CN109163547A - The drying means of poplar veneer - Google Patents
The drying means of poplar veneer Download PDFInfo
- Publication number
- CN109163547A CN109163547A CN201810969973.4A CN201810969973A CN109163547A CN 109163547 A CN109163547 A CN 109163547A CN 201810969973 A CN201810969973 A CN 201810969973A CN 109163547 A CN109163547 A CN 109163547A
- Authority
- CN
- China
- Prior art keywords
- dry kiln
- product
- poplar veneer
- dried
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of drying means of poplar veneer, include the following steps, poplar veneer is piled up in dry kiln;It is 50-55 DEG C that dry kiln temperature, which is arranged, and being dried to moisture content is 25%-30%;It is 40-50 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 80%-90%, and being dried to moisture content is 18%-20%;It is 35-45 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 70%-80%, and being dried to moisture content is 13%-17%;It is 30-40 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 60%-70%, and being dried to moisture content is 8%-10%, kiln discharge;By poplar veneer in temperature be 25-30 DEG C, humidity be 40%-50% environment in, place 1-3 days obtain finished product.The problem of poplar veneer is dried using the present invention, can solve deformation in poplar veneer drying process, cracking and shrinkage.
Description
Technical field
The present invention relates to the drying means technical field of wood single-plate, especially a kind of drying means of poplar veneer.
Background technique
In recent years, poplar wood is in Wood Flooring Industry using more and more extensive.Poplar wood is that a kind of speed of growth is exceedingly fast
Fast growing wood, 10-15 can become a useful person, but the poplar density of trees is low, and material is loose, using the dry poplar of conventional drying means
Veneer, poplar veneer are easily deformed in the drying process, cracking and shrinkage.Therefore using conventional drying means to poplar
Veneer is dried, and there are problems that poplar veneer is easily deformed, cracks and shrinkage.
Summary of the invention
The purpose of the present invention is the provision of a kind of drying means of poplar veneer.Using the dry poplar wood of the present invention
Veneer can solve and be easily deformed, crack and the problem of shrinkage in poplar veneer drying process.
Technical solution of the present invention: the drying means of poplar veneer includes the following steps,
A, poplar veneer is piled up in dry kiln;
B, it is 50-55 DEG C that dry kiln temperature, which is arranged, and it is 25%-30% that poplar veneer, which is dried to moisture content, obtains B product;
C, it is 40-50 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 80%-90%, B product is dried to aqueous
Rate is 18%-20%, obtains C product;
D, it is 35-45 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 70%-80%, C product is dried to aqueous
Rate is 13%-17%, obtains D product;
E, it is 30-40 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 60%-70%, D product is dried to aqueous
Rate is 8%-10%, and kiln discharge obtains E product;
It F, is 25-30 DEG C in temperature by E product, humidity is to place 1-3 days to obtain finished product in 40%-50% environment.
In the drying means of poplar veneer above-mentioned, in step B, the heating rate of the dry kiln is 1-2 per hour
℃。
In the drying means of poplar veneer above-mentioned, in step B, it is 28% that poplar veneer, which is dried to moisture content,.
In the drying means of poplar veneer above-mentioned, in step C, the heating rate of the dry kiln is 1-2 per hour
℃。
In the drying means of poplar veneer above-mentioned, in step D, the heating rate of the dry kiln is 0.5- per hour
1℃。
In the drying means of poplar veneer above-mentioned, in step E, the heating rate of the dry kiln is 0.5- per hour
1℃。
Compared with the prior art, poplar veneer is first put into dry kiln by the present invention, in 50-55 DEG C of drying to aqueous
Rate is 25%-30%, is 40-50 DEG C then at temperature, and humidity is dried to moisture content under conditions of being 80%-90 be 18%-20%, then
It is 35-45 DEG C in temperature, humidity is dried to moisture content under conditions of being 70%-80% be 13%-17%, is 30-40 then at temperature
DEG C, moisture content is 8%-10% under conditions of humidity is 60%-70%, finally in temperature be 25-30 DEG C, humidity 40%-
In 50% environment, finished product is placed 1-3 days to obtain.The present invention uses low temperature drying when board using poplar board moisture content is larger, does not control wet
Degree, then gradually decreasing temperature and increasing humidity, is finally 25-30 DEG C in temperature, humidity is health in 40%-50% environment.The present invention can be kept away
The concentration for exempting from the drying stress and the mobile tension of moisture in poplar veneer drying process, it is dried to greatly reduce poplar veneer
It deforms, crack and the probability of shrinkage in journey, the present invention is reduced in conventional method ratio, the defect rate of deformation, cracking and shrinkage
8-12%.Using the dry poplar veneer of the present invention, it can solve and be easily deformed, crack and wrinkle in poplar veneer drying process
The problem of contracting.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.The drying means of poplar veneer, includes the following steps,
A, poplar veneer is piled up in dry kiln;
B, it is 50 DEG C that dry kiln temperature, which is arranged, and it is 25% that poplar veneer, which is dried to moisture content, obtains B product;
C, it is 40 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 80%, and B product, which are dried to moisture content, is
18%, obtain C product;
D, it is 35 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 70%, and C product, which are dried to moisture content, is
13%, obtain D product;
E, it is 30 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 60%, and it is 8% that D product, which are dried to moisture content,
Kiln discharge obtains E product;
It F, is 25 DEG C in temperature by E product, humidity is to place 1 day to obtain finished product in 40% environment.
