CN109251391A - A kind of anti-cracking Polywoven Bag - Google Patents
A kind of anti-cracking Polywoven Bag Download PDFInfo
- Publication number
- CN109251391A CN109251391A CN201810901631.9A CN201810901631A CN109251391A CN 109251391 A CN109251391 A CN 109251391A CN 201810901631 A CN201810901631 A CN 201810901631A CN 109251391 A CN109251391 A CN 109251391A
- Authority
- CN
- China
- Prior art keywords
- parts
- cracking
- polywoven bag
- bag according
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to woven bags, a kind of anti-cracking Polywoven Bag is specifically disclosed, raw material includes: 60-75 parts of polyethylene, 12-21 parts of polyoxymethylenes, 4.5-12.5 parts of anti-cracking agent, 2-6 parts of pla-pcl, 2.5-9 parts of lignin, 1-5 parts of acrylate, 0.5-5.5 parts of deca-BDE, 0.7-1.8 parts of zinc stearate, 1.5-5 parts of clay, 3.5-7.5 parts of antioxidant, 1-5 parts of antimony oxide, 1-3.5 parts of defoaming agent by weight.The present invention has excellent anti-cracking performance.
Description
Technical field
The present invention relates to woven bags, and in particular to a kind of anti-cracking Polywoven Bag.
Background technique
Most of Polywoven Bag currently on the market is using polypropylene (PP) as raw material, it is always that growth is most fast
Main thermoplastic, especially fiber and long filament, film extrusion, in terms of.The fabulous flowing of polypropylene
The flow velocity and other unique polymer properties of performance and wide scope combine, it is made to have excellent processing performance.It is lower
Flow velocity be able to satisfy the processing request of compressive zone, band-like long filament and monofilament etc., moreover it is possible to so that finished product is had tensile strength and low extensibility,
The case where keeping enough lateral integralities simultaneously, making the splitting and dust from flying on filament winding machine guiding device reaches minimum journey
Degree.Main feature: nontoxic, tasteless, density is small, and intensity, rigidity, hardness heat resistance are superior to low pressure polyethylene, has higher anti-
Bending fatigue strength.But fracture phenomena easily occurs for traditional Polywoven Bag, limits the use of its daily life.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of anti-cracking Polywoven Bags.The present invention has
Excellent anti-cracking performance.
A kind of anti-cracking Polywoven Bag proposed by the present invention, raw material include: 60-75 parts of polyethylene, polyoxy by weight
Change methylene 12-21 parts, 4.5-12.5 parts of anti-cracking agent, 2-6 parts of pla-pcl, 2.5-9 parts of lignin, dimethyl aminoethyl
1-5 parts of ester, 0.5-5.5 parts of deca-BDE, 0.7-1.8 parts of zinc stearate, 1.5-5 parts of clay, 3.5-7.5 parts of antioxidant, three
Aoxidize 1-5 parts of two antimony, 1-3.5 parts of defoaming agent.
Preferably, the anti-cracking agent the preparation method comprises the following steps: take sepiolite, deionized water is added, ultrasonic disperse obtains Hai Pao
Stone dispersion liquid;Under stirring condition, sodium alginate is added into sepiolite dispersion liquid, heats up, continues to be stirred to react, filters, it is dry,
Grinding, obtains anti-cracking agent.
Preferably, the mass ratio of the sepiolite and sodium alginate is 1:0.3-1.4.
Preferably, the power of the ultrasonic disperse is 50-200W, time 25-55min.
Preferably, the temperature being stirred to react is 45-60 DEG C, time 30-65min.
Preferably, the temperature of the drying is 70-85 DEG C, time 20-50min.
Preferably, described to be ground to ground 80-200 mesh.
Preferably, the polyethylene is by medium density polyethylene and low density polyethylene (LDPE) according to the weight ratio group of 1:0.2-1.5
At.
The present invention can be prepared conventionally.
