CN109181116A - A kind of preparation method of high abrasion scratch resistance polypropylene pipe - Google Patents
A kind of preparation method of high abrasion scratch resistance polypropylene pipe Download PDFInfo
- Publication number
- CN109181116A CN109181116A CN201810944391.0A CN201810944391A CN109181116A CN 109181116 A CN109181116 A CN 109181116A CN 201810944391 A CN201810944391 A CN 201810944391A CN 109181116 A CN109181116 A CN 109181116A
- Authority
- CN
- China
- Prior art keywords
- scratch resistance
- high abrasion
- preparation
- polypropylene pipe
- abrasion scratch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of high abrasion scratch resistance polypropylene pipe.Include following components in percentage by weight: PP resin 70 ~ 85%, calcium sulfate crystal whiskers 8 ~ 20%, silicone powder 1 ~ 3%, aluminium oxide 2 ~ 8%, fluorine-containing auxiliary agent 0.1 ~ 3%, antioxidant 0.1 ~ 0.5%.Polypropylene pipe of the present invention has the characteristics that high abrasion scratch resistance and excellent in mechanical performance, while extrusion pressure when can reduce processing, reduces energy consumption, eliminates melt fracture, improves the processing performance of material.
Description
Technical field
The present invention relates to a kind of preparations of high abrasion scratch resistance random copolymerization polypropylene pipe.
Background technique
Polypropylene random copolymer pipe (PPR pipe), have light weight, excellent shock resistance, long-term creep resistance it is good,
Pressure-and heat-resistance, it is resistant to chemical etching the advantages that, be the energy saving and environment friendly plastic pipe of a new generation.But what PPR pipe was used to convey for a long time
When, tube wall can cause scratch, abrasion because of the erosion of fluid, and scratch will lead to stress concentration, and abrasion causes wall thickness thinning,
The mechanical property for thereby reducing tubing makes tubing rupture and leakage.Simultaneously PPR pipe since molecular weight is larger, poor processability,
It is easy to produce melt fracture, " sharkskin " phenomenon occurs;Phenomena such as production efficiency is low, die head buildup.
Fluoropolymer additive is that have extremely low surface energy using fluorine compounds, can be reduced and adds in plastic processing
Interior friction between work molecular resin increases the morphotropism of melting rate and melt, reduces apparent melt viscosity, improves overall plasticizing
Effect.Simultaneously it processing resin in solubility it is lower, incompatible, bath surface is exuded to from melt in process,
Separation layer is formed at resin-equipment interface, reduces the adhesion strength of melt and body, die orifice metal surface, is reduced melt and is being transported
The friction generated during dynamic with wall improves the uneven state of bath movement in process.
Summary of the invention
It is an object of the invention to prepare a kind of high abrasion scratch resistance random copolymerization polypropylene pipe and preparation method thereof, lead to
It crosses and adds the processing performance that a fluorine auxiliary agent improves tubing, reduce extrusion pressure, reduce energy consumption, improve the production effect of tubing
Rate.
To achieve the above object, the technical scheme adopted by the invention is as follows: PP resin 70 ~ 85%, calcium sulfate crystal whiskers 8 ~ 20%, silicon
Ketone powder 1 ~ 3%, aluminium oxide 2 ~ 8%, fluorine-containing auxiliary agent 0.1 ~ 3%, antioxidant 0.1 ~ 0.5%.
Preferably, PP resin 75 ~ 80%, preferably atactic copolymerized polypropene (PPR).
Preferably, antioxidant preferably three [2.4- di-tert-butyl-phenyl] phosphite ester: four [β-(3,5- di-t-butyl -4- hydroxyls
Base phenyl) propionic acid] pentaerythritol ester=1:2.
Preferably, aluminium oxide is α-nano aluminium oxide.
Preferably, fluorine-containing auxiliary agent is fluoroelastomer, and fluoropolymer mass fraction is 99%.
Preferably, the fluorine-containing auxiliary agent is the copolymer of Fluorine containing olefine or the copolymer of fluoroolefin and other alkene.
Preferably, it is extruded as twin-screw extrusion, extrusion process is 160 ~ 170 DEG C of area's temperature, two area's temperature 165 ~ 175
DEG C, three 170 ~ 180 DEG C of area's temperature, four 170 ~ 180 DEG C of area's temperature, five 170 ~ 180 DEG C of area's temperature, 170 ~ 185 DEG C of head temperature, master
300 ~ 450 revs/min of machine revolving speed.
The invention has the benefit that
PPR pipe of the invention has high abrasion scratch resistance, and excellent in mechanical performance, surface is smooth, high production efficiency.It simultaneously can
Extrusion pressure when reducing processing reduces energy consumption, eliminates melt fracture, improves the processing performance of material.
