CN109111835A - A kind of double-component aqueous woodenware coating structure of anti-bleeding red oak - Google Patents
A kind of double-component aqueous woodenware coating structure of anti-bleeding red oak Download PDFInfo
- Publication number
- CN109111835A CN109111835A CN201810588587.0A CN201810588587A CN109111835A CN 109111835 A CN109111835 A CN 109111835A CN 201810588587 A CN201810588587 A CN 201810588587A CN 109111835 A CN109111835 A CN 109111835A
- Authority
- CN
- China
- Prior art keywords
- agent
- double
- parts
- component aqueous
- woodenware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of anti-double-component aqueous woodenware coating structure of bleeding red oak, the coating structure is followed successively by double-component aqueous wooden ware sealing primer coating, double-component aqueous woodenware polishing primer coating and double-component aqueous lacquer as woodenware finish coating on red oak substrate surface；Double-component aqueous wooden ware sealing priming paint, double-component aqueous woodenware polishing priming paint, double-component aqueous lacquer as woodenware finish include host agent, waterborne curing agent and water.Every layer of the structure includes the two-component of the acrylic acid dispersion containing OH functional group and the waterborne curing agent containing NCO functional group, two-component system densification cross-linked structure has barrier and sealing process to pigment, the tannic acid of red oak substrate, solves the problems, such as paint vehicle film discoloration caused by seeping on the tannic acid in red oak.Seal coat coating and polishing primer coating have the characteristics that adhesive force is strong, easy to polish, and topcoat has good smoothness, flatness, resistance to marring, hardness of paint film and excellent resistance to soiling.
Description
Technical field
The invention belongs to wood coating technical fields, and in particular to a kind of anti-double-component aqueous woodenware coating of bleeding red oak
Structure.
Background technique
Red oak is added due to its hard heavy wooden, unique wood grain, good surface treatment characteristics and good machine
Work performance, which becomes, manufactures all kinds of furniture, floor and the ideal material of bin.But contain a large amount of tannic acid, tannin in red oak
Acid is a kind of yellow polyphenolic substance, and great amount of hydroxy group is contained in molecule, and soluble easily in water, ethyl alcohol, glycerol etc. have as timber
Hydrophily, and water is one of main constituent of water paint.Colored component when coating is coated on wood surface, in timber
It can be dissolved into the continuous phase of coating rapidly -- in water, just as being added to color in coating, to change the form and aspect of coating.It is single
Rather seeping on acid causes film discoloration and adhesive force to be deteriorated, and all has a certain impact to stain for wood, covering with paint, eventually leads to film effect
Fruit is deteriorated.Because the good coating structure of a set of closing tannic acid effect of the invention is necessary.
Summary of the invention
The purpose of the present invention is to solve seep that the discoloration of paint vehicle film and adhesive force is caused to be deteriorated on tannic acid in red oak
The problem of, a kind of double-component aqueous woodenware coating structure of anti-bleeding red oak is provided.
The purpose of the present invention is achieved by the following technical scheme:
A kind of double-component aqueous woodenware coating structure of anti-bleeding red oak, the coating structure is on red oak substrate surface
It is followed successively by double-component aqueous wooden ware sealing primer coating, double-component aqueous woodenware polishing primer coating and double-component aqueous woodenware face
Lacquer coat；
Double-component aqueous wooden ware sealing priming paint, double-component aqueous woodenware polishing priming paint, double-component aqueous lacquer as woodenware finish wrap
Include host agent, waterborne curing agent and water；
The host agent of the double-component aqueous wooden ware sealing priming paint is by including that the raw material of following parts by weight forms: water-based emulsion
75-85 parts, 2-5 parts of coalescing agent, 0.1 part of pH adjusting agent, 0.3-0.5 parts of substrate wetting agents, 0.3-0.4 parts of defoaming agent, anti-corrosion
0.2 part of agent, 0.8-1 parts of thickener, 11-18.5 parts of deionized water；It is host agent in the double-component aqueous wooden ware sealing priming paint, aqueous
The weight ratio of curing agent and water is 100:13-15:20；
The host agent of the double-component aqueous woodenware polishing priming paint is by including that the raw material of following parts by weight forms: water-based emulsion
40-50 parts, 3-4 parts of coalescing agent, 0.1 part of pH adjusting agent, 0.3-0.6 parts of substrate wetting agents, 0.3-0.4 parts of defoaming agent, dispersion
1 part of agent, 34-39 parts of filler, 2 parts of grinding auxiliary agent, 0.2 part of preservative, 0.6-0.7 parts of thickener, 8.1-12.4 parts of deionized water；
The weight ratio of host agent, waterborne curing agent and water is 100:5-10:15 in the double-component aqueous woodenware polishing priming paint；
The host agent of the double-component aqueous lacquer as woodenware finish is by including that the raw material of following parts by weight forms: water-based emulsion 57-60
Part, 2-3 parts of coalescing agent, 0.1 part of pH adjusting agent, 0.4 part of substrate wetting agents, 0.6 part of defoaming agent, 0.5 part of dispersing agent, filler 20
Part, 2-3 parts of waterborne wax emulsion, 0.2 part of preservative, 0.8-0.9 parts of thickener, 11.4-16.3 parts of deionized water；The two-component
The weight ratio of host agent, waterborne curing agent and water is 100:10-15:25 in aqueous wooden ware finishing coat.
