CN109127338A - A kind of stainless steel wire drawing technique - Google Patents
A kind of stainless steel wire drawing technique Download PDFInfo
- Publication number
- CN109127338A CN109127338A CN201811016025.5A CN201811016025A CN109127338A CN 109127338 A CN109127338 A CN 109127338A CN 201811016025 A CN201811016025 A CN 201811016025A CN 109127338 A CN109127338 A CN 109127338A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel plate
- membrane material
- wire drawing
- photocureable coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stainless steel wire drawing techniques, are related to stainless steel production field, comprising the following steps: Step 1: stainless steel metal plate surface degreasing；Step 2: stainless steel plate front applies photocureable coating；Step 3: membrane material is covered in stainless steel plate front；Step 4: photocuring；After being air-dried to stainless steel plate degreasing, passivation and cleaning, in the front surface coated photocureable coating of stainless steel plate, and tool membrane material is pasted in the side of setting inorganic agent, so that photocureable coating is contacted according to the lines on membrane material with stainless steel plate, to make photocureable coating be reacted according to the lines on membrane material with stainless steel plate, to carry out chemical wire drawing to stainless steel plate.
Description
Technical field
The present invention relates to stainless steel production fields, more specifically, being related to a kind of stainless steel wire drawing technique.
Background technique
Stainless steel wire drawing is a kind of metal working process, is a kind of processing technique of stainless steel surface.
Stainless steel is in addition to industrially applying, it may also be used for production ornaments such as baldric, craftwork generally use stainless
Steel drawing process is made.In process, the impurity contained in stainless steel can aoxidize, so that its color be made to be deteriorated, hold
Easy garland, surface are easily dirty etc..Surface wire drawing process is to form the surface treatment means of strain line in workpiece surface by grinding.
Traditional stainless steel wire drawing is carried out, production technology is extremely complex, and time-consuming for production, and production generation pollution is big, because of grinding
The particle contamination of generation, easily causes environmental pollution；It is very easy to be disconnected during stainless steel wire drawing due to being mechanical wire drawing.
The prior art can refer to the Chinese invention patent application that application publication number is CN107377331A, that application discloses
A kind of preparation method of no fingerprint wire drawing stainless-steel sheet, mainly comprises the steps that wire drawing, alkali cleaning, electrolysis, pickling, cleaning
Drying, oiling, levelling, baking and cooling packing.
But using the preparation method in wire drawing, need to toast and cooling, in baking, paint solvent can be evaporated,
It pollutes；In addition, needing to be cooled down after baking, the time of processing is increased, is not easy to produce.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of stainless steel wire drawing technique, advantage
It is that wire drawing is carried out to stainless steel plate by photocuring, so that the evaporation of coating is reduced, to reduce pollution；Stainless steel metal
It does not need to be cooled down after plate wire drawing, reduces the time of processing, consequently facilitating the production to stainless steel plate.
To achieve the above object, the present invention provides the following technical scheme that a kind of stainless steel wire drawing technique, including following step
It is rapid:
Step 1: stainless steel metal plate surface degreasing: being passivated to stainless steel plate, and in stainless steel plate degreasing
Afterwards, stainless steel plate is cleaned and is air-dried；
Step 2: stainless steel plate front applies photocureable coating: it is coated using surface of the photocureable coating to workpiece,
Photocureable coating includes acrylic resin；
Step 3: membrane material is covered in stainless steel plate front: after having coated photocureable coating in stainless steel plate, not
Membrane material is covered on rust steel metal plate, membrane material is provided with lines close to the side of stainless steel plate；
Step 4: photocuring；The stainless steel plate for covering membrane material is subjected to ultraviolet light irradiation, so that in stainless steel plate
Photocureable coating solidification, after the completion of solidification, membrane material is removed.