Raw material of the invention includes polyethylene, polyoxymethylenes, anti-cracking agent, pla-pcl, lignin, acrylic acid dimethyl
Amino ethyl ester, deca-BDE, zinc stearate, clay, antioxidant, antimony oxide, defoaming agent, each materials compatibility is good, matches
It can assign the present invention good basic property after cooperation use, in preferred embodiment, in the preparation of anti-cracking agent, selection uses alginic acid
Sodium is modified sepiolite, wherein it is the tubulose connected pathways of 0.36nm × 1.06nm and larger that sepiolite, which has sectional area,
Surface area, and sepiolite octahedral site is rich in a large amount of magnesium ions;Sodium alginate is by beta-D-mannuronic acid (β-D-
Mannuronic, M) and α-L- guluronic acid (α-L-guluronic, G) by (1 → 4) key connection made of;In specific temperature
Under, with the magnesium ion on sepiolite surface ion-exchange reactions can occur for the sodium ion in sodium alginate, and then make seaweed acidic group
Team knowledge enables its surface property change in the surface or channel of sepiolite, is changed into lipophilicity by original hydrophily,
Increase channel cross-sectional area simultaneously, improves dispersibility of the sepiolite between the macromolecule raw materials such as polyethylene, make the present invention to impact energy
The dispersibility and absorbability of amount improve, and cause toughness to increase, and sepiolite can be formed with macromolecule raw materials such as polyethylene
Much larger than the effect of Van der Waals force, while meerschaum particle has stronger rigidity, deflection can be brought it about in crack propagation,
Energy is absorbed, crackle is terminated, plays the effect of toughening, in addition, sodium alginate is when occurring ion-exchange reactions, G unit can
Accumulation forms cross-linked network structure in sepiolite channel, significantly improves the rigidity and toughness of sepiolite, advanced optimizes above-mentioned
Toughening effect, and then make the present invention that there is excellent anti-cracking performance.In addition, the addition of sepiolite can be improved the anti-flammability of invention
Energy.
Specific embodiment
In the following, technical solution of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of anti-cracking Polywoven Bag, raw material include: 60 parts of polyethylene, 21 parts of polyoxymethylenes, anti-cracking by weight
4.5 parts of agent, 6 parts of pla-pcl, 2.5 parts of lignin, 5 parts of acrylate, 0.5 part of deca-BDE, tristearin
1.8 parts of sour zinc, 1.5 parts of clay, 7.5 parts of antioxidant, 1 part of antimony oxide, 3.5 parts of defoaming agent.
Embodiment 2
A kind of anti-cracking Polywoven Bag, raw material include: 75 parts of polyethylene, 12 parts of polyoxymethylenes, anti-cracking by weight
12.5 parts of agent, 2 parts of pla-pcl, 9 parts of lignin, 1 part of acrylate, 5.5 parts of deca-BDE, stearic acid
0.7 part of zinc, 5 parts of clay, 3.5 parts of antioxidant, 5 parts of antimony oxide, 1 part of defoaming agent;
Wherein, the anti-cracking agent the preparation method comprises the following steps: take sepiolite, deionized water is added, ultrasonic disperse obtains sepiolite
Dispersion liquid;Under stirring condition, sodium alginate is added into sepiolite dispersion liquid, heats up, continues to be stirred to react, filters, it is dry, it grinds
Mill, obtains anti-cracking agent.
Embodiment 3
A kind of anti-cracking Polywoven Bag, raw material include: 68 parts of polyethylene, 16 parts of polyoxymethylenes, anti-cracking by weight
8 parts of agent, 4 parts of pla-pcl, 5 parts of lignin, 3 parts of acrylate, 3 parts of deca-BDE, zinc stearate 1.2
Part, 3 parts of clay, 5 parts of antioxidant, 3 parts of antimony oxide, 2.5 parts of defoaming agent;
Wherein, the anti-cracking agent the preparation method comprises the following steps: take sepiolite, deionized water is added, ultrasonic disperse obtains sepiolite
Dispersion liquid;Under stirring condition, sodium alginate is added into sepiolite dispersion liquid, heats up, continues to be stirred to react, filters, it is dry, it grinds
Mill, obtains anti-cracking agent;
The mass ratio of the sepiolite and sodium alginate is 1:0.8;
The power of the ultrasonic disperse is 150W, time 35min;
The temperature being stirred to react is 50 DEG C, time 50min;
The temperature of the drying is 78 DEG C, time 35min;
It is described to be ground to ground 150 mesh;
The polyethylene is made of medium density polyethylene and low density polyethylene (LDPE) according to the weight ratio of 1:1.
Embodiment 4
A kind of anti-cracking Polywoven Bag, raw material include: 65 parts of polyethylene, 14 parts of polyoxymethylenes, anti-cracking by weight
6 parts of agent, 3 parts of pla-pcl, 3 parts of lignin, 2 parts of acrylate, 1.5 parts of deca-BDE, zinc stearate 1
Part, 2.5 parts of clay, 4 parts of antioxidant, 2 parts of antimony oxide, 2 parts of defoaming agent;
Wherein, the anti-cracking agent the preparation method comprises the following steps: take sepiolite, deionized water is added, ultrasonic disperse obtains sepiolite
Dispersion liquid;Under stirring condition, sodium alginate is added into sepiolite dispersion liquid, heats up, continues to be stirred to react, filters, it is dry, it grinds
Mill, obtains anti-cracking agent;
The mass ratio of the sepiolite and sodium alginate is 1:0.3;
The power of the ultrasonic disperse is 200W, time 25min;
The temperature being stirred to react is 60 DEG C, time 30min;
The temperature of the drying is 85 DEG C, time 20min;
It is described to be ground to ground 200 mesh;
The polyethylene is made of medium density polyethylene and low density polyethylene (LDPE) according to the weight ratio of 1:0.2.
