CN109233234A - The granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable - Google Patents
The granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable Download PDFInfo
- Publication number
- CN109233234A CN109233234A CN201811064041.1A CN201811064041A CN109233234A CN 109233234 A CN109233234 A CN 109233234A CN 201811064041 A CN201811064041 A CN 201811064041A CN 109233234 A CN109233234 A CN 109233234A
- Authority
- CN
- China
- Prior art keywords
- unsaturated polyester
- moulding compound
- high electric
- granular
- injection moldable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable, the granular unsaturated polyester UP moulding compound of the high electric strength of the injection moldable is grouped as by following groups by weight percentage: the unsaturated polyester resin A15%-25% of high relative molecular low-unsaturation-degree;The unsaturated polyester resin B10%-15% of the lower high degree of unsaturation of molecular mass;Crosslinking agent 0.5%-2%;Reactive plasticizer 1%-3%;Polymerization inhibitor 0.01%-0.02%;Flame-proof filling material 35%-55%;Release agent 1%-3%;Reinforcing fiber 10%-20%.The present invention passes through the unsaturated polyester resin A of combination higher molecular weight low-unsaturation-degree and the unsaturated polyester resin B (A be hard resin with B) of the high degree of unsaturation of lower molecular weight, it ensure that in the case where less reactive plasticizer content, this moulding compound has viscosity higher not lose mobility again within the scope of processing temperature, while guaranteeing that moulding compound solidifies rapidly in a mold.
Description
Technical field
The present invention relates to plastics, in particular to a kind of granular unsaturated polyester UP moulds of high electric strength of injection moldable
Plastics.
Background technique
Unsaturated polyester (UP) UP moulding compound adds mould made of curing agent, filler (frequently with glass fibre) etc. unsaturated polyester (UP)
Plastics.Two class of fragment shape unsaturated polyester die plastic (SMC) and bulk unsaturated polyester die plastic (DMC), product feature are
Mechanical strength height, good stability of the dimension.Various unsaturated polyester (UP)s are to be added each when uncured from low viscosity to highly viscous liquid
Be heating and curing after kind of additive, after solidification rigid or elastic plastics, can be transparent or opaque.Unsaturation is poly-
Glass reinforced plastic is made with glass fiber reinforcement in being mainly used for of ester, and is one of the principal item in reinforced plastics, but existing
Unsaturated polyester (UP) UP moulding compound easily loses flowability in viscosity higher, and curing rate is slow, and mechanical energy can be not good enough.
Summary of the invention
To solve the problems mentioned in the above background technology, the purpose of the present invention is to provide a kind of height of injection moldable
The granular unsaturated polyester UP moulding compound of electrical strength, insulating properties is fine, mechanical strength, and heat distortion temperature is higher.
In order to solve the above technical problems, technical solution provided by the invention are as follows:
The granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable, the height electricity of the injection moldable
The granular unsaturated polyester UP moulding compound of gas intensity is grouped as by following groups by weight percentage: the low insatiable hunger of high relative molecular
With the unsaturated polyester resin A15%-25% of degree;The unsaturated polyester resin B10%- of the lower high degree of unsaturation of molecular mass
15%;Crosslinking agent 0.5%-2%;Reactive plasticizer 1%-3%;Polymerization inhibitor 0.01%-0.02%;Flame-proof filling material 35%-55%;
Release agent 1%-3%;Reinforcing fiber 10%-20%.
As an improvement, the unsaturated polyester resin A and unsaturated polyester resin B are by monounsaturated dicarboxylic acid, insatiable hunger
With line polymer made of binary acid and dihydric alcohol polycondensation.
As an improvement, the crosslinking agent is cumyl peroxide or benzoyl peroxide, the reactive plasticizer is neighbour
Dially phthalate, three allyl rouge of cyanuric acid or maleic anhydride diallyl, the polymerization inhibitor include benzenediol,
Tert-butyl catechol and copper naphthenate, flame-proof filling material are aluminium hydroxide or magnesium hydroxide, and the release agent is talcum powder, cloud
The mixture of female powder, clay and starching clay, the reinforcing fiber are glass fibre, the inorfils such as carbon fiber.
As an improvement, the granular unsaturated polyester UP moulding compound processing temperature of the high electric strength of the injection moldable
It is 80 DEG C -95 DEG C.
The beneficial effects of the present invention are:
Unsaturated polyester resin A and lower molecular weight high insatiable hunger of the present invention by combination higher molecular weight low-unsaturation-degree
With the unsaturated polyester resin B of degree (A be hard resin with B), ensure that in the case where less reactive plasticizer content, it is this
Moulding compound (80 DEG C -95 DEG C) within the scope of processing temperature has viscosity higher not lose mobility again, while guaranteeing moulding compound in mold
In solidify rapidly, the most prominent advantage of the present invention is that resin total amount A+B is very high, and the electrical insulating property of products obtained therefrom is fine, electrical strong
Degree reaches 25MV/m or more, and mechanical strength, heat distortion temperature are higher, and flame retardant property can reach UL94FV0 grades.
