CN109111192A - A kind of Cement fibre foamed board - Google Patents
A kind of Cement fibre foamed board Download PDFInfo
- Publication number
- CN109111192A CN109111192A CN201811120460.2A CN201811120460A CN109111192A CN 109111192 A CN109111192 A CN 109111192A CN 201811120460 A CN201811120460 A CN 201811120460A CN 109111192 A CN109111192 A CN 109111192A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- water
- fibre
- stalk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of Cement fibre foamed boards, it is characterised in that including following parts by weight of component: 50-60 parts of stalk fibre, 20-25 parts of silicon-aluminum sol, 14-18 parts of binder, 10-12 parts of propylparaben, 6-10 parts of hydrotalcite, 12-15 parts of barium silicate, 10-14 parts of crushed crude pearlite, 30-40 parts of cement, 0.2-0.3 parts of water-retaining agent, 0.3-0.5 parts of waterproofing agent, 4-6 parts of flocculant, Methane Carboxylic Acid 10-12 parts poly-, 1.5-2 parts of calcium stearate, 0.6-1 parts of lauryl sodium sulfate, 30-40 parts of water.The present invention is using stalk fibre made of agricultural waste material stalk as raw material, and blended cement foams, and Mold Making is manufactured at low cost at Cement fibre foamed board, product energy conservation and environmental protection；And can fire-proof and thermal-insulation, meet building heat preservation demand；Product lightweight facilitates installation.
Description
Technical field
The present invention relates to integrated wall plate technical field more particularly to a kind of Cement fibre foamed boards.
Background technique
Fiberboard, which refers to be interweaved lignocellulose fiber, to be formed and utilizes wood-based plate made of its intrinsic glueability.It is fine
Dimension plate has many advantages, such as that uniform in material, intensity difference is not small, easy to crack in length and breadth, widely used.
Existing fiberboard is all made of bamboo fibre and wood-fibred is made, and the material utilized is that timber and bamboo wood produce
Raw, with social development, the supply of the great attention of Environmental, timber and bamboo wood is persistently reduced, so that fiberboard
Cost cannot reduce.
Foamed cement is using cement as major gelled material, by cement slurry and the foam made of chemical foaming technology
The light porous material being mixed.The unique architectural characteristic of foamed cement assigns its excellent thermal property.With traditional architecture
Material is compared, and foamed cement has many advantages, such as lightweight, fire prevention, heat-insulated.
Existing building fiberboard generally uses plastics addition bamboo and woods fiber to be processed, and material weight is big, and cannot be real
The effect of existing fire-proof and thermal-insulation is needed to carry out multiple working procedure using bamboo and wood materials to finish repeatedly, be produced using bamboo and woods fiber
It is at high cost.
Summary of the invention
Present invention aim to address above-mentioned deficiencies, provide a kind of Cement fibre foamed board.
A kind of Cement fibre foamed board provided by the invention, it is characterised in that including following parts by weight of component: stalk fibre
50-60 parts, 20-25 parts of silicon-aluminum sol, 14-18 parts of binder, 10-12 parts of propylparaben, 6-10 parts of hydrotalcite, silicon
Sour barium 12-15 parts, 10-14 parts of crushed crude pearlite, 30-40 parts of cement, 0.2-0.3 parts of water-retaining agent, 0.3-0.5 parts of waterproofing agent, flocculation
4-6 parts of agent, Methane Carboxylic Acid 10-12 parts poly-, 1.5-2 parts of calcium stearate, 0.6-1 parts of lauryl sodium sulfate, 30-40 parts of water.
Further, a kind of Cement fibre foamed board, it is characterised in that including following parts by weight of component: stalk fibre 52
Part, 20 parts of silicon-aluminum sol, 18 parts of binder, 10 parts of propylparaben, 8 parts of hydrotalcite, 12 parts of barium silicate, crushed crude pearlite
10 parts, 35 parts of cement, 0.2 part of water-retaining agent, 0.5 part of waterproofing agent, 6 parts of flocculant, 12 parts of poly- Methane Carboxylic Acid, 2 parts of calcium stearate, ten
1 part of sodium dialkyl sulfate, 40 parts of water.
