CN109050786A - A kind of highstrenghtpiston's fishing boat - Google Patents
A kind of highstrenghtpiston's fishing boat Download PDFInfo
- Publication number
- CN109050786A CN109050786A CN201811206286.3A CN201811206286A CN109050786A CN 109050786 A CN109050786 A CN 109050786A CN 201811206286 A CN201811206286 A CN 201811206286A CN 109050786 A CN109050786 A CN 109050786A
- Authority
- CN
- China
- Prior art keywords
- hull
- highstrenghtpiston
- fishing boat
- connecting sleeve
- deck
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of highstrenghtpiston's fishing boats, it includes hull；The two sides of the hull are equipped with gunnel；Front deck is successively arranged from fore to stern in the hull, holds cabin and rear deck；Storage tank is respectively equipped in the front deck and rear deck；Connecting plate is equipped with behind the hull；The connecting plate is equipped with the connecting hole of fixed conveyor device；The bottom of the hull is equipped with connecting sleeve；Clump weight is equipped in the connecting sleeve；The end of the connecting sleeve is equipped with plug；The two sides of the gunnel are equipped with the fixing clamp for holding quant.Structure of the invention is reasonable, and structural strength is high, is equipped with clump weight in hull bottom, make hull more steady in water, the plastics fishing boat of the effective solution prior art technical problem low and inconvenient to use there are structural strength.
Description
Technical field
The invention belongs to fishing boat manufacturing technology fields, and in particular to a kind of highstrenghtpiston's fishing boat.
Background technique
Plastics fishing boat individual is smaller, generally uses in the lake and river in inland, for aquaculture, fish, water quality takes
The fields such as sample use relatively broad.
The plastics fishing boat of the prior art includes plastic hull, and hull mainly uses polyethylene material, and cabin is divided into several sections,
This plastics fishing boat structure is simple, low cost.When in use, drinking water degree is shallower for this plastics fishing boat, thus it is very unstable,
Especially in the moment of upper people, it is easy to cause to tilt and topple.Plastics fishing boat uses polyethylene material, acid and alkali-resistance, corrosion-resistant, but
It is that aging is easy in long-term solarization and bubble, service life is shorter.Hull is usually if be fixed on bank, often and bank
The frictional impacts such as stone, the pool wall on side, are easy breakage, and structural strength is lower.The sundries such as the intracorporal quant of ship, fishing net are put mixed
Disorderly, it uses inconvenient.
Summary of the invention
Present invention aim to address the plastics fishing boat of the prior art, that there are easy to aging, structural strengths is low and inconvenient to use
The technical issues of, a kind of highstrenghtpiston's fishing boat is provided, so as to solve the deficiencies in the prior art.
To achieve the goals above, the invention adopts the following technical scheme:
A kind of highstrenghtpiston's fishing boat, it includes hull；The two sides of the hull are equipped with gunnel；From fore to ship in the hull
Tail is successively arranged front deck, holds cabin and rear deck；Storage tank is respectively equipped in the front deck and rear deck；It is equipped with behind the hull
Connecting plate；The connecting plate is equipped with the connecting hole of fixed conveyor device；The bottom of the hull is equipped with connecting sleeve；The company
Clump weight is equipped in female connector pipe；The end of the connecting sleeve is equipped with plug；The two sides of the gunnel are equipped with and hold consolidating for quant
Clamp.
Further, the hull is equipped with the air interlayer of 2-5cm using the double-deck setting, centre；The upper surface of described hull
Equipped with the intercommunicating pore being connected to interlayer, intercommunicating pore is blocked by rubber stopper.
Further, the gunnel is equipped with handrail corresponding with front deck and rear deck respectively；The both ends of the handrail are logical
Perforative bolt is crossed to be fixedly connected with gunnel.
Further, the storage tank is in front deck and rear deck respectively close to forward andor aft；The height of the storage tank
For the half of hull height；The top surface of the storage tank is plane；The upper surface of the storage tank, front deck and rear deck is respectively equipped with
Anti-skid bulge.
Further, the bottom of the hull is equipped with equally distributed 1-3 connecting sleeve；The centre of the connecting sleeve
Equipped with cavity；The clump weight is placed in cavity；Corresponding screw thread is equipped between the plug and the cavity end of connecting sleeve,
Plug twist-on is in connecting sleeve.
