CN109161430A - A kind of composition and preparation method of low smell cable pulley type electric glass lifter lubricating grease - Google Patents
A kind of composition and preparation method of low smell cable pulley type electric glass lifter lubricating grease Download PDFInfo
- Publication number
- CN109161430A CN109161430A CN201810812126.7A CN201810812126A CN109161430A CN 109161430 A CN109161430 A CN 109161430A CN 201810812126 A CN201810812126 A CN 201810812126A CN 109161430 A CN109161430 A CN 109161430A
- Authority
- CN
- China
- Prior art keywords
- lubricating grease
- added
- cable pulley
- composition according
- pulley type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the compositions and preparation method of a kind of low smell cable pulley type electric glass lifter lubricating grease;The composition of low smell cable pulley type electric glass lifter lubricating grease, it is made of the raw material of base oil 80~85%, 10~15% percent mass proportioning of thickening agent, adds extreme pressure anti-wear additives 1.5%, antioxidant 0.5%, antirust agent 0.5%, dispersing agent 1.5%, metal deactivator 1%.The present invention is by selecting product formula chinese raw materials type, the investigation of additional amount, cable pulley type glass lifter lubricating grease prepared by technique strict control has excellent resistant of high or low temperature, mechanical stability, extreme pressure anti-wear, colloid stability, good rustless property and long-life in preparation process, it is provided simultaneously with environment-protecting and non-poisonous requirement, belongs to low smell lubriation material.
Description
Technical field
The present invention relates to technical field of lubricating grease, in particular to cable pulley type electric glass lifter lubricating grease and preparation side
Method.
Background technique
The electric glass lifter of car is mostly by motor, retarder, conductor rope, guide plate, glass mounting bracket etc.
Composition.Because the material or manufacture craft mode of conductor rope are different, and it is divided into three kinds of cable pulley type, cable type and plastics belt electric driven glass
Lifter.The first two kind is with wirerope as conductor rope, and latter is with plastic tape as conductor rope.With the cable pulley type electricity generally used
For dynamic glass-frame riser, it is made of components such as motor, retarder, wirerope, guide plate and glass mounting brackets,
Door glass is fixed in glass mounting bracket when installation, and glass guide groove is parallel with wirerope guide plate.Motor is opened, by
Motor driving reducer output power pulls wirerope movable glass mounting bracket, door glass is forced to rise or fall
Linear motion.
In the process of running, the position for needing to lubricate mainly has: between 1. wirerope and casing, this lubrication belongs to steel to modeling
The friction type for expecting (based on POM, PE liner), mainly has lower coefficient of friction to the performance requirement of lubricating grease, preferable oil
Film thickness, preferable mechanical stability and preferable colloid stability prevent grease from low phenomenon occur;It requires to lubricate simultaneously
Rouge has good compatibility to plastic parts such as POM, PE, it is ensured that deformation does not occur in lubricant housings;2. wirerope and POM roller
Wheel, this lubrication form are similar to wirerope to casing;3. between wirerope and guide plate, this lubricates the friction shape for belonging to steel to steel
Formula needs lubricating grease to have excellent wear resistence, preferable oil film thickness, lower coefficient of friction, while lubricating grease being required to have
There is preferable anti-medium (water, dust, salt fog etc.), it is ensured that the smooth lubrication of lubricating component;4. the lubrication of slowing-down structure in motor,
This lubrication form is primarily present steel to steel, steel to modeling and moulds to three kinds of forms (according to different materials) of modeling, to the property of lubricating grease
Can require mainly to have: excellent low-temperature startup, lower operation noise, preferable oil film thickness ensure abrasion, preferable machine
Tool stability and colloid stability etc..By the analysis above to lubricant housings, comprehensively consider, PERFORMANCE OF GREASES is required to conclude
Be following: excellent resistant of high or low temperature, mechanical stability, extreme pressure anti-wear, colloid stability and rust-preventing characteristic and overlength make
With the service life, it is provided simultaneously with environment-protecting and non-poisonous requirement.
