CN109206115A - A kind of construction material and its manufacture craft of feature of environmental protection Concave-convex clay rod - Google Patents
A kind of construction material and its manufacture craft of feature of environmental protection Concave-convex clay rod Download PDFInfo
- Publication number
- CN109206115A CN109206115A CN201811036097.6A CN201811036097A CN109206115A CN 109206115 A CN109206115 A CN 109206115A CN 201811036097 A CN201811036097 A CN 201811036097A CN 109206115 A CN109206115 A CN 109206115A
- Authority
- CN
- China
- Prior art keywords
- agent
- construction material
- high speed
- convex clay
- clay rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of construction material of feature of environmental protection Concave-convex clay rod, which is made of the raw material of following percentage: water 35 ~ 48%, thixotropic agent 0.35 ~ 0.75%, titanium dioxide 8 ~ 10%, germproof matter 0.23 ~ 0.30%, defoaming agent 0.1 ~ 0.2%, anti-settling agent 2 ~ 5%, anti-sag agent 0.2 ~ 0.5%, catalyst 0.1 ~ 0.4%, desiccant 0.4 ~ 0.7%, thickener 3 ~ 5%, sodium metasilicate 5 ~ 8%, talcum powder 14 ~ 19%, filler 10 ~ 20%.The utility model has the advantages that having stronger absorption property, there is fungi-proofing property, product can be kept steady in a long-term.
Description
Technical field
The present invention relates to building material technical fields, it particularly relates to a kind of building of feature of environmental protection Concave-convex clay rod
Material and its manufacture craft.
Background technique
Building materials are the general designations of material used in civil engineering and architectural engineering.Can be divided into structural material, ornament materials and
Certain proprietary materials.Structural material includes timber, bamboo wood, stone material, cement, concrete, metal, brick and tile, ceramics, glass, engineering
Plastics, composite material etc..Ornament materials includes various coating, paint, coating, veneer, assorted ceramic tile, the glass with special-effect
Glass etc.；Proprietary material refers to for waterproof, moisture-proof, anti-corrosion, fire prevention, fire-retardant, sound insulation, heat-insulated, heat preservation, sealing etc..
The patent document of Patent No. CN103554850A discloses a kind of environment-friendly type anti-cracking corrosion-resistant waterproof material and its system
Preparation Method, including 10 parts of polyester (polyethylene terephthalate), 5 parts of ethylene ethyl acrylate copolymer, whiskerettes sulfuric acid
It 3 parts of calcium, 2 parts of microcrystalline cellulose, 0.2 part of hydroxyethylmethylcellulose, 50 parts of ethyl alcohol, 29.8 parts of normal propyl alcohol, can effectively rise
To the inside and outside effect protected.But the anti-adsorptivity of material and fungi-proofing property are weaker in this programme, thus cannot
The stability of product is kept for a long time and influences construction technology.
In conclusion how reinforcing material adsorptivity and fungi-proofing property be current technical problem urgently to be solved.
Summary of the invention
For the problems in the relevant technologies, the present invention proposes the construction material and its system of a kind of feature of environmental protection Concave-convex clay rod
Make technique, to overcome above-mentioned technical problem present in existing the relevant technologies.
The technical scheme of the present invention is realized as follows:
According to an aspect of the invention, there is provided a kind of construction material of feature of environmental protection Concave-convex clay rod.
The construction material is made of the raw material of following percentage:
Water 35 ~ 48%, thixotropic agent 0.35 ~ 0.75%, titanium dioxide 8 ~ 10%, germproof matter 0.23 ~ 0.30%, defoaming agent 0.1
~ 0.2%, anti-settling agent 2 ~ 5%, anti-sag agent 0.2 ~ 0.5%, catalyst 0.1 ~ 0.4%, desiccant 0.4 ~ 0.7%, thickener 3 ~
5%, sodium metasilicate 5 ~ 8%, talcum powder 14 ~ 19%, filler 10 ~ 20%.
Preferably, the thixotropic agent is one of bentonite, white carbon black and organic rheology modifier or a variety of.
Preferably, thickener includes inorganic thickening agent, cellulose family, polyacrylate and association type polyurethane thickener.
Preferably, the inorganic thickening agent includes bentonite, attapulgite, alumina silicate.
Preferably, the defoaming agent is a kind of in organic silicon defoamer or compounding class defoaming agent.
Preferably, the anti-settling agent is any one in OPTIGEL, VM/WA/CK/LT.
According to another aspect of the present invention, a kind of production work of the construction material of feature of environmental protection Concave-convex clay rod is provided
Skill.