Specific embodiment
Illustrate the present invention with specific embodiment below, is not limitation of the present invention.
Embodiment one
The granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable, the height electricity of the injection moldable
The granular unsaturated polyester UP moulding compound of gas intensity is grouped as by following groups by weight percentage: the low insatiable hunger of high relative molecular
With the unsaturated polyester resin A15% of degree;The unsaturated polyester resin B10% of the lower high degree of unsaturation of molecular mass;Crosslinking agent
0.5%;Reactive plasticizer 1%;Polymerization inhibitor 0.01%;Flame-proof filling material 35%;Release agent 1%;Reinforcing fiber 10%.
The unsaturated polyester resin A and unsaturated polyester resin B be by monounsaturated dicarboxylic acid, unsaturated dibasic acid and
Line polymer made of dihydric alcohol polycondensation.
The crosslinking agent is cumyl peroxide or benzoyl peroxide, and the reactive plasticizer is phthalic acid two
Allyl ester, three allyl rouge of cyanuric acid or maleic anhydride diallyl, the polymerization inhibitor include benzenediol, tert-butyl o benzene
Diphenol and copper naphthenate, flame-proof filling material are aluminium hydroxide or magnesium hydroxide, and the release agent is talcum powder, mica powder, clay
And the mixture of starching clay, the reinforcing fiber are glass fibre, the inorfils such as carbon fiber.
The granular unsaturated polyester UP moulding compound processing temperature of the high electric strength of the injection moldable is 80 DEG C.
Embodiment two
The granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable, the height electricity of the injection moldable
The granular unsaturated polyester UP moulding compound of gas intensity is grouped as by following groups by weight percentage: the low insatiable hunger of high relative molecular
With the unsaturated polyester resin A25% of degree;The unsaturated polyester resin B15% of the lower high degree of unsaturation of molecular mass;Crosslinking agent
2%;Reactive plasticizer 3%;Polymerization inhibitor 0.02%;Flame-proof filling material 55%;Release agent 3%;Reinforcing fiber 20%.
The unsaturated polyester resin A and unsaturated polyester resin B be by monounsaturated dicarboxylic acid, unsaturated dibasic acid and
Line polymer made of dihydric alcohol polycondensation.
The crosslinking agent is cumyl peroxide or benzoyl peroxide, and the reactive plasticizer is phthalic acid two
Allyl ester, three allyl rouge of cyanuric acid or maleic anhydride diallyl, the polymerization inhibitor include benzenediol, tert-butyl o benzene
Diphenol and copper naphthenate, flame-proof filling material are aluminium hydroxide or magnesium hydroxide, and the release agent is talcum powder, mica powder, clay
And the mixture of starching clay, the reinforcing fiber are glass fibre, the inorfils such as carbon fiber.
The granular unsaturated polyester UP moulding compound processing temperature of the high electric strength of the injection moldable is 90 DEG C.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. the granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable, which is characterized in that the injectable
The granular unsaturated polyester UP moulding compound of molding high electric strength is grouped as by following groups by weight percentage: higher molecular
The unsaturated polyester resin A15%-25% of quality low-unsaturation-degree;The unsaturated polyester (UP) tree of the lower high degree of unsaturation of molecular mass
Rouge B10%-15%;Crosslinking agent 0.5%-2%;Reactive plasticizer 1%-3%;Polymerization inhibitor 0.01%-0.02%;Flame-proof filling material
35%-55%;Release agent 1%-3%;Reinforcing fiber 10%-20%.
2. the granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable according to claim 1, special
Sign is, the unsaturated polyester resin A and unsaturated polyester resin B be by monounsaturated dicarboxylic acid, unsaturated dibasic acid and
Line polymer made of dihydric alcohol polycondensation.
3. the granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable according to claim 1, special
Sign is that the crosslinking agent is cumyl peroxide or benzoyl peroxide, and the reactive plasticizer is phthalic acid two
Allyl ester, three allyl rouge of cyanuric acid or maleic anhydride diallyl, the polymerization inhibitor include benzenediol, tert-butyl o benzene
Diphenol and copper naphthenate, flame-proof filling material are aluminium hydroxide or magnesium hydroxide, and the release agent is talcum powder, mica powder, clay
And the mixture of starching clay, the reinforcing fiber are glass fibre, the inorfils such as carbon fiber.
4. the granular unsaturated polyester UP moulding compound of the high electric strength of injection moldable according to claim 1, special
Sign is that the granular unsaturated polyester UP moulding compound processing temperature of the high electric strength of the injection moldable is 80 DEG C -95
℃。