CN109056415A - A kind of preparation method of two-sided high gloss tissue paper - Google Patents
A kind of preparation method of two-sided high gloss tissue paper Download PDFInfo
- Publication number
- CN109056415A CN109056415A CN201810762220.6A CN201810762220A CN109056415A CN 109056415 A CN109056415 A CN 109056415A CN 201810762220 A CN201810762220 A CN 201810762220A CN 109056415 A CN109056415 A CN 109056415A
- Authority
- CN
- China
- Prior art keywords
- drying cylinder
- parts
- slurry
- drying
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to pulp technology for making paper, provide a kind of preparation method of two-sided high gloss tissue paper, solve the problems, such as that the prior art only has single side to have high glaze, comprising the following steps: 1) slurrying, the beating degree of slurry are 70~75 ° of SR；2) desanding；3) copy paper, after mixing slurry after desanding is diluted with water, successively through pressurized screen, flow box, wet end, press section, drying portion, batch, cut and obtain finished product, the drying portion includes the first drying cylinder set gradually, the second drying cylinder, third drying cylinder and the atomizer that each inlet for drying cylinder is arranged in, each drying cylinder has high rigidity, best bright finish cylinder face, the atomizer sprays the remover that adds lustre to of atomization to each drying cylinder face, and second drying cylinder two sides are provided with carrying roller.
Description
Technical field
The present invention relates to pulp technology for making paper more particularly to a kind of preparation methods of two-sided high gloss tissue paper.
Background technique
Tissue paper currently produced on the market is that only single side has high glaze, and the glossiness on two sides differs greatly, city
Field needs to provide a kind of tissue paper of two-sided high gloss, improves appearance packaging quality, promotes class, is different from and uses in the market
Machine glazing tissue paper.The preparation method of existing tissue paper is: (1) slurrying: according to proportion by softwood pulp and deinking
Slurry is put into togerther size degradation in pulper and mixes, and is then beaten together, concentration is adjusted after mashing, entered by regulating box
Papermaking approach system.(2) papermaking: by slurrying materials by rush stock tank dilution and flow box it is evenly dispersed, with certain speed
It flows on wire-cloth, then by squeezing, drying, batching, is most cut, is packed in storage afterwards.Wherein baking process can pass through
Using high rigidity, best bright finish cylinder face major diameter drying cylinder and obtain higher one-side finish degree tissue paper, but cannot provide double
The high glaze in face.
Summary of the invention
Therefore, for the above content, the present invention provides a kind of preparation method of two-sided high gloss tissue paper, solves existing
There is technology to only have single side that there is the problem of high glaze.
In order to achieve the above objectives, the present invention is achieved by the following technical solutions:
A kind of preparation method of two-sided high gloss tissue paper, step are as follows:
1) slurrying: softwood pulp is successively kowtowed forebay, mill machine and kowtows after-bay and be beaten through pulper size degradation, deinking
Secondary stock is individually beaten；The beating degree of above two slurry is 70~75 ° of SR；By above two slurry by 1:1-1:3's
Weight ratio and slurry adjust concentration, and paper making additive are added；
2) desanding: above-mentioned mixing slurry is successively copied to forebay, header box, intermediate pool, removes sand pump and desander desanding；
3) copy paper: after the mixing slurry after desanding is diluted with water, successively through pressurized screen, flow box, wet end, press section, baking
Cadre batches, cuts and obtain finished product, and the drying portion includes the first drying cylinder set gradually, the second drying cylinder, third drying
Cylinder and the atomizer that each inlet for drying cylinder is arranged in, each drying cylinder have high rigidity, best bright finish cylinder
Face, the atomizer spray the remover that adds lustre to of atomization to each drying cylinder face, and second drying cylinder two sides are provided with
Carrying roller.
A further improvement is that: the paper making additive is made of each raw material of following parts by weight: 10-15 parts of guar gum, season
20-25 parts of amine type starch, 1-5 parts of alum, 10-15 parts of melamine, 50-60 parts of bloom paraffin, the auxiliary dosage are slurry
The 3-10% of weight；
A further improvement is that: the remover that adds lustre to is made of each raw material of following parts by weight: 10-20 parts of organosilicon,
0-10 parts of bloom wax, 70-80 parts of water, dosage is the 0.05-0.1% of slurry weight, and is diluted with 50-100 times of water.
A further improvement is that: each drying cylinder surfaces hardness is consistent with finish.
By using preceding solution, the beneficial effects of the present invention are:
1, atomizer and carrying roller are set by adjusting beating degree and in drying section, make the two sides of tissue paper that can there is height
Glossiness；70~75 ° of SR of the beating degree improve beating degree, promote brooming rate, can increase transparency, glossiness；Described
The carrying roller of two drying cylinder two sides settings is close to page with cylinder face, improves the page degree of beating, surface smoothness, and then improve page light
Damp degree.