The manufacture craft of the construction material, comprising the following steps:
Natural attapulgite clay raw material is chosen, carries out being processed into Concave-convex clay rod by high-tech special process；
Each raw material is weighed according to the weight percent pre-set；
At room temperature, by germproof matter, defoaming agent, anti-settling agent, anti-sag agent, catalyst, desiccant and thickener
It pours into stirred tank, water is added and carries out uniform stirring, obtains mixture one；
Mixture one is placed in high speed disperser and is dispersed, mixture two is obtained；
Titanium dioxide, sodium metasilicate, talcum powder and filler are sequentially added in mixture two, and is uniformly divided in high speed disperser
It dissipates, obtains mixture three；
Water is mixed into mixture three and carries out uniform stirring, obtains mixed liquor one；
Mixed liquor one is poured slowly into thixotropic agent, uniform stirring is carried out in high speed disperser, the revolving speed of high speed disperser is
400 ~ 550r/min, time are 10 ~ 15min, obtain mixed liquor two；
The mixed liquor two stirred evenly is discharged and filtered, the Concave-convex clay rod material of the feature of environmental protection is obtained；
Inspection by sampling, qualified post package.
Preferably, the revolving speed of the high speed disperser is 700 ~ 780r/min, and the time is 20 ~ 26min.
Preferably, the revolving speed of the high speed disperser is 600 ~ 1000r/min, and the time is 15 ~ 20min.
Wherein, material component of the present invention is described below:
Thixotropic agent: when lubricating grease is sheared, consistency becomes smaller, and when stopping shearing, increased property is thixotropy to consistency again.Touching
Change is also known as shaken in denaturation.It is the reversible colloidal sol phenomenon that gelinite occurs under the action of the mechanical forces such as oscillation, compressing.Elongated
Grain links to form reticular structure by weak chemical bond, it is easy to be destroyed by external force, be widely used in building, coating industry.
Titanium dioxide: titanium dioxide scientific name is titanium dioxide, it is a kind of dyestuff and pigment, molecular formula TiO2, molecular weight
It is 79.8658.For painting, ink, plastics, rubber, papermaking, the industries such as chemical fibre；For welding rod, titanium and manufacture titanium white are refined
Powder, titanium dioxide (nanoscale) are widely used in the white inorganic pigments such as function ceramics, catalyst, cosmetics and light-sensitive material.It is
Strongest one kind of tinting strength, tinting power in white pigment, with excellent covering power and color fastness, suitable for opaque white article.
Germproof matter: with inhibit or kill paste dye, liquid dyes, earnestly float shape dyestuff in mould substance pact agent
Door, dust head have organic acid, aldehyde, phenol etc., such as multi-chlorophenol sodium, sodium benzoate, organic aldehyde.
Defoaming agent: defoaming agent is also known as anti-foaming agent, and many unwanted bubbles can be generated during industrial production, needs to add
Add defoaming agent.It is widely used in removing latex, textile sizing, food fermentation, biological medicine, pesticide, coating, petrochemical industry, makes
The unwanted bubbles generated during the industry productions such as paper, industry cleaning link.Due to the special chemical structure of silicone oil, make it neither with water
Or the substance of polar functionalities mixes, also not with hydro carbons or the organic matter containing alkyl mixes.Therefore, organic silicon defoamer water,
It is uniformly dissolved in vegetable and animals oils and higher boiling mineral oil.Since silicone oil is to the insoluble of each substance, thus wide application, both made
Fresh water supply system defoaming, and can be used in oil systems.
Anti-settling agent: being the rheology control agent of a kind of coating, it makes coating have thixotropy, and viscosity greatly improves.Anti-settling agent
It plays an important role in modern coatings, the production of coating, storage, coating and film performance is had an important influence on, thus its
Using being paid more and more attention, and constantly develop the novel kind with more preferable performance.
Anti-sag agent: anti-sagging agent refers to the viscosity that paint can be improved, and can hinder in paint curing or work progress
A kind of compound that fluid stopping is hung.
Catalyst: catalyst has in Chemical Manufacture important and is widely applied, and produces chemical fertilizer, pesticide, a variety of chemical industry
Raw material etc. will use catalyst.
Desiccant: suitable for preventing instrument, instrument, electrical equipment, drug, food, textile and other various packing materials
Product dampness, in sea-freight, desiccant is also widely used on the way, because cargo often makes moist change because temperature is big during transportation
Matter, with desiccant can effective moisture excluding, so that the quality of cargo is protected.
Thickener: being a kind of auxiliary rheological agents, can not only coating be made to thicken, and prevents sagging phenomenon occur in construction, and
The excellent mechanical performance of coating and storage stability can be assigned.For water paint lower for viscosity, it is very important
One analog assistant.