Further, the fixing clamp includes upper and lower two arc gripper jaws；The fixing clamp is by self-tapping screw or glues
In the two sides of gunnel, every side board side is set there are two fixing clamp for glue connection, clamps the both ends of quant.
As another inventive point of the invention, the present invention also improves hull material, improves the ageing-resistant of hull
Ability, intensity and toughness further increase, and specifically, the hull is prepared in accordance with the following steps:
Step 1) weighs raw material according to following weight proportion: 50 parts of high density polyethylene (HDPE), 30 parts of low density polyethylene (LDPE), and polycarbonate
10 parts, 8 parts of polymethyl methacrylate, 5 parts of ageing-resistant reinforcing agent, 2 parts of curing agent, 2 parts of oxidized polyethylene wax, nylon fiber 2
Part, 1 part of dilauryl thiodipropionate, 1 part of stearic acid, 1 part of talcum powder；
High density polyethylene (HDPE), low density polyethylene (LDPE), polycarbonate and polymethyl methacrylate are first put into mixing by step 2
With 90 DEG C of mixing 3min in machine, be then added ageing-resistant reinforcing agent, curing agent, nylon fiber, dilauryl thiodipropionate with
And stearic acid, continue mixing 5min；
Step 3) puts into extruding pelletization in the double screw extruder that draw ratio is 35:1, extruder temperature setting a: area 165 again
DEG C, two 175 DEG C of areas, three 190 DEG C of areas, four 175 DEG C of areas, five 165 DEG C of areas, six 155 DEG C of areas, double screw extruder revolving speed is
100rpm；
Step 3) products therefrom is sent into molding equipment by step 4), while oxidized polyethylene wax and talcum powder is added, sufficiently mixed
It is even, then machine to form melting charge by plastic extrusion, be finally injected into mold and be formed, die sinking take out to get.
Preferably,
The ageing-resistant reinforcing agent is prepared according to following technique: by diatomite, bentonite and ethylene oxide according to 3:2:2
Mass ratio mixing, 10min is ground with the grinding rate of 1000rpm, is then allowed to stand 30min, then add identical as ethylene oxide
70% ethyl alcohol of quality, 200rpm stir 10min, stand 15min, and precipitating is collected in filtering, and drying crushes to obtain the final product.
Preferably,
The curing agent is mixed according to the mass ratio of 1:2 by ammonium chloride and 2 hydroxy ethylamine and is made.
Compared with prior art, the beneficial effect that the present invention obtains mainly includes but is not limited to the following aspects:
Structure of the invention is reasonable, and structural strength is high, is equipped with clump weight in hull bottom, makes hull more steady in water, effectively
The plastics fishing boat for solving the prior art technical problem low and inconvenient to use there are easy to aging, structural strength.The present invention
Hull material is improved, ageing-resistant performance is improved, intensity and toughness are also promoted；The present invention is by using a variety of
Material improves polyethylene, and material combination is reasonable, improves ageing-resistant performance, and mechanical property also greatly improves；High density
Polyethylene and the mutual compatibility of low density polyethylene (LDPE) improve stability while proof strength；Polymethyl methacrylate tool
There are good chemical stability and weatherability；Polycarbonate is able to ascend the toughness and acid-proof alkaline of product；The present invention adds
Add special antiager, in diatomite and bentonite surface aggregate ethylene oxide, so that the compatibility of inorganic material improves,
On the basis of guaranteeing inorganic material filling capacity, intensity, toughness and ageing-resistant heat resistance are improved.
Detailed description of the invention
Fig. 1 is schematic structural view of the invention；
Fig. 2 is overlooking structure diagram of the present invention；
Fig. 3 is clump weight connection schematic diagram of the present invention；
Fig. 4 is fixing clamp connection schematic diagram of the present invention.
1, gunnel 2 in figure, handrail 3, front deck 4, hold cabin 5, rear deck 6, storage tank 7, connecting plate 8, hull 9,
Connecting sleeve 10, clump weight 11, plug 12, intercommunicating pore 13, fixation hole 14, anti-skid bulge 15, fixing clamp 16, connection
Hole.
