CN109183435A - A kind of coating process of sun-proof tentage cloth - Google Patents
A kind of coating process of sun-proof tentage cloth Download PDFInfo
- Publication number
- CN109183435A CN109183435A CN201810801688.1A CN201810801688A CN109183435A CN 109183435 A CN109183435 A CN 109183435A CN 201810801688 A CN201810801688 A CN 201810801688A CN 109183435 A CN109183435 A CN 109183435A
- Authority
- CN
- China
- Prior art keywords
- base fabric
- adhesive glue
- sun
- proof
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of coating process of sun-proof tentage cloth, comprise the following steps that, base fabric are put into containing impregnating in slurry, the component of slurry are as follows: anti-aging agent, anti-yellow agent, plasticizer, stabilizer, adhesive, resin；Base fabric is put into drying box and is dried, coats adhesive glue in the side of base fabric, the sunscreen layer of preparation is quickly covered in coating adhesive glue, and sunscreen layer and base fabric are compressed；Sub-cooled, adhesive glue quickly solidify, and the other side of base fabric coats adhesive glue, and PVC coating is adhered in the adhesive glue of P7, obtain tent cloth after cooling.The invention discloses a kind of coating process of sun-proof tentage cloth, the tent cloth sun-proof result of preparation is good, and sun-proof coating is firmly bonded with tent base fabric, and sun-proof coating is not easily to fall off；And anti-aging effect is good, is effectively isolated ultraviolet light.
Description
Technical field
The present invention relates to the treatment process of tent cloth, specially a kind of coating process of sun-proof tentage cloth.
Background technique
Tent is the common equipment of outdoor activities, and tent is to support to cover Feng Yu ﹑ daylight and the canopy for temporarily living on the ground
Son.Multi-purpose canvas is made into, and together with the thing of support, can remove transfer at any time.Tent is carried in a manner of component, is reached existing
It is just assembled after, it is therefore desirable to various parts and tool.The title and application method for understanding all parts, are familiar with tent
Construction, could quickly and easily set up tent.
Main problem existing for tent cloth in the prior art are as follows: 1, the sun-proof result of existing tent it is poor, use
When, it is easy jaundice, it is difficult to effective isolation ultraviolet；2, it when in use due to tent, needs to fold, expansion；And its damage account
The sun-proof coating of tarpaulin material, using after a certain period of time, poor toughness, sun-proof coating is easy to fall off tent cloth；3, existing tent
The complex production process of cloth.
Summary of the invention
To solve the above problems, the invention discloses a kind of coating process of sun-proof tentage cloth, the tent cloth of preparation
Sun-proof result is good, and sun-proof coating is firmly bonded with tent base fabric, and sun-proof coating is not easily to fall off；And anti-aging effect is good, effectively
Isolation ultraviolet.
In order to reach the goals above, the invention provides the following technical scheme:
A kind of coating process of sun-proof tentage cloth, comprises the following steps that,
P1: base fabric is impregnated, and base fabric is put into containing impregnating in slurry, soaking time 30-120min, the component of slurry are as follows:
Anti-aging agent, anti-yellow agent, plasticizer, stabilizer, adhesive, resin；
P2: base fabric is put into 40-80 degrees Celsius of drying box and dries by base fabric drying, drying time 20-60min；
P3: the preparation of sunscreen layer,
P4: coating adhesive glue coats adhesive glue in the side of base fabric, carries out bottoming processing to base fabric；Adhesive glue carries out at heating
Reason, heating temperature are 120-200 degrees Celsius, so that adhesive glue is molten, are then uniformly coated in the side of base fabric；
P5: the sunscreen layer that will be prepared during P3 is quickly covered in coating adhesive glue, and sunscreen layer and base fabric are compressed；
P6: the base fabric after compression, sub-cooled, adhesive glue quickly solidify, while cooling in cooling chamber, using pressing roller into
The compression of one step；
P7: the other side of base fabric coats adhesive glue, carries out bottoming processing to base fabric, adhesive glue is heated, heating temperature
It is 80-120 degrees Celsius, so that adhesive glue is molten, is then uniformly coated in the other side of base fabric；
P8: PVC coating is adhered in the adhesive glue of P7, obtains tent cloth after cooling.
Further, the component of sunscreen layer are as follows: polyurethane, filler, film forming agent, defoaming agent, ultraviolet absorbing agent, titanium white
Powder, water.