Sodium metasilicate: being commonly called as sodium silicate, is a kind of water-soluble silicate, and aqueous solution is commonly called as waterglass, is a kind of mine bonding
Agent.Its chemical formula is R2OnSiO2, and R2O is alkali metal oxide in formula, and n is silica and alkali metal oxide molal quantity
Ratio, the referred to as number that rubs of waterglass.Common waterglass is the aqueous solution of sodium metasilicate in building.
Talcum powder: greasy feeling is touched with for white or off-white color, fine, without grittiness powder, hand.It is odorless, it is tasteless.This product exists
It is insoluble in water, dilute mine acid or dilute alkali hydroxide solution.It can make medicinal.Talcum have lubricity, it is anti-stick, help stream, fire resistance,
Acid-resisting, insulating properties, fusing point height, the chemically excellent object such as torpescence, covering power good, softness, good luster, strong adsorption force
Reason, chemical characteristic, since the crystal structure of talcum is in stratiform, so having the trend and special cunning for easily splitting into scale
Lubricant nature can lower its insulating properties if the content of Fe2O3 is very high.
The invention has the benefit that
1, using Concave-convex clay rod is contained as new construction material, there is stronger absorption property.
2 and contain good suspendability and bonding capacity.
3, in addition, passing through the anti-sagging agent being added, the viscosity of paint can be improved, it can in paint curing or work progress
To prevent a kind of compound of sagging, to effectively prevent point water and precipitating.
4, by the way that sodium metasilicate is added, so that having salt resistance alkali, high temperature resistant.
It 5, is in chemical inertness, it is insensitive to pH value variation, it is environmentally protective.
6, there is fungi-proofing property, product can be kept steady in a long-term.
Detailed description of the invention
It in order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, below will be to institute in embodiment
Attached drawing to be used is needed to be briefly described, it should be apparent that, the accompanying drawings in the following description is only some implementations of the invention
Example, for those of ordinary skill in the art, without creative efforts, can also obtain according to these attached drawings
Obtain other attached drawings.
Fig. 1 is a kind of fabrication processing of the construction material of feature of environmental protection Concave-convex clay rod according to an embodiment of the present invention
Figure.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art's every other embodiment obtained belong to what the present invention protected
Range.
According to an embodiment of the invention, providing a kind of construction material of feature of environmental protection Concave-convex clay rod.
Construction material according to an embodiment of the present invention, the construction material are made of the raw material of following percentage:
Water 35 ~ 48%, thixotropic agent 0.35 ~ 0.75%, titanium dioxide 8 ~ 10%, germproof matter 0.23 ~ 0.30%, defoaming agent 0.1
~ 0.2%, anti-settling agent 2 ~ 5%, anti-sag agent 0.2 ~ 0.5%, catalyst 0.1 ~ 0.4%, desiccant 0.4 ~ 0.7%, thickener 3 ~
5%, sodium metasilicate 5 ~ 8%, talcum powder 14 ~ 19%, filler 10 ~ 20%.
Above-mentioned technical proposal of the invention is understood in order to clearer, below by way of specific example to above-mentioned side of the invention
Case is described in detail.
Embodiment one, the thixotropic agent are one of bentonite, white carbon black and organic rheology modifier or a variety of.
Embodiment two, thickener include inorganic thickening agent, cellulose family, polyacrylate and the thickening of association type polyurethane
Agent.
Embodiment three, the inorganic thickening agent include bentonite, attapulgite, alumina silicate.
Example IV, the defoaming agent are a kind of in organic silicon defoamer or compounding class defoaming agent.
Embodiment five, the anti-settling agent are any one in OPTIGEL, VM/WA/CK/LT.
As shown in Figure 1, according to an embodiment of the invention, additionally providing a kind of construction material of feature of environmental protection Concave-convex clay rod
Manufacture craft.
The following steps are included:
Step S101 chooses natural attapulgite clay raw material, carries out being processed into attapulgite by high-tech special process
Clay；
Step S103 weighs each raw material according to the weight percent pre-set；
Step S105, at room temperature, by germproof matter, defoaming agent, anti-settling agent, anti-sag agent, catalyst, desiccant with
And thickener pours into stirred tank, and water is added and carries out uniform stirring, obtains mixture one；
Mixture one is placed in high speed disperser and disperses by step S107, obtains mixture two；
Step S109 sequentially adds titanium dioxide, sodium metasilicate, talcum powder and filler in mixture two, and in high speed disperser
In it is evenly dispersed, obtain mixture three；
Water is mixed into mixture three and carries out uniform stirring by step S111, obtains mixed liquor one；
Mixed liquor one is poured slowly into thixotropic agent by step S113, and uniform stirring, high speed disperser are carried out in high speed disperser
Revolving speed be 400 ~ 550r/min, the time be 10 ~ 15min, obtain mixed liquor two；
The mixed liquor two stirred evenly is discharged and is filtered by step S115, obtains the Concave-convex clay rod material of the feature of environmental protection
Material；
Step S117, inspection by sampling, qualified post package.
