CN109135893A - Coal mine waterpower measure drill rod thread stop-leak compound - Google Patents
Coal mine waterpower measure drill rod thread stop-leak compound Download PDFInfo
- Publication number
- CN109135893A CN109135893A CN201811058028.5A CN201811058028A CN109135893A CN 109135893 A CN109135893 A CN 109135893A CN 201811058028 A CN201811058028 A CN 201811058028A CN 109135893 A CN109135893 A CN 109135893A
- Authority
- CN
- China
- Prior art keywords
- parts
- drill rod
- coal mine
- leak compound
- hydroquinone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of coal mine waterpower measure drill rod thread stop-leak compounds, including methacrylic acid, triethylene-glycol, sulfuric acid, hydroquinone, toluene, poly- 2,6- dimethyl-Isosorbide-5-Nitrae-phenylate, polyvinyl acetate, styrenic elastomer, mica, superfine graphite powder, ceramic particle, polypropylene fibre, isopropyl benzene hydroperoxide, N methyldiethanol amine, acidification saccharin, polymerization inhibitor, antioxidant, tackifier;The partial size of the ceramic particle is 2.8 μm;High temperature resistant is up to 700 DEG C, high pressure resistant 100MPa, wellability is good, and stop-leak compound can be sufficient filling with all possible leakage paths of screw thread, and be formed by curing a kind of lastics polymer, sealant is formed in thread surface, make no hole and gap at sealing, therefore moisture or other corrosive substances will not be retained, reduces corrosiveness, good airproof performance, and without grease, unleaded, heavy metal free, it is nontoxic, without non-biodegradation ingredient, lubricity is good, can prevent thread gluing phenomenon generate.
Description
Technical field
The present invention relates to a kind of stop-leak compound, in particular to a kind of coal mine waterpower measure drill rod thread stop-leak compound.
Background technique
Gas Disaster is an important factor for restricting China's coal-mine safety in production and Dissertation of Development of Coal Industry.With coal mining depth
The continuous increase of scale, coal seam geological condition more sophisticated are exploited in the increase of degree, and gas drainage difficulty increases, and safety of coal mines is asked
It inscribes more and more prominent.The waterpower measure such as hydraulic fracturing, hydraulic slotted liner technique, hydraulic flushing in hole, coal-bed flooding is as coal seam pressure relief and permeability improvement
And the key technology of regional gas control, remarkable result is achieved in underground coal mine.Currently, the relevant technologies just continuing to develop with it is complete
It is kind, and promoted and applied.Waterpower measure described above requires high pressure water is defeated by drilling rod in the specific implementation process
It is sent to predetermined position progress waterpower and is turned into industry, the sealing performance and construction effect of drilling rod are closely related.It is not high for pressure requirements
Measures, the sealing performance of common drilling rod such as hydraulic flushing in hole, coal-bed flooding can meet the requirements;But for hydraulic fracturing, waterpower
The high measure of the pressure requirements such as slot, the sealing performance of common drilling rod have been unable to meet demand, generally use special high densification
Seal drill rod.However, on the one hand structure is complicated, involves great expense for special drilling rod;On the other hand, since repeated removal, high temperature and pressure are held
Sealing ring damage is easily caused to influence construction effect, these factors all limit the popularization and application of every waterpower measure.Therefore, urgently
The drilling rod sealing means of waterpower measure need to be improved and perfect.
Smearing thread sealing grease in drill rod thread junction is a kind of effective way for improving drilling rod sealing effect.Common
When drilling rod intensity is met the requirements, it can replace special drilling rod and used in waterpower measure, to reduce operational sequence, reduce equipment
Cost, the application effect for expanding application range, improving waterpower measure.Common oil base rouge thread compound is before being applied to screw thread
It is sticky paste, when any variation not occurring using rear state under normal conditions, but being influenced by high temperature and pressure, can gradually loses
Its constituent part is removed, and finally powdered in drying up, the effect for playing its auxiliary seal Yu anti-adhesive buckle can not be continued.Meanwhile it is existing
Some thread compound carriers are still grease, and filler uses polytetrafluoroethylene (PTFE) (teflon P T F E), leads to the clear of residue
There are still pollution problems for reason and processing;In addition, the sealing performance and assembly and disassembly operability to these products are evaluated, produce
Satisfactory result is not achieved in the lubricity and leakproofness of product.
