CN109174038A - The absorption cleaning agent of free formaldehyde content in a kind of reduction impregnated paper - Google Patents
The absorption cleaning agent of free formaldehyde content in a kind of reduction impregnated paper Download PDFInfo
- Publication number
- CN109174038A CN109174038A CN201811170379.5A CN201811170379A CN109174038A CN 109174038 A CN109174038 A CN 109174038A CN 201811170379 A CN201811170379 A CN 201811170379A CN 109174038 A CN109174038 A CN 109174038A
- Authority
- CN
- China
- Prior art keywords
- cleaning agent
- impregnated paper
- absorption cleaning
- added
- free formaldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to new function material technical fields, disclose a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper, with diatomite, cerous nitrate, ferric nitrate etc. is that raw material prepares absorption cleaning agent, the absorption cleaning agent being prepared is added in impregnating resin, it can with very high surface-active and surface, absorption property is excellent, there is lesser aperture and Kong Rong simultaneously, it can play the role of retention to stop, pass through photocatalytic degradation, innocuous substance is converted by formaldehyde, overcome residues of formaldehyde problem caused by being not thorough due to adsorbent material purification, and adhesion strength and ageing-resistant performance improve, free formaldehyde content is less than 0.06% in resin, reach European E0 grade standard, formaldehyde later period burst size is lower than 0.55 milligram/100 grams, can effectively solve the problem that Form aldehyde release, there is chronicity, intractable With repetitious problem, ensure that the safety in utilization of impregnated paper, the service performances such as the wear-resisting, water-fast of impregnated paper, resistant get a promotion.
Description
Technical field
The invention belongs to new function material technical fields, and in particular to a kind of to reduce free formaldehyde content in impregnated paper
Absorption cleaning agent.
Background technique
Impregnated paper is a kind of plain color paper or printed decoration paper by impregnating resin, and dry to obtaining afterwards to a certain degree
, the bond paper with certain resin content and volatile content is glued with artificial board substrate after hot pressing.Impregnated paper and its
Its surface decoration material compares, and has operating procedure simple, and surface property is excellent, and surface detail is beautiful, cheap, resistance to height
The advantages that warm.Phenol glue water retting paper is a kind of decorative paper impregnated through phenolic resin, for improving the surface property of wood-based plate,
It has been widely used in building plain form industry.PSF can generate self-curing under high temperature, condition of high voltage, be used in hardwood,
Plate and cork clad can with bottom paper.Advantage has: widely used-PSF serves many purposes, and is such as used for cement formwork, vehicle
Compartment bottom plate, container, cabinet, storage shelf and bin etc.;Acidproof, alkaline-resisting, the resistance to organic chemicals of persistence-PSF, resistance to neutrality
And ackd salt, therefore substantially increase the number of turnover of cement formwork;Outdoor application-PSF overlaid wood based panel weatherability is good,
It is handled without finishing;Visual effect-can cover the random defect of substrate, and form uniform solid object surface;Processing
Property-sawing, fluting, drilling property it is good, the breakage and chipping of veneer can be reduced.
As the step of urban construction is accelerated, ornament materials has obtained faster development, and impregnated paper industry is due to starting point
Lower, currently, professional is few in industry, so that industry development level is uneven, product quality cannot be ensured.Impregnated paper is in life
The release that the greatest problem faced in use process is exactly pernicious gas is produced, particularly pertinent is that content of formaldehyde is exceeded.This is to ring
Border and human body cause great harm.And solution is mostly by controlling synthetic ratio at present, optimized production process uses envelope
That closes material prevention formaldehyde is released to major way, and can not have the function that thorough absorption cleaning, still can be in the later period
Free formaldehyde is continually released, interior is entered, is done harm to huamn body.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of absorption for reducing free formaldehyde content in impregnated paper is provided
Cleanser, free formaldehyde content reaches European E0 grade standard, formaldehyde later period burst size is lower than 0.55 milli less than 0.06% in resin
Gram/100 grams, it can effectively solve the problem that Form aldehyde release there is chronicity, intractable and repetitious problem, has ensured impregnated paper
Safety in utilization.
