CN109020460A - A kind of preparation method of compound grass-planting brick raw material - Google Patents
A kind of preparation method of compound grass-planting brick raw material Download PDFInfo
- Publication number
- CN109020460A CN109020460A CN201811011654.9A CN201811011654A CN109020460A CN 109020460 A CN109020460 A CN 109020460A CN 201811011654 A CN201811011654 A CN 201811011654A CN 109020460 A CN109020460 A CN 109020460A
- Authority
- CN
- China
- Prior art keywords
- raw material
- preparation
- planting brick
- parts
- grass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of preparation methods of compound grass-planting brick raw material, belong to building material technical field.The present invention is by mixing ooze with aluminium ash, increase the content of aluminium in ooze, then again with change waste residue material in advance and mixed, then impregnated again with hydrochloric acid, it is acted on by hydrochloric acid, release the metal in the metal oxide in raw material in the form of an ion, then it is in as the effect of additive makes metal ion flocculating setting on the surface of raw material, then by being mixed with frerrous chloride, mesoporous nano iron oxide is formed under alkaline condition and forms aluminium hydroxide is deposited on raw material surface, increase the anti-freezing property of grass-planting brick, and it joined pretreated straw powder, the fiber in stalk is exposed by pretreatment, again with the maleic anhydride of addition, polyethyleneimine is combined reaction, improve water retention property.
Description
Technical field
The present invention relates to a kind of preparation methods of compound grass-planting brick raw material, belong to building material technical field.
Background technique
Grass-planting brick is that have the quality materials such as concrete, river sand, pigment to press by the vibration of high brick machine, completely non-burning brick,
Reach the requirement of environmental protection production, grass-planting brick laying has good stability on the ground, and green coverage is wide, is amenable to pedestrian, vehicle
Spreading without being damaged, while the root of greenweed be grown in grass-planting brick in the following, will not therefore and enable hurt to grass roots
Evil, therefore build base grass-planting brick and be widely used in a variety of applications.But existing grass-planting brick has the disadvantage in that 1) its conduct can load-bearing
Surface, compression strength need to improve;2) grass-planting brick high expensive, up for reducing.Chinese Patent Application No.
CN201410157310.4 discloses a kind of grass-planting brick and its manufacturing method using the manufacture of sintering flue gas semi-dry desulphurization ash, should
Component and its weight percent content proportion of grass-planting brick are as follows: semi-dry desulphurization ash: 5~25%;Steel slag: 30~50%;Miberal powder:
10~30%;Cement: 0~10%;Gather materials: 5~20%.Method includes the following steps: the component after 1) drying being taken to grind by
The proportion is mixed to form siccative, then will be added water and stirred uniformly in siccative, forms wet mixture;2) wet mixture is injected and is planted
Idiosome is pressed under room temperature and 170~550 tons of pressure in careless bricks die;3) idiosome is conserved 7~8 days in outdoor room temperature, the phase
Between fetch water and keep idiosome surface wettability, idiosome is placed 28~30 days naturally then, obtains high-intensitive grass-planting brick.The grass-planting brick
7 days compression strength reaches 10MPa or more, and 28 days compression strength reaches 15MPa, higher by 50% than existing common grass-planting brick, and plant greatly improved
The compression strength of careless brick and the recycling for realizing waste residue, but water retention is low, and frost resistance is poor, causes product strength loss big.
Therefore, the grass-planting brick for how realizing that a kind of water retention is high, frost resistance is good, loss of strength is small is that technology urgently to be resolved in the industry is asked
Topic not only has necessary meaning to the field of building materials, also has necessary meaning to the development of grass-planting brick.
Summary of the invention
The technical problems to be solved by the invention: it is low for current grass-planting brick water retention, and the problem of frost resistance difference, this hair
It is bright to provide a kind of preparation method of compound grass-planting brick raw material.
In order to solve the above technical problems, the present invention is using technical solution as described below:
A kind of preparation method of compound grass-planting brick raw material, the preparation method include the following steps:
(1) ooze, aluminium ash 4~6:3 in mass ratio are put into ball mill and carry out ball milling, collect ball milling object, by ball milling object, water,
Change waste residue material 7~9:10:3 in mass ratio~5 in advance and carry out ultrasonic vibration, stand, filters, it is dry, obtain base-material;
(2) base-material, hydrochloric acid 3:7~9 in mass ratio are stirred, add the additive of base-material 8~10%, carry out ultrasonic shake
It swings, stands, filter residue is collected in filtering;
(3) according to parts by weight, take 90~95 parts of water, 26~32 parts of filter residues, 13~15 parts of frerrous chlorides, 9~15 parts of sodium metasilicate,
8~13 parts of pretreatment plant straw powders, 3~8 parts of ammonium hydrogen carbonate, 2~4 parts of surfactants, 1~3 part of dispersing agent, 1~3 part
Auxiliary agent;
(4) water, filter residue, frerrous chloride, ammonium hydrogen carbonate are put into reactor first, microwave heating, place into surfactant,
Dispersing agent, auxiliary agent adjust pH to 8.0~8.5 using ammonium hydroxide, stir 60~80min, and pretreatment plant straw powder is added, stirs
30~35min is mixed, sodium metasilicate is added, is stirred, collects mixture, spray drying collects dried object to get compound grass-planting brick
Raw material.
