CN109202315A - 两种金属材料叠加焊接的方法 - Google Patents
两种金属材料叠加焊接的方法 Download PDFInfo
- Publication number
- CN109202315A CN109202315A CN201811315668.XA CN201811315668A CN109202315A CN 109202315 A CN109202315 A CN 109202315A CN 201811315668 A CN201811315668 A CN 201811315668A CN 109202315 A CN109202315 A CN 109202315A
- Authority
- CN
- China
- Prior art keywords
- welding
- metal material
- torque
- kinds
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供不同材料叠加焊接的方法，包括第一种金属材料、第二种金属材料和焊接扭矩，所述焊接扭矩与所述第二种金属材料为相同材质，且为焊接性能优先的材质；本发明方案是利用搅拌摩擦焊接工艺将所述第一种金属材料与所述焊接扭矩的一端进行焊接，再将所述焊接扭矩的另一端与所述第二种金属材料进行焊接。本发明对焊接扭矩的巧妙使用能够加强不同金属材料的叠加焊接的强度，降低焊接难度，同时当其焊接接触面积可控，还避免不同材料之间电化学反应的发生。
Description
技术领域
本发明涉及同种或者异种材料焊接的技术领域，尤其涉及两种金属材料叠加焊接的方法。
背景技术
人们在对不同材质的金属材料焊接时，常规的方法是采用焊接金属性能优先的焊条选用原则。即两种材质的金属焊接时，以材质焊接性能较好的金属为标准选用一根焊条进行焊接。这样的焊接方法中，金属的材质与焊条材质相同时，焊接融合金属的各种性能较好，但是因另一材质的金属与焊条材质不同，在焊接融合过程中两种材质的金属只能是直线接触状微融合连接，其焊接的性能强度大大降低。中国专利CN200310117843.1公开了一种不同材质金属材料的焊接方法，在焊接时采用通常的焊接工具及焊接条件。在焊接时在一个焊钳内同时夹持分别与金属材料相对应的两根焊条，并排同时焊接。在焊接时，可以使焊条及焊枪在焊接处呈锯齿形摆动。此发明方法可以使焊条适应各自相对应的金属材料，分别融化焊口，使焊条之间相互融合。但是不能用于不同材料的叠加焊接，目前焊接技术中用于焊接不同材料叠加的方法有激光焊接工艺和超声焊接工艺，这两种焊接工艺焊接面积小，焊接结构强度偏弱，对于某些材料还会发生电化学反应。
发明内容
为了解决以上技术问题，本发明提供两种金属材料叠加焊接的方法，包括第一种金属材料、第二种金属材料和焊接扭矩，所述焊接扭矩与所述第二种金属材料为相同材质，且为焊接性能优先的材质；本发明方案如下：利用搅拌摩擦焊接工艺将所述第一种金属材料与所述焊接扭矩的一端进行焊接，再将所述焊接扭矩的另一端与所述第二种金属材料进行焊接。
进一步的，所述焊接扭矩为有一定厚度的柱体，且焊接完成后其厚度忽略不计；
进一步的，所述焊接扭矩与所述第二种金属材料为相同材质；
进一步的，所述第二种金属材料为焊接性能优先的金属材质；
进一步的，所述焊接扭矩的横截面远小于两种被焊接的金属材料的焊接面；
进一步的，搅拌摩擦焊接的焊接轨迹与所述焊接扭矩横截面形状相同，且焊接面积与所述焊接扭矩横截面积大小一致。
有益效果
本发明所提供的两种金属材料叠加焊接的方法在焊接时采用通常的焊接工具及焊接条件，利用焊接扭矩为焊接媒介先与第一种金属材料采用搅拌摩擦焊接工艺进行焊接，再与第二种金属材料进行焊接，本发明对焊接扭矩的巧妙使用能够加强不同材料的叠加焊接的强度，降低焊接难度，同时其焊接接触面积可控，还避免不同材料之间电化学反应的发生。
附图说明
图1为第一种金属材料焊接结构示意图
图2为第二种金属材料焊接结构示意图
图中各标记的含义为：1，金属铜，2铝柱，3，金属铝，4，焊接轨迹
为了使本发明的技术方案及优点更易于理解，下面将结合附图和具体实施方式对本发明做进一步详细说明。
具体实施方式
应当理解，此处的具体实施方式仅仅用于解释本发明并不用于限定本发明。
在本实施例中，本发明提供的两种金属材料叠加焊接的方法，包括第一种金属材料金属铜1，第二种金属材料金属铝2和焊接扭矩铝柱3，本发明是利用所述铝柱3为焊接媒介，与所述金属铜1焊接，再与所述金属铝2焊接；其方案步骤如下：
首先，将所述金属铜1与所述铝柱3的一端固定在焊接工装上，
然后，将搅拌摩擦焊接机焊接探头插入到所述金属铜1与所述铝柱3接触面，沿接触轨迹进行焊接；
最后，将所述铝柱3的另一端与所述金属铝2利用激光焊接工艺进行焊接；
优选的，铝柱厚度为0.35~0.55毫米；
进一步的，所述铝柱3的横截面面积远小于所述金属铜1和所述金属铝2；
进一步的，所述焊接轨迹4与铝柱3横截面形状相同，且焊接面积与铝柱3横截面积大小一致。
进一步的，本发明所提供的两种金属材料叠加焊接的方法在焊接时采用通常的焊接工具及焊接条件。
上面结合附图和具体实施方式对本发明的两种不同金属材料叠加焊接的方法做了详细的说明，但是本发明并不限于上面所描述的铜和铝之间的叠加焊接，总之，在本领域技术人员所具备的知识范围内，不脱离本发明构思作出的各种变化，仍落在本发明的保护范围内。
Claims (3)
1.本发明提供两种不同金属材料叠加焊接的方法，其特征在于，包括第一种金属材料、第二种金属材料和焊接扭矩，所述焊接扭矩与所述第二种金属材料为相同材质，且为焊接性能优先的材质；本发明方案是利用搅拌摩擦焊接工艺将所述第一种金属材料与所述焊接扭矩的一端进行焊接，再将所述焊接扭矩的另一端与所述第二种金属材料进行焊接。
2.根据权利要求1所述的两种不同金属材料叠加焊接的方法，其特征在于，所述焊接扭矩为有一定厚度的柱体，且焊接完成后其厚度忽略不计。
3.根据权利要求1所述的两种不同金属材料叠加焊接的方法，其特征在于，所述焊接扭矩的横截面远小于两种被焊接的金属材料的焊接面。