CN109096906A - A kind of high-performance terminal box special coating and preparation method thereof - Google Patents
A kind of high-performance terminal box special coating and preparation method thereof Download PDFInfo
- Publication number
- CN109096906A CN109096906A CN201811010837.9A CN201811010837A CN109096906A CN 109096906 A CN109096906 A CN 109096906A CN 201811010837 A CN201811010837 A CN 201811010837A CN 109096906 A CN109096906 A CN 109096906A
- Authority
- CN
- China
- Prior art keywords
- parts
- terminal box
- special coating
- performance terminal
- box special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of high-performance terminal box special coating and preparation method thereof, it is related to technical field of coatings, the high-performance terminal box special coating is prepared from the following raw materials: aqueous polyurethane emulsion, polyacrylate dispersion, styrene-acrylic emulsion, reinforcing fiber, cenosphere, alcohol ester 12, pigment, hexenyl bis-stearamides, higher aliphatic, inorganic filler, triethanolamine, Nacl, ethylene glycol, hexamethylol methyl-etherified melamine, silicone emulsion, Hinered phenols antioxidant, non-ion fluorin surfactant, waterproofing agent of organosilicon, anticorrosion and bactericidal agent and brominated flame retardant, the present invention acts synergistically by the mutual cooperation between each raw material and mutually, substantially increase the waterproof of coating, antisepsis and sterilization and crack resistence performance, the present invention not only has the advantages that anti-corrosion good water-proof effect, weatherability is also very excellent, good leveling property, and Not easily to fall off, life cycle is long, sprayable, can also brush, and has very excellent covering to microscopic checks.
Description
Technical field
The present invention relates to technical field of coatings, and in particular to a kind of high-performance terminal box special coating and preparation method thereof.
Background technique
Coating, in the entitled paint of Chinese tradition.So-called coating be coated in the body surface being protected or decorated, and
The continuous film of firm attachment can be formed with coated article, usually based on resin or oil or lotion, add or do not add face
Material, filler add corresponding additive, the thick liquid being formulated with organic solvent or water.
In terminal box field, people protect terminal box by the surface coating paint in terminal box, still, due to long-term
It is placed in outdoor, coating is easy to weather stain, and is easy to wear, existing coating weatherability (low temperature resistant, acid and alkali-resistance, it is resistance to
High temperature, UV resistant) it is poor, antisepsis and sterilization effect is poor, do not have some properties such as uvioresistant, fire-retardant, antistatic yet, and
Easy to fall off, removing；The coating that is largely using also has the shortcomings that life cycle is short and not scratch-resistant now, it is thus impossible to
Meet requirement of the people to high-performance coating.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of high-performance terminal box special coating and preparation method thereof,
So that the performance that coating not only has waterproof, uvioresistant, fire-retardant, antistatic etc. special, but also it is long to benefit from the service life, scratch-resistant.
In order to achieve the above object, the present invention is achieved by the following technical programs:
A kind of high-performance terminal box special coating, is prepared from the following raw materials in parts by weight:
40-60 parts of aqueous polyurethane emulsion, 20-30 parts of polyacrylate dispersion, 20-30 parts of styrene-acrylic emulsion, reinforcing fiber
6-12 parts, 5-8 parts of cenosphere, 12 0.5-1 parts of alcohol ester, 1-3 parts of pigment, 3-6 parts of hexenyl bis-stearamides, higher aliphatic
0.5-1 parts of alcohol, 10-20 parts of inorganic filler, 1-2 parts of triethanolamine, 2-3 parts of Nacl, 1-3 parts of ethylene glycol, hexamethylol methyl ether
Change melamine 0.1-0.4 parts, 3-5 parts of silicone emulsion, 3-5 parts of Hinered phenols antioxidant, non-ion fluorin surfactant 0.4-
0.6 part, 0.5-1 parts of waterproofing agent of organosilicon, 0.3-0.7 parts of anticorrosion and bactericidal agent, 2-4 parts of brominated flame retardant.
Preferably, the reinforcing fiber is glass fibre.
Preferably, the inorganic filler by titanium dioxide, talcum powder, calcium carbonate and barium sulfate according to etc. mass ratioes mixing and
At.
Preferably, the Hinered phenols antioxidant is by 2,6- three-level butyl -4- methylphenol and pentaerythritol ester according to matter
Amount is mixed than 1:1.