Summary of the invention
In view of this, the purpose of the present invention is to provide a kind of coal mine waterpower measure drill rod thread stop-leak compound, heatproof
Resistance to pressure is good, be free of lubricant component, and unleaded, heavy metal free, it is nontoxic, without non-biodegradation ingredient, lubricity is good, can prevent from gluing
Phenomenon is detained to generate.
Coal mine waterpower measure drill rod thread stop-leak compound of the invention, the sealing fat raw material includes following by weight
Component: 30-40 parts of methacrylic acid, 25-35 parts of triethylene-glycol, 1-3 parts of sulfuric acid, 0.1-0.6 parts of hydroquinone, toluene
0.1-0.6 parts, poly- 2-6 parts of 2,6- dimethyl -1,4- phenylate, 5-10 parts of polyvinyl acetate, 5-10 parts of styrenic elastomer, cloud
10-20 parts female, 5-15 parts of superfine graphite powder, 5-15 parts of ceramic particle, 1-5 parts of polypropylene fibre, isopropyl benzene hydroperoxide 1-4
Part, 3-8 parts of N methyldiethanol amine, acidification saccharin 5-10 parts, 1-3 parts of polymerization inhibitor, 1-5 parts of antioxidant, 1-3 parts of tackifier;
The partial size of the ceramic particle is 2.8 μm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two contractings
It is stirred and heated to after temperature is 80 DEG C after triethylene glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then in temperature
Reflux is kept the temperature at 80-100 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense food
Then reaction solution decompression is sloughed benzene, it is equal to then add the remaining raw materials stirring by salt water washing reaction liquid until pH value is 6-7
It is even;
Further, the sealing fat raw material includes following components by weight: 35 parts of methacrylic acid, triethylene-glycol
30 parts, 2 parts of sulfuric acid, 0.3 part of hydroquinone, 0.3 part of toluene, poly- 4 parts of 2,6- dimethyl -1,4- phenylate, polyvinyl acetate 8
Part, 8 parts of styrenic elastomer, 15 parts of mica, 10 parts of superfine graphite powder, 10 parts of ceramic particle, 3 parts of polypropylene fibre, isopropylbenzene
2 parts of hydrogen peroxide, 5 parts of N methyldiethanol amine, acidification 8 parts of saccharin, 2 parts of polymerization inhibitor, 3 parts of antioxidant, 2 parts of tackifier;
Further, the polypropylene fibre partial size is 0.1mm~3mm;The styrenic elastomer is Taipol SEBS;
Further, the polymerization inhibitor is the mixture of 2,5- di-tert-butyl hydroquinone and mantoquita, the tertiary fourth of 2, the 5- bis-
The weight ratio of base hydroquinone and mantoquita is 5:1;
Further, the antioxidant is 2,6-di-tert-butyl p-cresol, the compounding for being alkylated base-alpha-naphthylamine and rosemary;
DBPC 2,6 ditertiary butyl p cresol in mass ratio: alkylation base-alpha-naphthylamine: rosemary=4:2:1;
Further, the tackifier are hydroxyl terminated butyl nitrile (HTBN) rubber.
Beneficial effects of the present invention: coal mine waterpower measure drill rod thread stop-leak compound of the invention, high temperature resistant is up to 700
DEG C, high pressure resistant 100MPa, wellability is good, and stop-leak compound can be sufficient filling with all possible leakage paths of screw thread, and be formed by curing one kind
Lastics polymer, thread surface formed sealant, make no hole and gap at sealing, thus will not retain moisture or its
Its corrosive substance, reduces corrosiveness, good airproof performance, and without grease, unleaded, heavy metal free, it is nontoxic, without abiotic drop
Ingredient is solved, lubricity is good, can prevent thread gluing phenomenon from generating.
