CN109160721A - A kind of production method of glare proof glass - Google Patents
A kind of production method of glare proof glass Download PDFInfo
- Publication number
- CN109160721A CN109160721A CN201811215527.0A CN201811215527A CN109160721A CN 109160721 A CN109160721 A CN 109160721A CN 201811215527 A CN201811215527 A CN 201811215527A CN 109160721 A CN109160721 A CN 109160721A
- Authority
- CN
- China
- Prior art keywords
- glass
- finished product
- antiglare material
- glass substrate
- glare proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of glare proof glass, comprising the following steps: step S1 is needed to process glass shape, be cleaned, obtains glass substrate by production；Step S2 sprays antiglare material with surface of the spray gun to glass substrate at normal temperature；Step S3, it is physical toughened to the glass substrate progress for coating antiglare material at 600-720 DEG C, obtain semi-finished product；Step S4 carries out silk-screen frame to semi-finished product, obtains finished product.The present invention first carries out spraying antiglare material and carries out again physical toughened, and silica dioxide granule can be embedded in glass surface at high temperature, and with glass ining conjunction with more preferably, antiglare material is not easy to fall off after obtaining finished product, and the service life is longer；The glare proof glass hardness of this method production can achieve 9H, and abrasion resistance has great raising up to 5000 times or more, compared with the prior art.
Description
Technical field
The present invention relates to glass production fields, particularly relate to a kind of production method of glare proof glass.
Background technique
The production method of glare proof glass is the surface for carrying out processing to bare glass and forming a relative coarseness, makes bare glass
Reflecting surface becomes dumb light diffusing reflection surface, reduces reflective influence, and glare proof glass surface anticorrosion, anti-scratch performance are strong.
The interference of low ambient light can drop in anti-dazzle glas, may be constructed transparent anti-glare, antireflection screen in conjunction with video imaging screen, solution
Certainly electronics screen, video screen generate reflective, glare problem under environment light source, improve the visible angle of display picture and bright
Degree reduces screen reflecting, allows image is apparent, color is more gorgeous, color is more saturated, and improves image frame quality.
There is a kind of glare proof glass production method at present, is to spray antiglare material by after glass tempering on surface, obtain
One surface with diffusing reflection effect.Heating temperature when due to current production technology glass tempering is sprayed at 700 DEG C or so
Heating temperature when painting has sprayed during being heating and curing after antiglare material that antiglare material can only only at 200 DEG C or so
It is attached to the surface of glass, antiglare material and glass combine bad, are easy to fall off, the glare proof glass for causing this method to produce
Service life is short, hardness is insufficient.
In view of this, the present inventor regarding to the issue above caused by many missings and inconvenience, and deeply conceive, and actively
Research improvement has a fling at and develops and design the present invention.
Summary of the invention
The purpose of the present invention is to provide a kind of production methods of glare proof glass, improve the knot of antiglare material and glass
Conjunction degree, to improve hardness and service life.
In order to achieve the above objectives, solution of the invention is:
A kind of production method of glare proof glass, comprising the following steps:
Step S1 cuts glass, is processed and cleaned, obtains glass substrate；
Step S2 sprays antiglare material with surface of the spray gun to glass substrate at normal temperature；
Step S3, it is physical toughened to the glass substrate progress for coating antiglare material at 600-720 DEG C, obtain semi-finished product；
Step S4 carries out silk-screen frame, and baking-curing ink to semi-finished product, obtains finished product.
The antiglare material is nanometer grade silica sol gel solution.
The present invention first carries out spraying antiglare material and carries out again physical toughened, and silica dioxide granule can be embedded at high temperature
Glass surface, more preferable in conjunction with glass, antiglare material is not easy to fall off after obtaining finished product, and the service life is longer；This method is raw
The glare proof glass hardness of production can achieve 9H, and abrasion resistance has great raising up to 5000 times or more, compared with the prior art；We
The step of method sprays just can be carried out at normal temperature, and condition more easily reachs, and technique is simpler.
Specific embodiment
In order to further explain the technical solution of the present invention, being explained in detail below by specific embodiment the present invention
It states.
A kind of production method of glare proof glass, comprising the following steps:
Step S1 is needed to cut glass, be processed and cleaned, obtains glass substrate by production；
Step S2 sprays antiglare material with surface of the spray gun to glass substrate at normal temperature；
Step S3, it is physical toughened to the glass substrate progress for coating antiglare material at 600-720 DEG C, obtain semi-finished product；
Step S4 carries out silk-screen frame, and baking-curing ink to semi-finished product, obtains finished product.
In above-mentioned steps S2, antiglare material is nanometer grade silica sol gel solution.
Through the above steps, it first carries out spraying antiglare material and carries out physical toughened, silica dioxide granule at high temperature again
It can be embedded in glass surface, more preferable in conjunction with glass, antiglare material is not easy to fall off after obtaining finished product, and the service life is longer；
The glare proof glass hardness of this method production can achieve 9H, and abrasion resistance has greatly up to 5000 times or more compared with the prior art
It improves；The step of this method sprays can be carried out at normal temperature, and condition is easier to realize, technique is simpler.
Below table is the comparison of existing glare proof glass and product of the invention, it can be seen that product of the invention exists
It is obviously improved in hardness, the performance of abrasion performance.
Surface pencil hardness compares:
| Surface pencil hardness test condition | Existing product | Product of the invention |
| Bear a heavy burden 1000g, pencil angle at 45 ° | 6H | 9H |
Abrasion resistance test compares:
Above-described embodiment and non-limiting product form and style of the invention, any person of an ordinary skill in the technical field couple
Its appropriate changes or modifications done all should be regarded as not departing from patent category of the invention.
Claims (2)
1. a kind of production method of glare proof glass, it is characterised in that the following steps are included:
Step S1 cuts glass, is processed and cleaned, obtains glass substrate；
Step S2 sprays antiglare material with surface of the spray gun to glass substrate at normal temperature；
Step S3, it is physical toughened to the glass substrate progress for coating antiglare material at 600-720 DEG C, obtain semi-finished product；
Step S4 carries out silk-screen frame, and baking-curing ink to semi-finished product, obtains finished product.
2. a kind of production method of glare proof glass as described in claim 1, it is characterised in that；The antiglare material is to receive
Meter level Silicon dioxide sol-gel solution.