By using above-mentioned technical proposal, after being air-dried to stainless steel plate degreasing, passivation and cleaning, in stainless steel metal
The front surface coated photocureable coating of plate, and tool membrane material is pasted in the side of setting inorganic agent, so that photocureable coating is according to film
Lines on material is contacted with stainless steel plate, to make photocureable coating according to the lines and stainless steel metal on membrane material
Plate is reacted；Ultraviolet light irradiation is carried out to the stainless steel plate for pasting membrane material, to make photocureable coating solidify, then
By the membrane material removal in stainless steel plate, to carry out chemical wire drawing to stainless steel plate；In drawing process, it is not required to
Photocureable coating is toasted and cooled down, to reduce pollution, shortened process time, improve working efficiency.
It does not need water in process to cool down, to reduce the pollution to water；Pass through membrane material and stainless steel gold
The contact for belonging to plate, is able to solve the problem that vision and tactile cannot be unified in existing drawing process；Wire drawing is carried out by this method
Afterwards, salient point in stainless steel plate is bad to be reduced to 0.01 Ge/㎡ by 0.5 traditional Ge/㎡.
The present invention is further arranged to: in the step 3, the lines on membrane material is band, vertical line or twill.
By using above-mentioned technical proposal, when replacing different texture layer, it is only necessary to make the lines on the membrane material pasted
It is different, so that different lines are processed in stainless steel plate under the premise of being changed without equipment.
The present invention is further arranged to: in the step 1, when carrying out degreasing to stainless steel plate, first to stainless steel gold
Belong to plate and carry out thick degreasing, smart degreasing then is carried out to stainless steel plate.
By using above-mentioned technical proposal, ungrease treatment twice is carried out to stainless steel plate, to reduce stainless steel gold
The impurity for belonging to plate surface, consequently facilitating the processing to stainless steel plate subsequent handling；In thick degreasing, gone with alkaline processing liquid
Except the antirust oil in stainless steel plate；In smart degreasing, residual alkalinity treatment fluid is removed with pure water.
The present invention is further arranged to: in the step 1, after air-drying to stainless steel plate, to stainless steel metal
Plate is passivated, and is dried after passivation.
By using above-mentioned technical proposal, stainless steel plate is passivated, consequently facilitating photocureable coating with it is stainless
The contact of steel metal plate, consequently facilitating reacting stainless steel plate, consequently facilitating carrying out wire drawing to stainless steel plate.
The present invention is further arranged to: the stainless steel plate when being passivated using the passivator containing Ni, Ni's
Content is 2 g/ ㎡ -15g/ ㎡.
By using above-mentioned technical proposal, the adhesive force of stainless steel plate can be increased using the passivator containing Ni.
In conclusion the invention has the following advantages:
1. after pair stainless steel plate degreasing, passivation and cleaning air-dry, being applied in the front surface coated photocuring of stainless steel plate
Material, and tool membrane material is pasted in the side of setting inorganic agent, so that photocureable coating is according to the lines and stainless steel on membrane material
Metal plate contact, so that photocureable coating be made to be reacted according to the lines on membrane material with stainless steel plate；To pasting film
The stainless steel plate of material carries out ultraviolet light irradiation, thus solidify photocureable coating, it then will be in stainless steel plate
Membrane material removal, to carry out chemical wire drawing to stainless steel plate；In drawing process, do not need to carry out photocureable coating
Baking and cooling shorten process time to reduce pollution, improve working efficiency.
It does not need water in process to cool down, to reduce the pollution to water；Pass through membrane material and stainless steel gold
The contact for belonging to plate, is able to solve the problem that vision and tactile cannot be unified in existing drawing process；Wire drawing is carried out by this method
Afterwards, salient point in stainless steel plate is bad to be reduced to 0.01 Ge/㎡ by 0.5 traditional Ge/㎡；
2. when replacing different texture layer, it is only necessary to keep the lines on the membrane material pasted different, thus being changed without equipment
Under the premise of different lines are processed in stainless steel plate；
3. pair stainless steel plate carries out ungrease treatment twice, so that the impurity of stainless steel metal plate surface is reduced, consequently facilitating
Processing to stainless steel plate subsequent handling.
Specific embodiment
A kind of embodiment 1: stainless steel wire drawing technique, comprising the following steps:
Stainless steel plate unreels: coiled stainless steel plate is placed on uncoiler and is unreeled, the thickness of stainless steel plate
Degree is 0.2mm, and the linear velocity unreeled is 1m/min.
