CN109096887A - A kind of dual purpose polyester wire enamel and preparation method thereof - Google Patents
A kind of dual purpose polyester wire enamel and preparation method thereof Download PDFInfo
- Publication number
- CN109096887A CN109096887A CN201810860206.XA CN201810860206A CN109096887A CN 109096887 A CN109096887 A CN 109096887A CN 201810860206 A CN201810860206 A CN 201810860206A CN 109096887 A CN109096887 A CN 109096887A
- Authority
- CN
- China
- Prior art keywords
- added
- wire enamel
- dual purpose
- hours
- warming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wire enamel production technology, specifically a kind of dual purpose polyester wire enamel and preparation method thereof.It includes ethylene glycol 690-710g, diethylene glycol ether 110-120g, dimethyl ester 980-1000 g, terephthalic acid (TPA) 90-100g, matches gram 1925-2030g, positive butyl titanate 3-4 g, trimellitic anhydride 550-570 g, diphenyl-methane 270g.After above-mentioned formula and method, due to reasonable selection various composition formula and define the ratio of various composition formula, in addition, it is added especially in manufacturing process by substep and matching is optimized to technique, so that the wire enamel prepared, it is used for felt and mould product simultaneously, effect to be very prominent.
Description
Technical field
The present invention relates to a kind of wire enamel production technology, specifically a kind of dual purpose polyester wire enamel and its system
Make method.
Background technique
Enameled wire is mainly used as winding coil, and effect is to realize that " electricity-magnetic " energy turns during component work
It changes, so enameled wire is also electromagnetic wire.The effect of wire enamel be make in winding to generate between conducting wire and conducting wire one layer it is good
Insulating layer, to prevent the circulation of electric current.Wire enamel belongs to electric insulation paint, in addition to requiring good dielectricity, chemistry
Outside performance, it is necessary to which there is excellent mechanical performance and hot property.With industrial electrical equipment, household electrical appliance, telecommunication, electronic product etc.
Rapid development, enameled wire market demand sharply expanded in recent years, this brings broader application to enameled wire industry and leads
Domain and market.
Currently used wire enamel type has acetal, polyurethane, polyester, polyester-imide, polyamidoimide, polyester-
Amide imines etc..However, due to the limitation of its products material and production method, mainly being used for polyester wire enamel
Thus way makes all because the basic performance of product is restricted or is only used for felt product or can only use mould product
Obtain the poor universality of product.
Summary of the invention
The dual purpose that can be used for felt and mould product simultaneously the technical problem to be solved in the present invention is to provide one kind is poly-
Ester wire enamel and preparation method thereof.
In order to solve the above-mentioned technical problem, dual purpose polyester wire enamel of the invention, including ethylene glycol 690-710g, two
Ethylene glycol ethyl ether 110-120g, dimethyl ester 980-1000 g, terephthalic acid (TPA) 90-100g match gram 1925-2030g, positive metatitanic acid fourth
Ester 3-4 g, trimellitic anhydride 550-570 g, diphenyl-methane 260-280g.
A kind of production method of such as above-mentioned dual purpose polyester wire enamel, specific steps are as follows:
A, ethylene glycol 590-600g, diethylene glycol ether 110-120g is added under normal temperature condition into reaction kettle, adds in heating
Enter dimethyl ester 980-1000 g, terephthalic acid (TPA) 90-100g;
B, match gram 1800-1900 g is added when temperature reaches 70-80 DEG C, then heats to 110-120 DEG C, positive metatitanic acid is then added
Butyl ester 3-4 g;
C, when being warming up to 125-135 DEG C, it is to slowly warm up to 145-155 DEG C;
D, reach 145-155 DEG C and keep the temperature 1-2 hours, ethylene glycol 100-110g is added in three times in the process, is warming up to
170-190℃;
E, 180 DEG C of heat preservations 1.5-2.5 hours are warming up to, confirmation coating is transparent, this section of liquid outlet quantity 300-310 g,
F, it is initially added into trimellitic anhydride 550-570 g, diphenyl-methane 260-280g when being cooled to 165-170 DEG C, matches gram 125-
130g;
G, it is warming up to 160-170 DEG C, records the time, then heats to 180-200 DEG C, keeps the temperature 1-2 hours,
I, constant temperature 1-2 hours again after being all added, simultaneously sample detection is switched over.
In the step D, feed intake within every minor tick 0.3-0.7 hours.
In the step F, trimellitic anhydride, diphenyl-methane, each point of four parts of additions of match gram.
After above-mentioned formula and method, due to reasonable selection various composition formula and define that various composition is matched
The ratio of side, in addition, being added especially in manufacturing process by substep and optimizing matching to technique, so that preparation
Wire enamel out, while it being used for felt and mould product, effect is very prominent.
Specific embodiment
With reference to embodiment, dual purpose polyester wire enamel of the invention and preparation method thereof is made further
It is described in detail.
Embodiment one:
Dual purpose polyester wire enamel of the present embodiment and preparation method thereof, specific steps are as follows:
A, ethylene glycol 590g, diethylene glycol ether 110g is added under normal temperature condition into reaction kettle, dimethyl ester is added in heating
980 g, terephthalic acid (TPA) 90g;
B, match gram 1800g is added when temperature reaches 70 DEG C, then heats to 110 DEG C, positive butyl titanate 3g is then added;
C, when being warming up to 125 DEG C, 145 DEG C are to slowly warm up to;
D, reach 145 DEG C and keep the temperature 1 hour, be separately added into ethylene glycol in three times in the process, such as 104g is added for the first time,
102g is added for the first time, 100g is added for the first time, is warming up to 170 DEG C, every minor tick feeds intake for 0.3 hour;
E, 180 DEG C are warming up to and keeps the temperature 1.5 hours, confirmation coating is transparent, this section of liquid outlet quantity 300g,
F, it is initially added into 550 g of trimellitic anhydride, diphenyl-methane 270g when being cooled to 165 DEG C, matches gram 125g, trimellitic anhydride,
Diphenyl-methane, each point of four parts of additions of match gram;
G, 166 DEG C are warming up to, the time is recorded, then heats to 180 DEG C, keeps the temperature 1 hour,
I, four parts be all added after constant temperature 1 hour again, switch over and sample detection.