The present invention is achieved by the following technical solutions:
The absorption cleaning agent of free formaldehyde content in a kind of reduction impregnated paper, preparation method includes the following steps:
(1) 33-35 grams of diatomite is weighed, 150-180 mesh of pulverizing is added 300-350 milliliters into diatomite in powder and goes
Ionized water is uniformly mixed to obtain slurry, and 50-60 milliliters of sodium hydroxide solutions are then added into slurry, is ultrasonically treated 15-
20 minutes, 6-7 hours are stood, upper layer suspension is gone, sediment is obtained, it is molten that 80-90 milliliters of hydrochloric acid are added into sediment
Liquid is stirred 40-50 minutes, is added in round-bottomed flask, is placed in water bath with thermostatic control that be heated to reflux 2-3 at 75-80 DEG C small
When, it is then filtered, obtained filter residue makes to be washed with deionized to pH between 6.5-6.8, is subsequently placed in 80-90 DEG C of baking
Drying is spare to constant weight in case;
(2) 6.6-6.8 grams of six nitric hydrate ceriums and 7.4-7.6 grams of Fe(NO3)39H2O are weighed, is placed in a beaker, 45-50 is added
Ml deionized water, heating water bath are added 2.2-2.4 grams of citric acid to 38-40 DEG C under magnetic stirring, stir 30-40 minutes
After form uniform mixture, using concentrated ammonia liquor regulation system pH value between 5.7-5.9, then freezed at a temperature of subzero 15 DEG C
Vacuum drying 10-12 hours, further pulverizes, is transferred in crucible, calcine 1.5-2.0 hours at 680-700 DEG C, from
It so is ground into uniform particle after cooling, obtains ferrocerium oxysome;
(3) dried object that step (1) is prepared is placed in conical flask, is added 170-180 milliliters by polyvinylpyrrolidone
The solvent being mixed to get with dehydrated alcohol according to the ratio that mass ratio is 1:8-9 after concussion uniformly, is added step (2) and is prepared into
The ferrocerium oxysome arrived continues magnetic agitation 50-60 minutes, stands 2-3 hours, is then transferred to high-magnitude DC electrostatic device for spinning
In, under the effect of high voltage electric field power, solvent volatilizees rapidly solidification, will volatilize rear cured product and is transferred to 110-115 DEG C of drying box
In, it is 8-10 hours dry, it is then placed in crucible, is placed in heating furnace, control heating rate is 6.5-7.0 DEG C/min, heating
To 720-740 DEG C, 2-3 hours are kept the temperature, with furnace cooled to room temperature after calcining, obtains the absorption cleaning agent of nano aperture.
It is further described as to above scheme, the absorption cleaning agent addition usage amount accounts for resin quality in impregnated paper
0.19-22% between.
It is further described as to above scheme, sodium hydroxide solution molar concentration is rubbed in step (1) for 2.0-2.2
You/liter.
It is further described as to above scheme, hydrochloric acid solution molar concentration is 2.8-3.0 mol/L in step (1).
It is further described as to above scheme, step (2) the concentrated ammonia liquor pH value is between 11.4-11.5.
It is further described as to above scheme, step (2) the ferrocerium oxysome particle size is between 1-80 nanometers.
It is further described as to above scheme, step (3) the application voltage is 16.5-17.0KV.
It is further described as to above scheme, the absorption cleaning agent pore size that step (3) is prepared is in 1-10
Between nanometer.