Stainless steel plate front applies photocureable coating: being carried out using front of the photocureable coating to stainless steel plate
Coating, is coated uniformly on photocureable coating in stainless steel plate, photocureable coating includes acrylic resin.
Membrane material is covered in stainless steel plate front: after having coated photocureable coating in stainless steel plate, by film
Material is covered on the side for being coated with the stainless steel plate of photocureable coating, and membrane material is arranged close to the side of stainless steel plate
There is lines, the lines on film is band.
Photocuring: the stainless steel plate for being covered with membrane material being placed into photocuring case and carries out photocuring, and photocuring applies
Material solidifies under the irradiation of ultraviolet lamp, and after the completion of solidification, membrane material is removed.
Winding: the stainless steel plate after having handled is placed on winder, the linear velocity of winder and uncoiler
Linear velocity is equal.
Through detecting, after stainless steel plate completes wire drawing, the salient point fraction defective of stainless steel metal plate surface is 0.2/㎡.
A kind of embodiment 2: stainless steel wire drawing technique, comprising the following steps:
Stainless steel plate unreels: coiled stainless steel plate is placed on uncoiler and is unreeled, the thickness of stainless steel plate
Degree is 0.5mm, and the linear velocity unreeled is 10m/min.
Stainless steel metal plate surface degreasing: thick degreasing first is carried out to stainless steel metal plate surface, is removed with alkaline processing liquid
Antirust oil in stainless steel plate；Then smart degreasing is carried out to stainless steel metal plate surface, at pure water removal residual alkalinity
Manage liquid；Stainless steel plate after ungrease treatment is cleaned with pure water, wind is carried out to the stainless steel plate that cleaning is completed
It is dry.
Stainless steel plate front applies photocureable coating: being carried out using front of the photocureable coating to stainless steel plate
Coating, is coated uniformly on photocureable coating in stainless steel plate, photocureable coating includes acrylic resin.
Membrane material is covered in stainless steel plate front: after the completion of being handled in stainless steel plate with photocureable coating,
Membrane material is covered on to the side for being coated with the stainless steel plate of photocureable coating, membrane material is close to the side of stainless steel plate
It is provided with lines, the lines on film is vertical line.
Photocuring: the stainless steel plate for being covered with membrane material being placed into photocuring case and carries out photocuring, and photocuring applies
Material solidifies under the irradiation of ultraviolet lamp, and after the completion of solidification, membrane material is removed.
Winding: the stainless steel plate after having handled is placed on winder, the linear velocity of winder and uncoiler
Linear velocity is equal
Through detecting, by defatting step and after completing wire drawing, the salient point fraction defective of stainless steel metal plate surface is 0.1/㎡.
A kind of embodiment 3: stainless steel wire drawing technique, comprising the following steps:
Stainless steel plate unreels: coiled stainless steel plate is placed on uncoiler and is unreeled, the thickness of stainless steel plate
Degree is 0.5mm, and the linear velocity unreeled is 10m/min.
Stainless steel metal plate surface degreasing: thick degreasing first is carried out to stainless steel metal plate surface, is removed with alkaline processing liquid
Antirust oil in stainless steel plate；Then smart degreasing is carried out to stainless steel metal plate surface, at pure water removal residual alkalinity
Manage liquid；Stainless steel plate after ungrease treatment is cleaned with pure water, wind is carried out to the stainless steel plate that cleaning is completed
It is dry.
The passivation of stainless steel plate front: the front of stainless steel plate is passivated, passivator is sprayed on stainless
On steel metal plate, Ni is contained in passivator, the content of Ni is 2 g/ ㎡.
Stainless steel plate front applies photocureable coating: being carried out using front of the photocureable coating to stainless steel plate
Coating, is coated uniformly on photocureable coating in stainless steel plate, photocureable coating includes acrylic resin.
Membrane material is covered in stainless steel plate front: after the completion of being handled in stainless steel plate with photocureable coating,
Membrane material is covered on to the side for being coated with the stainless steel plate of photocureable coating, membrane material is close to the side of stainless steel plate
It is provided with lines, the lines on film is twill.