Further, the mass fraction of each component of sunscreen layer are as follows: 20-40 parts of polyurethane, 10-25 parts of filler, film forming agent
5-10 parts, 2-5 parts of defoaming agent, 3-10 parts of ultraviolet absorbing agent, 0.5-5 parts of titanium dioxide, 15-25 parts of water.
Further, filler uses the one of which of Concave-convex clay rod, calcium carbonate.
Further, ultraviolet absorbing agent is benzotriazole, 2,4-DihydroxyBenzophenone and single benzoic acid isophthalic two
The one or more of them of phenolic ester.
Further, the sunscreen layer the preparation method comprises the following steps: the component case mass fraction ratio of sunscreen layer mixes, mixing
It stirs in the process, ultrasonic procedure, film forming is squeezed after the completion of stirring, form sunscreen layer.
The present invention has the advantage that
The coating process of sun-proof tentage cloth of the present invention, so that tent cloth has good sun-proof result, using tow sides point
Not Tu Fu sunscreen layer and layer of PVC, realize good sun-proof result, and tent is not easy to turn to be yellow, good isolation ultraviolet；Sun-proof painting
Layer and the bonding of tent base fabric are firm, and sun-proof coating is not easily to fall off.Technological operation simultaneously is simple, realizes good industrialized production
The tent cloth good toughness of manufacture, sun-proof performance are high.
Specific embodiment
The present invention relates to the coating process for a kind of sun-proof tentage cloth, are a kind of preparation methods of tent cloth.
Herein with respect to its feature, aspect and example it is various illustrate the present invention in certain embodiments can be by structure
Making is to include, and forms or substantially by these features, some or all of aspect and example composition are used as its element and component
It is aggregated to constitute various further embodiments of the invention.The present invention is correspondingly imagined with various arrangements and combination in this hair
These features in bright range, aspect and example or selected one or more features, aspect and example.
With reference to embodiment, the present invention is furture elucidated, it should be understood that following specific embodiments are only used for
It is bright the present invention rather than limit the scope of the invention.
Embodiment 1
A kind of coating process of sun-proof tentage cloth, comprises the following steps that,
P1: base fabric is impregnated, and base fabric is put into containing impregnating in slurry, soaking time 30-120min, the component of slurry are as follows:
Anti-aging agent, anti-yellow agent, plasticizer, stabilizer, adhesive, resin；
P2: base fabric is put into 40-80 degrees Celsius of drying box and dries by base fabric drying, drying time 20-60min；
P3: the preparation of sunscreen layer, sunscreen layer the preparation method comprises the following steps: the component case mass fraction ratio of sunscreen layer mixes, mixing
It stirs in the process, ultrasonic procedure, film forming is squeezed after the completion of stirring, form sunscreen layer；
P4: coating adhesive glue coats adhesive glue in the side of base fabric, carries out bottoming processing to base fabric；Adhesive glue carries out at heating
Reason, heating temperature are 120-200 degrees Celsius, so that adhesive glue is molten, are then uniformly coated in the side of base fabric；
P5: the sunscreen layer that will be prepared during P3 is quickly covered in coating adhesive glue, and sunscreen layer and base fabric are compressed；
P6: the base fabric after compression, sub-cooled, adhesive glue quickly solidify, while cooling in cooling chamber, using pressing roller into
The compression of one step；
P7: the other side of base fabric coats adhesive glue, carries out bottoming processing to base fabric, adhesive glue is heated, heating temperature
It is 80-120 degrees Celsius, so that adhesive glue is molten, is then uniformly coated in the other side of base fabric；
P8: PVC coating is adhered in the adhesive glue of P7, obtains tent cloth after cooling.
In the present embodiment, the component of sunscreen layer are as follows: polyurethane, filler, film forming agent, defoaming agent, ultraviolet absorbing agent, titanium
White powder, water.
In the present embodiment, filler uses the one of which of Concave-convex clay rod, calcium carbonate.
In the present embodiment, ultraviolet absorbing agent is between benzotriazole, 2,4-DihydroxyBenzophenone and single benzoic acid
The one or more of them of benzenediol ester.
Embodiment 2
In the present embodiment, the mass fraction of each component of sunscreen layer are as follows: 20 parts of polyurethane, 5 parts of film forming agent, disappears at 10 parts of filler
2 parts of infusion, 3 parts of ultraviolet absorbing agent, 0.5 part of titanium dioxide, 15 parts of water.
In the present embodiment, filler uses Concave-convex clay rod.