Specific embodiment
Technical solution of the present invention is clearly and completely described below in conjunction with attached drawing, in the description of the present invention,
Obvious embodiment described below is a part of the embodiment of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment 1
According to Fig. 1-Fig. 4, a kind of highstrenghtpiston's fishing boat, it includes hull 8；The two sides of the hull 8 are equipped with gunnel 1；It is described
Front deck 3 is successively arranged from fore to stern in hull 8, holds cabin 4 and rear deck 5；Storage is respectively equipped in the front deck 3 and rear deck 5
Object case 6；Connecting plate 7 is equipped with behind the hull 7；The connecting plate is equipped with the connecting hole 16 of fixed conveyor device；It is described
The bottom of hull 8 is equipped with connecting sleeve 9；Clump weight 10 is equipped in the connecting sleeve 9；The end of the connecting sleeve is equipped with stifled
First 11；The two sides of the gunnel 1 are equipped with the fixing clamp 15 for holding quant.
The ship length is 2-5m, and according to ship length difference, the quantity for holding cabin 4 is 1-3 group, described to hold
Cabin is equipped with the cover board being flexibly connected.
Transmission device on the connecting plate 7 includes motor and propeller, and connection type and working principle belong to existing
Technology is no longer described in detail, and transmission device is fixed on connecting hole 16 by bolt or pin shaft, quickly can connect and tear open
It unloads.
In use, then personnel are rided in the front deck 3 and rear deck 5 of hull 8 by life jacket is worn first, according to hull 8
Scale, purposes, distance etc. select hand stroke or machine driving.Holding for hull can hold water, fish, fishing net etc. in cabin 4
Article.
The hull 8 is equipped with the air interlayer of 2-5cm using the double-deck setting, centre；The upper surface of described hull is equipped with and folder
The intercommunicating pore 12 of layer connection, intercommunicating pore 12 are blocked by rubber stopper.
Hull 8 is using the double-deck setting, and after cabin fills water, hull 8 still maintains floating；Hull occurs broken in use
When damage cracking, is still separated with waters in the cabin of hull 8, avoid shipwreck.
The gunnel 1 is equipped with handrail 2 corresponding with front deck and rear deck respectively；The both ends of the handrail pass through perforative
Bolt is fixedly connected with gunnel.
During seating, both hands hold the handrail 2 of two sides respectively, itself can be allowed steady, while hull being allowed to keep flat
Weighing apparatus state.
The storage tank 6 is in front deck and rear deck respectively close to forward andor aft；The height of the storage tank is that hull is high
The half of degree；The top surface of the storage tank is plane；The upper surface of the storage tank, front deck and rear deck is respectively equipped with anti-skid bulge
14。
Effect of the upper surface of storage tank 6 in cabin is stool surface, is taken for personnel；It is equipped with matter storage lattice in storage tank 6, contains
The sundries such as fishing net, rope, level are put, the upper surface of storage tank 6 is the cover board of hinge connection.Anti-skid bulge 14 allows personnel standing
It prevents from slipping under state.
The anti-skid bulge 14 uses hemispherical protuberances or strip bulge, using being in array distribution when hemispherical protuberances, adopts
It is distributed in a crisscross manner with when strip bulge.
The bottom of the hull 8 is equipped with equally distributed 1-3 connecting sleeve 9；The centre of the connecting sleeve is equipped with sky
Chamber；The clump weight 10 is placed in cavity；It is equipped with corresponding screw thread between the plug 11 and the cavity end of connecting sleeve, blocks up
Head twist-on is in connecting sleeve.
The connecting sleeve and hull 8 are casting integrated, and clump weight 10 allows the draft of hull between 1/5-1/4, match
Pouring weight 10 is using the metal block of mopping, and the outermost end of clump weight 10 is equipped with knob, by shaking hands to clump weight 10 in connecting sleeve
Interior pick-and-place, by plug twist-on after placement.
The fixing clamp 15 includes upper and lower two arc gripper jaws；The fixing clamp is connected to by self-tapping screw or viscose glue
The two sides of gunnel, every side board side are set there are two fixing clamp, clamp the both ends of quant.
The gripper jaw of fixing clamp 15 uses elastic material, and preferred rubber material, the gripping of quant is resilient clamp in fixation
In the gripper jaw of folder 15.
