CN109251554A - Chromoplastic material process recipe - Google Patents
Chromoplastic material process recipe Download PDFInfo
- Publication number
- CN109251554A CN109251554A CN201811401786.2A CN201811401786A CN109251554A CN 109251554 A CN109251554 A CN 109251554A CN 201811401786 A CN201811401786 A CN 201811401786A CN 109251554 A CN109251554 A CN 109251554A
- Authority
- CN
- China
- Prior art keywords
- chromoplastic
- accounts
- chromoplastic material
- mass percent
- colour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of chromoplastic material process recipe, the chromoplastic material is by plastic body, colour-changing agent, photochromic material, oxidant and combination of stabilizers form, the photochromic material is that spiral shell adjoins class material of muttering, the plastic body accounts for the 35%-50% of the chromoplastic material mass percent, the colour-changing agent accounts for the 10%-15% of the chromoplastic material mass percent, the photochromic material accounts for the 5%-10% of the chromoplastic material mass percent, the oxidant accounts for the 3%-5% of the chromoplastic material mass percent, the stabilizer accounts for the 35%-40% of the chromoplastic material mass percent.The present invention provides a kind of chromoplastic material, has the advantages that nontoxic and beautiful novel.
Description
Technical field
The present invention relates to a kind of chromoplastic material process recipe more particularly to a kind of chromoplastic materials of life.
Background technique
Plastics are the high-molecular compound { polymer (polymer) } of synthesis, and can be described as macromolecule or giant molecule
(macromolecules), the plastics (plastics) or resin (resin) and being generally commonly called as, can freely change body
Pattern.It is the material using raw material monomer to synthesize or condensation reaction is polymerized, by synthetic resin and filler, plasticizer, steady
Determine the additives such as agent, lubricant, colorant composition.According to American Society for Testing Materials's definition, plastics be it is a kind of with
High molecular weight organic substancess material as main component, solid shape is presented when completing the process for it, manufacture and it is processed
Cheng Zhong can borrow flowing (flow) to carry out moulding.Therefore, thus illustrated that we understand available following items:
1. it is macromolecular organic compound,
2. it can exist such as liquid solid colloidal solution with a variety of kenels,
3. it can shape (moldable),
4. it is many kinds of, because different monomers and its composition can synthesize different plastics,
5. diversification is presented in widely used product.
6. having different property.
7. different processing methods (processing method) can be used, plastics and the two nouns of resin are also often mixed.Modeling
Material can divide into thermosetting property and two class of thermoplasticity, the former can not refigure use, the latter can duplication of production again and again.Plastics high score
There are two types of types substantially for the structure of son: the first is linear structure；Second is three-dimensional-structure.
Summary of the invention
The present invention provides a kind of chromoplastic material, has the advantages that nontoxic and beautiful novel.
The technical scheme is that the chromoplastic material is by plastic body, colour-changing agent, photochromic material, oxygen
Agent and combination of stabilizers form, and the photochromic material is that spiral shell adjoins class material of muttering, and the plastic body accounts for described
The 35%-50% of chromoplastic material mass percent, the colour-changing agent account for the 10%- of the chromoplastic material mass percent
15%, the photochromic material accounts for the 5%-10% of the chromoplastic material mass percent, and the oxidant accounts for institute
The 3%-5% for the chromoplastic material mass percent stated, the stabilizer account for the 35%- of the chromoplastic material mass percent
40%.
In a preferred embodiment of the invention, the stabilizer is liquid calcium zinc stabilizer, is in pale yellowish oil
Liquid.
In a preferred embodiment of the invention, the plastic body accounts for the chromoplastic material amount percentage
50%, the colour-changing agent accounts for the 10% of the chromoplastic material amount percentage, and the photochromic material accounts for the change
The 10% of color amount of plastic percentage, the stabilizer account for the 30% of the chromoplastic material amount percentage.
Specific embodiment
The preferred embodiments of the present invention will be described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
Wherein, the stabilizer is liquid calcium zinc stabilizer, is in pale yellowish oil liquid.Zinc stabilizer is by calcium salt, zinc
Salt, lubricant, antioxidant etc. are that main component is synthesized using special combination process.It can not only replace lead cadmium salt class and have
The toxic stabilizers such as machine tin class, and there is fairly good thermal stability, photostability and the transparency and tinting strength, tinting power.Practice card
Bright, in polyvinyl chloride resin product, processing performance is good, and heat stabilization is equivalent to lead salt stabilizer, is a kind of good nontoxic steady
Determine agent.Liquid calcium zinc stabilizer usually has biggish solubility, and has good dispersibility in PVC resin powder, to saturating
The influence of lightness is also far smaller than powder stabilizer.But the risk that liquid stabilisers have precipitation is larger.It needs to select to be suitble to
Solvent.There are a good dispersibility, compatibility, processing fluidity, wide adaptability, product surface finish is excellent；Thermal stability is excellent
Good, initial stage form and aspect are small, no precipitation phenomenon；Without heavy metal and other toxic components, no sulfation；The Congo red testing time
It is long, there is excellent electrical insulating property, free from admixture has efficient weatherability；Applied widely, practical, dosage is few, has more
It is functional.
It further illustrates, the off-color material of the light is that spiral shell adjoins class material of muttering, and spiral shell adjoins that mutter be organic photochromic material
One of middle research and earliest, the widest system of application, under ultraviolet light, colourless spiral shell adjoins the fracture of the mono- O key of C in structure of muttering
Open loop, molecule locally rotate and to form a coplanar merocyanine structure with crying to make an uproar and develop the color, and absorption spectrum is accordingly red
It moves.Under the action of visible light or heat, open loop body can be returned to spirane structure again.The rupture time of mono- O key of C is in picosecond,
Color change is exceedingly fast.But merocyanine stores a few minutes to a few hours at room temperature and will be automatically converted to colourless loop coil knot
Structure, in addition, photochemistry side reaction can occur in stining inverse process, so that the cycle-index of reversible transition is influenced, these deficiency limits
Spiral shell processed adjoins the application muttered in terms of photochemical molecular lock.
A specific embodiment of the invention, but scope of protection of the present invention is not limited thereto, it is any to be familiar with this field
Within the technical scope disclosed by the invention, changes or replacements that can be thought of without creative work should all be contained technical staff
Lid is within protection scope of the present invention.Therefore, protection scope of the present invention should be to protect model defined by claims
Subject to enclosing.
Claims (3)
1. a kind of chromoplastic material process recipe, it is characterised in that: the chromoplastic material is by plastic body, colour-changing agent, photic
Off-color material, oxidant and combination of stabilizers form, and the photochromic material is that spiral shell adjoins class material of muttering, the plastics sheet
Body accounts for the 35%-50% of the chromoplastic material mass percent, and the colour-changing agent accounts for the chromoplastic material quality percentage
The 10%-15% of ratio, the photochromic material account for the 5%-10% of the chromoplastic material mass percent, the oxygen
Agent accounts for the 3%-5% of the chromoplastic material mass percent, and the stabilizer accounts for the chromoplastic material quality percentage
The 35%-40% of ratio.
2. chromoplastic material process recipe according to claim 1, it is characterised in that: the stabilizer is that liquid calcium zinc is steady
Determine agent, is in pale yellowish oil liquid.
3. chromoplastic material process recipe according to claim 1, it is characterised in that: the plastic body accounts for the change
The 50% of color amount of plastic percentage, the colour-changing agent account for the 10% of the chromoplastic material amount percentage, the light-induced variable
Color material accounts for the 10% of the chromoplastic material amount percentage, and the stabilizer accounts for the chromoplastic material amount percentage
30%.