Further, the water-based emulsion be AC31, A2651, A2470, XP-2592,2042,6516, STW168,
One of AC2598,938T, ENCOR2171,6810, XK-102, WE-6173, XK-14, R2180, E-129,2008 are more
Kind；
The coalescing agent be -1,3 pentanediol mono isobutyrate of 2,2,4- trimethyl, dipropylene, propylene glycol,
One of dipropylene glycol methyl ether, tripropylene glycol methyl ether, propandiol butyl ether, propylene glycol phenylate, dioctyl phthalate diisobutyl ester, OE300
Or it is a variety of；
The defoaming agent is one of CF698, Tego810, Tego902W, BYK025, BYK028 or a variety of；
The substrate wetting agents be Coatosil1211, LCN407, Tego Wet KL 245, Tego Wet 270,
1065, one of D-504, BYK-346 or a variety of；
The dispersing agent is one of Tego715W, Tego740W, BYK192, BYK190, SN5040 or a variety of；
The waterborne wax emulsion is one of ML190, D-816, E-360；
The grinding auxiliary agent is one of 1007,1097A, SAK-ZS-PLB；
The filler is one of R706, R996,902+, 1000 mesh coarse whitings, 1250 mesh talcum powder or a variety of；
The pH adjusting agent is one of AMP-95, CH27, BS-198 or a variety of；
The preservative is one of CI-15HS, LX300,551S, Rocima342 or a variety of；
The thickener is one of RM-8W, PUR60, PUR69, RM-2020, XS71, Rheolate299 or a variety of.
Further, the waterborne curing agent be Aquolin 268, XP 2655, it is a kind of or more in 3592T, OS-9018
Kind.
Further, the wet-film thickness of the double-component aqueous wooden ware sealing primer coating is 100-150 μm, described double groups
The wet-film thickness of part aqueous wooden ware polishing primer coating is 100-150 μm, the wet film of the double-component aqueous lacquer as woodenware finish coating
With a thickness of 100-200 μm.
Double-component aqueous wooden ware sealing primer coating in woodenware coating structure of the present invention is that a kind of pair of wood substrate has
High osmosis, strong adhesive force is easy to polish, there is the environment-friendly double-component aqueous wooden ware of high closeness to seal grease, tannic acid etc.
Priming paint is closed, the upper infiltration of pigment in red oak, tannic acid can be prevented well, there is excellent comprehensive performance；Double-component aqueous wood
Device polishing primer coating has the characteristics that fillibility is good, adhesive force is strong, grinability is excellent, ties because its two-component system densification is crosslinked
Structure makes it also have certain barrier and sealing process to pigment, the tannic acid of bottom exudation；Double-component aqueous lacquer as woodenware finish coating
With good smoothness, flatness, resistance to marring, hardness of paint film and excellent resistance to soiling, two-component system densification crosslinking
Structure realizes the strong sealing process of third layer.Double-component aqueous woodenware coating structure of the invention makes red oak have surface effect
Excellent, non-discolouring advantage.
The invention has the following advantages:
The double-component aqueous woodenware coating structure of anti-bleeding red oak provided by the invention, including seal coat coating, polishing
Primer coating, topcoat, every layer includes the acrylic acid dispersion containing OH functional group and containing the aqueous solid of NCO functional group
The two-component of agent, two-component system densification cross-linked structure there is barrier and closing to make pigment, the tannic acid of red oak substrate
With, solve the problems, such as on the tannic acid in red oak seep caused by paint vehicle film discoloration.Seal coat coating and polishing priming paint
Coating has the characteristics that adhesive force is strong, easy to polish, and topcoat has good smoothness, flatness, resistance to marring, paint film hard
Degree and excellent resistance to soiling, make coating structure of the invention have the advantages that surface effect is excellent, adhesion property is strong.
