CN109097973A - A kind of dust-removal cloth-bag ferric trichloride-electret modification nonwoven cloth preparation method - Google Patents
A kind of dust-removal cloth-bag ferric trichloride-electret modification nonwoven cloth preparation method Download PDFInfo
- Publication number
- CN109097973A CN109097973A CN201810957796.8A CN201810957796A CN109097973A CN 109097973 A CN109097973 A CN 109097973A CN 201810957796 A CN201810957796 A CN 201810957796A CN 109097973 A CN109097973 A CN 109097973A
- Authority
- CN
- China
- Prior art keywords
- ferric trichloride
- electret
- woven fabrics
- dry
- dust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dust-removal cloth-bag ferric trichloride-electret modification nonwoven cloth preparation methods; dry polybutylene terephthalate (PBT) slice and flow ability modifying agent are blended in double screw extruder; after melt stream condensation; it is air-dried through air-dry machine, pelleter pelletizing, obtains modified polybutylene terephthalate (PBT) slice;Modified slice is squeezed out after heating melting through spinning nozzle in screw extruder, melt stream is drawn into fiber, and cooling and solidifying, autoadhesion acts on forming non-woven fabrics;Gained non-woven fabrics is immersed in after being reacted in the corrosive liquid that ferric trichloride is formed with aqueous sulfuric acid, it is dry, it impregnates in water at room temperature, re-dry, ferric trichloride modified non-woven fabrics is made;The ferric trichloride modified non-woven fabrics of gained is cut, is then placed under Xelminator and slowly moves, surface electrostatic is removed, after being heated, carries out corona charging, obtained dust-removal cloth-bag modification nonwoven cloth with electret equipment.
Description
Technical field
The invention belongs to dust-removal cloth-bag Material Fields, and in particular to a kind of dust-removal cloth-bag modified nothing of ferric trichloride-electret
The preparation method of woven fabric.
Background technique
Polybutylene terephthalate (PBT) is a kind of crystalline thermoplastic polyester, its fast, mechanical strength with crystallization rate
The features such as height, dimensionally stable, good electrical insulation capability, additionally has heat-resisting, acidproof, resistance to greasy dirt outstanding and resistant to chemical etching
Performance.The non-woven fabrics fiber of meltblown preparation is thin and soft, is a kind of ideal filtering material.The present invention is directed to by suitable stream
Dynamic modifying agent, which is added in slice, carries out blending and modifying, and fluidity of molten in melt-blown processing is substantially improved;And prepare a kind of aperture
Smaller, the higher modified melt spraying non-woven fabrics filter core of filtering accuracy, to there is good application prospect in terms of dust-removal cloth-bag.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of modified nothing of dust-removal cloth-bag ferric trichloride-electret is provided
The preparation method of woven fabric, the dust-removal cloth-bag modification nonwoven cloth made according to this method are excellent to the strainability of air.
The present invention is achieved by the following technical solutions:
A kind of dust-removal cloth-bag ferric trichloride-electret modification nonwoven cloth preparation method, which comprises the steps of:
(1) blending and modifying of polybutylene terephthalate (PBT) slice:
By 94-96 parts of dry polybutylene terephthalate (PBT) slices and 4-6 parts of flow ability modifying agents in double screw extruder
It is blended, after melt stream condensation, is air-dried through air-dry machine, pelleter pelletizing, obtain modified polybutylene terephthalate (PBT) slice;
Modified slice is squeezed out after heating melting through spinning nozzle in screw extruder, melt stream is drawn into fiber, cooling
Solidification, autoadhesion act on forming non-woven fabrics;
(2) preparation of ferric trichloride modified non-woven fabrics:
Gained non-woven fabrics in (1) is immersed in the corrosive liquid that ferric trichloride and aqueous sulfuric acid are formed, is reacted at 30-40 DEG C
After 3-5h, in 60-80 DEG C of dry 1-2h, 5-10h is impregnated in water at room temperature, then at 60-80 DEG C of dry 1-2h, tri-chlorination is made
Iron modification nonwoven cloth;
(3) method of electret modification nonwoven cloth:
The ferric trichloride modified non-woven fabrics of gained in (2) is cut, is then placed under Xelminator and slowly moves, remove table
Face electrostatic after being heated at 105-115 DEG C, carries out corona charging with electret equipment, and dust-removal cloth-bag is made and is modified
Non-woven fabrics.
