CN109183428A - A kind of production method of anti-static function fabric - Google Patents
A kind of production method of anti-static function fabric Download PDFInfo
- Publication number
- CN109183428A CN109183428A CN201811379346.1A CN201811379346A CN109183428A CN 109183428 A CN109183428 A CN 109183428A CN 201811379346 A CN201811379346 A CN 201811379346A CN 109183428 A CN109183428 A CN 109183428A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- static function
- production method
- following
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production method of anti-static function fabric, the charge density of Antistatic Fabric prepared by the present invention is 1.8-2.8 μ e/m2, electrostatic potential is between 210-220V, sheet resistance 6.5 × 106~7.5 × 106Ω illustrates that Antistatic Fabric of the invention has good antistatic property；In addition, preparation process of the invention is simple, production cost is low, there is the preferable market competitiveness.
Description
Technical field
The invention belongs to field of textile, and in particular to a kind of production method of anti-static function fabric.
Background technique
Fabric is formed by warp thread and weft yarn according to certain density weave, with mentioning for people's material and cultural life
Height, common fabric are increasingly difficult to meet the requirement of people's diversification under varying environment, different condition, functional fiber and face
Material then embodies oneself inborn advantage in this respect, can satisfy requirement of the people to the more and more members of fabric.
Existing fabric is usually to be made of chemical fibre fabric, which is easy to volatilize, and environment is more dry
Dry season, electrostatic just at problem, electrostatic can generally allow the easy pilling of Antistatic Fabric, become easily infected by dust dirt, patch
Nearly skin and with electric-shock feeling etc..Especially the arriving of autumn and winter, temperature are begun to decline, air humidity relative reduction, therefore,
Autumn and winter, which wears the clothes etc., has been easier electrostatic, some industries for example print medical care industry, stringenter for the requirement for controlling electrostatic.
The prior art generally uses hydrophilic finiss or adds the method for conductive fiber, keeps fabric conductive, to have
Antistatic property, these are all that so that fabric is had antistatic property by post-processing, and complex process wastes a large amount of people
Power resource.
Summary of the invention
The technical problem to be solved by the present invention is for the difference of anti-static function existing for existing anti-static function fabric and
The series of problems such as production cost height, providing one kind not only has preferable anti-static function, also has resisting for good comfort quiet
Electricity Functional fabric.
The technical solution adopted in the present invention is as follows:
A kind of production method of anti-static function fabric, comprising the following steps:
(1) face liber described in is made of the raw material of following parts by weight meter: 10-30 parts of polyvinyl chloride, poly terephthalic acid second
5-10 parts of diol ester, 0.5-4 parts of coconut oil diethanol amide, 10-30 parts of zinc stearate, 2-8 parts of silica, asphalt mixtures modified by epoxy resin
3-5 parts of rouge, 10-15 parts of filler；
(2) it rinses and dries after padding the face liber of step (1) in the liquid antistatic of following weight percent: 0.5-
2% antistatic agent, the binder of 0.5-1.5%, the ethyl alcohol of 6-12% and 70-90% water；
(3) fabric after step (2) drying is put into forming machine and is formed, forming machine is warming up to 160- with 5 ~ 20 DEG C/min
165 DEG C, anti-static function fabric can be obtained.
Based on the above technical solution, in above-mentioned steps (1) face liber preferably by the raw material of following parts by weight meter
It is made: 20 parts of polyvinyl chloride, 8 parts of polyethylene terephthalate, 2 parts of coconut oil diethanol amide, zinc stearate 120
Part, 5 parts of silica, 4 parts of epoxy resin, 12 parts of filler.
Further, liquid antistatic preferably comprises the following raw materials by weight percent in above-mentioned steps (2):
1% antistatic agent, 1% binder, 10% ethyl alcohol and 88% water.
Compared with prior art, the device have the advantages that it is as follows:
The charge density of Antistatic Fabric prepared by the present invention is 1.8-2.8 μ e/m2, electrostatic potential between 210-220V,
Sheet resistance 6.5 × 106~7.5 × 106Ω illustrates that Antistatic Fabric of the invention has good antistatic property, avoids
Fabric is since material easily generates electrostatic between skin below for dehydration, and structure is simple, and the coefficient of friction of fabric can be effectively reduced, subtract
The yield of electrostatic charge, static electricity resistance with higher in few friction；In addition, preparation process of the invention is simple, production cost
It is low, there is the preferable market competitiveness.
Specific embodiment
Of the invention for ease of understanding, it is as follows that the present invention enumerates embodiment.Those skilled in the art are it will be clearly understood that the implementation
Example is used only for helping to understand the present invention, should not be regarded as a specific limitation of the invention.
Unless specific instructions, various raw materials of the invention can be by being commercially available；Or the routine side according to this field
Method is prepared.Unless otherwise defined or described herein, all professional and scientific terms and art technology used herein are ripe
It is identical to practice meaning known to the person of entering.Furthermore any method similar to or equal to what is recorded and material all can be applied to this
In inventive method.Unless otherwise stated, all professional and scientific terms and those skilled in the art used herein
Known meaning is identical.