Detailed description of the invention
Fig. 1 is the structure chart of the anti-double-component aqueous woodenware coating structure of bleeding red oak of the present invention.
In figure: the double-component aqueous wooden ware sealing primer coating of 1-；The double-component aqueous woodenware polishing primer coating of 2-；Bis- groups of 3-
Part aqueous wooden ware topcoat.
Specific embodiment
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Raw material in the embodiment of the present invention is that market can obtain product, in which:
The preferred AC31 of water-based emulsion (Opel enlightening), A2651 (Bayer), A 2470 (Bayer), XP-2592 (Bayer), 2042
(ten thousand China), 6516 (Niu Peisi), STW168 (Hua Yi), AC2598 (Opel enlightening), 938T (BASF), ENCOR2171 (A Ke
Ma), 6810 (Niu Peisi), XK-102 (Royal DSM), WE-6173 (rich sea fine chemistry industry), XK-14 (Royal DSM), R2180 (Supreme Being
Si Man), E-129 (Royal DSM), 2008 (monkey sage chemical industry)；
The preferred TEXANOL of coalescing agent (- 1,3 pentanediol mono isobutyrate of 2,2,4- trimethyl), DPNB (dipropylene glycol fourth
Ether), propylene glycol, DPM (dipropylene glycol methyl ether), TPM (tripropylene glycol methyl ether), PNB (propandiol butyl ether), PPH value (propylene glycol phenyl
Ether), DIB (dioctyl phthalate diisobutyl ester), one of OE300 (Yi Shiman) or a variety of；
The preferred CF698 of defoaming agent (Blackburn), Tego810 (Digao), Tego902W (Digao), BYK025 (Bi Kehua
Learn), BYK028 (Bi Ke chemistry)；
The preferred Coatosil1211 of substrate wetting agents (step figure), LCN407 (Clariant), TegoWet KL 245 (Digao),
Tego Wet 270 (Digao), 1065 (CHT), D-504 (Silcona), BYK-346 (Bi Ke chemistry)；
The preferred Tego715W of dispersing agent (Digao), Tego740W (Digao), BYK192 (Bi Ke), BYK190 (Bi Ke),
SN5040 (Nuo Puke)；
The preferred ML190 of waterborne wax emulsion (Mai Kemen), D-816 (Weng Kaier), E-360 (Weng Kaier)；
Grinding auxiliary agent preferably 1007 (BASF), 1097A (BASF), SAK-ZS-PLB (SUNACE)；
The preferred R706 of filler (Du Pont), R996 (imperial boa), 902+ (Du Pont), 1000 mesh coarse whitings, 1250 mesh talcum powder；
The preferred AMP-95 of pH adjusting agent (Tao Shi), CH27 (attaining product in Shanghai), BS-198 (Wa Ke)；
The preferred CI-15HS of preservative (Clariant), LX300 (Tao Shi), 551S (Tao Shi), Rocima342 (Tao Shi)；
The preferred RM-8W of thickener (Tao Shi), PUR60 (bright icepro chemical industry), PUR69 (bright icepro chemical industry), RM-2020 (Tao Shi),
XS71 (Gao Tai), Rheolate299 (hamming this)；
The preferred Aquolin 268 (ten thousand China) of waterborne curing agent, XP 2655 (Bayer), 3592T (connection is solid), OS-9018 (hat
Will).
A kind of double-component aqueous woodenware coating structure of anti-bleeding red oak, forming method are as follows:
(1) base material treatment
Using 320 or 400 mesh sand paper, along the grain direction integrally polishes flat, removal substrate surface burr, spot, glue etc.
Impurity.With surface defects such as aqueous putty repairing hole for nailing, place of colliding with, worm channels.Equally with 320 or 400 after poly-putty base parches
Mesh sand paper polishing repairing edge is to flat and smooth.It is required that substrate moisture rate is not higher than 12%.With banister brush or clean towel will beat
Mill dust cleans up.
(2) double-component aqueous wooden ware sealing primer coating is covered with paint, lacquer, colour wash, etc.