Preferably, the anticorrosion and bactericidal agent is mixed by di-2-ethylhexylphosphine oxide thiocyanates and benzothiazole -3- ketone according to mass ratio 2:1
It closes.
A kind of preparation method of above-mentioned high-performance terminal box special coating, comprising the following steps:
(1) each raw material of formula ratio is weighed, and inorganic filler is ground into fine powder, it is spare；
(2) by aqueous polyurethane emulsion, polyacrylate dispersion, styrene-acrylic emulsion, reinforcing fiber, cenosphere and moiety alcohol
Ester 12 is added in dispersion machine, and be uniformly dispersed 30-40min under 1100-1300r/min mixing speed；
(3) dispersing speed is improved to 2000-2400r/min, hexenyl bis-stearamides, advanced is added while stirring
Fatty alcohol, triethanolamine, Nacl, silicone emulsion and non-ion fluorin surfactant continue after being dispersed with stirring 2-3h, to dispersion
Remaining each raw material is added in machine, is stirred when high speed dispersion to grain fineness is less than 30 μm, then with the revolving speed of 800-1000r/min
1-2h to get.
The utility model has the advantages that
The present invention provides a kind of high-performance terminal box special coating and preparation method thereof, hexenyl is double stearic in the present invention
Amide stearmide is used in combination with higher aliphatic, can improve lubricated with coating and thermal stability；The present invention uses brominated flame retardant,
The flameproof effect of brominated flame retardant is good, and brominated flame retardant can also hinder the climing of high fire in addition to that can reduce a possibility that on fire
Prolong；Waterproofing agent of organosilicon can completely cut off extraneous water and air to play waterproof action, and it is not only waterproof but also can breathe freely；Add
Enter reinforcing fiber and the scratch-resistant performance of product can be improved in cenosphere, cenosphere can improve coating appearance, eliminate glass fibers
Exposing phenomenon is tieed up, cenosphere can also improve the mobile performance of coating, reduce the dosage of glass fibre, reduce cost.
Alcohol ester 12 of the present invention is used as coalescing agent, is easy to be absorbed by latex particle, can form excellent continuous film, separately
Outside, alcohol ester 12 can obviously reduce the minimum film formation temperature of coating, improve cohesiveness, weatherability, scrub resistance and the exhibition of coating
Color, alcohol ester 12 add in two times, and half is added in the grinding stage, facilitates the wetting and dispersing of pigments and fillers, letdown phase adds
Half helps to inhibit the generation of bubble.
The present invention acts synergistically by the mutual cooperation between each raw material and mutually, substantially increases waterproof, the anti-corrosion of coating
Bactericidal properties and crack resistence performance, increase the levelability and coating of coating, and the present invention not only has anti-corrosion good water-proof effect
Advantage, weatherability is also very excellent, good leveling property, and not easily to fall off, and life cycle is long, sprayable, can also brush, and splits to fine
It is sewed with very excellent covering.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.
Embodiment 1:
A kind of high-performance terminal box special coating, is prepared from the following raw materials in parts by weight:
It is 40 parts of aqueous polyurethane emulsion, 30 parts of polyacrylate dispersion, 20 parts of styrene-acrylic emulsion, 12 parts of glass fibre, hollow
5 parts of microballon, 12 parts of alcohol ester, 3 parts of pigment, 6 parts of hexenyl bis-stearamides, 0.5 part of higher aliphatic, 20 parts of inorganic filler,
1 part of triethanolamine, 1 part of ethylene glycol, 0.4 part of hexamethylol methyl-etherified melamine, 3 parts of silicone emulsion, is obstructed at 3 parts of Nacl
5 parts of phenolic antioxidant, 0.4 part of non-ion fluorin surfactant, 0.5 part of waterproofing agent of organosilicon, 0.7 part of anticorrosion and bactericidal agent, bromination
2 parts of fire retardant.
Wherein, inorganic filler by titanium dioxide, talcum powder, calcium carbonate and barium sulfate according to etc. mass ratioes mix；It is obstructed
Phenolic antioxidant is mixed by 2,6- three-level butyl -4- methylphenol and pentaerythritol ester according to mass ratio 1:1；Antisepsis and sterilization
Agent is mixed by di-2-ethylhexylphosphine oxide thiocyanates and benzothiazole -3- ketone according to mass ratio 2:1.