2, the performances such as paper water resistant, oil resistant, anti-printing ink can be improved in further improved paper making additive, can be improved simultaneously
Slickness, hydrophobicity, printing adaptability, and can provide high-luster.
3, not only fissility is good for the further improved remover that adds lustre to, and light enhancing effect is also apparent from.
4, further improved each drying cylinder surfaces hardness is consistent with glossiness, can make finished product tissue paper two sides
Glossiness it is consistent.
Detailed description of the invention
Fig. 1 is one drying section structural schematic diagram of the embodiment of the present invention.
Specific embodiment
Carry out the embodiment that the present invention will be described in detail below with reference to specific embodiment, how skill is applied to the present invention whereby
Art means solve technical problem, and the realization process for reaching technical effect can fully understand and implement.
Unless otherwise specified, the conventional hand that technological means employed in embodiment is well known to those skilled in the art
Section, used reagent and product are also available commercial.The source of agents useful for same, trade name and it is necessary to list it
Constituent person is indicated on the first occurrence.
Embodiment one
A kind of preparation method of two-sided high gloss tissue paper, step are as follows:
1) slurrying: softwood pulp is successively kowtowed forebay, mill machine and kowtows after-bay and be beaten through pulper size degradation, deinking
Secondary stock is individually beaten；The beating degree of above two slurry is 70 ° of SR；By above two slurry by 1:1 weight ratio and
Slurry adjusts concentration, and paper making additive is added；The paper making additive is made of each raw material of following parts by weight: 10 parts of guar gum, season
25 parts of amine type starch, 5 parts of alum, 10 parts of melamine, 50 parts of bloom paraffin, the auxiliary dosage are the 3% of slurry weight；Melon
When your glue is as paper making additive, can be improved paper strength, reduction greyness forms and improves paper formation, but it the shortcomings that be
Cause drainage difficult, to reduce yield or improve drying load；Quaternary amine type starch helps to improve fiber fines and fills out
Material is kept, and is accelerated the drainage of paper stock and is improved paper strength；The effect of alum is to neutralize the strong paper stock component of anion, is avoided
The excessive absorption quaternary amine type starch of the strong paper stock component of anionic property and the effect for influencing its retention and enhancing；Melamine conduct
Fire retardant is released ammonia, carbon dioxide, ammonia etc. by thermal decomposition when burning, these non-flammable compressive gases largely dilute
Oxygen and fuel gas, play fire retardation.
2) desanding: above-mentioned mixing slurry is successively copied to forebay, header box, intermediate pool, removes sand pump and desander desanding；
3) copy paper: after the mixing slurry after desanding is diluted with water, successively through pressurized screen, flow box, wet end, press section, baking
Cadre batches, cuts and obtain finished product, and the drying portion includes that the first drying cylinder 1, second set gradually dries cylinder 2, third is dried
Vatting 3 and the atomizer 4 that each inlet for drying cylinder is arranged in, each drying cylinder have high rigidity, height bright and clean
Cylinder face is spent, each atomizer 4 sprays the remover that adds lustre to of atomization, second 2 liang of cylinder of the drying to each drying cylinder face
Side is each provided with carrying roller 5；The remover that adds lustre to is made of each raw material of following parts by weight: 10 parts of organosilicon, 10 parts of bloom wax,
80 parts of water, dosage is the 0.05% of slurry weight, and is diluted with 50 times of water；Each drying cylinder surfaces hardness and finish one
It causes.The carrying roller improves the page degree of beating, surface smoothness, and then improve page glossiness for being close to page with cylinder face.
Embodiment two
A kind of preparation method of two-sided high gloss tissue paper, step are as follows:
1) slurrying: softwood pulp is successively kowtowed forebay, mill machine and kowtows after-bay and be beaten through pulper size degradation, deinking
Secondary stock is individually beaten；The beating degree of above two slurry is 75 ° of SR；By above two slurry by 1:3 weight ratio and
Slurry adjusts concentration, and paper making additive is added；The paper making additive is made of each raw material of following parts by weight: 15 parts of guar gum, season
20 parts of amine type starch, 1 part of alum, 15 parts of melamine, 60 parts of bloom paraffin, the auxiliary dosage are the 10% of slurry weight；
2) desanding: above-mentioned mixing slurry is successively copied to forebay, header box, intermediate pool, removes sand pump and desander desanding；
3) copy paper: after the mixing slurry after desanding is diluted with water, successively through pressurized screen, flow box, wet end, press section, baking
Cadre batches, cuts and obtain finished product, and the drying portion includes the first drying cylinder set gradually, the second drying cylinder, third drying
Cylinder and the atomizer that each inlet for drying cylinder is arranged in, each drying cylinder have high rigidity, best bright finish cylinder
Face, each atomizer spray the remover that adds lustre to of atomization to each drying cylinder face, and second drying cylinder two sides are respectively set
It is equipped with carrying roller；The remover that adds lustre to is made of each raw material of following parts by weight: 20 parts of organosilicon, 0 part of bloom wax, and 80 parts of water,
Dosage is the 0.1% of slurry weight, and is diluted with 100 times of water.