The effect that double-component aqueous wooden ware sealing primer coating primarily serves pigment in closing red oak, seeps on tannic acid.
Wet film is sprayed with 71 type spray gun even application, one and half cross in processing cleaning, smooth red oak substrate surface
Film thickness 100-150um, with 400 mesh sand paper, along the grain direction integrally gently polishes flat after drying 24 hours, with banister brush or does
Net towel cleans up polishing dust.
(3) double-component aqueous woodenware polishing primer coating is covered with paint, lacquer, colour wash, etc.
Double-component aqueous woodenware polishing primer coating primarily serves the work for improving paint film richness, fillibility and grinability
With.
On the seal coat after polishing flat, cleaning, with 71 type spray gun even application, one and half cross, wet film film is sprayed
Thick 100-150um after integrally being polished flat after 24 hours dry with 600 mesh sand paper, will be polished grey with banister brush or clean towel
Dirt cleans up.Again, with 71 type spray gun even application, one and half cross, wet film film thickness 100-150um is sprayed, it is 24 hours dry
After integrally being polished flat with 800 mesh sand paper afterwards, polishing dust is cleaned up with banister brush or clean towel.
(4) double-component aqueous lacquer as woodenware finish coating is covered with paint, lacquer, colour wash, etc.
Double-component aqueous lacquer as woodenware finish coating primarily serves protections and the decorative timbers such as scratch resistance, strong resistant, low permeability rate
Effect.
With 71 type spray gun even application two or two and half crosses, wet film film thickness 100-200um, air drying 36- are sprayed
Encapsulation can be packaged after 48 hours.
Bulk coat performance detection
It is hard with water-borne wood coating paint film property measuring method detection coating according to GB/T23999-2009 indoor decorating
Degree, adhesive force, resistance to soiling, yellowing resistance.
Coating water penetration is detected according to JG/T 210-2007 primer for interior and exterior wall water penetration measuring method.
Resistance to bleed energy is assessed with ocular estimate: being mark with glass plate spraying two-component polishing priming paint, two-component lacquer as woodenware finish
Standard does not spray seal coat part yellow jacket plank as comparison template, coats seal coat sample by exchanging different angle range estimation
Plate paint film form and aspect difference.
Embodiment 1
(1) double-component aqueous wooden ware sealing priming paint, weighs the following raw material by weight: aqueous acrylic emulsion AC2598
75 parts, 1 part of coalescing agent DPM, 3.5 parts of coalescing agent DPNB, 0.3 part of defoaming agent Tego810, substrate wetting agents
0.4 part of Coatosil1211, it 0.1 part of pH adjusting agent AMP-95,0.2 part of preservative CI-15HS, 1 part of thickener XS71, goes
One 18.5 parts of ionized water, 268 15 parts of waterborne curing agent Aquolin, 2 20 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Preservative, thickener, deionized water one are added sequentially in aqueous acrylic emulsion, and after being uniformly dispersed, host agent completes；It applies
Waterborne curing agent and deionized water two is added before dress construction, after stirring evenly no particle, filtering uses in 3 hours.
(2) double-component aqueous woodenware polishing priming paint, weighs the following raw material: aqueous acrylic emulsion XK-102 by weight
40 parts, 1 part of coalescing agent DPM, 3 parts of coalescing agent DPNB, 0.3 part of defoaming agent CF698, substrate wetting agents D-504 0.4
Part, 1 part of dispersing agent Tego715W, 13 parts of filler R706,10 parts of 1000 mesh coarse whiting of filler, is filled out at AMP-950.1 parts of pH adjusting agent
Expect 16 parts of 1250 mesh talcum powder, 2 parts of grinding auxiliary agent 1097A, 0.2 part of preservative CI-15HS, thickener Rheolate299
0.2 part, 0.4 part of thickener XS71, one 12.4 parts of deionized water, 268 5 parts of waterborne curing agent Aquolin, deionized water two
15 parts.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Dispersing agent, filler, grinding auxiliary agent, preservative, thickener, deionized water one are added sequentially in aqueous acrylic emulsion, dispersion
After uniformly, host agent completes；Waterborne curing agent and deionized water two, after stirring evenly no particle, mistake are added before coating decoration
Filter uses in 3 hours.
