CN109031506A - One kind being used for ADS type composite light guide plate - Google Patents
One kind being used for ADS type composite light guide plate Download PDFInfo
- Publication number
- CN109031506A CN109031506A CN201810854633.7A CN201810854633A CN109031506A CN 109031506 A CN109031506 A CN 109031506A CN 201810854633 A CN201810854633 A CN 201810854633A CN 109031506 A CN109031506 A CN 109031506A
- Authority
- CN
- China
- Prior art keywords
- guide plate
- light guide
- site
- type composite
- toughener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to be used for ADS type composite light guide plate, including substrate and site, the material quality percentage of the site are as follows: polymethyl methacrylate 58%-65%, polycarbonate 5%-10%, silicon dioxide gel 2%-5%, guide-lighting powder 2-7%, photoinitiator 1%-3%, nano powder 0.2%-0.35%, toughener 0.1%-0.5%, bonding agent 0.1%-0.5%, defoaming agent 0.1-0.5%, deionized water surplus.The present invention can reduce friction effect between reflective surface coatings and light guide plate, to effectively reduce the influence to entire backlight panel light-emitting surface, will not there is the different situation of site uniformity.
Description
Technical field
It is specifically a kind of to be used for ADS type composite light guide plate the present invention relates to field of new materials.
Background technique
So-called backlight panel is a kind of light source positioned at liquid crystal display behind, its illumination effect will directly influence liquid
Brilliant display module visual effect.Liquid crystal itself does not shine, it shows figure or character is its result to light modulation.With
The continuous development of LCD technology, the application field of liquid crystal display especially colour liquid crystal display device are also constantly being widened.
The quality of backlight performance is other than it will have a direct impact on LCD imaging quality, and the cost of backlight accounts for the 30-50% of LCD module, institute
The electric power of consumption more accounts for the 75% of module, can say it is considerable spare part in LCD module.
Light guide plate is acrylic/PC plate material using optical grade, and then using has high reflectivity and the not high-tech of extinction
Skill material is the core of backlight panel, and the site of light guide plate is broadly divided into printing-type: after light guide plate completes sharp processing,
Site is imprinted on reflecting surface with mode of printing;Non-printing formula: by site light guide plate shape when direct forming in reflecting surface;Mainly
Method (V-cut), photolithography (Stamper), the internal method spread are portrayed for precision machinery.
Since the technique of non-printing formula site requires high, cost height;So existing popular style display screen majority uses
Printing-type technique.But for the backlight panel of ADS type, since its structure narrows partially, the dot surface of light guide plate and anti-
The contact amplitude for penetrating piece is very big, and dot surface is caused to there is abrasion risk, so after prolonged use, often result in light guide plate
Light quality decline.
Summary of the invention
The purpose of the present invention is to provide one kind to be used for ADS type composite light guide plate, to solve in above-mentioned background technique
The problem of proposition.
To achieve the above object, the invention provides the following technical scheme:
One kind being used for ADS type composite light guide plate, including substrate and site, the material quality percentage of the site
Are as follows: polymethyl methacrylate 58%-65%, polycarbonate 5%-10%, silicon dioxide gel 2%-5%, guide-lighting powder 2-
7%, photoinitiator 1%-3%, nano powder 0.2%-0.35%, toughener 0.1%-0.5%, bonding agent 0.1%-0.5% disappear
Infusion 0.1-0.5%, deionized water surplus.
As a further solution of the present invention: the material quality percentage of the site are as follows: polymethyl methacrylate
58%, polycarbonate 8%, silicon dioxide gel 4.5%, guide-lighting powder 5%, photoinitiator 3%, nano powder 0.35%, toughener
0.4%, bonding agent 0.4%, defoaming agent 0.35%, deionized water surplus.
As a further solution of the present invention: the material quality percentage of the site are as follows: polymethyl methacrylate
65%, polycarbonate 5%, silicon dioxide gel 2.5%, guide-lighting powder 2%, photoinitiator 1%, nano powder 0.2%, toughener
0.2%, bonding agent 0.2%, defoaming agent 0.25%, deionized water surplus.
As a further solution of the present invention: the material quality percentage of the site are as follows: polymethyl methacrylate
62%, polycarbonate 7%, silicon dioxide gel 3.5%, guide-lighting powder 4%, photoinitiator 2%, nano powder 3%, toughener
0.3%, bonding agent 0.3%, defoaming agent 0.3%, deionized water surplus.
As a further solution of the present invention: the substrate is acrylic or PC plate material.
As a further solution of the present invention: the photoinitiator be 2- hydroxy-2-methyl -1- phenyl -1- acetone, 2,4,
Any one of 6- trimethylbenzoyl diethyl phosphonate, 2- phenyl -2,2- dimethylamino -1-4- morpholinyl phenyl -1- butanone or
Several mixtures.