The present invention has the advantage that compared with prior art cannot be effective in order to solve free formaldehyde content in existing impregnated paper
The problem of control, the present invention provides a kind of absorption cleaning agent of free formaldehyde content in reduction impregnated paper, by what is be prepared
Absorption cleaning agent is added in impregnating resin, have very high surface-active and surface can, absorption property is excellent, at the same have compared with
Small aperture and Kong Rong can play the role of retention and stop, by photocatalytic degradation, convert innocuous substance for formaldehyde, gram
Residues of formaldehyde problem caused by being not thorough due to adsorbent material purification is taken, and adhesion strength and ageing-resistant performance improve, tree
Free formaldehyde content reaches European E0 grade standard less than 0.06% in rouge, and burst size is lower than 0.20 milligram/100 after formaldehyde 30 days
Gram, can effectively solve the problem that Form aldehyde release, there is chronicity, intractable and repetitious problems, have ensured the use peace of impregnated paper
Quan Xing, the service performances such as the wear-resisting, water-fast of impregnated paper, resistant get a promotion, the present invention be prepared for reducing impregnated paper
The absorption cleaning agent of middle free formaldehyde content solves the problems, such as that free formaldehyde content cannot be controlled effectively in existing impregnated paper,
Higher Vapor recovery unit is kept, promotion of the impregnated paper ornament materials in decorative and green safe property has been taken into account, has improved
The development and utilization of impregnated paper ornament materials can be realized raising impregnated paper ornament materials safety in utilization and extend its applicable neck
The realistic meaning in domain is a kind of technical solution being extremely worth of widely use.
Specific embodiment
To make the purpose of the present invention, technical solution and effect clearer, clear and definite, combined with specific embodiments below to this hair
It is bright to be described further, it should be understood that the specific embodiments described herein are merely illustrative of the present invention, is not used to limit
Technical solution provided by the present invention.
Embodiment 1
The absorption cleaning agent of free formaldehyde content in a kind of reduction impregnated paper, preparation method includes the following steps:
(1) 33 grams of diatomite are weighed, 300 ml deionized waters are added into diatomite in powder for 150 meshes of pulverizing, stirring
It is uniformly mixed and obtains slurry, 50 milliliters of sodium hydroxide solutions are then added into slurry, be ultrasonically treated 15 minutes, stand 6 hours,
Upper layer suspension is gone, sediment is obtained, 80 milliliters of hydrochloric acid solutions are added into sediment, are stirred 40 minutes, is added
It into round-bottomed flask, is placed in water bath with thermostatic control at 75 DEG C and is heated to reflux 2 hours, then filtered, obtained filter residue uses
Deionized water is washed to pH between 6.5-6.8, and it is spare to constant weight to be subsequently placed in drying in 80 DEG C of baking ovens;
(2) 6.6 gram of six nitric hydrate cerium and 7.4 grams of Fe(NO3)39H2Os are weighed, is placed in a beaker, 45 milliliters of deionizations are added
2.2 grams of citric acids are added to 38 DEG C in water, heating water bath under magnetic stirring, and stirring formed uniform mixture after 30 minutes, used
Concentrated ammonia liquor regulation system pH value is between 5.7-5.9, then vacuum freezedrying 10 hours at a temperature of subzero 15 DEG C, further
It pulverizes, is transferred in crucible, calcined 1.5 hours at 680 DEG C, uniform particle is ground into after natural cooling, obtains ferrocerium
Oxysome;
(3) dried object that step (1) is prepared is placed in conical flask, is added 170 milliliters by polyvinylpyrrolidone and nothing
After concussion uniformly, the cerium that step (2) are prepared is added in the solvent that water-ethanol is mixed to get according to the ratio that mass ratio is 1:8
Ferrite continues magnetic agitation 50 minutes, stands 2 hours, is then transferred in high-magnitude DC electrostatic device for spinning, in high-voltage electricity
Under field force effect, solvent volatilizees rapidly solidification, will volatilize rear cured product and is transferred in 110 DEG C of drying boxes, dries 8 hours, so
After be put into crucible, be placed in heating furnace, control heating rate is 6.5 DEG C/min, is warming up to 720 DEG C, keeps the temperature 2 hours, calcining
Afterwards with furnace cooled to room temperature, the absorption cleaning agent of nano aperture is obtained.
It is further described as to above scheme, the absorption cleaning agent addition usage amount accounts for resin quality in impregnated paper
0.19-22% between.
It is further described as to above scheme, sodium hydroxide solution molar concentration is 2.0 mol/Ls in step (1).
It is further described as to above scheme, hydrochloric acid solution molar concentration is 2.8 mol/Ls in step (1).
It is further described as to above scheme, step (2) the concentrated ammonia liquor pH value is between 11.4-11.5.
It is further described as to above scheme, step (2) the ferrocerium oxysome particle size is between 1-80 nanometers.
It is further described as to above scheme, step (3) the application voltage is 16.5KV.