Embodiment 2:
A kind of high-performance terminal box special coating, is prepared from the following raw materials in parts by weight:
It is 60 parts of aqueous polyurethane emulsion, 20 parts of polyacrylate dispersion, 30 parts of styrene-acrylic emulsion, 6 parts of glass fibre, hollow micro-
8 parts of pearl, 12 parts of alcohol ester, 1 part of pigment, 3 parts of hexenyl bis-stearamides, 1 part of higher aliphatic, 10 parts of inorganic filler, three
2 parts of ethanol amine, 2 parts of Nacl, 3 parts of ethylene glycol, 0.1 part of hexamethylol methyl-etherified melamine, 3 parts of silicone emulsion, hindered phenol
3 parts of kind antioxidant, 0.6 part of non-ion fluorin surfactant, 1 part of waterproofing agent of organosilicon, 0.3 part of anticorrosion and bactericidal agent, brominated flame retardant
4 parts of agent.
Wherein, inorganic filler by titanium dioxide, talcum powder, calcium carbonate and barium sulfate according to etc. mass ratioes mix；It is obstructed
Phenolic antioxidant is mixed by 2,6- three-level butyl -4- methylphenol and pentaerythritol ester according to mass ratio 1:1；Antisepsis and sterilization
Agent is mixed by di-2-ethylhexylphosphine oxide thiocyanates and benzothiazole -3- ketone according to mass ratio 2:1.
Embodiment 3:
A kind of high-performance terminal box special coating, is prepared from the following raw materials in parts by weight:
It is 50 parts of aqueous polyurethane emulsion, 25 parts of polyacrylate dispersion, 25 parts of styrene-acrylic emulsion, 9 parts of glass fibre, hollow micro-
6.5 parts of pearl, 12 parts of alcohol ester, 2 parts of pigment, 4.5 parts of hexenyl bis-stearamides, 0.7 part of higher aliphatic, inorganic filler
15 parts, 1.5 parts of triethanolamine, 2.5 parts of Nacl, 2 parts of ethylene glycol, 0.3 part of hexamethylol methyl-etherified melamine, silicone emulsion
4 parts, 4 parts of Hinered phenols antioxidant, 0.5 part of non-ion fluorin surfactant, 0.8 part of waterproofing agent of organosilicon, anticorrosion and bactericidal agent 0.5
Part, 3 parts of brominated flame retardant.
Wherein, inorganic filler by titanium dioxide, talcum powder, calcium carbonate and barium sulfate according to etc. mass ratioes mix；It is obstructed
Phenolic antioxidant is mixed by 2,6- three-level butyl -4- methylphenol and pentaerythritol ester according to mass ratio 1:1；Antisepsis and sterilization
Agent is mixed by di-2-ethylhexylphosphine oxide thiocyanates and benzothiazole -3- ketone according to mass ratio 2:1.
Embodiment 4:
A kind of high-performance terminal box special coating, is prepared from the following raw materials in parts by weight:
It is 55 parts of aqueous polyurethane emulsion, 27 parts of polyacrylate dispersion, 26 parts of styrene-acrylic emulsion, 11 parts of glass fibre, hollow
7 parts of microballon, 12 parts of alcohol ester, 2.5 parts of pigment, 5 parts of hexenyl bis-stearamides, 0.9 part of higher aliphatic, inorganic filler
18 parts, 1.6 parts of triethanolamine, 2.8 parts of Nacl, 2.5 parts of ethylene glycol, 0.3 part of hexamethylol methyl-etherified melamine, emulsification silicon
Oily 4.5 parts, 4 parts of Hinered phenols antioxidant, 0.5 part of non-ion fluorin surfactant, 0.8 part of waterproofing agent of organosilicon, antisepsis and sterilization
0.4 part of agent, 3.5 parts of brominated flame retardant.
Wherein, inorganic filler by titanium dioxide, talcum powder, calcium carbonate and barium sulfate according to etc. mass ratioes mix；It is obstructed
Phenolic antioxidant is mixed by 2,6- three-level butyl -4- methylphenol and pentaerythritol ester according to mass ratio 1:1；Antisepsis and sterilization
Agent is mixed by di-2-ethylhexylphosphine oxide thiocyanates and benzothiazole -3- ketone according to mass ratio 2:1.