Specific embodiment
Embodiment 1
A kind of high abrasion scratch resistance polypropylene pipe compound additive and preparation method thereof.Group comprising following weight percent
Point: atactic copolymerized polypropene 75%, calcium sulfate crystal whiskers 17%, silicone powder 2.4%, aluminium oxide 5%, fluorine-containing auxiliary agent 0.3% (P990, on
Hai Weiyi Chemical Industry Science Co., Ltd), three [2.4- di-tert-butyl-phenyl] phosphite esters 0.3% be blended, be extruded as twin-screw
It squeezes out, extrusion process is 165 DEG C of area's temperature, two 170 DEG C of area's temperature, three 175 DEG C of area's temperature, four 175 DEG C of area's temperature, five area's temperature
175 DEG C of degree, 350 revs/min of engine speed, obtains random copolymerization polypropylene pipe by 175 DEG C of head temperature.
Embodiment 2
A kind of high abrasion scratch resistance polypropylene pipe compound additive and preparation method thereof.Group comprising following weight percent
Point: atactic copolymerized polypropene 75%, calcium sulfate crystal whiskers 15%, silicone powder 2.4%, aluminium oxide 7%, fluorine-containing auxiliary agent 0.3%(P990, Shanghai
The easy Chemical Industry Science Co., Ltd of Wei), three [2.4- di-tert-butyl-phenyl] phosphite esters 0.3% be blended, be extruded as twin-screw squeeze
Out, extrusion process is 165 DEG C of area's temperature, two 170 DEG C of area's temperature, three 175 DEG C of area's temperature, four 175 DEG C of area's temperature, five area's temperature
175 DEG C, 175 DEG C of head temperature, 350 revs/min of engine speed, obtain random copolymerization polypropylene pipe.
Embodiment 3
A kind of high abrasion scratch resistance polypropylene pipe compound additive and preparation method thereof.Group comprising following weight percent
Point: atactic copolymerized polypropene 75%, calcium sulfate crystal whiskers 17%, silicone powder 2.4%, aluminium oxide 5%, fluorine-containing auxiliary agent 0.3% (P960S, on
Hai Weiyi Chemical Industry Science Co., Ltd), three [2.4- di-tert-butyl-phenyl] phosphite esters 0.3% be blended, be extruded as twin-screw
It squeezes out, extrusion process is 165 DEG C of area's temperature, two 170 DEG C of area's temperature, three 175 DEG C of area's temperature, four 175 DEG C of area's temperature, five area's temperature
175 DEG C of degree, 350 revs/min of engine speed, obtains random copolymerization polypropylene pipe by 175 DEG C of head temperature.
1 performance test project of table and standard
2 sample testing result of table
Finally, it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention rather than protects model to the present invention
The limitation enclosed, although the invention is described in detail with reference to the preferred embodiments, those skilled in the art should understand that,
It can be with modification or equivalent replacement of the technical solution of the present invention are made, without departing from the essence and model of technical solution of the present invention
It encloses.
Claims (10)
1. a kind of preparation method of high abrasion scratch resistance polypropylene pipe, which is characterized in that by following components in percentage by weight
It is made: PP resin 70 ~ 85%, calcium sulfate crystal whiskers 8 ~ 20%, silicone powder 1 ~ 3%, aluminium oxide 2 ~ 8%, fluorine-containing auxiliary agent 0.1 ~ 3%, antioxidant
0.1~0.5%。
2. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as described in claim 1, it is characterised in that: the PP tree
Rouge is atactic copolymerized polypropene.
3. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as described in claim 1, it is characterised in that: aluminium oxide is
Alumina in Nano level.
4. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as claimed in claim 3, it is characterised in that: the nanometer
Aluminium oxide is Alpha-alumina.
5. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as described in claim 1, it is characterised in that: calcium sulfate is brilliant
Palpus draw ratio is 5-80.
6. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as described in claim 1, it is characterised in that: the antioxygen
Agent is three [2.4- di-tert-butyl-phenyl] phosphite esters and four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythrites
The mixture of ester, three [2.4- di-tert-butyl-phenyl] phosphite ester and four [β-(3,5- di-tert-butyl-hydroxy phenyl) third
Acid] pentaerythritol ester weight ratio be 1:2.
7. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as described in claim 1, it is characterised in that: described fluorine-containing
Auxiliary agent is fluoropolymer auxiliary agent, and fluoropolymer auxiliary agent is fluoroelastomer, and the fluoropolymer mass fraction in fluoroelastomer is
99%。
8. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as claimed in claim 7, it is characterised in that: described fluorine-containing
Auxiliary agent is the copolymer of Fluorine containing olefine or the copolymer of fluoroolefin and other alkene.
9. a kind of preparation method of high abrasion scratch resistance polypropylene pipe, it is characterised in that: weigh PP resin, the sulfuric acid of formula ratio
Calcium pyroborate, silicone, aluminium oxide, fluorine-containing auxiliary agent, antioxidant, carry out high speed blending, and extrusion molding obtains high abrasion scratch resistance poly- third
Alkene tubing.
10. a kind of preparation method of high abrasion scratch resistance polypropylene pipe as claimed in claim 9, it is characterised in that: squeeze out
For twin-screw extrusion, extrusion process is 160 ~ 170 DEG C of area's temperature, two 165 ~ 175 DEG C of area's temperature, three 170 ~ 180 DEG C of area's temperature,
Four 170 ~ 180 DEG C of area's temperature, five 170 ~ 180 DEG C of area's temperature, 170 ~ 185 DEG C of head temperature, 300 ~ 450 revs/min of engine speed.