It is further described as to above scheme, the absorption cleaning agent pore size that step (3) is prepared is in 1-10
Between nanometer.
Embodiment 2
The absorption cleaning agent of free formaldehyde content in a kind of reduction impregnated paper, preparation method includes the following steps:
(1) 34 grams of diatomite are weighed, 330 ml deionized waters are added into diatomite in powder for 160 meshes of pulverizing, stirring
It is uniformly mixed and obtains slurry, 55 milliliters of sodium hydroxide solutions are then added into slurry, be ultrasonically treated 18 minutes, it is small to stand 6.5
When, upper layer suspension is gone, sediment is obtained, 85 milliliters of hydrochloric acid solutions are added into sediment, is stirred 45 minutes, adds
Enter into round-bottomed flask, is placed in water bath with thermostatic control at 78 DEG C and is heated to reflux 2.5 hours, then filtered, obtained filter residue
Make to be washed with deionized to pH between 6.5-6.8, it is spare to constant weight to be subsequently placed in drying in 85 DEG C of baking ovens;
(2) 6.7 gram of six nitric hydrate cerium and 7.5 grams of Fe(NO3)39H2Os are weighed, is placed in a beaker, 48 milliliters of deionizations are added
2.3 grams of citric acids are added to 39 DEG C in water, heating water bath under magnetic stirring, and stirring formed uniform mixture after 35 minutes, used
Concentrated ammonia liquor regulation system pH value is between 5.7-5.9, then vacuum freezedrying 11 hours at a temperature of subzero 15 DEG C, further
It pulverizes, is transferred in crucible, calcined 1.8 hours at 690 DEG C, uniform particle is ground into after natural cooling, obtains ferrocerium
Oxysome;
(3) dried object that step (1) is prepared is placed in conical flask, is added 175 milliliters by polyvinylpyrrolidone and nothing
The solvent that water-ethanol is mixed to get according to the ratio that mass ratio is 1:8.5, after concussion uniformly, what addition step (2) was prepared
Ferrocerium oxysome continues magnetic agitation 55 minutes, stands 2.5 hours, is then transferred in high-magnitude DC electrostatic device for spinning, in height
Under the effect of piezoelectric field power, solvent volatilizees rapidly solidification, will volatilize rear cured product and is transferred in 112 DEG C of drying boxes, and it is small to dry 9
When, it is then placed in crucible, is placed in heating furnace, control heating rate is 6.8 DEG C/min, is warming up to 730 DEG C, heat preservation 2.5 is small
When, with furnace cooled to room temperature after calcining, obtain the absorption cleaning agent of nano aperture.
It is further described as to above scheme, the absorption cleaning agent addition usage amount accounts for resin quality in impregnated paper
0.19-22% between.
It is further described as to above scheme, sodium hydroxide solution molar concentration is 2.1 mol/Ls in step (1).
It is further described as to above scheme, hydrochloric acid solution molar concentration is 2.9 mol/Ls in step (1).
It is further described as to above scheme, step (2) the concentrated ammonia liquor pH value is between 11.4-11.5.
It is further described as to above scheme, step (2) the ferrocerium oxysome particle size is between 1-80 nanometers.
It is further described as to above scheme, step (3) the application voltage is 16.8KV.
It is further described as to above scheme, the absorption cleaning agent pore size that step (3) is prepared is in 1-10
Between nanometer.