Embodiment 5
A kind of anti-cracking Polywoven Bag, raw material include: 72 parts of polyethylene, 18 parts of polyoxymethylenes, anti-cracking by weight
10 parts of agent, 5 parts of pla-pcl, 7 parts of lignin, 4 parts of acrylate, 4.5 parts of deca-BDE, zinc stearate
1.5 parts, 4 parts of clay, 6 parts of antioxidant, 4 parts of antimony oxide, 3 parts of defoaming agent;
Wherein, the anti-cracking agent the preparation method comprises the following steps: take sepiolite, deionized water is added, ultrasonic disperse obtains sepiolite
Dispersion liquid;Under stirring condition, sodium alginate is added into sepiolite dispersion liquid, heats up, continues to be stirred to react, filters, it is dry, it grinds
Mill, obtains anti-cracking agent;
The mass ratio of the sepiolite and sodium alginate is 1:1.4;
The power of the ultrasonic disperse is 50W, time 55min;
The temperature being stirred to react is 45 DEG C, time 65min;
The temperature of the drying is 70 DEG C, time 50min;
It is described to be ground to ground 80 mesh;
The polyethylene is made of medium density polyethylene and low density polyethylene (LDPE) according to the weight ratio of 1:1.5.
Comparative example 1
A kind of anti-cracking Polywoven Bag, raw material include: 72 parts of polyethylene, 18 parts of polyoxymethylenes, anti-cracking by weight
10 parts of agent, 5 parts of pla-pcl, 7 parts of lignin, 4 parts of acrylate, 4.5 parts of deca-BDE, zinc stearate
1.5 parts, 4 parts of clay, 6 parts of antioxidant, 4 parts of antimony oxide, 3 parts of defoaming agent;
Wherein, the anti-cracking agent is common anti-cracking agent;
The polyethylene is made of medium density polyethylene and low density polyethylene (LDPE) according to the weight ratio of 1:1.5.
Test example
Anti-cracking performance test is carried out with XWP-5B puller system to the obtained woven bag of embodiment 1-5 and comparative example 1 respectively, according to
It is secondary to be denoted as test group 1-5 and control group.Test result is as follows table:
As can be seen from the above table, the present invention assigns the excellent anti-cracking performance of the present invention by adding specific anti-cracking agent.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of anti-cracking Polywoven Bag, which is characterized in that its raw material includes: 60-75 parts of polyethylene, polyoxygenated first by weight
12-21 parts of alkene, 4.5-12.5 parts of anti-cracking agent, 2-6 parts of pla-pcl, 2.5-9 parts of lignin, acrylate 1-
5 parts, 0.5-5.5 parts of deca-BDE, 0.7-1.8 parts of zinc stearate, 1.5-5 parts of clay, 3.5-7.5 parts of antioxidant, three oxidations
Two 1-5 parts of antimony, 1-3.5 parts of defoaming agent.
2. anti-cracking Polywoven Bag according to claim 1, which is characterized in that the anti-cracking agent the preparation method comprises the following steps: taking sea
Afrodite, is added deionized water, and ultrasonic disperse obtains sepiolite dispersion liquid;Under stirring condition, sea is added into sepiolite dispersion liquid
Mosanom, heating, continues to be stirred to react, and filters, dry, and grinding obtains anti-cracking agent.
3. anti-cracking Polywoven Bag according to claim 2, which is characterized in that the mass ratio of the sepiolite and sodium alginate
For 1:0.3-1.4.
4. the anti-cracking Polywoven Bag according to Claims 2 or 3, which is characterized in that the power of the ultrasonic disperse is 50-
200W, time 25-55min.
5. the anti-cracking Polywoven Bag according to Claims 2 or 3, which is characterized in that the temperature being stirred to react is 45-60
DEG C, time 30-65min.
6. the anti-cracking Polywoven Bag according to Claims 2 or 3, which is characterized in that the temperature of the drying is 70-85 DEG C,
Time is 20-50min.
7. the anti-cracking Polywoven Bag according to Claims 2 or 3, which is characterized in that described to be ground to ground 80-200 mesh
Sieve.
8. anti-cracking Polywoven Bag according to claim 1, which is characterized in that the polyethylene is by medium density polyethylene and low
Density polyethylene is formed according to the weight ratio of 1:0.2-1.5.