Specific embodiment
Embodiment one
The coal mine waterpower measure drill rod thread stop-leak compound of the present embodiment, the sealing fat raw material include by weight with
Lower component: 30 parts of methacrylic acid, 25 parts of triethylene-glycol, 1 part of sulfuric acid, 0.1 part of hydroquinone, 0.1 part of toluene, poly- 2,6-
2 parts of dimethyl -1,4- phenylate, 5 parts of polyvinyl acetate, 5 parts of styrenic elastomer, 10 parts of mica, 5 parts of superfine graphite powder, pottery
5 parts of porcelain particle, 1 part of polypropylene fibre, 1 part of isopropyl benzene hydroperoxide, 3 parts of N methyldiethanol amine, 5 parts of saccharin of acidification, polymerization inhibitor
1 part of agent, 1 part of antioxidant, 1 part of tackifier;
The partial size of the ceramic particle is 2.8 μm;The polypropylene fibre partial size is 0.1mm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two contractings
It is stirred and heated to after temperature is 80 DEG C after triethylene glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then in temperature
Reflux is kept the temperature at 80 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense saline solution
Then reaction solution decompression is sloughed benzene, then adds the remaining raw materials and stir evenly by washing reaction liquid until pH value is 6-7.
Embodiment two
The coal mine waterpower measure drill rod thread stop-leak compound of the present embodiment, the sealing fat raw material include by weight with
Lower component: 40 parts of methacrylic acid, 35 parts of triethylene-glycol, 3 parts of sulfuric acid, 0.6 part of hydroquinone, 0.6 part of toluene, poly- 2,6-
6 parts of dimethyl -1,4- phenylate, 10 parts of polyvinyl acetate, 10 parts of styrenic elastomer, 20 parts of mica, 15 parts of superfine graphite powder,
15 parts of ceramic particle, 5 parts of polypropylene fibre, 4 parts of isopropyl benzene hydroperoxide, 8 parts of N methyldiethanol amine, acidification 10 parts of saccharin,
3 parts of polymerization inhibitor, 5 parts of antioxidant, 3 parts of tackifier;
The partial size of the ceramic particle is 2.8 μm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two contractings
It is stirred and heated to after temperature is 80 DEG C after triethylene glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then in temperature
Reflux is kept the temperature at 100 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense salt
Then reaction solution decompression is sloughed benzene, then adds the remaining raw materials and stir evenly by water washing reaction solution until pH value is 6-7.
Embodiment three
The coal mine waterpower measure drill rod thread stop-leak compound of the present embodiment, the sealing fat raw material include by weight with
Lower component: 30 parts of methacrylic acid, 35 parts of triethylene-glycol, 1 part of sulfuric acid, 0.6 part of hydroquinone, 0.1 part of toluene, poly- 2,6-
6 parts of dimethyl -1,4- phenylate, 5 parts of polyvinyl acetate, 10 parts of styrenic elastomer, 10 parts of mica, 15 parts of superfine graphite powder,
5 parts of ceramic particle, 5 parts of polypropylene fibre, 1 part of isopropyl benzene hydroperoxide, 8 parts of N methyldiethanol amine, 5 parts of saccharin of acidification, resistance
3 parts of poly- agent, 1 part of antioxidant, 3 parts of tackifier;
The partial size of the ceramic particle is 2.8 μm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two contractings
It is stirred and heated to after temperature is 80 DEG C after triethylene glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then in temperature
Reflux is kept the temperature at 80 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense saline solution
Then reaction solution decompression is sloughed benzene, then adds the remaining raw materials and stir evenly by washing reaction liquid until pH value is 6-7.