Further, a kind of production method of Cement fibre foamed board, as follows:
Step 1, lauryl sodium sulfate is added according to the ratio with water and is mixed, mixing speed is 120-140 revs/min
Clock stirs 10 minutes；
Step 2, by hydrotalcite, barium silicate, crushed crude pearlite, cement, water-retaining agent, waterproofing agent, flocculant, poly- Methane Carboxylic Acid, tristearin
Sour calcium is added in the mixture that step 1 obtains according to the ratio and stirs, and mixing speed is 80-100 revs/min, stirs 5 minutes；
Step 3, by stalk fibre, silicon-aluminum sol, binder, propylparaben be added that step 2 obtains according to the ratio it is mixed
It closes and is stirred in object, mixing speed is 80-100 revs/min, is stirred 5 minutes；
Step 4, mixture step 3 obtained is poured into plate forming mold, pours 80% that fluence is rated weight, molding 3
After minute, then it is poured the mixture progress coagulation forming of residue 20%；Demoulding finishing obtains Cement fibre foaming after maintenance 24 hours
Plate.
A kind of Cement fibre foamed board provided by the invention, using stalk fibre made of agricultural waste material stalk as
Raw material, and blended cement foams, Mold Making is manufactured at low cost at Cement fibre foamed board, product energy conservation and environmental protection；And
Can fire-proof and thermal-insulation, meet building heat preservation demand；Product lightweight facilitates installation.
Specific embodiment
Below by embodiment to further instruction of the present invention, the embodiment of the present invention is with technical solution of the present invention
Premised under implemented, the detailed implementation method and specific operation process are given, but protection scope of the present invention is unlimited
In following embodiments:
Embodiment 1:
Step 1,1 part of lauryl sodium sulfate, 40 parts of water are added according to the ratio and is mixed, mixing speed 120-140
Rev/min, it stirs 10 minutes；
Step 2, by 8 parts of hydrotalcite, 12 parts of barium silicate, 10 parts of crushed crude pearlite, 35 parts of cement, 0.2 part of water-retaining agent, waterproofing agent 0.5
Part, 6 parts of flocculant, 12 parts of poly- Methane Carboxylic Acid, 2 parts of calcium stearate are added in the mixture that step 1 obtains stir according to the ratio, stirring
Speed is 80-100 revs/min, is stirred 5 minutes；
Step 3,52 parts of stalk fibre, 20 parts of silicon-aluminum sol, 18 parts of binder, 10 parts of propylparaben are added according to the ratio
Enter and stirred in the mixture that step 2 obtains, mixing speed is 80-100 revs/min, is stirred 5 minutes；
Step 4, mixture step 3 obtained is poured into plate forming mold, pours 80% that fluence is rated weight, molding 3
After minute, then it is poured the mixture progress coagulation forming of residue 20%；Demoulding finishing obtains Cement fibre foaming after maintenance 24 hours
Plate.
Embodiment 2:
Step 1,0.6-1 parts of lauryl sodium sulfate, 30-40 parts of water are added according to the ratio and is mixed, mixing speed is
It 120-140 revs/min, stirs 10 minutes；
Step 2, by 6-10 parts of hydrotalcite, 12-15 parts of barium silicate, 10-14 parts of crushed crude pearlite, 30-40 parts of cement, water-retaining agent 0.2-
0.3 part, 0.3-0.5 parts of waterproofing agent, 4-6 parts of flocculant, it is Methane Carboxylic Acid 10-12 parts poly-, 1.5-2 parts of calcium stearate be added according to the ratio
It is stirred in the mixture that step 1 obtains, mixing speed is 80-100 revs/min, is stirred 5 minutes；
Step 3, by 50-60 parts of stalk fibre, 20-25 parts of silicon-aluminum sol, 14-18 parts of binder, propylparaben 10-
It is stirred in 12 parts of mixtures that addition step 2 obtains according to the ratio, mixing speed is 80-100 revs/min, is stirred 5 minutes；
Step 4, mixture step 3 obtained is poured into plate forming mold, pours 80% that fluence is rated weight, molding 3
After minute, then it is poured the mixture progress coagulation forming of residue 20%；Demoulding finishing obtains Cement fibre foaming after maintenance 24 hours
Plate.