Embodiment 1
A kind of production method of anti-static function fabric, comprising the following steps:
(1) face liber described in is made of the raw material of following parts by weight meter: 20 parts of polyvinyl chloride, poly terephthalic acid second two
8 parts of alcohol ester, 2 parts of coconut oil diethanol amide, 120 parts of zinc stearate, 5 parts of silica, 4 parts of epoxy resin, filler 12
Part；
(2) it rinses and dries after padding the face liber of step (1) in the liquid antistatic of following weight percent: 1%
Antistatic agent, 1% binder, 10% ethyl alcohol and 88% water；
(3) fabric after step (2) drying is put into forming machine and is formed, forming machine is warming up to 162 DEG C with 10 DEG C/min, i.e.,
Anti-static function fabric can be obtained.
The performance parameter for testing fabric prepared by the present embodiment is as follows:
Charge density is 2.5 μ e/m2, electrostatic potential is between 215V, sheet resistance 7.0 × 106Ω shows the present embodiment
Antistatic Fabric has good antistatic property.
Embodiment 2
A kind of production method of anti-static function fabric, comprising the following steps:
(1) face liber described in is made of the raw material of following parts by weight meter: 10 parts of polyvinyl chloride, poly terephthalic acid second two
5 parts of alcohol ester, 0.5 part of coconut oil diethanol amide, 10 parts of zinc stearate, 2 parts of silica, 3 parts of epoxy resin, filler
10 parts；
(2) it rinses and dries after padding the face liber of step (1) in the liquid antistatic of following weight percent: 1%
Antistatic agent, 1% binder, 10% ethyl alcohol and 88% water；
(3) fabric after step (2) drying is put into forming machine and is formed, forming machine is warming up to 162 DEG C with 10 DEG C/min, i.e.,
Anti-static function fabric can be obtained.
The performance parameter for testing fabric prepared by the present embodiment is as follows:
Charge density is 2.0 μ e/m2, electrostatic potential is between 210V, sheet resistance 6.5 × 106Ω shows the present embodiment
Antistatic Fabric has good antistatic property.
Embodiment 3
A kind of production method of anti-static function fabric, comprising the following steps:
(1) face liber described in is made of the raw material of following parts by weight meter: 30 parts of polyvinyl chloride, poly terephthalic acid second two
10 parts of alcohol ester, 4 parts of coconut oil diethanol amide, 30 parts of zinc stearate, 8 parts of silica, 5 parts of epoxy resin, filler 15
Part；
(2) it rinses and dries after padding the face liber of step (1) in the liquid antistatic of following weight percent: 1%
Antistatic agent, 1% binder, 10% ethyl alcohol and 88% water；
(3) fabric after step (2) drying is put into forming machine and is formed, forming machine is warming up to 162 DEG C with 10 DEG C/min, i.e.,
Anti-static function fabric can be obtained.
The performance parameter for testing fabric prepared by the present embodiment is as follows:
Charge density is 2.6 μ e/m2, electrostatic potential is between 220V, sheet resistance 7.2 × 106Ω shows the present embodiment
Antistatic Fabric has good antistatic property.
Although the detailed description and description of the specific embodiments of the present invention are given above, it should be noted that
We can carry out various equivalent changes and modification to above embodiment according to the concept of the present invention, and generated function is made
It, should all be within protection scope of the present invention when with the spirit still covered without departing from specification.
Claims (3)
1. a kind of production method of anti-static function fabric, which comprises the following steps:
(1) face liber described in is made of the raw material of following parts by weight meter: 10-30 parts of polyvinyl chloride, poly terephthalic acid second
5-10 parts of diol ester, 0.5-4 parts of coconut oil diethanol amide, 10-30 parts of zinc stearate, 2-8 parts of silica, asphalt mixtures modified by epoxy resin
3-5 parts of rouge, 10-15 parts of filler；
(2) it rinses and dries after padding the face liber of step (1) in the liquid antistatic of following weight percent: 0.5-
2% antistatic agent, the binder of 0.5-1.5%, the ethyl alcohol of 6-12% and 70-90% water；
(3) fabric after step (2) drying is put into forming machine and is formed, forming machine is warming up to 160- with 5 ~ 20 DEG C/min
165 DEG C, anti-static function fabric can be obtained.
2. such as wanting a kind of production method of anti-static function fabric described in claim 1, which is characterized in that the step (1)
Middle face liber is made of the raw material of following parts by weight meter: 20 parts of polyvinyl chloride, 8 parts of polyethylene terephthalate, coconut palm
2 parts of seed oil diglycollic amide, 120 parts of zinc stearate, 5 parts of silica, 4 parts of epoxy resin, 12 parts of filler.
3. such as wanting a kind of production method of anti-static function fabric described in claim 1, which is characterized in that the step (2)
Middle liquid antistatic comprises the following raw materials by weight percent:
1% antistatic agent, 1% binder, 10% ethyl alcohol and 88% water.