose a kind of technique of die casting surface wire drawing, including step 1: preparing die casting；Step 2: die casting is subjected to plated film；Step 3: the die casting surface after plated film is subjected to wire drawing；Step 4: the die casting after wire drawing after plated film is subjected to anode oxidation coloration and obtains the die casting with drawing pattern of required color.Then the present invention carries out wire drawing, anode oxidation coloration, obtains the die casting with drawing pattern of required color, product is beautiful and generous, has good metal wire-drawing texture by carrying out plated film to common die casting.
Description
Technical field:
The present invention relates to process for treating surface, in particular to a kind of die casting surface drawing process.
Background technique:
Die casting refers to the metal materials such as aluminum or aluminum alloy, magnesium or magnesium alloy, zinc and plastic cement etc., carries out melting,
Then it is cast by mold, the technique of extrusion forming.The consumer electronics products such as mobile phone, metal shell of IT product etc. are matched
Part much uses drawing process, but such product is the materials such as raffinal or stainless steel to increase the aesthetics of product
Expect first shell molds, then wire drawing, material, processing cost are high.
Summary of the invention:
The object of the present invention is to provide a kind of die casting surface drawing process, cause material, processing for solving the prior art
Disadvantage with high costs, in order to achieve the above object, the technical solution of the present invention is as follows:
A kind of die casting surface drawing process, comprising:
Step 1 prepares die casting；
Die casting is carried out plated film by step 2；
Die casting surface after plated film is carried out wire drawing by step 3；
Step 4, by after wire drawing after plated film die casting carry out anode oxidation coloration obtain required color have drawing pattern
Die casting.
The die casting can be aluminum or Al-alloy parts.
The die casting can be magnesia or magnesium alloy member.
The die casting can be plastic parts.
The plated film is aluminizer.
The plated film is plating titanium film.
The thickness of the plated film is between 0.01~0.2mm.
The method of the plated film is vacuum plating.
The drawing pattern can be the wire drawing lines of circular ring shape, linear or other geometric figures.
The invention has the advantages that being solved by the processing for preparing die casting, plated film, wire drawing, anode oxidation coloration
The high disadvantage of material, processing cost, product is exquisite beautiful, with good metal wire-drawing texture, adapt to market and consumption
The demand of person.
Specific embodiment:
Embodiments of the present invention are further illustrated by the following examples:
Embodiment one:
A kind of die casting surface drawing process, comprising:
Step 1 prepares aluminum die-casting part；
Aluminum die-casting part is carried out plated film by step 2；
Aluminum die-casting part surface after plated film is carried out wire drawing by step 3；
Aluminum die-casting part after wire drawing after plated film is carried out anode oxidation coloration, obtains having for required color by step 4
The aluminum die-casting part of drawing pattern.
The plated film is aluminizer.
The thickness of the plated film is between 0.01~0.2mm.
The method of the plated film is vacuum plating.
The drawing pattern can be the wire drawing lines of circular ring shape, linear or other geometric figures.
Embodiment two:
A kind of die casting surface drawing process, comprising:
Step 1 prepares aluminum alloy die casting；
Aluminum alloy die casting is carried out plated film by step 2；
Aluminum alloy die casting surface after plated film is carried out wire drawing by step 3；
Aluminum alloy die casting after wire drawing after plated film is carried out anode oxidation coloration, obtains the tool of required color by step 4
There is the aluminum alloy die casting of drawing pattern.
The plated film is aluminizer.
The thickness of the plated film is between 0.01~0.2mm.
The method of the plated film is vacuum plating.
The drawing pattern can be the wire drawing lines of circular ring shape, linear or other geometric figures.
Embodiment three:
A kind of die casting surface drawing process, comprising:
Step 1 prepares magnesia die casting；
Magnesia die casting is carried out plated film by step 2；
Magnesia die casting surface after plated film is carried out wire drawing by step 3；
Magnesia die casting after wire drawing after plated film is carried out anode oxidation coloration, obtains having for required color by step 4
The magnesia die casting of drawing pattern.
The plated film is aluminizer.
The thickness of the plated film is between 0.01~0.2mm.
The method of the plated film is vacuum plating.
The drawing pattern can be the wire drawing lines of circular ring shape, linear or other geometric figures.
Example IV:
A kind of die casting surface drawing process, comprising:
Step 1 prepares magnesium alloy die casting；
Magnesium alloy die casting is carried out plated film by step 2；
Magnesium alloy die casting surface after plated film is carried out wire drawing by step 3；
Step 4: the magnesium alloy die casting after wire drawing after plated film is subjected to anode oxidation coloration, obtains the tool of required color
There is the magnesium alloy die casting of drawing pattern.
The plated film is aluminizer.
The thickness of the plated film is between 0.01~0.2mm.
The method of the plated film is vacuum plating.
The drawing pattern can be the wire drawing lines of circular ring shape, linear or other geometric figures.
Embodiment five:
A kind of die casting surface drawing process, comprising:
Step 1 prepares plastic cement die casting；
Plastic cement die casting is carried out plated film by step 2；
Plastic cement die casting surface after plated film is carried out wire drawing by step 3；
Plastic cement die casting after plated film wire drawing is carried out anode oxidation coloration by step 4, is obtained having for required color and is drawn
The plastic cement die casting of silking.
The plated film is aluminizer.
The thickness of the plated film is between 0.01~0.2mm.
The method of the plated film is vacuum plating.
The drawing pattern can be the wire drawing lines of circular ring shape, linear or other geometric figures.
Embodiment six:
A kind of die casting surface drawing process, comprising:
Step 1 prepares magnesium alloy die casting；
Magnesium alloy die casting is carried out plated film by step 2；
Plastic cement die casting surface after plated film is carried out wire drawing by step 3；
Plastic cement die casting after plated film wire drawing is carried out anode oxidation coloration by step 4, is obtained having for required color and is drawn
The plastic cement die casting of silking.
The plated film is plating titanium film.
The thickness of the plated film is between 0.01~0.2mm.
The method of the plated film is vacuum plating.
The drawing pattern can be the wire drawing lines of circular ring shape, linear or other geometric figures.
Embodiment described above is merely illustrative of the invention's technical idea and feature, and the description thereof is more specific and detailed,
Its object is to make those skilled in the art can understand the content of the present invention and implement it accordingly, therefore cannot be only with this
To limit the scope of the patents of the invention, it is noted that for those of ordinary skill in the art, do not departing from this hair
Under the premise of bright design, various modifications and improvements can be made, i.e., all any modifications made according to an embodiment of the present invention, etc.
With variation and modification, in the range of still falling within technical solution of the present invention.
Claims (9)
1. a kind of die casting surface drawing process, it is characterised in that: including
Step 1 prepares die casting；
Die casting is carried out plated film by step 2；
Die casting surface after plated film is carried out wire drawing by step 3；
Die casting after wire drawing after plated film is carried out anode oxidation coloration and obtains the pressure with drawing pattern of required color by step 4
Casting.
2. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the die casting be aluminum or
Al-alloy parts.
3. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the die casting be it is magnesia or
Magnesium alloy member.
4. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the die casting is plastic cement
Part.
5. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the plated film is aluminizer.
6. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the plated film is plating titanium film.
7. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the thickness of the plated film exists
Between 0.01~0.2mm.
8. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the method for the plated film is true
Dummy plating.
9. a kind of die casting surface drawing process according to claim 1, it is characterised in that: the drawing pattern can be circle
The lines of annular, linear or other geometric figures.