Embodiment three
A kind of preparation method of two-sided high gloss tissue paper, step are as follows:
1) slurrying: softwood pulp is successively kowtowed forebay, mill machine and kowtows after-bay and be beaten through pulper size degradation, deinking
Secondary stock is individually beaten；The beating degree of above two slurry is 73 ° of SR；By above two slurry by 1:2 weight ratio and
Slurry adjusts concentration, and paper making additive is added；The paper making additive is made of each raw material of following parts by weight: 12 parts of guar gum, season
23 parts of amine type starch, 3 parts of alum, 12 parts of melamine, 55 parts of bloom paraffin, the auxiliary dosage are the 6% of slurry weight；
2) desanding: above-mentioned mixing slurry is successively copied to forebay, header box, intermediate pool, removes sand pump and desander desanding；
3) copy paper: after the mixing slurry after desanding is diluted with water, successively through pressurized screen, flow box, wet end, press section, baking
Cadre batches, cuts and obtain finished product, and the drying portion includes the first drying cylinder set gradually, the second drying cylinder, third drying
Cylinder and the atomizer that each inlet for drying cylinder is arranged in, each drying cylinder have high rigidity, best bright finish cylinder
Face, each atomizer spray the remover that adds lustre to of atomization to each drying cylinder face, and second drying cylinder two sides are respectively set
It is equipped with carrying roller；The remover that adds lustre to is made of each raw material of following parts by weight: 15 parts of organosilicon, 5 parts of bloom wax, and 70 parts of water,
Dosage is the 0.08% of slurry weight, and is diluted with 80 times of water.
It is additionally provided with smooth roll finishing section between the drying portion and curled portion, the surface luminous intensity of tissue paper is further added
Work.
The foregoing descriptions are merely the embodiment using this origination techniques content, any those skilled in the art use this wound
Make done modifications and changes, all belong to the scope of the patents of this creation opinion, and is not limited to those disclosed embodiments.
Claims (4)
1. a kind of preparation method of two-sided high gloss tissue paper, it is characterised in that: the following steps are included:
1) slurrying: softwood pulp is successively kowtowed forebay, mill machine and kowtows after-bay and be beaten through pulper size degradation, deinked waste paper
Slurry is individually beaten；The beating degree of above two slurry is 70~75 ° of SR；Above two slurry is pressed to the weight of 1:1-1:3
Than and slurry, adjust concentration, and paper making additive be added；
2) desanding: above-mentioned mixing slurry is successively copied to forebay, header box, intermediate pool, removes sand pump and desander desanding；
3) copy paper: after the mixing slurry after desanding is diluted with water, successively through pressurized screen, flow box, wet end, press section, drying portion,
Batch, cut and obtain finished product, the drying portion include the first drying cylinder, the second drying cylinder, third drying cylinder that set gradually with
And the atomizer of the inlet of each drying cylinder is set, each drying cylinder has high rigidity, best bright finish cylinder face, institute
The remover that adds lustre to that atomizer sprays atomization to each drying cylinder face is stated, second drying cylinder two sides are provided with carrying roller.
2. a kind of preparation method of two-sided high gloss tissue paper according to claim 1, it is characterised in that: the papermaking
Auxiliary agent is made of each raw material of following parts by weight: 10-15 parts of guar gum, 20-25 parts of quaternary amine type starch, 1-5 parts of alum, melamine
10-15 parts of amine, 50-60 parts of bloom paraffin, the auxiliary dosage are the 3-10% of slurry weight.
3. a kind of preparation method of two-sided high gloss tissue paper according to claim 1, it is characterised in that: described to add lustre to
Remover is made of each raw material of following parts by weight: 10-20 parts of organosilicon, 0-10 parts of bloom wax, 70-80 parts of water, dosage is slurry
Expect the 0.05-0.1% of weight, and is diluted with 50-100 times of water.
4. a kind of preparation method of two-sided high gloss tissue paper according to claim 1, it is characterised in that: each baking
Vatting surface hardness is consistent with finish.