As further scheme of the invention: the toughener is any one of epoxy resin or phenolic resin or two
The mixture of kind.
The present invention also provides a kind of site production methods for ADS type composite light guide plate, which is characterized in that packet
Include following steps:
1) washing cleaning is carried out to substrate using deionized water;
2) according to the composition of raw materials of site, quantitative polymethyl methacrylate is weighed, polycarbonate, silica is molten
Glue, guide-lighting powder, photoinitiator, nano powder, toughener, bonding agent, defoaming agent, deionized water.
3) the step 2) formula is mixed, and be placed in heating container, stirring while is rapid with 4-10 DEG C/min
It is warming up to 150-180 DEG C;Again with the speed of 7-14 DEG C/min by material warms to 280-350 DEG C, and material is made to be maintained at smaller
Temperature fluctuation range in, obtain ink melt matter;
4) it will only the molten matter of configured ink be printed on substrate, and form site on substrate;The site diameter is most
Big value is no more than 250 μm, and the minimum value of the site diameter requires to be not less than 130 μm
5) substrate of printed ink is prevented and under UV lamps environment, carries out ultraviolet curing, curing time is 3 points
Clock;
6) light guide plate for completing ultraviolet curing stands 10min, places into near-infrared transmission furnace and is heating and curing,
Curing time is 10 minutes.
7) standing cooling is carried out to the light guide plate completed the process.
Compared with prior art, the beneficial effects of the present invention are:
One, the nose of the site after moulding be in flat, the change of this shape, can reduce reflective surface coatings with
Friction effect between light guide plate, and then reflector plate and light guide plate generate buffing, to effectively reduce to entire backlight panel
The influence of light-emitting surface.Meanwhile even if reflective surface coatings and light guide plate generate friction, flatness shadow of the friction effect to site
Sound is smaller.After light guide plate is used for a long time, there will not be the different situation of site uniformity.
Two, the present invention can effectively improve the optical homogeneity property of the type, and promotion amplitude can achieve 3%~6%, especially
It is the type relatively low for optics, promotion amplitude can achieve 5%~6%.It can effectively solve the problem that existing ADS type optics is uniform
The relatively low problem of property.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention.
Fig. 2 is schematic cross-section of the invention.
Fig. 3 is cross-section comparison's figure of the embodiment of the present invention and comparative example;
In figure: 1- substrate, the site 2-, 3- are left white area, the site 4- area, 5- terminal notch
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Please refer to Fig. 1 and Fig. 2, in the embodiment of the present invention, one kind being used for ADS type composite light guide plate, including including base
Plate 1 and site 2, the bottom surface of the substrate 1 are provided with site area 4 and are left white area 3, and the width for being left white area 3 is 1 width of substrate
7.43%, the site 2 is printed in site area 4, and described one end for being left white area 3 is provided with terminal notch 5, is used for and LED
The assembling of lamp bar terminal.
The some preferred embodiments, comparative example and performance comparison examination of formulation for coating material proportion of the present invention are given below
Test data:
Embodiment one:
One kind being used for ADS type composite light guide plate, including substrate and site, and the substrate is acryl plates, described
The material quality percentage of site are as follows: polymethyl methacrylate 58%, polycarbonate 8%, silicon dioxide gel 4.5% are led
Light powder 5%, photoinitiator 3%, nano powder 0.35%, toughener 0.4%, bonding agent 0.4%, defoaming agent 0.35%, deionization
Water surplus.The photoinitiator is 2- hydroxy-2-methyl -1- phenyl -1- acetone and 2,4,6- trimethylbenzoyl phosphonic acids diethyl
Ester is mixed by 1:3;The toughener is that epoxy resin and phenolic resin are mixed according to 1:1.
The above-mentioned site production method for ADS type composite light guide plate, comprising the following steps:
1) washing cleaning is carried out to substrate using deionized water;
2) according to the composition of raw materials of site, quantitative polymethyl methacrylate is weighed, polycarbonate, silica is molten
Glue, guide-lighting powder, photoinitiator, nano powder, toughener, bonding agent, defoaming agent, deionized water.
3) the step 2) formula is mixed, and be placed in heating container, stirring while is rapid with 4-10 DEG C/min
It is warming up to 150-180 DEG C;Again with the speed of 7-14 DEG C/min by material warms to 280-350 DEG C, and material is made to be maintained at smaller
Temperature fluctuation range in, obtain ink melt matter;
4) it will only the molten matter of configured ink be printed on substrate, and form site on substrate;The site diameter is most
Big value is no more than 250 μm, and the minimum value of the site diameter requires to be not less than 130 μm
5) substrate of printed ink is prevented and under UV lamps environment, carries out ultraviolet curing, curing time is 3 points
Clock;
6) light guide plate for completing ultraviolet curing stands 10min, places into near-infrared transmission furnace and is heating and curing,
Curing time is 10 minutes.