In one embodiment, the revolving speed of the high speed disperser is 700 ~ 780r/min, and the time is 20 ~ 26min.
In one embodiment, the revolving speed of the high speed disperser is 600 ~ 1000r/min, and the time is 15 ~ 20min.
In conclusion, by the construction material containing Concave-convex clay rod, being made by means of above-mentioned technical proposal of the invention
Absorption property must be increased, additionally by the suspension thixotropic agent of addition, so that having good suspendability and bonding capacity, and added
The anti-settling agent entered, so that the inorganic inert powder of acicular texture is formed, to have thixotropy.Under the action of high shear force,
Spicule in colloid system is separated from each other, in parallel, so that colloid thins out；And when shearing force stopping, these spicule phases
It mutually intersects, it is netted to reform into firm colloid.This (for shearing force there are thinning, external force stops retrogradation) mutually conversion
Can be with Infinite Cyclic, thus have the function of the excellent anti-settling, anti-sag of suspension.In addition, mould proof fungi-proofing by containing
The content of agent so that prevent material mouldy and generate bacterium the phenomenon that, improve the environmental-protecting performance of material, thus improve material
Fire prevention, outside moisture-proof and absorption property, greatly improve the environmental-protecting performance of material, be conducive to be directly used in construction
In.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of construction material of feature of environmental protection Concave-convex clay rod, which is characterized in that the construction material by following percentage original
Material is made:
Water 35 ~ 48%, thixotropic agent 0.35 ~ 0.75%, titanium dioxide 8 ~ 10%, germproof matter 0.23 ~ 0.30%, defoaming agent 0.1
~ 0.2%, anti-settling agent 2 ~ 5%, anti-sag agent 0.2 ~ 0.5%, catalyst 0.1 ~ 0.4%, desiccant 0.4 ~ 0.7%, thickener 3 ~
5%, sodium metasilicate 5 ~ 8%, talcum powder 14 ~ 19%, filler 10 ~ 20%.
2. construction material according to claim 1, which is characterized in that the thixotropic agent is bentonite, white carbon black and organic
One of rheology modifier is a variety of.
3. construction material according to claim 1, which is characterized in that thickener includes
Inorganic thickening agent, cellulose family, polyacrylate and association type polyurethane thickener.
4. construction material according to claim 3, which is characterized in that the inorganic thickening agent includes
Bentonite, attapulgite, alumina silicate.
5. construction material according to claim 1, which is characterized in that the defoaming agent is organic silicon defoamer or compounding class
It is a kind of in defoaming agent.
6. construction material according to claim 1, which is characterized in that the anti-settling agent is OPTIGEL, VM/WA/CK/LT
In any one.
7. a kind of manufacture craft of the construction material of feature of environmental protection Concave-convex clay rod, which is characterized in that for described in claim 1
Construction material preparation, comprising the following steps:
Natural attapulgite clay raw material is chosen, carries out being processed into Concave-convex clay rod by high-tech special process；
Each raw material is weighed according to the weight percent pre-set；
At room temperature, by germproof matter, defoaming agent, anti-settling agent, anti-sag agent, catalyst, desiccant and thickener
It pours into stirred tank, water is added and carries out uniform stirring, obtains mixture one；
Mixture one is placed in high speed disperser and is dispersed, mixture two is obtained；
Titanium dioxide, sodium metasilicate, talcum powder and filler are sequentially added in mixture two, and is uniformly divided in high speed disperser
It dissipates, obtains mixture three；
Water is mixed into mixture three and carries out uniform stirring, obtains mixed liquor one；
Mixed liquor one is poured slowly into thixotropic agent, uniform stirring is carried out in high speed disperser, the revolving speed of high speed disperser is
400 ~ 550r/min, time are 10 ~ 15min, obtain mixed liquor two；
The mixed liquor two stirred evenly is discharged and filtered, the Concave-convex clay rod material of the feature of environmental protection is obtained；
Inspection by sampling, qualified post package.
8. construction material according to claim 7, which is characterized in that the revolving speed of the high speed disperser is 700 ~ 780r/
Min, time are 20 ~ 26min.
9. construction material according to claim 7, which is characterized in that the revolving speed of the high speed disperser is 600 ~ 1000r/
Min, time are 15 ~ 20min.