CN109162024A - A kind of imitated furs compound base fabric material and its moulding process - Google Patents
A kind of imitated furs compound base fabric material and its moulding process Download PDFInfo
- Publication number
- CN109162024A CN109162024A CN201811220896.9A CN201811220896A CN109162024A CN 109162024 A CN109162024 A CN 109162024A CN 201811220896 A CN201811220896 A CN 201811220896A CN 109162024 A CN109162024 A CN 109162024A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- material layer
- selects
- base fabric
- imitated furs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of imitated furs compound base fabric material and its moulding process, the imitated furs compound base fabric material includes by that can melt the shiny surface and needling process is used to be fixed on the villous surface on shiny surface that material layer is formed after the sizing of high temperature roller, and the material layer that melts is spunbond method PP non-woven cloth or stitch-bonding nonwoven-fabrics.Compared with prior art, the present invention not only solves the poor dimensional stability and disadvantage on the high side of true fur material, and is not required to the various chemical pre-treating technologies by true fur, Environmental Safety.
Description
Technical field
The present invention relates to imitated furs compound base fabric fields, and in particular to be a kind of imitated furs compound base fabric material and its at
Type technique.
Background technique
In recent years, shoe-making industry generally develops towards direction light, comfortable and that leisure is ventilative.But with people's environmental protection
Consciousness enhancing and the influence of National Sustainable Development Strategies, the price of true fur can not have always been high any more, in order to adapt to fierce city
Field competition, in this context, market gradually highlight the selectivity imitation of fur, since people pursue the consciousness of comfort
Still constantly enhancing, but also market is higher and higher to the pursuit of imitated furs quality and quantity.
In view of this, the applicant furthers investigate regarding to the issue above, there is this case generation then.
Summary of the invention
The main purpose of the present invention is to provide a kind of imitated furs compound base fabric materials, are light on one side as fur
Sliding surface is cashmere shell-fabric on one side, and also has the characteristics that strength is high and low-cost.
In order to achieve the above objectives, solution of the invention is:
A kind of imitated furs compound base fabric material, wherein including what is formed after the sizing of high temperature roller by material layer can be melted
Shiny surface and use needling process are fixed on the villous surface on shiny surface, and the material layer that melts is that spunbond method PP is non-woven
Cloth or stitch-bonding nonwoven-fabrics.
Further, the first polyester fiber, the 15wt%-25wt% for melting material layer and using 40wt%-50wt%
The second polyester fiber and 25wt%-45wt% ES fiber, go out soluble material layer through loop bonding method machine-shaping;Described first
Polyester fiber selects 2D or 3D*64mm, and second polyester fiber selects 6D*64mm, and the ES fiber selects 2.5D*51mm.
Further, the villous surface is using the three-dimensional hollow polyester fiber of 50wt%-60wt%, 20wt%-30wt%
The 4th polyester fiber of third polyester fiber and 10wt%-30wt% are molded over by needling process and can be melted in material layer;Institute
It states three-dimensional hollow polyester fiber and selects 7.0D*64mm, the third polyester fiber selects 6D*64mm, the 4th polyester fiber
Select 2.5D*51mm.
Another object of the present invention is to provide a kind of moulding process of imitated furs compound base fabric material, wherein including such as
Lower step:
1. material layer can be melted by molding;
2. material layer can be melted as substrate, then above substrate through combing, networking and needle thorn mold tool it is villous
Ventilative lamina reticularis, to form preliminary molding composite material;
3. preliminary molding composite material through two groups of rollers up and down of different temperatures is formed to obtain finished product imitated furs compound
Scrim material, the soluble material layer are contacted with high temperature roller, and the ventilative lamina reticularis is contacted with low temperature roller.
Further, the material layer that melts is spunbond method PP non-woven cloth or stitch-bonding nonwoven-fabrics.
Further, the first polyester fiber, the 15wt%-25wt% for melting material layer and using 40wt%-50wt%
The second polyester fiber and 25wt%-45wt% ES fiber, go out soluble material layer through loop bonding method machine-shaping;Described first
Polyester fiber selects 2D or 3D*64mm, and second polyester fiber selects 6D*64mm, and the ES fiber selects 2.5D*51mm.
Further, step 2. in, using the three-dimensional hollow polyester fiber of 50wt%-60wt%, 20wt%-30wt%
4th polyester fiber of third polyester fiber and 10wt%-30wt%;The three-dimensional hollow polyester fiber selects 7.0D*64mm,
The third polyester fiber selects 6D*64mm, and the 4th polyester fiber selects 2.5D*51mm.