Embodiment 3
The absorption cleaning agent of free formaldehyde content in a kind of reduction impregnated paper, preparation method includes the following steps:
(1) 35 grams of diatomite are weighed, 350 ml deionized waters are added into diatomite in powder for 180 meshes of pulverizing, stirring
It is uniformly mixed and obtains slurry, 60 milliliters of sodium hydroxide solutions are then added into slurry, be ultrasonically treated 20 minutes, stand 7 hours,
Upper layer suspension is gone, sediment is obtained, 90 milliliters of hydrochloric acid solutions are added into sediment, are stirred 50 minutes, is added
It into round-bottomed flask, is placed in water bath with thermostatic control at 80 DEG C and is heated to reflux 3 hours, then filtered, obtained filter residue uses
Deionized water is washed to pH between 6.5-6.8, and it is spare to constant weight to be subsequently placed in drying in 90 DEG C of baking ovens;
(2) 6.8 gram of six nitric hydrate cerium and 7.6 grams of Fe(NO3)39H2Os are weighed, is placed in a beaker, 50 milliliters of deionizations are added
2.4 grams of citric acids are added to 40 DEG C in water, heating water bath under magnetic stirring, and stirring forms uniform mixture after forty minutes, uses
Concentrated ammonia liquor regulation system pH value is between 5.7-5.9, then vacuum freezedrying 12 hours at a temperature of subzero 15 DEG C, further
It pulverizes, is transferred in crucible, calcined 2.0 hours at 700 DEG C, uniform particle is ground into after natural cooling, obtains ferrocerium
Oxysome;
(3) dried object that step (1) is prepared is placed in conical flask, is added 180 milliliters by polyvinylpyrrolidone and nothing
After concussion uniformly, the cerium that step (2) are prepared is added in the solvent that water-ethanol is mixed to get according to the ratio that mass ratio is 1:9
Ferrite continues magnetic agitation 60 minutes, stands 3 hours, is then transferred in high-magnitude DC electrostatic device for spinning, in high-voltage electricity
Under field force effect, solvent volatilizees rapidly solidification, will volatilize rear cured product and is transferred in 115 DEG C of drying boxes, dries 10 hours, so
After be put into crucible, be placed in heating furnace, control heating rate is 7.0 DEG C/min, is warming up to 740 DEG C, keeps the temperature 3 hours, calcining
Afterwards with furnace cooled to room temperature, the absorption cleaning agent of nano aperture is obtained.
It is further described as to above scheme, the absorption cleaning agent addition usage amount accounts for resin quality in impregnated paper
0.19-22% between.
It is further described as to above scheme, sodium hydroxide solution molar concentration is 2.2 mol/Ls in step (1).
It is further described as to above scheme, hydrochloric acid solution molar concentration is 3.0 mol/Ls in step (1).
It is further described as to above scheme, step (2) the concentrated ammonia liquor pH value is between 11.4-11.5.
It is further described as to above scheme, step (2) the ferrocerium oxysome particle size is between 1-80 nanometers.
It is further described as to above scheme, step (3) the application voltage is 17.0KV.
It is further described as to above scheme, the absorption cleaning agent pore size that step (3) is prepared is in 1-10
Between nanometer.
Comparative example 1
Difference with embodiment 1 is only that, in the preparation of absorption cleaning agent, omits the preparation addition of material in step (1), remaining
It is consistent.
Comparative example 2
Difference with embodiment 2 is only that, in the preparation of absorption cleaning agent, omits the addition of six nitric hydrate ceriums in step (2),
Remaining is consistent.
Comparative example 3
Difference with embodiment 3 is only that, in the preparation of absorption cleaning agent, omits the addition of Fe(NO3)39H2O in step (2),
Remaining is consistent.
Comparative example 4
Difference with embodiment 3 is only that, in the preparation of absorption cleaning agent, polyvinylpyrrolidone and anhydrous second in step (3)
Alcohol is mixed according to the ratio that mass ratio is 1:6, remaining is consistent.
Comparative example 5
Difference with embodiment 3 is only that, in the preparation of absorption cleaning agent, step (3) the control heating rate be 8.0 DEG C/
Minute, 750 DEG C are warming up to, keeps the temperature 3.5 hours, remaining is consistent.
Comparative experiments
The absorption cleaning of free formaldehyde content in impregnated paper is reduced using the method preparation of embodiment 1-3 and comparative example 1-5 respectively
Agent, be incorporated as when glue mixing resin quality 1.7% melamine method as a control group, will be each in embodiment and comparative example
The absorption cleaning agent that group is prepared is added in Lauxite, free formaldehyde content is measured using formaldehyde tester, according to phase
Impregnated paper is prepared with method processing, carries out later period burst size of methanal tracking and testing, irrelevant variable is consistent in holding test, and statistics has
Average value is imitated, as a result as shown in the table:
(GB/T 18580-2001 " release in indoor decorating and refurnishing materials wood-based plate and its product by formaldehyde according to national standards in test
Put limitation " as defined in method measurement)
The absorption cleaning agent for reducing free formaldehyde content in impregnated paper that the present invention is prepared solves existing impregnated paper
The problem of middle free formaldehyde content cannot be controlled effectively keeps higher Vapor recovery unit, has taken into account impregnated paper ornament materials
Promotion in decorative and green safe property, improves the development and utilization of impregnated paper ornament materials, can be realized raising dipping
Paper ornament materials safety in utilization and the realistic meaning for extending its suitable application area are a kind of technologies being extremely worth of widely use
Scheme.
