CN109021721A - A kind of wear-resisting paint vehicle of fire extinguisher - Google Patents
A kind of wear-resisting paint vehicle of fire extinguisher Download PDFInfo
- Publication number
- CN109021721A CN109021721A CN201810935056.4A CN201810935056A CN109021721A CN 109021721 A CN109021721 A CN 109021721A CN 201810935056 A CN201810935056 A CN 201810935056A CN 109021721 A CN109021721 A CN 109021721A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire extinguisher
- wear
- paint vehicle
- resisting paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear-resisting paint vehicles of fire extinguisher, are made of following substance: styrene-acrylic emulsion, Lauxite, terpene resin, mica powder, ethyl acetate, diethyl phthalate, nano zine oxide, kaolin, attapulgite, calgon, corn fiber gum, fatty alcohol polyoxyethylene ether, deionized water.Improvement is optimized to the ingredient of paint vehicle in the present invention, and component is simple, and collocation is reasonable, manufactured paint vehicle film layer consistency is high, and the combination strength of bottle body is big, and abrasion-proof corrosion-proof performance is good, improve stability and service life of the fire extinguisher in routine use, great application value.
Description
Technical field
The invention belongs to fire-fighting equipment working process technical fields, and in particular to a kind of wear-resisting paint vehicle of fire extinguisher.
Background technique
Fire extinguisher is one of common equipment in fire-fighting domain, easy to carry, the quick place for small area fire etc.
Reason.And generally for the service life for identifying or being promoted fire extinguisher bottle, it requires to carry out it surface paint processing, i.e., using paint
Coating processing is carried out to bottle body surface.Existing commercially available most paint vehicle quality parameters are single, cause using effect make us not very
It is satisfied, need further Optimal improvements.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of wear-resisting paint vehicle of fire extinguisher is provided.
The present invention is achieved by the following technical solutions:
A kind of wear-resisting paint vehicle of fire extinguisher, is made of the substance of following parts by weight:
35 ~ 40 parts of styrene-acrylic emulsions, 13 ~ 16 parts of Lauxites, 6 ~ 9 parts of terpene resins, 4 ~ 7 parts of mica powders, 5 ~ 8 parts of ethyl acetate, 4
~ 6 parts of diethyl phthalates, 2 ~ 4 parts of nano zine oxides, 1 ~ 3 part of kaolin, 2 ~ 5 parts of attapulgites, 1.5 ~ 2.5 part six partially
Sodium phosphate, 1 ~ 2 part of corn fiber gum, 0.5 ~ 1 part of fatty alcohol polyoxyethylene ether, 45 ~ 50 parts of deionized waters.
Preferably, it is made of the substance of following parts by weight:
38 parts of styrene-acrylic emulsions, 15 parts of Lauxites, 8 parts of terpene resins, 6 parts of mica powders, 7 parts of ethyl acetate, 5 parts of phthalic acids
Diethylester, 3 parts of nano zine oxides, 2 parts of kaolin, 4 parts of attapulgites, 2 parts of calgons, 1.5 parts of corn fiber gums, 0.8
Part fatty alcohol polyoxyethylene ether, 47 parts of deionized waters.
Further, the solid content in the styrene-acrylic emulsion is 45 ~ 50%.
Further, the grain diameter of the mica powder is 300 ~ 400 mesh.
Further, the grain diameter of the nano zine oxide is 20 ~ 70nm.
Further, the kaolinic grain diameter is 100 ~ 200 mesh.
Further, the grain diameter of the attapulgite is 500 ~ 600 mesh.
The present invention has the advantage that compared with prior art
Improvement is optimized to the ingredient of paint vehicle in the present invention, and component is simple, and collocation is reasonable, manufactured paint vehicle film layer consistency
Height, and the combination strength of bottle body are big, and abrasion-proof corrosion-proof performance is good, improve stability and service life of the fire extinguisher in routine use,
Great application value.
Specific embodiment
Embodiment 1
A kind of wear-resisting paint vehicle of fire extinguisher, is made of the substance of following parts by weight:
35 parts of styrene-acrylic emulsions, 13 parts of Lauxites, 6 parts of terpene resins, 4 parts of mica powders, 5 parts of ethyl acetate, 4 parts of phthalic acids
Diethylester, 2 parts of nano zine oxides, 1 part of kaolin, 2 parts of attapulgites, 1.5 parts of calgons, 1 part of corn fiber gum, 0.5
Part fatty alcohol polyoxyethylene ether, 45 parts of deionized waters.
Further, the solid content in the styrene-acrylic emulsion is 45%.