In the present embodiment, ultraviolet absorbing agent is benzotriazole and 2,4-DihydroxyBenzophenone, mass fraction
Ratio is 1:1.
Remaining step is same as Example 1.
Embodiment 3
In the present embodiment, the mass fraction of each component of sunscreen layer are as follows: 40 parts of polyurethane, 10 parts of film forming agent, disappears at 25 parts of filler
5 parts of infusion, 10 parts of ultraviolet absorbing agent, 5 parts of titanium dioxide, 25 parts of water.
In the present embodiment, filler uses calcium carbonate.
In the present embodiment, ultraviolet absorbing agent is 2,4-DihydroxyBenzophenone and single benzoic acid resorcinol,
Mass fraction ratio is 3:2.
Remaining step is same as Example 1.
Embodiment 4
In the present embodiment, the mass fraction of each component of sunscreen layer are as follows: 30 parts of polyurethane, 8 parts of film forming agent, disappears at 15 parts of filler
3 parts of infusion, 6 parts of ultraviolet absorbing agent, 2 parts of titanium dioxide, 18 parts of water.
In the present embodiment, filler uses Concave-convex clay rod.
In the present embodiment, ultraviolet absorbing agent is between benzotriazole, 2,4-DihydroxyBenzophenone and single benzoic acid
Benzenediol ester, mass fraction ratio are 1:1:1.
Remaining step is same as Example 1.
The technical means disclosed in the embodiments of the present invention is not limited only to technological means disclosed in above embodiment, further includes
Technical solution consisting of any combination of the above technical features.It should be pointed out that for those skilled in the art
For, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (6)
1. a kind of coating process of sun-proof tentage cloth, it is characterised in that:
It comprises the following steps that,
P1: base fabric is impregnated, and base fabric is put into containing impregnating in slurry, soaking time 30-120min, the component of slurry are as follows:
Anti-aging agent, anti-yellow agent, plasticizer, stabilizer, adhesive, resin；
P2: base fabric is put into 40-80 degrees Celsius of drying box and dries by base fabric drying, drying time 20-60min；
P3: the preparation of sunscreen layer,
P4: coating adhesive glue coats adhesive glue in the side of base fabric, carries out bottoming processing to base fabric；Adhesive glue carries out at heating
Reason, heating temperature are 120-200 degrees Celsius, so that adhesive glue is molten, are then uniformly coated in the side of base fabric；
P5: the sunscreen layer that will be prepared during P3 is quickly covered in coating adhesive glue, and sunscreen layer and base fabric are compressed；
P6: the base fabric after compression, sub-cooled, adhesive glue quickly solidify, while cooling in cooling chamber, using pressing roller into
The compression of one step；
P7: the other side of base fabric coats adhesive glue, carries out bottoming processing to base fabric, adhesive glue is heated, heating temperature
It is 80-120 degrees Celsius, so that adhesive glue is molten, is then uniformly coated in the other side of base fabric；
P8: PVC coating is adhered in the adhesive glue of P7, obtains tent cloth after cooling.
2. a kind of coating process of sun-proof tentage cloth as described in claim 1, it is characterised in that: the component of sunscreen layer are as follows:
Polyurethane, filler, film forming agent, defoaming agent, ultraviolet absorbing agent, titanium dioxide, water.
3. a kind of coating process of sun-proof tentage cloth as claimed in claim 2, it is characterised in that: each component of sunscreen layer
Mass fraction are as follows: 20-40 parts of polyurethane, 10-25 parts of filler, 5-10 parts of film forming agent, 2-5 parts of defoaming agent, ultraviolet absorbing agent 3-
10 parts, 0.5-5 parts of titanium dioxide, 15-25 parts of water.
4. a kind of coating process of sun-proof tentage cloth as claimed in claim 2 or claim 3, it is characterised in that: filler is using concave-convex
The one of which of stick stone clay, calcium carbonate.
5. a kind of coating process of sun-proof tentage cloth as claimed in claim 2 or claim 3, it is characterised in that: ultraviolet absorbing agent
For benzotriazole, the one or more of them of 2,4 dihydroxyl benzophenone and single benzoic acid resorcinol.
6. a kind of coating process of sun-proof tentage cloth as described in claim 1, it is characterised in that: the preparation of the sunscreen layer
Method are as follows: the component case mass fraction ratio of sunscreen layer mixes, and stirs in mixed process, ultrasonic procedure, squeezes after the completion of stirring
It is pressed into film, forms sunscreen layer.