Further, step 3. in, the temperature of the high temperature roller is 170-190 DEG C, and the temperature of the low temperature roller is
100-130℃。
After adopting the above structure, a kind of imitated furs compound base fabric material of the present invention and its moulding process are passed through
A+B composite material is formed after first one-step forming, A+B composite material is then allowed to be formed by two groups of rollers up and down of different temperatures,
It can melt and melt the shiny surface for being shaped into compound base fabric material after material layer is handled through high temperature roller, another side then forms multiple
The villous surface for closing scrim material, so obtains that cheap, intensity is high, wearability is good and the imitated furs composite base of safety and environmental protection
Cloth material.
Detailed description of the invention
Fig. 1 is that the present invention relates to a kind of structural schematic diagrams of imitated furs compound base fabric material.
Fig. 2 is that the present invention relates to the schematic diagrames that the moulding process in the middle of the roller of imitated furs compound base fabric material is formed.
In figure:
Shiny surface -1;Material layer 11 can be melted;
Villous surface -2;Ventilative lamina reticularis 21;
High temperature roller -31;Low temperature roller -32.
Specific embodiment
In order to further explain the technical solution of the present invention, being explained in detail below by specific embodiment the present invention
It states.
As shown in Figure 1, a kind of imitated furs compound base fabric material of the present invention, including shiny surface 1 and villous surface 2, institute
It states shiny surface 1 and is formed after the sizing of high temperature roller 31 by material layer 11 can be melted, the villous surface 2 is fixed on using needling process
On shiny surface 1, the material layer 11 that melts is spunbond method PP non-woven cloth or stitch-bonding nonwoven-fabrics.
Specifically, as a kind of specific embodiment, the material layer 11 that melts is washed using the first of 40wt%-50wt%
The ES fiber of synthetic fibre fiber, the second polyester fiber of 15wt%-25wt% and 25wt%-45wt% goes out through loop bonding method machine-shaping
Soluble material layer;First polyester fiber selects 2D or 3D*64mm, and second polyester fiber selects 6D*64mm, described
ES fiber selects 2.5D*51mm.First polyester fiber is whole for improving as material of main part, second polyester material
The feel of a material, the ES fiber are bi-component sheath-core structure composite fibers, and cortical tissue's fusing point is low and flexibility is good, sandwich layer
Then fusing point is high, intensity is high for tissue.This fiber is after Overheating Treatment, and cortex a part melts and plays cementation, remaining is still protected
The feature stayed fiber condition, while having percent thermal shrinkage small.
Specifically, as a kind of specific embodiment, the villous surface 2 uses the three-dimensional hollow terylene of 50wt%-60wt%
4th polyester fiber of fiber, the third polyester fiber of 20wt%-30wt% and 10wt%-30wt% is formed by needling process
On it can melt material layer 11;The three-dimensional hollow polyester fiber selects 7.0D*64mm, and the third polyester fiber selects 6D*
64mm, the 4th polyester fiber select 2.5D*51mm.The three-dimensional hollow polyester fiber is for improving permeability
Material of main part, the third polyester fiber are for improving the entanglement effect between fiber, and the 4th polyester fiber is to be used for
Improve base fabric density.It is that substrate is netted through breathing freely of being formed of high speed needling process that the villous surface 2, which is can melt material layer 11,
Structure.
The present invention also provides a kind of moulding process of imitated furs compound base fabric material, include the following steps:
1. material layer 11 can be melted by molding;Specifically, the moulding process for melting material layer 11 can be spunbond
Method PP non-woven cloth or stitch-bonding nonwoven-fabrics, but it is not limited to above two molding mode, it can also be other implementations;
As a kind of specific embodiment of loop bonding method, first polyester fiber for melting the use of material layer 11 40wt%-50wt%,
The second polyester fiber of 15wt%-25wt% and the ES fiber of 25wt%-45wt% go out to can dissolve material through loop bonding method machine-shaping
The bed of material;First polyester fiber selects 2D or 3D*64mm, and second polyester fiber selects 6D*64mm, the ES fiber choosing
Use 2.5D*51mm;
2. material layer 11 can be melted for substrate, then piercing and molding with villus through combing, networking and needle above substrate
Ventilative lamina reticularis 21, to form preliminary molding composite material;Step 2. in, using in the three-dimensional of 50wt%-60wt%
4th polyester fiber of empty polyester fiber, the third polyester fiber of 20wt%-30wt% and 10wt%-30wt%;The three-dimensional
Hollow terylene selects 7.0D*64mm, and the third polyester fiber selects 6D*64mm, and the 4th polyester fiber is selected
2.5D*51mm;
3. preliminary molding composite material through two groups of rollers up and down of different temperatures is formed to obtain finished product imitated furs compound
Scrim material, the soluble material layer are contacted with high temperature roller 31, and the ventilative lamina reticularis 21 is contacted with low temperature roller 32.It is excellent
Selection of land, step 3. in, the temperature of the high temperature roller 31 is 170-190 DEG C, and the temperature of the low temperature roller 32 is 100-130
℃。
In this way, a kind of imitated furs compound base fabric material of the present invention and its moulding process, by first one-step forming it
A+B composite material is formed afterwards, then allows A+B composite material by two groups of roller sizings up and down of different temperatures, it can molten materials
Layer 11 melts the shiny surface 1 for being shaped into compound base fabric material after handling through high temperature roller 31, and another side then forms composite base
The villous surface 2 of cloth material.Compared with prior art, the present invention is far below fur material in price;In addition, of the present invention
Compound base fabric material intensity under dry and wet state is constant, has the characteristics that intensity is high;Its wearability is only second to polyamide fibre simultaneously
Dimension, wearability are good;Simultaneously after tested, it when extending 5%-6%, can almost restore to the original state completely, there is modification to reply
The high feature of ability, furthermore chemical pretreatment procedure of the present invention due to needing not move through true fur, also with safety and environmental protection
Feature.