Example IV
The coal mine waterpower measure drill rod thread stop-leak compound of the present embodiment, the sealing fat raw material include by weight with
Lower component: 40 parts of methacrylic acid, 25 parts of triethylene-glycol, 3 parts of sulfuric acid, 0.1 part of hydroquinone, 0.6 part of toluene, poly- 2,6-
2 parts of dimethyl -1,4- phenylate, 10 parts of polyvinyl acetate, 5 parts of styrenic elastomer, 20 parts of mica, 5 parts of superfine graphite powder, pottery
15 parts of porcelain particle, 1 part of polypropylene fibre, 4 parts of isopropyl benzene hydroperoxide, 3 parts of N methyldiethanol amine, 10 parts of saccharin of acidification, resistance
1 part of poly- agent, 5 parts of antioxidant, 1 part of tackifier;
The partial size of the ceramic particle is 2.8 μm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two contractings
It is stirred and heated to after temperature is 80 DEG C after triethylene glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then in temperature
Reflux is kept the temperature at 85 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense saline solution
Then reaction solution decompression is sloughed benzene, then adds the remaining raw materials and stir evenly by washing reaction liquid until pH value is 6-7.
Embodiment five
The coal mine waterpower measure drill rod thread stop-leak compound of the present embodiment, the sealing fat raw material include by weight with
Lower component: 35 parts of methacrylic acid, 28 parts of triethylene-glycol, 1 part of sulfuric acid, 0.6 part of hydroquinone, 0.3 part of toluene, poly- 2,6-
2- parts of dimethyl -1,4- phenylate, 10 parts of polyvinyl acetate, 7 parts of styrenic elastomer, 10 parts of mica, 15 parts of superfine graphite powder,
13 parts of ceramic particle, 1 part of polypropylene fibre, 4 parts of isopropyl benzene hydroperoxide, 7 parts of N methyldiethanol amine, 6 parts of saccharin of acidification, resistance
2 parts of poly- agent, 4 parts of antioxidant, 3 parts of tackifier;
The partial size of the ceramic particle is 2.8 μm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two contractings
It is stirred and heated to after temperature is 80 DEG C after triethylene glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then in temperature
Reflux is kept the temperature at 95 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense saline solution
Then reaction solution decompression is sloughed benzene, then adds the remaining raw materials and stir evenly by washing reaction liquid until pH value is 6-7.
Embodiment six
The coal mine waterpower measure drill rod thread stop-leak compound of the present embodiment, the sealing fat raw material include by weight with
Lower component: 35 parts of methacrylic acid, 30 parts of triethylene-glycol, 2 parts of sulfuric acid, 0.3 part of hydroquinone, 0.3 part of toluene, poly- 2,6-
4 parts of dimethyl -1,4- phenylate, 8 parts of polyvinyl acetate, 8 parts of styrenic elastomer, 15 parts of mica, 10 parts of superfine graphite powder, pottery
10 parts of porcelain particle, 3 parts of polypropylene fibre, 2 parts of isopropyl benzene hydroperoxide, 5 parts of N methyldiethanol amine, 8 parts of saccharin of acidification, polymerization inhibitor
2 parts of agent, 3 parts of antioxidant, 2 parts of tackifier;
The partial size of the ceramic particle is 2.8 μm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two contractings
It is stirred and heated to after temperature is 80 DEG C after triethylene glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then in temperature
Reflux is kept the temperature at 80-100 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense food
Then reaction solution decompression is sloughed benzene, it is equal to then add the remaining raw materials stirring by salt water washing reaction liquid until pH value is 6-7
It is even.
In above-described embodiment, the styrenic elastomer is Taipol SEBS;The polymerization inhibitor is 2,5- di-t-butyl pair
The weight ratio of the mixture of benzenediol and mantoquita, 2, the 5- di-tert-butyl hydroquinone and mantoquita is 5:1;The antioxidant is
DBPC 2,6 ditertiary butyl p cresol, the compounding for being alkylated base-alpha-naphthylamine and rosemary;DBPC 2,6 ditertiary butyl p cresol in mass ratio:
It is alkylated base-alpha-naphthylamine: rosemary=4:2:1;The tackifier are hydroxyl terminated butyl nitrile (HTBN) rubber.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to skill of the invention
Art scheme is modified or replaced equivalently, and without departing from the objective and range of technical solution of the present invention, should all be covered at this
In the scope of the claims of invention.