The lubricating grease that cable pulley type glass lifter manufacturing enterprise of foreign countries such as Bosch, Bo Ze, extra large moral generation etc. uses at present is equal
It can satisfy the service life of resistant of high or low temperature, mechanical stability, extreme pressure anti-wear, colloid stability and rust-preventing characteristic and overlength
Requirement, but deposit following problems: there is noise problem in the process of running in 1. cable pulley type electric glass lifters;2. cable pulley type is electric
There is Caton phenomenon in varying environment (- 40 DEG C to 80 DEG C) operational process in dynamic glass-frame riser, especially at low ambient temperatures (-
25 DEG C to -40 DEG C) appearance lifting speed is slow, or even not operating condition;3. there is smell after being assembled on lifter in lubricating grease
It is pungent, VOC, situations such as poisonous and harmful substance content is exceeded.Domestic cable pulley type glass lifter manufacturing enterprise majority is joint enterprise
Industry, there is also the problems same as external grease for the grease used.Certainly will there is an urgent need for research and develop it is a meet performance requirement, together
When meet the grease product of (environmentally friendly) requirement of special characteristics again for current to solve on cable pulley type glass lifter
Problem.
To reach greasy property requirement, while meeting environment-protecting and non-poisonous evil and requiring, solves following technological difficulties:
1. select the raw material of nonhazardous, by strict control process conditions, it is pungent to solve smell, VOC and toxic has
Evil substance excessive problem;
2. solve cable pulley type electric glass lifter there is noise problem in the process of running;
3. solving under cable pulley type electric glass lifter varying environment and Caton and not operation problem occur.
Summary of the invention
The present invention is by selecting product formula chinese raw materials type, the investigation of additional amount, and technique is stringent in preparation process
The prepared lubricating grease of control has excellent resistant of high or low temperature, mechanical stability, extreme pressure anti-wear, colloid stability, good
Rustless property and the long-life, be provided simultaneously with environment-protecting and non-poisonous requirement.
Low smell cable pulley type electric glass lifter lubricating grease, it is characterised in that: component and mass percent are as follows:
Base oil 80~85%,
Thickening agent 10~15%,
Based on above-mentioned two components total amount 100%, following additive mass percent is added:
Base oil is that (40 DEG C of viscosity are 70-90mm/s to Poly alpha Olefins (PAO) synthetic oil in formula2);Thickening agent selects ten dihydroxy
Lithium stearate and polyethylene are prepared according to 1:3 mass ratio;
Solid lubricant Nano grade zinc oxide and nano-zinc sulfide are added according to 1:1 mass ratio;Bis- uncle of antioxidant 2,6-
Butyl paracresol;
Antirust agent carboxylic acid and its derivative dodecenylsuccinic acid ester;
Dispersing agent succinate;
Metal deactivator thiadiazoles derivative.
Low smell cable pulley type electric glass lifter lubricating grease preparation method of the invention, characterization step are as follows:
(1) Poly alpha Olefins (PAO) synthetic oil, ten dihydroxystearic acids, dispersing agent are separately added into reaction kettle, open stirring, adds
Lithium hydroxide aqueous solution is added to 80~85 DEG C in heat, reacts 90~120 minutes with this condition;
(2) after reaction, polyethylene is added, is heated to 140~145 DEG C and is reacted, reaction time control 60~
80 minutes;
(3) after reaction, temperature is risen to 215~220 DEG C, constant temperature 3~5 minutes;
(4) after constant temperature, stop heating agent, naturally cool between 80~100 DEG C, be separately added into antirust agent, metal subtracts
Agent living;
(5) temperature is down between 50~60 DEG C, and solid lubricant is added, and is stirred 120 minutes;
(6) after stirring, by reaction mass by preparing lubricating grease after homogenizer homogeneous.
White uniformity ointment is presented in the lubricating grease appearance of preparation, has excellent resistant of high or low temperature, mechanical stability, extreme pressure
Wear resistence, colloid stability, good rustless property and long-life, Odor Evaluations are 2.5 grades, while VOC and venomous injurant
Matter content is all satisfied requirement (subordinate list).
Subordinate list components VOC and the requirement of poisonous and harmful substance limit value
Specific embodiment
Embodiment 1
Base oil 80%,
Thickening agent 20%,
By above-mentioned two components total amount, following additive mass percent is added:
1600g Poly alpha Olefins (PAO) synthetic oil and ten dihydroxystearic acid of 100g and 30g succinate are added in reaction kettle, opened
Stirring is opened, is heated to 83 DEG C, 14g lithium hydroxide aqueous solution is added, is reacted 120 minutes with this condition;After reaction, add
Enter 300g polyethylene, be heated to 142 DEG C of progress secondary responses, the reaction time controlled at 80 minutes;After reaction, by temperature liter
To 217 DEG C, constant temperature for 5 minutes;After constant temperature, stops heating agent, naturally cool to 90 DEG C, be separately added into 10g antirust agent laurylene
Base succinate, 10g metal deactivator thiadiazoles derivative;Temperature is down to 60 DEG C, and 15g Nano-class zinc oxide and 15g sulphur is added
Change zinc solid lubricant, stirs 120 minutes;After stirring, by reaction mass by that after import homogenizer homogeneous and can prepare
Lubricating grease.