In step B, the heating rate of the dry kiln is 1 DEG C per hour.
In step C, the heating rate of the dry kiln is 1 DEG C per hour.
In step D, the heating rate of the dry kiln is 0.5 DEG C per hour.
In step E, the heating rate of the dry kiln is 0.5 DEG C per hour.
Embodiment 2.The drying means of poplar veneer, includes the following steps,
A, poplar veneer is piled up in dry kiln;
B, it is 55 DEG C that dry kiln temperature, which is arranged, and it is 30% that poplar veneer, which is dried to moisture content, obtains B product;
C, it is 50 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 90%, and B product, which are dried to moisture content, is
20%, obtain C product;
D, it is 45 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 80%, and C product, which are dried to moisture content, is
17%, obtain D product;
E, it is 40 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 70%, and D product, which are dried to moisture content, is
10%, kiln discharge obtains E product;
It F, is 30 DEG C in temperature by E product, humidity is to place 3 days to obtain finished product in 50% environment.
In step B, the heating rate of the dry kiln is 2 DEG C per hour.
In step C, the heating rate of the dry kiln is 2 DEG C per hour.
In step D, the heating rate of the dry kiln is 1 DEG C per hour.
In step E, the heating rate of the dry kiln is 1 DEG C per hour.
Embodiment 3.The drying means of poplar veneer, includes the following steps,
A, poplar veneer is piled up in dry kiln;
B, it is 52 DEG C that dry kiln temperature, which is arranged, and it is 28% that poplar veneer, which is dried to moisture content, obtains B product;
C, it is 45 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 85%, and B product, which are dried to moisture content, is
19%, obtain C product;
D, it is 40 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 75%, and C product, which are dried to moisture content, is
15%, obtain D product;
E, it is 35 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 65%, and it is 9% that D product, which are dried to moisture content,
Kiln discharge obtains E product;
It F, is 27 DEG C in temperature by E product, humidity is to place 2 days to obtain finished product in 45% environment.
In step B, the heating rate of the dry kiln is 1.5 DEG C per hour.
In step C, the heating rate of the dry kiln is 1.5 DEG C per hour.
In step D, the heating rate of the dry kiln is 0.7 DEG C per hour.
In step E, the heating rate of the dry kiln is 0.7 DEG C per hour.
Certainly, the present invention can also have other various embodiments, without deviating from the spirit and substance of the present invention, ripe
It knows those skilled in the art and makes various corresponding changes and modifications, but these corresponding changes and change in accordance with the present invention
Shape all should fall within the scope of protection of the appended claims of the present invention.
Claims (6)
1. the drying means of poplar veneer, it is characterised in that: include the following steps,
A, poplar veneer is piled up in dry kiln;
B, it is 50-55 DEG C that dry kiln temperature, which is arranged, and it is 25%-30% that poplar veneer, which is dried to moisture content, obtains B product;
C, it is 40-50 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 80%-90%, and B product, which are dried to moisture content, is
18%-20% obtains C product;
D, it is 35-45 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 70%-80%, and C product, which are dried to moisture content, is
13%-17% obtains D product;
E, it is 30-40 DEG C that dry kiln temperature, which is arranged, and controlling humidity in dry kiln is 60%-70%, and D product, which are dried to moisture content, is
8%-10%, kiln discharge obtain E product;
It F, is 25-30 DEG C in temperature by E product, humidity is to place 1-3 days to obtain finished product in 40%-50% environment.
2. the drying means of poplar veneer according to claim 1, it is characterised in that: in step B, the dry kiln
Heating rate is 1-2 DEG C per hour.
3. the drying means of poplar veneer according to claim 1, it is characterised in that: in step B, by poplar veneer
Being dried to moisture content is 28%.
4. the drying means of poplar veneer according to claim 1, it is characterised in that: in step C, the dry kiln
Heating rate is 1-2 DEG C per hour.
5. the drying means of poplar veneer according to claim 1, it is characterised in that: in step D, the dry kiln
Heating rate is 0.5-1 DEG C per hour.
6. the drying means of poplar veneer according to claim 1, it is characterised in that: in step E, the dry kiln
Heating rate is 0.5-1 DEG C per hour.