Claims (6)
1. a kind of coal mine waterpower measure drill rod thread stop-leak compound, it is characterised in that: the sealing fat raw material wraps by weight
Include following components: 30-40 parts of methacrylic acid, 25-35 parts of triethylene-glycol, 1-3 parts of sulfuric acid, 0.1-0.6 parts of hydroquinone,
0.1-0.6 parts of toluene, poly- 2-6 parts of 2,6- dimethyl -1,4- phenylate, 5-10 parts of polyvinyl acetate, styrenic elastomer 5-10
Part, 10-20 parts of mica, 5-15 parts of superfine graphite powder, 5-15 parts of ceramic particle, 1-5 parts of polypropylene fibre, isopropyl benzene hydroperoxide
1-4 parts, 3-8 parts of N methyldiethanol amine, acidification saccharin 5-10 parts, 1-3 parts of polymerization inhibitor, 1-5 parts of antioxidant, 1-3 parts of tackifier;
The partial size of the ceramic particle is 2.8 μm;
The coal mine waterpower measure is prepared with drill rod thread stop-leak compound by following manner: by methacrylic acid, two three second of contracting
It is stirred and heated to after temperature is 80 DEG C after glycol, hydroquinone and toluene mixing and adds sulfuric acid dropwise, be then 80- in temperature
Reflux is kept the temperature at 100 DEG C, the saline solution neutralization containing 5% sodium carbonate is then added and removes sulfuric acid and hydroquinone, then with dense salt
Then reaction solution decompression is sloughed benzene, then adds the remaining raw materials and stir evenly by water washing reaction solution until pH value is 6-7.
2. coal mine waterpower measure drill rod thread stop-leak compound according to claim 1, it is characterised in that: the stop-leak compound
Raw material includes following components by weight: 35 parts of methacrylic acid, 30 parts of triethylene-glycol, 2 parts of sulfuric acid, hydroquinone 0.3
Part, 0.3 part of toluene, poly- 4 parts of 2,6- dimethyl -1,4- phenylate, 8 parts of polyvinyl acetate, 8 parts of styrenic elastomer, mica 15
Part, 10 parts of superfine graphite powder, 10 parts of ceramic particle, 3 parts of polypropylene fibre, 2 parts of isopropyl benzene hydroperoxide, N methyldiethanol amine
5 parts, acidification 8 parts of saccharin, 2 parts of polymerization inhibitor, 3 parts of antioxidant, 2 parts of tackifier.
3. coal mine waterpower measure drill rod thread stop-leak compound according to claim 1, it is characterised in that: the polypropylene
Fiber diameter is 0.1mm~3mm;The styrenic elastomer is Taipol SEBS.
4. coal mine waterpower measure drill rod thread stop-leak compound according to claim 3, it is characterised in that: the polymerization inhibitor
For the mixture of 2,5- di-tert-butyl hydroquinone and mantoquita, the weight ratio of 2, the 5- di-tert-butyl hydroquinone and mantoquita is
5:1.
5. coal mine waterpower measure drill rod thread stop-leak compound according to claim 4, it is characterised in that: the antioxidant
For the compounding of DBPC 2,6 ditertiary butyl p cresol, alkylation base-alpha-naphthylamine and rosemary;2,6- di-t-butyl in mass ratio is to first
Phenol: alkylation base-alpha-naphthylamine: rosemary=4:2:1.
6. coal mine waterpower measure drill rod thread stop-leak compound according to claim 5, it is characterised in that: the tackifier
For hydroxyl terminated butyl nitrile (HTBN) rubber.