Claims (8)
1. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper, which is characterized in that preparation method includes following
Step:
(1) 33-35 grams of diatomite is weighed, 150-180 mesh of pulverizing is added 300-350 milliliters into diatomite in powder and goes
Ionized water is uniformly mixed to obtain slurry, and 50-60 milliliters of sodium hydroxide solutions are then added into slurry, is ultrasonically treated 15-
20 minutes, 6-7 hours are stood, upper layer suspension is gone, sediment is obtained, it is molten that 80-90 milliliters of hydrochloric acid are added into sediment
Liquid is stirred 40-50 minutes, is added in round-bottomed flask, is placed in water bath with thermostatic control that be heated to reflux 2-3 at 75-80 DEG C small
When, it is then filtered, obtained filter residue makes to be washed with deionized to pH between 6.5-6.8, is subsequently placed in 80-90 DEG C of baking
Drying is spare to constant weight in case;
(2) 6.6-6.8 grams of six nitric hydrate ceriums and 7.4-7.6 grams of Fe(NO3)39H2O are weighed, is placed in a beaker, 45-50 is added
Ml deionized water, heating water bath are added 2.2-2.4 grams of citric acid to 38-40 DEG C under magnetic stirring, stir 30-40 minutes
After form uniform mixture, using concentrated ammonia liquor regulation system pH value between 5.7-5.9, then freezed at a temperature of subzero 15 DEG C
Vacuum drying 10-12 hours, further pulverizes, is transferred in crucible, calcine 1.5-2.0 hours at 680-700 DEG C, from
It so is ground into uniform particle after cooling, obtains ferrocerium oxysome;
(3) dried object that step (1) is prepared is placed in conical flask, is added 170-180 milliliters by polyvinylpyrrolidone
The solvent being mixed to get with dehydrated alcohol according to the ratio that mass ratio is 1:8-9 after concussion uniformly, is added step (2) and is prepared into
The ferrocerium oxysome arrived continues magnetic agitation 50-60 minutes, stands 2-3 hours, is then transferred to high-magnitude DC electrostatic device for spinning
In, under the effect of high voltage electric field power, solvent volatilizees rapidly solidification, will volatilize rear cured product and is transferred to 110-115 DEG C of drying box
In, it is 8-10 hours dry, it is then placed in crucible, is placed in heating furnace, control heating rate is 6.5-7.0 DEG C/min, heating
To 720-740 DEG C, 2-3 hours are kept the temperature, with furnace cooled to room temperature after calcining, obtains the absorption cleaning agent of nano aperture.
2. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper as described in claim 1, which is characterized in that described
Absorption cleaning agent addition usage amount accounts in impregnated paper between the 0.19-22% of resin quality.
3. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper as described in claim 1, which is characterized in that step
(1) sodium hydroxide solution molar concentration is 2.0-2.2 mol/L in.
4. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper as described in claim 1, which is characterized in that step
(1) hydrochloric acid solution molar concentration is 2.8-3.0 mol/L in.
5. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper as described in claim 1, which is characterized in that step
(2) the concentrated ammonia liquor pH value is between 11.4-11.5.
6. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper as described in claim 1, which is characterized in that step
(2) the ferrocerium oxysome particle size is between 1-80 nanometers.
7. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper as described in claim 1, which is characterized in that step
(3) the application voltage is 16.5-17.0KV.
8. a kind of absorption cleaning agent for reducing free formaldehyde content in impregnated paper as described in claim 1, which is characterized in that step
(3) the absorption cleaning agent pore size being prepared is between 1-10 nanometers.