The performance indicator of product is shown in Table 1.
Table 1
Embodiment 2
Base oil 85%,
Thickening agent 15%,
By above-mentioned two components total amount, following additive mass percent is added:
1700g Poly alpha Olefins (PAO) synthetic oil and ten dihydroxystearic acid of 75g and 30g succinate are added in reaction kettle, opened
Stirring is opened, is heated to 83 DEG C, 10.5g lithium hydroxide aqueous solution is added, is reacted 120 minutes with this condition;After reaction,
225g polyethylene is added, is heated to 142 DEG C of progress secondary responses, the reaction time controlled at 80 minutes;After reaction, by temperature
215 DEG C are risen to, constant temperature for 5 minutes;After constant temperature, stops heating agent, naturally cool to 90 DEG C, be separately added into 10g antirust agent 12
Alkenyl succinic acid ester, 10g metal deactivator thiadiazoles derivative;Temperature is down to 60 DEG C, and 15g Nano-class zinc oxide and 15g is added
Zinc sulphide solid lubricant stirs 120 minutes;After stirring, by reaction mass by that after import homogenizer homogeneous and can make
Standby lubricating grease.
The performance indicator of product is shown in Table 2.
Table 2
Embodiment 3
Base oil 82%,
Thickening agent 18%,
By above-mentioned two components total amount, following additive mass percent is added:
1640g Poly alpha Olefins (PAO) synthetic oil and ten dihydroxystearic acid of 90g and 30g succinate are added in reaction kettle, opened
Stirring is opened, is heated to 83 DEG C, 12.5g lithium hydroxide aqueous solution is added, is reacted 120 minutes with this condition;After reaction,
270g polyethylene is added, is heated to 140 DEG C of progress secondary responses, the reaction time controlled at 80 minutes;After reaction, by temperature
216 DEG C are risen to, constant temperature for 5 minutes;After constant temperature, stops heating agent, naturally cool to 90 DEG C, be separately added into 10g antirust agent 12
Alkenyl succinic acid ester, 10g metal deactivator thiadiazoles derivative;Temperature is down to 60 DEG C, and 15g Nano-class zinc oxide and 15g is added
Zinc sulphide solid lubricant stirs 120 minutes;After stirring, by reaction mass by that after import homogenizer homogeneous and can make
Standby lubricating grease.
The performance indicator of product is shown in Table 3.
Table 3
Embodiment 4
Base oil 83%,
Thickening agent 17%,
By above-mentioned two components total amount, following additive mass percent is added:
1660g Poly alpha Olefins (PAO) synthetic oil and ten dihydroxystearic acid of 85g and 30g succinate are added in reaction kettle, opened
Stirring is opened, is heated to 83 DEG C, 12g lithium hydroxide aqueous solution is added, is reacted 120 minutes with this condition;After reaction, add
Enter 255g polyethylene, be heated to 140 DEG C of progress secondary responses, the reaction time controlled at 80 minutes;After reaction, by temperature liter
To 216 DEG C, constant temperature for 5 minutes;After constant temperature, stops heating agent, naturally cool to 90 DEG C, be separately added into 10g antirust agent laurylene
Base succinate, 10g metal deactivator thiadiazoles derivative;Temperature is down to 60 DEG C, and 15g Nano-class zinc oxide and 15g sulphur is added
Change zinc solid lubricant, stirs 120 minutes;After stirring, by reaction mass by that after import homogenizer homogeneous and can prepare
Lubricating grease.
The performance indicator of product is shown in Table 4.