Embodiment 3:
Step 1,0.6-1 parts of lauryl sodium sulfate, 30-40 parts of water are added according to the ratio and is mixed, mixing speed is
It 120-140 revs/min, stirs 10 minutes；
Step 2, by 8 parts of hydrotalcite, 12 parts of barium silicate, 10 parts of crushed crude pearlite, 35 parts of cement, 0.2 part of water-retaining agent, waterproofing agent 0.5
Part, 6 parts of flocculant, 12 parts of poly- Methane Carboxylic Acid, 2 parts of calcium stearate are added in the mixture that step 1 obtains stir according to the ratio, stirring
Speed is 80-100 revs/min, is stirred 5 minutes；
Step 3, by 50-60 parts of stalk fibre, 20-25 parts of silicon-aluminum sol, 14-18 parts of binder, propylparaben 10-
It is stirred in 12 parts of mixtures that addition step 2 obtains according to the ratio, mixing speed is 80-100 revs/min, is stirred 5 minutes；
Step 4, mixture step 3 obtained is poured into plate forming mold, pours 80% that fluence is rated weight, molding 3
After minute, then it is poured the mixture progress coagulation forming of residue 20%；Demoulding finishing obtains Cement fibre foaming after maintenance 24 hours
Plate.
Claims (3)
1. a kind of Cement fibre foamed board, it is characterised in that including following parts by weight of component: 50-60 parts of stalk fibre, sial are molten
20-25 parts of glue, 14-18 parts of binder, 10-12 parts of propylparaben, 6-10 parts of hydrotalcite, 12-15 parts of barium silicate, treasure
10-14 parts of pearl rock powder, 30-40 parts of cement, 0.2-0.3 parts of water-retaining agent, 0.3-0.5 parts of waterproofing agent, 4-6 parts of flocculant, poly-vinegar acid
10-12 parts of acetic acid, 1.5-2 parts of calcium stearate, 0.6-1 parts of lauryl sodium sulfate, 30-40 parts of water.
2. a kind of Cement fibre foamed board as described in claim 1, it is characterised in that including following parts by weight of component: stalk is fine
Tie up 52 parts, 20 parts of silicon-aluminum sol, 18 parts of binder, 10 parts of propylparaben, 8 parts of hydrotalcite, 12 parts of barium silicate, pearl
10 parts of rock powder, 35 parts of cement, 0.2 part of water-retaining agent, 0.5 part of waterproofing agent, 6 parts of flocculant, 12 parts of poly- Methane Carboxylic Acid, calcium stearate 2
Part, 1 part of lauryl sodium sulfate, 40 parts of water.
3. a kind of production method of Cement fibre foamed board as described in claim 1, it is characterised in that as follows:
Step 1, lauryl sodium sulfate is added according to the ratio with water and is mixed, mixing speed is 120-140 revs/min
Clock stirs 10 minutes；
Step 2, by hydrotalcite, barium silicate, crushed crude pearlite, cement, water-retaining agent, waterproofing agent, flocculant, poly- Methane Carboxylic Acid, tristearin
Sour calcium is added in the mixture that step 1 obtains according to the ratio and stirs, and mixing speed is 80-100 revs/min, stirs 5 minutes；
Step 3, by stalk fibre, silicon-aluminum sol, binder, propylparaben be added that step 2 obtains according to the ratio it is mixed
It closes and is stirred in object, mixing speed is 80-100 revs/min, is stirred 5 minutes；
Step 4, mixture step 3 obtained is poured into plate forming mold, pours 80% that fluence is rated weight, molding 3
After minute, then it is poured the mixture progress coagulation forming of residue 20%；Demoulding finishing obtains Cement fibre foaming after maintenance 24 hours
Plate.