Further, the grain diameter of the mica powder is 300 mesh.
Further, the grain diameter of the nano zine oxide is 20 ~ 70nm.
Further, the kaolinic grain diameter is 100 mesh.
Further, the grain diameter of the attapulgite is 500 mesh.
Embodiment 2
A kind of wear-resisting paint vehicle of fire extinguisher, is made of the substance of following parts by weight:
38 parts of styrene-acrylic emulsions, 15 parts of Lauxites, 8 parts of terpene resins, 6 parts of mica powders, 7 parts of ethyl acetate, 5 parts of phthalic acids
Diethylester, 3 parts of nano zine oxides, 2 parts of kaolin, 4 parts of attapulgites, 2 parts of calgons, 1.5 parts of corn fiber gums, 0.8
Part fatty alcohol polyoxyethylene ether, 47 parts of deionized waters.
Further, the solid content in the styrene-acrylic emulsion is 48%.
Further, the grain diameter of the mica powder is 350 mesh.
Further, the grain diameter of the nano zine oxide is 20 ~ 70nm.
Further, the kaolinic grain diameter is 150 mesh.
Further, the grain diameter of the attapulgite is 560 mesh.
Embodiment 3
A kind of wear-resisting paint vehicle of fire extinguisher, is made of the substance of following parts by weight:
40 parts of styrene-acrylic emulsions, 16 parts of Lauxites, 9 parts of terpene resins, 7 parts of mica powders, 8 parts of ethyl acetate, 6 parts of phthalic acids
Diethylester, 4 parts of nano zine oxides, 3 parts of kaolin, 5 parts of attapulgites, 2.5 parts of calgons, 2 parts of corn fiber gums, 1 part
Fatty alcohol polyoxyethylene ether, 50 parts of deionized waters.
Further, the solid content in the styrene-acrylic emulsion is 45 ~ 50%.
Further, the grain diameter of the mica powder is 400 mesh.
Further, the grain diameter of the nano zine oxide is 20 ~ 70nm.
Further, the kaolinic grain diameter is 200 mesh.
Further, the grain diameter of the attapulgite is 600 mesh.
The wear-and corrosion-resistant performance of paint vehicle of the present invention is good, the service life of fire extinguisher bottle can be extended 30% or more, great market is competing
Strive power and application value.
Claims (7)
1. a kind of wear-resisting paint vehicle of fire extinguisher, which is characterized in that be made of the substance of following parts by weight:
35 ~ 40 parts of styrene-acrylic emulsions, 13 ~ 16 parts of Lauxites, 6 ~ 9 parts of terpene resins, 4 ~ 7 parts of mica powders, 5 ~ 8 parts of ethyl acetate, 4
~ 6 parts of diethyl phthalates, 2 ~ 4 parts of nano zine oxides, 1 ~ 3 part of kaolin, 2 ~ 5 parts of attapulgites, 1.5 ~ 2.5 part six partially
Sodium phosphate, 1 ~ 2 part of corn fiber gum, 0.5 ~ 1 part of fatty alcohol polyoxyethylene ether, 45 ~ 50 parts of deionized waters.
2. a kind of wear-resisting paint vehicle of fire extinguisher according to claim 1, which is characterized in that by the substance system of following parts by weight
At:
38 parts of styrene-acrylic emulsions, 15 parts of Lauxites, 8 parts of terpene resins, 6 parts of mica powders, 7 parts of ethyl acetate, 5 parts of phthalic acids
Diethylester, 3 parts of nano zine oxides, 2 parts of kaolin, 4 parts of attapulgites, 2 parts of calgons, 1.5 parts of corn fiber gums, 0.8
Part fatty alcohol polyoxyethylene ether, 47 parts of deionized waters.
3. a kind of wear-resisting paint vehicle of fire extinguisher according to claim 1 or 2, which is characterized in that in the styrene-acrylic emulsion
Solid content be 45 ~ 50%.
4. a kind of wear-resisting paint vehicle of fire extinguisher according to claim 1 or 2, which is characterized in that of the mica powder
Grain partial size is 300 ~ 400 mesh.
5. a kind of wear-resisting paint vehicle of fire extinguisher according to claim 1 or 2, which is characterized in that the nano zine oxide
Grain diameter be 20 ~ 70nm.
6. a kind of wear-resisting paint vehicle of fire extinguisher according to claim 1 or 2, which is characterized in that described kaolinic
Grain partial size is 100 ~ 200 mesh.
7. a kind of wear-resisting paint vehicle of fire extinguisher according to claim 1 or 2, which is characterized in that the attapulgite
Grain diameter is 500 ~ 600 mesh.