To sum up, the present invention not only solves the poor dimensional stability and disadvantage on the high side of true fur material, and not
It need to be by the various chemical pre-treating technologies of true fur, Environmental Safety.
Above-described embodiment and schema and non-limiting product form and style of the invention, any technical field it is common
The appropriate changes or modifications that technical staff does it all should be regarded as not departing from patent category of the invention.
Claims (8)
1. a kind of imitated furs compound base fabric material, which is characterized in that including by material layer shape after the sizing of high temperature roller can be melted
At shiny surface and the villous surface on shiny surface is fixed on using needling process, the material layer that melts is that spunbond method PP is non-
Woven cloths or stitch-bonding nonwoven-fabrics.
2. a kind of imitated furs compound base fabric material as described in claim 1, which is characterized in that described to melt material layer use
The ES of the first polyester fiber of 40wt%-50wt%, the second polyester fiber of 15wt%-25wt% and 25wt%-45wt% is fine
Dimension, goes out soluble material layer through loop bonding method machine-shaping;First polyester fiber selects 2D or 3D*64mm, and described second washs
Synthetic fibre fiber selects 6D*64mm, and the ES fiber selects 2.5D*51mm.
3. a kind of imitated furs compound base fabric material as described in claim 1, which is characterized in that the villous surface uses
The three-dimensional hollow polyester fiber of 50wt%-60wt%, the third polyester fiber of 20wt%-30wt% and 10wt%-30wt%
4th polyester fiber is molded over by needling process and can be melted in material layer;The three-dimensional hollow polyester fiber selects 7.0D*
64mm, the third polyester fiber select 6D*64mm, and the 4th polyester fiber selects 2.5D*51mm.
4. a kind of moulding process of imitated furs compound base fabric material, which comprises the steps of:
1. material layer can be melted by molding;
2. material layer can be melted as substrate, then being molded above substrate through combing, networking and needle thorn and having villous breathe freely
Lamina reticularis, to form preliminary molding composite material;
3. preliminary molding composite material is formed to obtain finished product imitated furs compound base fabric through two groups of rollers up and down of different temperatures
Material, the soluble material layer are contacted with high temperature roller, and the ventilative lamina reticularis is contacted with low temperature roller.
5. a kind of moulding process of imitated furs scrim material as claimed in claim 4, which is characterized in that it is described can molten materials
Layer is spunbond method PP non-woven cloth or stitch-bonding nonwoven-fabrics.
6. a kind of moulding process of imitated furs scrim material as claimed in claim 4, which is characterized in that it is described can molten materials
Layer is using the first polyester fiber of 40wt%-50wt%, the second polyester fiber and 25wt%-45wt% of 15wt%-25wt%
ES fiber, go out soluble material layer through loop bonding method machine-shaping;First polyester fiber selects 2D or 3D*64mm, described
Second polyester fiber selects 6D*64mm, and the ES fiber selects 2.5D*51mm.
7. a kind of moulding process of imitated furs scrim material as claimed in claim 4, which is characterized in that step 2. in, adopt
With the three-dimensional hollow polyester fiber of 50wt%-60wt%, the third polyester fiber and 10wt%-30wt% of 20wt%-30wt%
The 4th polyester fiber;The three-dimensional hollow polyester fiber selects 7.0D*64mm, and the third polyester fiber selects 6D*64mm,
4th polyester fiber selects 2.5D*51mm.
8. a kind of moulding process of imitated furs scrim material as claimed in claim 4, which is characterized in that step 3. in, institute
The temperature for stating high temperature roller is 170-190 DEG C, and the temperature of the low temperature roller is 100-130 DEG C.