Table 4
Embodiment 5
Base oil 84%,
Thickening agent 16%,
By above-mentioned two components total amount, following additive mass percent is added:
1680g Poly alpha Olefins (PAO) synthetic oil and ten dihydroxystearic acid of 80g and 30g succinate are added in reaction kettle, opened
Stirring is opened, is heated to 83 DEG C, 11.2g lithium hydroxide aqueous solution is added, is reacted 120 minutes with this condition;After reaction,
240g polyethylene is added, is heated to 142 DEG C of progress secondary responses, the reaction time controlled at 80 minutes;After reaction, by temperature
217 DEG C are risen to, constant temperature for 5 minutes;After constant temperature, stops heating agent, naturally cool to 90 DEG C, be separately added into 10g antirust agent 12
Alkenyl succinic acid ester, 10g metal deactivator thiadiazoles derivative;Temperature is down to 60 DEG C, and 10g Nano-class zinc oxide and 10g is added
Zinc sulphide solid lubricant stirs 120 minutes;After stirring, by reaction mass by that after import homogenizer homogeneous and can make
Standby lubricating grease.
The performance indicator of product is shown in Table 5.
Table 5
Comparative example 1
Cable pulley type glass lifter lubricating grease of the invention can be obtained with external competing product M PERFORMANCE OF GREASES index correlation data
Out, high and low temperature resistance, mechanical stability energy, extreme pressure and antiwear behavior, colloid stability energy and rustless property are superior to competing product M profit
Consistent lubricant.
The performance of product and the comparison of competing product M lubricating grease achievement data are shown in Table 6.
Table 6
Comparative example 2
With domestic competing product N PERFORMANCE OF GREASES index correlation data it can be concluded that, high and low temperature resistance, mechanical stability energy,
Extreme pressure and antiwear behavior, colloid stability energy and rustless property are superior to competing product N lubricating grease
The performance of product and the comparison of competing product N lubricating grease achievement data are shown in Table 7.
Table 7
The performance data comparison of embodiment 1-5 is shown in Table 8
Table 8
The performance data comparison of comparative example 1-2 is shown in Table 9
Table 9
As seen from Table 8, there is excellent resistance to height using the lubricating grease embodiment 1 to 5 prepared within the scope of inventive formulation
Warm nature, mechanical stability, extreme pressure anti-wear, colloid stability, good rustless property and long-life, it is provided simultaneously with excellent ring
Border friendly.
As seen from Table 9, the lubricating grease of invention and external competing product A lubricating grease, domestic competing product B PERFORMANCE OF GREASES index compare number
According to it can be concluded that, work as in terms of greasy property with external competing condition, but in lubricating grease smell and VOC poisonous and harmful substance index
Aspect is superior to competing product.
Claims (9)
1. a kind of composition of low smell cable pulley type electric glass lifter lubricating grease, it is characterised in that: component and quality percentage
Than as follows:
Base oil 80~85%,
Thickening agent 10~15%,
By above-mentioned two components total amount, following additive mass percent is added:
。
2. composition according to claim 1, it is characterized in that base oil is Poly alpha Olefins (PAO) synthetic oil, 40 DEG C of viscosity are 70-
90mm/s2。
3. composition according to claim 1, it is characterized in that lithium 12-hydroxy stearate and polyethylene are compared to according to 1:3 mass
For thickening agent.
4. composition according to claim 1, it is characterized in that solid lubricant Nano grade zinc oxide and nano-zinc sulfide
It is prepared according to 1:1 mass ratio.
5. composition according to claim 1, it is characterized in that 2,6-di-tert-butyl p-cresol is as antioxidant.
6. composition according to claim 1, it is characterized in that antirust agent is dodecenylsuccinic acid ester.
7. composition according to claim 1, it is characterized in that dispersing agent is succinate.
8. composition according to claim 1, it is characterized in that metal deactivator is thiadiazoles derivative.
9. the method that composition according to claim 1 prepares low smell cable pulley type electric glass lifter lubricating grease,
Characterization step is as follows:
(1) Poly alpha Olefins (PAO) synthetic oil, ten dihydroxystearic acids, dispersing agent are separately added into reaction kettle, open stirring, is heated to
80~85 DEG C, lithium hydroxide aqueous solution is added, reacts 90~120 minutes with this condition;
(2) after reaction, polyethylene is added, is heated to 140~145 DEG C and is reacted, the reaction time is 60~80 minutes;
(3) after reaction, temperature is risen to 215~220 DEG C, constant temperature 3~5 minutes;
(4) after constant temperature, stop heating agent, naturally cool between 80~100 DEG C, be separately added into antirust agent, metal deactivator;
(5) temperature is down between 50~60 DEG C, and solid lubricant is added, and is stirred 120 minutes;
(6) after stirring, by reaction mass by that after import homogenizer homogeneous and can prepare lubricating grease.