(3) double-component aqueous lacquer as woodenware finish, weighs the following raw material by weight: 45 parts of water-based emulsion A2651, aqueous cream
13 parts of liquid R2180,2 parts of coalescing agent DPNB, 0.3 part of defoaming agent CF698,0.3 part of defoaming agent Tego902W, substrate wetting
0.4 part of agent D-504,0.1 part of pH adjusting agent CH27,0.5 part of dispersing agent Tego715W, 20 parts of filler R706, water-borne wax cream
3 parts of liquid D-816,0.1 part of preservative LX300,0.1 part of preservative 551S, 0.2 part of thickener Rheolate299, thickener
0.7 part of XS71, one 14.3 parts of deionized water, 2,655 12 parts of waterborne curing agent XP, 2 25 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Dispersing agent, filler, waterborne wax emulsion, preservative, thickener, deionized water one are added sequentially in water-based emulsion, are uniformly dispersed
Afterwards, host agent completes；Waterborne curing agent and deionized water two are added before coating decoration, after stirring evenly no particle, filtering, 3
It is used in hour.
Bulk coat performance test results are as follows:
Form and aspect difference: not spraying seal coat yellow jacket plank and on-gauge plate form and aspect has more apparent difference, slight yellowing；This hair
Bright embodiment template and on-gauge plate form and aspect no significant difference.
Hardness: H
Adhesive force: 0 grade
Resistance to soiling: without exception
Yellowing resistance: Δ E=1
Water penetration: water penetration=0.1mL
Embodiment 2
(1) double-component aqueous wooden ware sealing priming paint, weighs the following raw material by weight: aqueous acrylic emulsion AC31 80
Part, 1 part of coalescing agent DPM, 4 parts of coalescing agent DPNB, 0.3 part of defoaming agent BYK025,1,065 0.3 parts of substrate wetting agents,
0.1 part of pH adjusting agent AMP-95,0.2 part of preservative CI-15HS, 1 part of thickener RM-2020, one 13.1 parts of deionized water,
13 parts of waterborne curing agent OS-9018,2 20 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Preservative, thickener, deionized water one are added sequentially in aqueous acrylic emulsion, and after being uniformly dispersed, host agent completes；It applies
Waterborne curing agent and deionized water two is added before dress construction, after stirring evenly no particle, filtering uses in 3 hours.
(2) double-component aqueous woodenware polishing priming paint, weighs the following raw material: aqueous acrylic emulsion STW168 by weight
45 parts, 1 part of coalescing agent DPM, 3 parts of coalescing agent DPNB, 0.3 part of defoaming agent Tego810, substrate wetting agents Tego Wet
270 0.3 parts, 0.1 part of pH adjusting agent BS-198,1 part of dispersant B YK192,13 parts of filler R706,1000 mesh coarse whiting of filler
10 parts, 16 parts of 1250 mesh talcum powder of filler, 1,007 2 parts of grinding auxiliary agent, 0.2 part of preservative CI-15HS, thickener
0.2 part of Rheolate299,0.5 part of thickener XS71, one 7.5 parts of deionized water, waterborne curing agent Aquolin 268 10
Part, 2 15 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Dispersing agent, filler, grinding auxiliary agent, preservative, thickener, deionized water one are added sequentially in aqueous acrylic emulsion, dispersion
After uniformly, host agent completes；Waterborne curing agent and deionized water two, after stirring evenly no particle, mistake are added before coating decoration
Filter uses in 3 hours.
(3) double-component aqueous lacquer as woodenware finish, weighs the following raw material by weight: 2,008 60 parts of water-based emulsion, coalescing agent
1 part of DPM, 2 parts of coalescing agent DPNB, 0.3 part of defoaming agent CF698,0.3 part of defoaming agent Tego902W, substrate wetting agents D-
504 0.4 parts, 0.1 part of pH adjusting agent CH27,0.5 part of dispersant B YK192,902+20 parts of filler, waterborne wax emulsion ML190
3 parts, 0.1 part of preservative LX300,0.1 part of preservative 551S, 0.2 part of thickener Rheolate299, thickener RM-2020
0.6 part, one 11.4 parts of deionized water, 2,655 10 parts of waterborne curing agent XP, 2 25 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Dispersing agent, filler, waterborne wax emulsion, preservative, thickener, deionized water one are added sequentially in water-based emulsion, are uniformly dispersed
Afterwards, host agent completes；Waterborne curing agent and deionized water two are added before coating decoration, after stirring evenly no particle, filtering, 3
It is used in hour.