Embodiment 2
The present invention also improves hull material, improves the ageing-resistant ability of hull, and intensity and toughness further increase, institute
Hull is stated to be prepared in accordance with the following steps:
Step 1) weighs raw material according to following weight proportion: 50 parts of high density polyethylene (HDPE), 30 parts of low density polyethylene (LDPE), and polycarbonate
10 parts, 8 parts of polymethyl methacrylate, 5 parts of ageing-resistant reinforcing agent, 2 parts of curing agent, 2 parts of oxidized polyethylene wax, nylon fiber 2
Part, 1 part of dilauryl thiodipropionate, 1 part of stearic acid, 1 part of talcum powder；
High density polyethylene (HDPE), low density polyethylene (LDPE), polycarbonate and polymethyl methacrylate are first put into mixing by step 2
With 90 DEG C of mixing 3min in machine, be then added ageing-resistant reinforcing agent, curing agent, nylon fiber, dilauryl thiodipropionate with
And stearic acid, continue mixing 5min；
Step 3) puts into extruding pelletization in the double screw extruder that draw ratio is 35:1, extruder temperature setting a: area 165 again
DEG C, two 175 DEG C of areas, three 190 DEG C of areas, four 175 DEG C of areas, five 165 DEG C of areas, six 155 DEG C of areas, double screw extruder revolving speed is
100rpm；
Step 3) products therefrom is sent into molding equipment by step 4), while oxidized polyethylene wax and talcum powder is added, sufficiently mixed
It is even, then machine to form melting charge by plastic extrusion, be finally injected into mold and be formed, die sinking take out to get.
The ageing-resistant reinforcing agent is prepared according to following technique: by diatomite, bentonite and ethylene oxide according to
The mass ratio of 3:2:2 mixes, and grinds 10min with the grinding rate of 1000rpm, is then allowed to stand 30min, then adds and ethylene oxide
70% ethyl alcohol of phase homogenous quantities, 200rpm stir 10min, stand 15min, and precipitating is collected in filtering, and drying crushes to obtain the final product.
The curing agent is mixed according to the mass ratio of 1:2 by ammonium chloride and 2 hydroxy ethylamine and is made.
Performance test:
Control group is set:
Control group 1: common polythene material；
Control group 2: not adding ageing-resistant reinforcing agent, remaining is the same as embodiment 2；
Experimental group: embodiment 2.
The performance test of each group material is shown in Table 1:
Table 1
| Index | Experimental group | Control group 1 | Control group 2 |
| Tensile strength Mpa | 55 | 34 | 39 |
| Elongation at break % | 163 | 131 | 154 |
| Bending modulus Gpa | 2.09 | 1.62 | 1.79 |
| Unnotched impact strength kJ/m2 | 48 | 25 | 36 |
| Yellowness index (Δ E value) | 3.4 | 3.9 | 4.5 |
The present invention also carries out artificially roughening to each group material respectively and is tested for the property: according to GB/T
16422.2-1999 plastics xenon source exposure test standard, using II type xenon lamp climatic test machine of SH60B to injection-molded test specimens into
It has gone artificial climate accelerated ageing in 28 days, has tested tensile strength and impact strength.Concrete outcome is shown in Table 2:
Table 2
| Index | Experimental group | Control group 1 | Control group 2 |
| Tensile strength Mpa | 53 | 30 | 35 |
| Unnotched impact strength kJ/m2 | 47 | 22 | 33 |
As it can be seen that the hull made of above-mentioned formula and technique, structural strength, toughness and anti-aging degree all get a promotion,
Service life is significantly improved.
In conclusion structure of the invention is reasonable, structural strength is high, is equipped with clump weight in hull bottom, allow hull in water
It is more steady, the plastics fishing boat of the effective solution prior art skill low and inconvenient to use there are easy to aging, structural strength
Art problem.
The above description of the embodiment is only used to help understand the method for the present invention and its core ideas.It should be pointed out that pair
For those skilled in the art, without departing from the principle of the present invention, the present invention can also be carried out
Some improvements and modifications, these improvements and modifications also fall within the scope of protection of the claims of the present invention.
