CN109208129A - A kind of island composite filament - Google Patents
A kind of island composite filament Download PDFInfo
- Publication number
- CN109208129A CN109208129A CN201710519936.9A CN201710519936A CN109208129A CN 109208129 A CN109208129 A CN 109208129A CN 201710519936 A CN201710519936 A CN 201710519936A CN 109208129 A CN109208129 A CN 109208129A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite filament
- fiber
- island composite
- flock
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of island composite filament, the component including following mass fraction: 11~23 parts of viscose fiber；10~16 parts of acetate fiber；3~8 parts of regenerated celulose fibre；2~6 parts of azlon；20~35 parts of polyacrylonitrile fibre；15~24 parts of chrysotile；It is the agent of oxidized starch gluing that it, which is stained with mixture,.The characteristic that there is the present invention general fiber can not have: high spreadability, soft, comfortable and easy to wear, fabric sheen is soft.
Description
Technical field
The invention belongs to chemical fibre related fieldss, and in particular to a kind of island composite filament.
Background technique
Sea-island fibre is to disperse a kind of polymer in another polymer, and dispersed phase is in " island " shape in fibre section
State, and parent is then equivalent to " sea " is a kind of state that ingredient is dispersed with fine in terms of the cross section of fiber by another kind at
Subpackage is round as marine there are many island.
Its " island " is continuous, intensive, equally distributed in the axial direction of fiber with " sea " ingredient.In process of production, it
Fiber number with conventional fibre, but " sea " ingredient is dissolved away with solvent, then it can obtain the superfine fibre beam of collection pencil.According to
The general classification of fiber, after sea-island fibre separation, only 0.05D, category superfine fibre, conventional spinning can not be accomplished filament number.
Summary of the invention
It is an object of the invention to aiming at the shortcomings in the prior art, provide a kind of island composite filament.
It in order to realize the present invention, is realized using following scheme: a kind of island composite filament, the group including following mass fraction
Point:
11~23 parts of viscose fiber；
10~16 parts of acetate fiber；
3~8 parts of regenerated celulose fibre；
2~6 parts of azlon；
20~35 parts of polyacrylonitrile fibre；
15~24 parts of chrysotile；
It is the agent of oxidized starch gluing that it, which is stained with mixture,.
The method for preparing the island composite filament, comprising the following steps:
(1) each raw material is measured by formula, raw material is loosened into the cotton block or flock of fritter；
(2) impurity in cotton block or flock, fault and staple fiber removal after step (1) being loosened；
(3) cotton block or flock are mixed using drawing frame, forms ripe bar；
(4) it is thin that ripe bar is equably elongated to pumping, and stretches fiber further in parallel, forms rove；
(5) rove is drawn and attenuated to required fineness, keep straightening of fibers parallel and is subject to turn, become thin with the twist and intensity
Yarn；
(6) finally by spun yarn-winding on bobbin.
Further, the raw material loosens into 3*3cm fritter.
Further, the rove is drawn and attenuated to 0.02mm.
The utility model has the advantages that the characteristic that there is the present invention general fiber can not have: high spreadability, soft, dress are relaxed
Suitable, fabric sheen is soft.
It is processed by the design of fabric, using the thin fibrillation feature of sea-island fibre extreme, many special knit can be obtained
Object style, such as Hair style, Glove suede, super high density fabric.This kind fabric can be widely used in clothes, dress ornament field, luggage, room
Interior articles and industrial field etc..
Using many performances of the flock suede fabric of sea-island fibre exploitation and no less than natural suede, there are many performances very
To better than natural suede.Its fabrics feel soft, drapability is good, and quality is frivolous, be corium half, can be made into different-thickness and
The fabric of weight；Various surface treatments can be carried out, panoramic surface effect is obtained.There are writing effect, three-dimensional sense in surface
It is good；Damp and hot contraction distortion is small, has good air permeable waterproof air permeability effect, and fabric intensity is high, is much better than natural suede.
Specific embodiment
Embodiment 1: the method for preparing the island composite filament, comprising the following steps:
(1) by each raw material of formula measurement: 16 parts of viscose fiber, 11 parts of acetate fiber, 4 parts of regenerated celulose fibre, regenerated protein
2 parts of matter fiber, 24 parts of polyacrylonitrile fibre, 21 parts of chrysotile, raw material is loosened into the cotton block or flock of fritter；
(2) impurity in cotton block or flock, fault and staple fiber removal after step (1) being loosened；
(3) cotton block or flock are mixed using drawing frame, forms ripe bar；
(4) it is thin that ripe bar is equably elongated to pumping, and stretches fiber further in parallel, forms rove；
(5) rove is drawn and attenuated to required fineness, keep straightening of fibers parallel and is subject to turn, become thin with the twist and intensity
Yarn；
(6) finally by spun yarn-winding on bobbin.
The raw material loosens into 3*3cm fritter, and the rove is drawn and attenuated to 0.02mm.
Embodiment 2: the method for preparing the island composite filament, comprising the following steps:
(1) by each raw material of formula measurement: 19 parts of viscose fiber, 13 parts of acetate fiber, 3 parts of regenerated celulose fibre, regenerated protein
3 parts of matter fiber, 28 parts of polyacrylonitrile fibre, 19 parts of chrysotile, raw material is loosened into the cotton block or flock of fritter；
(2) impurity in cotton block or flock, fault and staple fiber removal after step (1) being loosened；
(3) cotton block or flock are mixed using drawing frame, forms ripe bar；
(4) it is thin that ripe bar is equably elongated to pumping, and stretches fiber further in parallel, forms rove；
(5) rove is drawn and attenuated to required fineness, keep straightening of fibers parallel and is subject to turn, become thin with the twist and intensity
Yarn；
(6) finally by spun yarn-winding on bobbin.
The raw material loosens into 3*3cm fritter, and the rove is drawn and attenuated to 0.02mm.
Claims (4)
1. a kind of island composite filament, which is characterized in that the component including following mass fraction:
11~23 parts of viscose fiber；
10~16 parts of acetate fiber；
3~8 parts of regenerated celulose fibre；
2~6 parts of azlon；
20~35 parts of polyacrylonitrile fibre；
15~24 parts of chrysotile；
It is the agent of oxidized starch gluing that it, which is stained with mixture,.
2. the method for preparing island composite filament described in claim 1, which comprises the following steps:
(1) each raw material is measured by formula, raw material is loosened into the cotton block or flock of fritter；
(2) impurity in cotton block or flock, fault and staple fiber removal after step (1) being loosened；
(3) cotton block or flock are mixed using drawing frame, forms ripe bar；
(4) it is thin that ripe bar is equably elongated to pumping, and stretches fiber further in parallel, forms rove；
(5) rove is drawn and attenuated to required fineness, keep straightening of fibers parallel and is subject to turn, become thin with the twist and intensity
Yarn；
(6) finally by spun yarn-winding on bobbin.
3. a kind of island composite filament according to claim 2, which is characterized in that the raw material loosens into 3*3cm fritter.
4. a kind of island composite filament according to claim 2, which is characterized in that drawing and attenuating the rove to 0.02mm.