CN109112588A - Using silver-colored graphite composite material as the non-cyanide silver coating method of matrix - Google Patents
Using silver-colored graphite composite material as the non-cyanide silver coating method of matrix Download PDFInfo
- Publication number
- CN109112588A CN109112588A CN201811060709.5A CN201811060709A CN109112588A CN 109112588 A CN109112588 A CN 109112588A CN 201811060709 A CN201811060709 A CN 201811060709A CN 109112588 A CN109112588 A CN 109112588A
- Authority
- CN
- China
- Prior art keywords
- silver
- beaker
- colored graphite
- water
- sample block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provide it is a kind of using silver-colored graphite composite material as the non-cyanide silver coating method of matrix, to solve the problems, such as be: how to reduce the silver-plated cost of silver-colored graphite composite material.The method is characterized in that preparing electroplate liquid, three kinds of raw materials, i.e. silver nitrate 40-45g, sodium thiosulfate 200-250 g and potassium metabisulfite 40-45 g are launched simultaneously in the following proportions in every liter of distilled water, is poured into beaker, while magnetic stirring apparatus is also put into beaker;Beaker is put into water-bath, by the tap water heating in water-bath to 25-35 DEG C;By after cleaning silver-colored graphite sample block and silver plate be put into beaker and be electroplated, start magnetic stirring apparatus simultaneously to be stirred filtered solution, mixing speed is 300-500 rpm, and the area ratio of silver plate and silver-colored graphite sample block is 1:1-1.5, and cathode-current density is 0.8-1.0 A/dm2, until electroplated layer reaches required thickness.
Description
Technical field
The present invention relates to a kind of techniques of silver-colored graphite composite material non-cyanide silver electroplating, are specifically with silver-colored graphite composite material
The electrosilvering method of matrix.
Background technique
This field follows the record of textbook at present, and the method for the electrosilvering used always includes preparing electroplate liquid, specifically
It is to launch five kinds of raw materials (solute), i.e. silver nitrate 40-45 g, sodium thiosulfate in the following proportions every liter of distilled water (solvent) is inner
200-250 g, potassium metabisulfite 40-45 g, ammonium acetate 20-30 g and thiosemicarbazide 0.6-0.8 g, are filtered again after mixing evenly
Decontamination is at electroplate liquid;This method further includes being electroplated at normal temperature in the silver-colored graphite sample block investment electroplate liquid after cleaning,
Cathode-current density is 0.1-0.3 A/dm when plating2, cathode and annode area ratio 1:2.This method has a defect that, is electroplated
Liquid is prepared using five kinds of raw materials, and higher cost, mainly ammonium acetate and thiosemicarbazide price are slightly higher.
Summary of the invention
The object of the present invention is to provide a kind of using silver-colored graphite composite material as the non-cyanide silver coating method of matrix.
The object of the present invention is achieved like this: it includes
Electroplate liquid is prepared, specifically launches three kinds of raw materials, i.e. silver nitrate 40-45g, sulphur simultaneously in the following proportions in every liter of distilled water
Sodium thiosulfate 200-250 g and potassium metabisulfite 40-45 g filters off impurity into electroplate liquid again after mixing evenly, pours into beaker,
Magnetic stirring apparatus is also put into beaker simultaneously;Beaker is put into water-bath, by the tap water heating in water-bath to 25-35
DEG C, the electroplate liquid height in water-bath in tap water height and beaker maintains an equal level;
Ultrasonic cleaning is carried out to silver-colored graphite sample block with acetone or alcohol, by after cleaning silver-colored graphite sample block and silver plate be put into beaker
In be electroplated, while starting magnetic stirring apparatus and filtered solution be stirred, mixing speed is 300-500 rpm, silver
The area ratio of plate and silver-colored graphite sample block is 1:1-1.5, and silver plate connects positive pole, and silver-colored graphite sample block connects power cathode, cathode current
Density is 0.8-1.0 A/dm2, until electroplated layer reaches required thickness.
Compared with prior art, the beneficial effects of the present invention are:
(1) electroplating cost is reduced.Raw material used in the relatively traditional electrosilvering of raw material used in the present invention is less, so plating
Cost about reduces by 20%.
(2) product quality is improved.The silver-colored graphite composite material being electroplated using the present invention, plating thickness is controllable, is electroplated
Layer with basal body binding force securely, be electroplated layer tissue it is fine and closely woven.
(3) overcome technology prejudice.
Specific embodiment
It includes preparing electroplate liquid, specifically launches three kinds of raw materials, i.e. nitric acid simultaneously in the following proportions in 1 liter of distilled water
Silver-colored 42g, 220 g of sodium thiosulfate and pyrosulfurous acid K42 g filter off impurity into electroplate liquid again after mixing evenly, pour into beaker
In, while magnetic stirring apparatus is also put into beaker;Beaker is put into water-bath, by the tap water heating in water-bath to 33
DEG C, the electroplate liquid height in water-bath in tap water height and beaker maintains an equal level;
Ultrasonic cleaning is carried out to silver-colored graphite sample block with acetone or alcohol, by after cleaning silver-colored graphite sample block and silver plate be put into beaker
In be electroplated, while starting magnetic stirring apparatus and filtered solution be stirred, mixing speed is 400 rpm, silver plate with
The area ratio of silver-colored graphite sample block is 1:1.2, and silver plate connects positive pole, and silver-colored graphite sample block connects power cathode, and cathode-current density is
0.9 A/dm2, until electroplated layer reaches required thickness.
Claims (1)
1. a kind of using silver-colored graphite composite material as the non-cyanide silver coating method of matrix, it includes
Electroplate liquid is prepared, specifically launches three kinds of raw materials, i.e. silver nitrate 40-45g, sulphur simultaneously in the following proportions in every liter of distilled water
Sodium thiosulfate 200-250 g and potassium metabisulfite 40-45 g filters off impurity into electroplate liquid again after mixing evenly, pours into beaker,
Magnetic stirring apparatus is also put into beaker simultaneously;Beaker is put into water-bath, by the tap water heating in water-bath to 25-35
DEG C, the electroplate liquid height in water-bath in tap water height and beaker maintains an equal level;
Ultrasonic cleaning is carried out to silver-colored graphite sample block with acetone or alcohol, by after cleaning silver-colored graphite sample block and silver plate be put into beaker
In be electroplated, while starting magnetic stirring apparatus and filtered solution be stirred, mixing speed is 300-500 rpm, silver
The area ratio of plate and silver-colored graphite sample block is 1:1-1.5, and silver plate connects positive pole, and silver-colored graphite sample block connects power cathode, cathode current
Density is 0.8-1.0 A/dm2, until electroplated layer reaches required thickness.