Photocuring: the stainless steel plate for being covered with membrane material is placed into photocuring case and carries out photocuring.
Winding: the stainless steel plate after having handled is placed on winder, the linear velocity of winder and uncoiler
Linear velocity is equal
Through detecting, by surface degreasing and passivation step and after completing wire drawing, the salient point fraction defective of stainless steel metal plate surface
For 0.01 Ge/㎡.
A kind of embodiment 4: stainless steel wire drawing technique, comprising the following steps:
Stainless steel plate unreels: coiled stainless steel plate is placed on uncoiler and is unreeled, the thickness of stainless steel plate
Degree is 0.5mm, and the linear velocity unreeled is 10m/min.
Stainless steel metal plate surface degreasing: thick degreasing first is carried out to stainless steel metal plate surface, is removed with alkaline processing liquid
Antirust oil in stainless steel plate；Then smart degreasing is carried out to stainless steel metal plate surface, at pure water removal residual alkalinity
Manage liquid；Stainless steel plate after ungrease treatment is cleaned with pure water, wind is carried out to the stainless steel plate that cleaning is completed
It is dry.
The passivation of stainless steel plate front: the front of stainless steel plate is passivated, passivator is sprayed on stainless
On steel metal plate, Ni is contained in passivator, the content of Ni is 15g/ ㎡.
Stainless steel plate front applies photocureable coating: being carried out using front of the photocureable coating to stainless steel plate
Coating, is coated uniformly on photocureable coating in stainless steel plate, photocureable coating includes acrylic resin.
Membrane material is covered in stainless steel plate front: after the completion of being handled in stainless steel plate with photocureable coating,
Membrane material is covered on to the side for being coated with the stainless steel plate of photocureable coating, membrane material is close to the side of stainless steel plate
It is provided with lines, the lines on film is twill.
Photocuring: the stainless steel plate for being covered with membrane material is placed into photocuring case and carries out photocuring.
Winding: the stainless steel plate after having handled is placed on winder, the linear velocity of winder and uncoiler
Linear velocity is equal
Through detecting, by surface degreasing and passivation step and after completing wire drawing, the salient point fraction defective of stainless steel metal plate surface
For 0.01 Ge/㎡
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-described embodiment,
All technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
For those of ordinary skill, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (5)
1. a kind of stainless steel wire drawing technique, which comprises the following steps:
Step 1: stainless steel metal plate surface degreasing: being passivated to stainless steel plate, and in stainless steel plate degreasing
Afterwards, stainless steel plate is cleaned and is air-dried；
Step 2: stainless steel plate front applies photocureable coating: it is coated using surface of the photocureable coating to workpiece,
Photocureable coating includes acrylic resin；
Step 3: membrane material is covered in stainless steel plate front: after having coated photocureable coating in stainless steel plate, not
Membrane material is covered on rust steel metal plate, membrane material is provided with lines close to the side of stainless steel plate；
Step 4: photocuring；The stainless steel plate for covering membrane material is subjected to ultraviolet light irradiation, so that in stainless steel plate
Photocureable coating solidification, after the completion of solidification, membrane material is removed.
2. a kind of stainless steel wire drawing technique according to claim 1, it is characterised in that: in the step 3, on membrane material
Lines be band, vertical line or twill.
3. a kind of stainless steel wire drawing technique according to claim 1, it is characterised in that: in the step 1, to stainless steel
When metal plate carries out degreasing, thick degreasing first is carried out to stainless steel plate, smart degreasing then is carried out to stainless steel plate.
4. a kind of stainless steel wire drawing technique according to claim 1, it is characterised in that: in the step 1, to stainless steel
Metal plate carries out after air-drying, and is passivated to stainless steel plate, and dried after passivation.
5. a kind of stainless steel wire drawing technique according to claim 4, it is characterised in that: the stainless steel plate is carrying out
Using the passivator containing Ni when passivation, the content of Ni is 2 g/ ㎡ -15g/ ㎡.