A kind of preparation method of high-performance terminal box special coating of above-described embodiment 1-4, comprising the following steps:
(1) each raw material of formula ratio is weighed, and inorganic filler is ground into fine powder, it is spare；
(2) by aqueous polyurethane emulsion, polyacrylate dispersion, styrene-acrylic emulsion, reinforcing fiber, cenosphere and moiety alcohol
Ester 12 is added in dispersion machine, and be uniformly dispersed 30-40min under 1100-1300r/min mixing speed；
(3) dispersing speed is improved to 2000-2400r/min, hexenyl bis-stearamides, advanced is added while stirring
Fatty alcohol, triethanolamine, Nacl, silicone emulsion and non-ion fluorin surfactant continue after being dispersed with stirring 2-3h, to dispersion
Remaining each raw material is added in machine, is stirred when high speed dispersion to grain fineness is less than 30 μm, then with the revolving speed of 800-1000r/min
1-2h to get.
Performance test: to by embodiment 1-4 coating obtained according to the method described above, according to the standard of GB/T21866-2008
It is tested for the property, test result is as follows:
To sum up, the embodiment of the present invention has the following beneficial effects: the coating as made from embodiment 1-4, as shown in Table 1, should
Coating surface drying time is short, and the ageing-resistant time is long, and has excellent water resistance, antibiotic property, weatherability and abrasion resistance.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (6)
1. a kind of high-performance terminal box special coating, which is characterized in that be prepared from the following raw materials in parts by weight: aqueous polyurethane
40-60 parts of lotion, 20-30 parts of polyacrylate dispersion, 20-30 parts of styrene-acrylic emulsion, 6-12 parts of reinforcing fiber, cenosphere 5-8
Part, 12 0.5-1 parts of alcohol ester, 1-3 parts of pigment, 3-6 parts of hexenyl bis-stearamides, 0.5-1 parts of higher aliphatic, inorganic filler
10-20 parts, 1-2 parts of triethanolamine, 2-3 parts of Nacl, 1-3 parts of ethylene glycol, hexamethylol methyl-etherified melamine 0.1-0.4
Part, 3-5 parts of silicone emulsion, 3-5 parts of Hinered phenols antioxidant, 0.4-0.6 parts of non-ion fluorin surfactant, waterproofing agent of organosilicon
0.5-1 parts, 0.3-0.7 parts of anticorrosion and bactericidal agent, 2-4 parts of brominated flame retardant.
2. high-performance terminal box special coating as described in claim 1, which is characterized in that the reinforcing fiber is glass fibers
Dimension.
3. high-performance terminal box special coating as described in claim 1, which is characterized in that the inorganic filler by titanium dioxide,
Talcum powder, calcium carbonate and barium sulfate according to etc. mass ratioes mix.
4. high-performance terminal box special coating as described in claim 1, which is characterized in that the Hinered phenols antioxidant by 2,
6- three-level butyl -4- methylphenol and pentaerythritol ester are mixed according to mass ratio 1:1.
5. high-performance terminal box special coating as described in claim 1, which is characterized in that the anticorrosion and bactericidal agent is by methylene
Rhodan ester and benzothiazole -3- ketone are mixed according to mass ratio 2:1.
6. the preparation method of high-performance terminal box special coating as described in claim 1, which is characterized in that including following step
It is rapid:
(1) each raw material of formula ratio is weighed, and inorganic filler is ground into fine powder, it is spare；
(2) by aqueous polyurethane emulsion, polyacrylate dispersion, styrene-acrylic emulsion, reinforcing fiber, cenosphere and moiety alcohol ester ten
Two are added in dispersion machine, and be uniformly dispersed 30-40min under 1100-1300r/min mixing speed；
(3) dispersing speed is improved to 2000-2400r/min, hexenyl bis-stearamides, higher aliphatic is added while stirring
Alcohol, triethanolamine, Nacl, silicone emulsion and non-ion fluorin surfactant continue after being dispersed with stirring 2-3h, into dispersion machine
Remaining each raw material is added, stirs 1- when high speed dispersion to grain fineness is less than 30 μm, then with the revolving speed of 800-1000r/min
2h to get.