Bulk coat performance test results are as follows:
Form and aspect difference: not spraying seal coat yellow jacket plank and on-gauge plate form and aspect has more apparent difference, slight yellowing；This hair
Bright embodiment template and on-gauge plate form and aspect no significant difference.
Hardness: H
Adhesive force: 0 grade
Resistance to soiling: without exception
Yellowing resistance: Δ E=1
Water penetration: water penetration=0.1mL
Embodiment 3
(1) double-component aqueous wooden ware sealing priming paint, weighs the following raw material by weight: aqueous acrylic emulsion A2651 85
Part, 2 parts of coalescing agent DPNB, 0.2 part of defoaming agent Tego810,0.2 part of defoaming agent Tego902W, substrate wetting agents Tego
245 0.5 parts of Wet KL, 0.1 part of pH adjusting agent AMP-95,0.2 part of preservative CI-15HS, thickener RM-2020 0.8
Part, one 11 parts of deionized water, 268 15 parts of waterborne curing agent Aquolin, 2 20 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Preservative, thickener, deionized water one are added sequentially in aqueous acrylic emulsion, and after being uniformly dispersed, host agent completes；It applies
Waterborne curing agent and deionized water two is added before dress construction, after stirring evenly no particle, filtering uses in 3 hours.
(2) double-component aqueous woodenware polishing priming paint, weighs the following raw material: aqueous acrylic emulsion by weight
50 parts of ENCOR2171,2 parts of coalescing agent DPM, OE3001 parts of coalescing agent, 0.4 part of defoaming agent CF698, substrate wetting agents
0.2 part of LCN407, it 1,065 0.4 parts of substrate wetting agents, 0.1 part of pH adjusting agent AMP-95,1 part of dispersing agent Tego715W, fills out
Expect 14 parts of R996,8 parts of 1000 mesh coarse whiting of filler, 12 parts of 1250 mesh talcum powder of filler, 2 parts of grinding auxiliary agent 1097A, preservative
It is 0.2 part of CI-15HS, 0.2 part of thickener RM-8W, 0.4 part of thickener RM-2020, one 8.1 parts of deionized water, aqueous solidified
268 5 parts of agent Aquolin, 2 15 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Dispersing agent, filler, grinding auxiliary agent, preservative, thickener, deionized water one are added sequentially in aqueous acrylic emulsion, dispersion
After uniformly, host agent completes；Waterborne curing agent and deionized water two, after stirring evenly no particle, mistake are added before coating decoration
Filter uses in 3 hours.
(3) double-component aqueous lacquer as woodenware finish, weighs the following raw material by weight: 2,042 42 parts of water-based emulsion, water-based emulsion
15 parts of E-129,2 parts of coalescing agent DPNB, 0.3 part of defoaming agent CF698,0.3 part of defoaming agent BYK025, substrate wetting agents D-
504 0.4 parts, 0.1 part of pH adjusting agent CH27,0.5 part of dispersant B YK192,902+20 parts of filler, waterborne wax emulsion E-360
2 parts, 0.1 part of preservative LX300,0.1 part of preservative 551S, 0.2 part of thickener RM-8W, 0.7 part of thickener XS71, go
One 16.3 parts of ionized water, 2,655 15 parts of waterborne curing agent XP, 2 25 parts of deionized water.
At medium rate of dispersion 500-1000rpm, by coalescing agent, defoaming agent, substrate wetting agents, pH adjusting agent,
Dispersing agent, filler, waterborne wax emulsion, preservative, thickener, deionized water one are added sequentially in water-based emulsion, are uniformly dispersed
Afterwards, host agent completes；Waterborne curing agent and deionized water two are added before coating decoration, after stirring evenly no particle, filtering, 3
It is used in hour.
Bulk coat performance test results are as follows:
Form and aspect difference: not spraying seal coat yellow jacket plank and on-gauge plate form and aspect has more apparent difference, slight yellowing；This hair
Bright embodiment template and on-gauge plate form and aspect no significant difference.