7) standing cooling is carried out to the light guide plate completed the process.
Embodiment two:
One kind being used for ADS type composite light guide plate, including substrate and site, and the substrate is acryl plates, described
The material quality percentage of site are as follows: polymethyl methacrylate 58%, polycarbonate 8%, silicon dioxide gel 4.5% are led
Light powder 5%, photoinitiator 3%, nano powder 0.35%, toughener 0.4%, bonding agent 0.4%, defoaming agent 0.35%, deionization
Water surplus.The photoinitiator is 2- hydroxy-2-methyl -1- phenyl -1- acetone and 2,4,6- trimethylbenzoyl phosphonic acids diethyl
Ester is mixed by 1:1;The toughener uses epoxy resin.
The site production method of its light guide plate is the same as embodiment one.
Embodiment three:
One kind being used for ADS type composite light guide plate, including substrate and site, and the substrate is PC plate material, the site
Material quality percentage are as follows: polymethyl methacrylate 62%, polycarbonate 7%, silicon dioxide gel 3.5%, guide-lighting powder
4%, photoinitiator 2%, nano powder 3%, toughener 0.3%, bonding agent 0.3%, defoaming agent 0.3%, deionized water surplus.Institute
Stating photoinitiator is that 2- hydroxy-2-methyl -1- phenyl -1- acetone and 2,4,6- trimethylbenzoyl diethyl phosphonate are mixed by 2:1
It closes;The toughener uses phenolic resin.
The site production method of its light guide plate is the same as embodiment one.
Comparative example one:
One kind being used for ADS type composite light guide plate, including substrate and site, and the substrate is acryl plates, described
The material quality percentage of site are as follows: polymethyl methacrylate 53%, omega-diol diacrylate 15%, SILICA FUME 6% are guide-lighting
Powder 3%, photoinitiator 3%, nano powder 0.35%, toughener 0.4%, bonding agent 0.4%, defoaming agent 0.35%, deionized water
Surplus.The photoinitiator is 2- hydroxy-2-methyl -1- phenyl -1- acetone and 2,4,6- trimethylbenzoyl diethyl phosphonate
It is mixed by 1:3;The toughener is that epoxy resin and phenolic resin are mixed according to 1:1.
The site production method of its light guide plate is the same as embodiment one.
Comparative example two:
One kind being used for ADS type composite light guide plate, including substrate and site, and the substrate is acryl plates, described
The material quality percentage of site are as follows: polymethyl methacrylate 48%, omega-diol diacrylate 23%, SILICA FUME 8% are guide-lighting
Powder 3%, photoinitiator 3%, nano powder 0.35%, toughener 0.4%, zirconium tetrafluoride 0.7%, zirconium tetrafluoride 0.6%, deionization
Water surplus.The photoinitiator is 2- hydroxy-2-methyl -1- phenyl -1- acetone and 2,4,6- trimethylbenzoyl phosphonic acids diethyl
Ester is mixed by 1:1;The toughener uses epoxy resin.
The site production method of its light guide plate is the same as embodiment one.
Comparative example three:
One kind being used for ADS type composite light guide plate, including substrate and site, and the substrate is PC plate material, the site
Material quality percentage are as follows: polymethyl methacrylate 48%, polycarbonate 5%, SILICA FUME 8%, light stabilizer powder 3%,
Photoinitiator 3%, omega-diol diacrylate 8%, toughener 0.4%, bonding agent 0.4%, defoaming agent 0.35%, nano powder
0.35%, ammonium hydroxide 0.5%, deionized water surplus.The photoinitiator be 2- hydroxy-2-methyl -1- phenyl -1- acetone and 2,4,
6- trimethylbenzoyl diethyl phosphonate is mixed by 2:1;The toughener uses phenolic resin.
The site production method of its light guide plate is the same as embodiment one.
The cross-sectional shapes of the light guide plate of the embodiment of the present invention 1~3, comparative example 1~3, contrast schematic diagram under the microscope,
It is illustrated in fig. 3 shown below:
Fig. 3-A is the cross-sectional shapes of the light guide plate of Examples 1 to 3;
Fig. 3-B is the cross-sectional shapes of the light guide plate of comparative example 1~3;
It can be seen that the shape of the light guide plate mesh point of the embodiment of the present invention compares there is different sites after moulding in comparative example
Nose is in flat, and the nose of the site of comparative example is in ellipticity, and the change of this shape can reduce reflecting surface painting
Friction effect between layer and light guide plate, and then reflector plate and light guide plate generate buffing, to effectively reduce to entire backlight
The influence of panel light-emitting surface.Meanwhile even if reflective surface coatings and light guide plate generate friction, friction effect is to the smooth of site
Degree influences smaller.After light guide plate is used for a long time, there will not be the different situation of site uniformity.