Embodiment two:
Dual purpose polyester wire enamel of the present embodiment and preparation method thereof, specific steps are as follows:
A, ethylene glycol 592g, diethylene glycol ether 118g is added under normal temperature condition into reaction kettle, dimethyl ester is added in heating
990 g, terephthalic acid (TPA) 94g;
B, match gram 1852 g are added when temperature reaches 75 DEG C, then heats to 115 DEG C, positive 3.5 g of butyl titanate is then added;
C, when being warming up to 130 DEG C, 150 DEG C are to slowly warm up to;
D, reach 150 DEG C and keep the temperature 1.5 hours, be separately added into ethylene glycol in three times in the process, such as be added for the first time
102g is added for the first time, 100g is added for the first time, is warming up to 170-190 DEG C, every minor tick feeds intake for 0.5 hour by 104g;
E, 180 DEG C are warming up to and keeps the temperature 2 hours, confirmation coating is transparent, this section of 302 g of liquid outlet quantity,
F, it is initially added into 562 g of trimellitic anhydride, diphenyl-methane 270g when being cooled to 168 DEG C, matches gram 127.5g, trimellitic acid
Acid anhydride, diphenyl-methane, each point of four parts of additions of match gram;
G, 170 DEG C are warming up to, the time is recorded, then heats to 190 DEG C, keeps the temperature 2 hours,
I, four parts be all added after constant temperature 2 hours again, switch over and sample detection.
Embodiment three:
Dual purpose polyester wire enamel of the present embodiment and preparation method thereof, specific steps are as follows:
A, ethylene glycol 600g, diethylene glycol ether 120g is added under normal temperature condition into reaction kettle, dimethyl ester is added in heating
1000 g, terephthalic acid (TPA) 100g;
B, match gram 1900 g are added when temperature reaches 80 DEG C, then heats to 120 DEG C, positive 4 g of butyl titanate is then added;
C, when being warming up to 135 DEG C, 155 DEG C are to slowly warm up to;
D, reach 155 DEG C and keep the temperature 2 hours, be separately added into ethylene glycol in three times in the process, such as 104g is added for the first time,
102g is added for the first time, 100g is added for the first time, is warming up to 170-190 DEG C, every minor tick feeds intake for 0.7 hour;
E, 180 DEG C are warming up to and keeps the temperature 2.5 hours, confirmation coating is transparent, this section of 310 g of liquid outlet quantity,
F, it is initially added into 570 g of trimellitic anhydride, diphenyl-methane 280g when being cooled to 170 DEG C, matches gram 130g, trimellitic anhydride,
Each point of diphenyl-methane, match gram four parts of additions;
G, 170 DEG C are warming up to, the time is recorded, then heats to 200 DEG C, keeps the temperature 2 hours,
I, four parts be all added after constant temperature 2 hours again, switch over and sample detection.
It is detected by practice, the product prepared through the invention, is suitable for JB/T 7599.6-2013 standard, and it refers to
Absolute altitude is in JB/T 7599.6-2013 standard.
Claims (4)
1. a kind of dual purpose polyester wire enamel, it is characterised in that: including ethylene glycol 690-710g, diethylene glycol ether 110-
120g, dimethyl ester 980-1000 g, terephthalic acid (TPA) 90-100g match gram 1925-2030g, positive butyl titanate 3-4 g, inclined benzene three
Acid anhydrides 550-570 g, diphenyl-methane 260-280g.
2. a kind of production method of dual purpose polyester wire enamel as described in claim 1, which is characterized in that concrete operation step
It is as follows:
A, ethylene glycol 590-600g, diethylene glycol ether 110-120g is added under normal temperature condition into reaction kettle, adds in heating
Enter dimethyl ester 980-1000 g, terephthalic acid (TPA) 90-100g;
B, match gram 1800-1900 g is added when temperature reaches 70-80 DEG C, then heats to 110-120 DEG C, positive metatitanic acid is then added
Butyl ester 3-4 g;
C, when being warming up to 125-135 DEG C, it is to slowly warm up to 145-155 DEG C;
D, reach 145-155 DEG C and keep the temperature 1-2 hours, ethylene glycol 100-110g is added in three times in the process, is warming up to
170-190℃;
E, 180 DEG C of heat preservations 1.5-2.5 hours are warming up to, confirmation coating is transparent, this section of liquid outlet quantity 300-310 g,
F, it is initially added into trimellitic anhydride 550-570 g, diphenyl-methane 260-280g when being cooled to 165-170 DEG C, matches gram 125-
130g;
G, it is warming up to 160-170 DEG C, records the time, then heats to 180-200 DEG C, keeps the temperature 1-2 hours,
I, constant temperature 1-2 hours again after being all added, simultaneously sample detection is switched over.
3. the production method of dual purpose polyester wire enamel according to claim 2, it is characterised in that: in the step D,
It feeds intake within every minor tick 0.3-0.7 hours.
4. the production method of dual purpose polyester wire enamel according to claim 2, it is characterised in that: in the step F,
Each point of trimellitic anhydride, diphenyl-methane, match gram four parts of additions.