Hardness: H
Adhesive force: 0 grade
Resistance to soiling: without exception
Yellowing resistance: Δ E=1
Water penetration: water penetration=0.1mL
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (4)
1. a kind of double-component aqueous woodenware coating structure of anti-bleeding red oak, which is characterized in that the coating structure is in red oak
Double-component aqueous wooden ware sealing primer coating, double-component aqueous woodenware polishing primer coating and two-component are followed successively by substrate surface
Aqueous wooden ware topcoat；
Double-component aqueous wooden ware sealing priming paint, double-component aqueous woodenware polishing priming paint, double-component aqueous lacquer as woodenware finish include master
Agent, waterborne curing agent and water；
The host agent of the double-component aqueous wooden ware sealing priming paint is by including that the raw material of following parts by weight forms: water-based emulsion 75-85
Part, 2-5 parts of coalescing agent, 0.1 part of pH adjusting agent, 0.3-0.5 parts of substrate wetting agents, 0.3-0.4 parts of defoaming agent, preservative 0.2
Part, 0.8-1 parts of thickener, 11-18.5 parts of deionized water；It is host agent in the double-component aqueous wooden ware sealing priming paint, aqueous solidified
The weight ratio of agent and water is 100:13-15:20；
The host agent of the double-component aqueous woodenware polishing priming paint is by including that the raw material of following parts by weight forms: water-based emulsion 40-50
Part, 3-4 parts of coalescing agent, 0.1 part of pH adjusting agent, 0.3-0.6 parts of substrate wetting agents, 0.3-0.4 parts of defoaming agent, 1 part of dispersing agent,
34-39 parts of filler, 2 parts of grinding auxiliary agent, 0.2 part of preservative, 0.6-0.7 parts of thickener, 8.1-12.4 parts of deionized water；It is described double
The weight ratio of host agent, waterborne curing agent and water is 100:5-10:15 in component aqueous woodenware polishing priming paint；
The host agent of the double-component aqueous lacquer as woodenware finish is by including that the raw material of following parts by weight forms: 57-60 parts of water-based emulsion, at
2-3 parts of film auxiliary agent, 0.1 part of pH adjusting agent, 0.4 part of substrate wetting agents, 0.6 part of defoaming agent, 0.5 part of dispersing agent, 20 parts of filler, water
2-3 parts of wax emulsion, 0.2 part of preservative, 0.8-0.9 parts of thickener, 11.4-16.3 parts of deionized water of property；It is described double-component aqueous
The weight ratio of host agent, waterborne curing agent and water is 100:10-15:25 in lacquer as woodenware finish.
2. the double-component aqueous woodenware coating structure of anti-bleeding red oak according to claim 1, which is characterized in that described
Water-based emulsion be AC31, A2651, A2470, XP-2592,2042,6516, STW168, AC2598,938T, ENCOR2171,
6810, one of XK-102, WE-6173, XK-14, R2180, E-129,2008 or a variety of；
The coalescing agent is -1,3 pentanediol mono isobutyrate of 2,2,4- trimethyl, dipropylene, propylene glycol, dipropyl
One of glycol methyl ether, tripropylene glycol methyl ether, propandiol butyl ether, propylene glycol phenylate, dioctyl phthalate diisobutyl ester, OE300 or more
Kind；
The defoaming agent is one of CF698, Tego810, Tego902W, BYK025, BYK028 or a variety of；
The substrate wetting agents are Coatosil1211, LCN407, Tego Wet KL 245, Tego Wet 270,1065, D-
504, one of BYK-346 or a variety of；
The dispersing agent is one of Tego715W, Tego740W, BYK192, BYK190, SN5040 or a variety of；
The waterborne wax emulsion is one of ML190, D-816, E-360；
The grinding auxiliary agent is one of 1007,1097A, SAK-ZS-PLB；
The filler is one of R706, R996,902+, 1000 mesh coarse whitings, 1250 mesh talcum powder or a variety of；
The pH adjusting agent is one of AMP-95, CH27, BS-198 or a variety of；
The preservative is one of CI-15HS, LX300,551S, Rocima342 or a variety of；
The thickener is one of RM-8W, PUR60, PUR69, RM-2020, XS71, Rheolate299 or a variety of.
3. the double-component aqueous woodenware coating structure of anti-bleeding red oak according to claim 1, which is characterized in that the water
Property curing agent be Aquolin 268, XP 2655, it is one or more in 3592T, OS-9018.
4. the double-component aqueous woodenware coating structure of anti-bleeding red oak according to claim 1, which is characterized in that described double
The wet-film thickness of component aqueous wooden ware sealing primer coating is 100-150 μm, the double-component aqueous woodenware polishing primer coating
Wet-film thickness be 100-150 μm, the wet-film thickness of the double-component aqueous lacquer as woodenware finish coating is 100-200 μm.