By the embodiment of the present invention 1~3 with 215-ADS-SN5497 in the prior art, 215-ADS-RD4867,215-
ADS-IS987A is replaced comparative test, and (215-ADS-SN5497,215-ADS-RD4867 are acrylic material light guide plate
Type, 215-ADS-IS987A are the type of PC material light guide plate)
The three groups of replacement tests of each type type, and its optical homogeneity property is detected respectively.
Comparing result is as shown in the table:
From test result can with find out, the present invention can effectively improve the optical homogeneity property of the type, and the amplitude that promoted can
To reach 3%~6%, especially for the type that optics is relatively low, promotion amplitude can achieve 5%~6%.It can effectively solve the problem that
The relatively low problem of existing ADS type optical homogeneity property.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (8)
1. one kind is used for ADS type composite light guide plate, including substrate and site, which is characterized in that the raw material matter of the site
Measure percentage are as follows: polymethyl methacrylate 58%-65%, polycarbonate 5%-10%, silicon dioxide gel 2%-5% are led
Light powder 2-7%, photoinitiator 1%-3%, nano powder 0.2%-0.35%, toughener 0.1%-0.5%, bonding agent 0.1%-
0.5%, defoaming agent 0.1-0.5%, deionized water surplus.
2. according to claim 1 be used for ADS type composite light guide plate, which is characterized in that the raw material matter of the site
Measure percentage are as follows: polymethyl methacrylate 58%, polycarbonate 8%, silicon dioxide gel 4.5%, guide-lighting powder 5%, light draws
Send out agent 3%, nano powder 0.35%, toughener 0.4%, bonding agent 0.4%, defoaming agent 0.35%, deionized water surplus.
3. according to claim 1 be used for ADS type composite light guide plate, which is characterized in that the raw material matter of the site
Measure percentage are as follows: polymethyl methacrylate 65%, polycarbonate 5%, silicon dioxide gel 2.5%, guide-lighting powder 2%, light draws
Send out agent 1%, nano powder 0.2%, toughener 0.2%, bonding agent 0.2%, defoaming agent 0.25%, deionized water surplus.
4. according to claim 1 be used for ADS type composite light guide plate, which is characterized in that the raw material matter of the site
Measure percentage are as follows: polymethyl methacrylate 62%, polycarbonate 7%, silicon dioxide gel 3.5%, guide-lighting powder 4%, light draws
Send out agent 2%, nano powder 3%, toughener 0.3%, bonding agent 0.3%, defoaming agent 0.3%, deionized water surplus.
5. according to claim 1 be used for ADS type composite light guide plate, which is characterized in that the substrate is acrylic
Or PC plate material.
6. according to claim 1 be used for ADS type composite light guide plate, which is characterized in that the photoinitiator is 2-
Hydroxy-2-methyl -1- phenyl -1- acetone, 2,4,6- trimethylbenzoyl diethyl phosphonate, 2- phenyl -2,2- dimethylamino -1-
The mixture of any one or more of 4- morpholinyl phenyl -1- butanone.
7. according to claim 1 be used for ADS type composite light guide plate, which is characterized in that the toughener is epoxy
Any one of resin or phenolic resin or two kinds of mixture.
8. the site production method as claimed in claim 1 for ADS type composite light guide plate, feature exist
In, comprising the following steps:
1) washing cleaning is carried out to substrate using deionized water;
2) according to the composition of raw materials of site, quantitative polymethyl methacrylate, polycarbonate are weighed, silicon dioxide gel is led
Light powder, photoinitiator, nano powder, toughener, bonding agent, defoaming agent, deionized water.
3) the step 2) formula is mixed, and be placed in heating container, stirring while is brought rapidly up with 4-10 DEG C/min
To 150-180 DEG C;Again with the speed of 7-14 DEG C/min by material warms to 280-350 DEG C, and material is made to be maintained at lesser temperature
It spends in fluctuation range, obtains ink and melt matter;
4) it will only the molten matter of configured ink be printed on substrate, and form site on substrate;The maximum value of the site diameter
No more than 250 μm, the minimum value of the site diameter requires to be not less than 130 μm
5) substrate of printed ink is prevented and under UV lamps environment, carries out ultraviolet curing, curing time is 3 minutes;
6) light guide plate for completing ultraviolet curing stands 10min, places into near-infrared transmission furnace and is heating and curing, solidifies
Time is 10 minutes.
7) standing cooling is carried out to the light guide plate completed the process.