Claims (9)
1. a kind of highstrenghtpiston's fishing boat, it includes hull；The two sides of the hull are equipped with gunnel；In the hull from fore to
Stern is successively arranged front deck, holds cabin and rear deck；Storage tank is respectively equipped in the front deck and rear deck；It is characterized in that the ship
Connecting plate is equipped with behind body；The connecting plate is equipped with the connecting hole of fixed conveyor device；The bottom of the hull, which is equipped with, to be connected
Female connector pipe；Clump weight is equipped in the connecting sleeve；The end of the connecting sleeve is equipped with plug；The two sides of the gunnel are equipped with
Hold the fixing clamp of quant.
2. a kind of highstrenghtpiston's fishing boat according to claim 1, it is characterized in that: the hull is arranged using double-deck, in
Between be equipped with 2-5cm air interlayer；The upper surface of described hull is equipped with the intercommunicating pore being connected to interlayer, and intercommunicating pore passes through rubber plug sealing
It is stifled.
3. a kind of highstrenghtpiston's fishing boat according to claim 1, it is characterized in that: the gunnel be equipped with respectively with front deck
Handrail corresponding with rear deck；The both ends of the handrail are fixedly connected by perforative bolt with gunnel.
4. a kind of highstrenghtpiston's fishing boat according to claim 1, it is characterized in that: the storage tank is in front deck and rear deck
Respectively close to forward andor aft；The height of the storage tank is the half of hull height；The top surface of the storage tank is plane；Institute
The upper surface for stating storage tank, front deck and rear deck is respectively equipped with anti-skid bulge.
5. a kind of highstrenghtpiston's fishing boat according to claim 1 uniformly divides it is characterized in that: the bottom of the hull is equipped with
1-3 connecting sleeve of cloth；The centre of the connecting sleeve is equipped with cavity；The clump weight is placed in cavity；The plug with
Corresponding screw thread is equipped between the cavity end of connecting sleeve, plug twist-on is in connecting sleeve.
6. a kind of highstrenghtpiston's fishing boat according to claim 1, it is characterized in that: the fixing clamp includes upper and lower two arcs
Shape gripper jaw；The fixing clamp is connected to the two sides of gunnel by self-tapping screw or viscose glue, and every side board side is set there are two fixing clamp,
Clamp the both ends of quant.
7. a kind of highstrenghtpiston's fishing boat according to claim 1, it is characterized in that: the hull is prepared in accordance with the following steps
And it obtains:
Step 1) weighs raw material according to following weight proportion: 50 parts of high density polyethylene (HDPE), 30 parts of low density polyethylene (LDPE), and polycarbonate
10 parts, 8 parts of polymethyl methacrylate, 5 parts of ageing-resistant reinforcing agent, 2 parts of curing agent, 2 parts of oxidized polyethylene wax, nylon fiber 2
Part, 1 part of dilauryl thiodipropionate, 1 part of stearic acid, 1 part of talcum powder；
High density polyethylene (HDPE), low density polyethylene (LDPE), polycarbonate and polymethyl methacrylate are first put into mixing by step 2
With 90 DEG C of mixing 3min in machine, be then added ageing-resistant reinforcing agent, curing agent, nylon fiber, dilauryl thiodipropionate with
And stearic acid, continue mixing 5min；
Step 3) puts into extruding pelletization in the double screw extruder that draw ratio is 35:1, extruder temperature setting a: area 165 again
DEG C, two 175 DEG C of areas, three 190 DEG C of areas, four 175 DEG C of areas, five 165 DEG C of areas, six 155 DEG C of areas, double screw extruder revolving speed is
100rpm；
Step 3) products therefrom is sent into molding equipment by step 4), while oxidized polyethylene wax and talcum powder is added, sufficiently mixed
It is even, then machine to form melting charge by plastic extrusion, be finally injected into mold and be formed, die sinking take out to get.
8. a kind of highstrenghtpiston's fishing boat according to claim 7, it is characterized in that: the ageing-resistant reinforcing agent is according to as follows
Technique is prepared: diatomite, bentonite and ethylene oxide being mixed according to the mass ratio of 3:2:2, grind 10min, then
30min is stood, then adds 70% ethyl alcohol with ethylene oxide phase homogenous quantities, 200rpm stirs 10min, then stands 15min, mistake
Filter, collects precipitating, and drying crushes to obtain the final product.
9. a kind of highstrenghtpiston's fishing boat according to claim 7, it is characterized in that: the curing agent is by ammonium chloride and 2- hydroxyl
Base ethamine is mixed according to the mass ratio of 1:2 and is made.