Further, the drying that polybutylene terephthalate (PBT) is sliced in step (1): by polybutylene terephthalate
Ester slice dry 4-6h in 104-106 DEG C of vacuum drying oven, for use;
Flow ability modifying agent is flow ability modifying agent FM, and melt-spraying spinning temperature is 225-390 DEG C.
Further, the electret charging time is 20-30s, charging distance 1-5min, charging voltage 10- in step (3)
15kV。
The present invention has the advantage that compared with prior art
(1) it is blended to be granulated using twin-screw and is prepared for the modified slice of polybutylene terephthalate (PBT)-flow ability modifying agent, mixture
In system, a small amount of flow ability modifying agent can be used as crystallization nucleating agent and promote crystallization, and flow ability modifying agent is to polybutylene terephthalate
The improvement effect of the mobility of ester is obvious;The fibre diameter of modified melt-blown sample and aperture are smaller, and pore-size distribution is also relatively equal
It is even, and the breaking strength of non-woven fabrics is not reduced.
(2) using ferric trichloride come modification nonwoven cloth, fiber surface feature changes, and non-woven fabrics fiber surface occurs
Phenomenon of rupture, hydrophilic angle also decrease;Air-treatment effect is more satisfactory, can meet standard.
(3) electret processing can be good at solving the contradiction between filtration resistance and filter efficiency, so that filtering material has
There are a high efficiency, the more brilliant filter capacity of lower resistance, treated that charged meltblown web can effectively filter sky for electret
Submicron Particles in gas;The surface potential of nonwoven cloth filter material is higher after electret processing, then its filter effect promotion is got over
Greatly;
Non-woven fabrics is made dust removal and filtration cloth bag, surface all by singing, the process such as press polish, prevent two caused by fibre shedding
Secondary pollution;High temperature resistant index, filtering accuracy, Air permenbility are attained by standard.
Specific embodiment
Embodiment 1
A kind of dust-removal cloth-bag ferric trichloride-electret modification nonwoven cloth preparation method, which comprises the steps of:
(1) blending and modifying of polybutylene terephthalate (PBT) slice:
94 parts of dry polybutylene terephthalate (PBT) slices and 4 parts of flow ability modifying agents are blended in double screw extruder,
It after melt stream condensation, is air-dried through air-dry machine, pelleter pelletizing, obtains modified polybutylene terephthalate (PBT) slice;It will change
Property after slice squeezed out after heating melting through spinning nozzle in screw extruder, melt stream is drawn into fiber, cooling and solidifying,
Autoadhesion acts on forming non-woven fabrics;
(2) preparation of ferric trichloride modified non-woven fabrics:
Gained non-woven fabrics in (1) is immersed in the corrosive liquid that ferric trichloride and aqueous sulfuric acid are formed, is reacted at 30-40 DEG C
After 3h, in 60-80 DEG C of dry 1h, 5h is impregnated in water at room temperature, then at 60-80 DEG C of dry 1h, ferric trichloride modified nothing is made
Woven fabric;
(3) method of electret modification nonwoven cloth:
The ferric trichloride modified non-woven fabrics of gained in (2) is cut, is then placed under Xelminator and slowly moves, remove table
Face electrostatic after being heated at 105-115 DEG C, carries out corona charging with electret equipment, and dust-removal cloth-bag is made and is modified
Non-woven fabrics.
Further, the drying that polybutylene terephthalate (PBT) is sliced in step (1): by polybutylene terephthalate
Ester slice dry 4h in 104-106 DEG C of vacuum drying oven, for use;
Flow ability modifying agent is flow ability modifying agent FM, and melt-spraying spinning temperature is 225-390 DEG C.
Further, the electret charging time is 20s, charging distance 1min, charging voltage 10kV in step (3).
Embodiment 2
A kind of dust-removal cloth-bag ferric trichloride-electret modification nonwoven cloth preparation method, which comprises the steps of:
(1) blending and modifying of polybutylene terephthalate (PBT) slice:
96 parts of dry polybutylene terephthalate (PBT) slices and 6 parts of flow ability modifying agents are blended in double screw extruder,
It after melt stream condensation, is air-dried through air-dry machine, pelleter pelletizing, obtains modified polybutylene terephthalate (PBT) slice;It will change
Property after slice squeezed out after heating melting through spinning nozzle in screw extruder, melt stream is drawn into fiber, cooling and solidifying,
Autoadhesion acts on forming non-woven fabrics;
(2) preparation of ferric trichloride modified non-woven fabrics:
Gained non-woven fabrics in (1) is immersed in the corrosive liquid that ferric trichloride and aqueous sulfuric acid are formed, is reacted at 30-40 DEG C
After 5h, in 60-80 DEG C of dry 2h, 10h is impregnated in water at room temperature, then at 60-80 DEG C of dry 2h, ferric trichloride modified nothing is made
Woven fabric;
(3) method of electret modification nonwoven cloth:
The ferric trichloride modified non-woven fabrics of gained in (2) is cut, is then placed under Xelminator and slowly moves, remove table
Face electrostatic after being heated at 105-115 DEG C, carries out corona charging with electret equipment, and the dust-removal cloth-bag is made and uses
Non-woven fabrics.
Further, the drying that polybutylene terephthalate (PBT) is sliced in step (1): by polybutylene terephthalate
Ester slice dry 6h in 104-106 DEG C of vacuum drying oven, for use;
Flow ability modifying agent is flow ability modifying agent FM, and melt-spraying spinning temperature is 225-390 DEG C.
Further, the electret charging time is 30s, charging distance 5min, charging voltage 15kV in step (3).
The dust-removal cloth-bag modification nonwoven cloth made according to the method for the present invention is excellent to the strainability of air, and high temperature resistant refers to
Mark, filtering accuracy, Air permenbility are attained by standard.
Claims (3)
1. a kind of dust-removal cloth-bag ferric trichloride-electret modification nonwoven cloth preparation method, which is characterized in that including walking as follows
It is rapid:
(1) blending and modifying of polybutylene terephthalate (PBT) slice:
By 94-96 parts of dry polybutylene terephthalate (PBT) slices and 4-6 parts of flow ability modifying agents in double screw extruder
It is blended, after melt stream condensation, is air-dried through air-dry machine, pelleter pelletizing, obtain modified polybutylene terephthalate (PBT) slice;
Modified slice is squeezed out after heating melting through spinning nozzle in screw extruder, melt stream is drawn into fiber, cooling
Solidification, autoadhesion act on forming non-woven fabrics;
(2) preparation of ferric trichloride modified non-woven fabrics:
Gained non-woven fabrics in (1) is immersed in the corrosive liquid that ferric trichloride and aqueous sulfuric acid are formed, is reacted at 30-40 DEG C
After 3-5h, in 60-80 DEG C of dry 1-2h, 5-10h is impregnated in water at room temperature, then at 60-80 DEG C of dry 1-2h, tri-chlorination is made
Iron modification nonwoven cloth;
(3) method of electret modification nonwoven cloth:
The ferric trichloride modified non-woven fabrics of gained in (2) is cut, is then placed under Xelminator and slowly moves, remove table
Face electrostatic after being heated at 105-115 DEG C, carries out corona charging with electret equipment, and dust-removal cloth-bag is made and is modified
Non-woven fabrics.
2. a kind of dust-removal cloth-bag according to claim 1 ferric trichloride-electret modification nonwoven cloth preparation method, special
Sign is, the drying that polybutylene terephthalate (PBT) is sliced in step (1): polybutylene terephthalate (PBT) slice is existed
Dry 4-6h in 104-106 DEG C of vacuum drying oven, for use;
Flow ability modifying agent is flow ability modifying agent FM, and melt-spraying spinning temperature is 225-390 DEG C.
3. a kind of dust-removal cloth-bag according to claim 1 ferric trichloride-electret modification nonwoven cloth preparation method, special
Sign is that the electret charging time is 20-30s, charging distance 1-5min, charging voltage 10-15kV in step (3).