The preparation method for changing waste residue material in the step (1) in advance is to stir dregs, blast furnace slag, iron filings by 7~9:4:1 of quality
Mixing is mixed, is squeezed, is crushed, sieving particle is put into hydrogen peroxide and impregnates, filters by sieving, collects filter residue, dry to get changing in advance
Property waste material.
Additive is to mix maleic anhydride, polyethyleneimine 1:3~5 in mass ratio in the step (2).
It is described pretreatment plant straw powder preparation method be by wheat stalk, corn stover by etc. mass mixings, powder
It is broken, 200 meshes are crossed, sieving particle are mixed with water 1:2 in mass ratio, steam blasting collects explosion object, and filter residue is done in filtering
It is dry to get pretreatment plant straw powder.
The surfactant is neopelex, any one in lauryl sodium sulfate.
The dispersing agent is odium stearate, any one in magnesium stearate.
The auxiliary agent is sodium gluconate, any one in sodium tartrate.
The present invention is compared with other methods, and advantageous effects are:
The present invention increases the content of aluminium in ooze by mixing ooze with aluminium ash, then again with change waste residue material in advance and carry out
Mixing, is then impregnated again with hydrochloric acid, is acted on by hydrochloric acid, makes metal in the metal oxide in raw material in the form of an ion
Release, be then in as the effect of additive makes metal ion flocculating setting on the surface of raw material, then by with chlorination
Ferrous iron is mixed, and forms mesoporous nano iron oxide under alkaline condition and formation aluminium hydroxide is deposited on raw material surface, increase
Add the anti-freezing property of grass-planting brick, and joined pretreated straw powder, exposes the fiber in stalk by pretreatment
Come, then be combined and react with the maleic anhydride of addition, polyethyleneimine, improves water retention property, and the work for passing through auxiliary agent
With effectively delaying the reaction speed of the ingredients such as tricalcium silicate in raw material, dicalcium silicate and water, delay within the scope of certain thickness
The setting time of raw material, so that condensation of the surface layer grass-planting brick in maintenance is later than internal makes easily to form hole inside it, increases suction
Water and water retention property.
Specific embodiment
Ooze is mainly made of four part such as crystalline solid, colloid, microorganism, mud.Crystalline solid is mainly by calcium sulfate, phosphoric acid
The inorganic substances such as calcium, calcium carbonate, magnesium phosphate, magnesium carbonate, ferric carbonate and silicate particulate mix.Inorganic matter has sulphur in colloid
Change iron, sulphur iron hydride, ferrous hydroxide, aluminium hydroxide, manganous hydroxide, aluminium oxide, manganese oxide, calcium oxide, magnesia, titanium oxide
It is formed with phosphorus pentoxide etc., the microorganisms such as hydrogen sulfide vibrios, spirillum desulfuricans and Beggiatoa is generated in ooze forming process
About more than 100 kinds.Mud is made of mineral salts, colloid part, the aqueous solution of organic substance and gas, in addition also containing micro
Rare earth element.
The preparation method for changing waste residue material in advance is to be stirred dregs, blast furnace slag, iron filings by 7~9:4:1 of quality, with 3MPa
10min is squeezed, is crushed, 200 meshes are crossed, sieving particle is put into 0.3mol/L hydrogen peroxide and impregnates 40min, is filtered, filter is collected
Slag, it is dry to get pre- modified waste material.
Additive is to mix maleic anhydride, polyethyleneimine 1:3~5 in mass ratio.
Pre-process plant straw powder preparation method be by wheat stalk, corn stover by etc. mass mixings, crush, mistake
200 meshes mix sieving particle with water 1:2 in mass ratio, steam blasting, pressure 2.6MPa, and maintenance pressure 120~
130s collects explosion object, filtering, by filter residue and drying to get pretreatment plant straw powder.
Surfactant is neopelex, any one in lauryl sodium sulfate.
Dispersing agent is odium stearate, any one in magnesium stearate.
Auxiliary agent is sodium gluconate, any one in sodium tartrate.
A kind of preparation method of compound grass-planting brick raw material, the preparation method include the following steps:
(1) ooze, aluminium ash 4~6:3 in mass ratio are put into ball mill, ball milling 30min is carried out with 500r/min, collects ball milling
Object by ball milling object, water, changes waste residue material 7~9:10:3 in mass ratio~5 progress ultrasonic vibration 15min in advance, stands 70min, mistake
Filter, it is dry, obtain base-material;
(2) base-material, 0.5mol/L hydrochloric acid 3:7~9 in mass ratio are stirred 1h, add the additive of base-material 8~10%,
Ultrasonic vibration 50min is carried out, 3h is stood, filter residue is collected in filtering;
(3) according to parts by weight, take 90~95 parts of water, 26~32 parts of filter residues, 13~15 parts of frerrous chlorides, 9~15 parts of sodium metasilicate,
8~13 parts of pretreatment plant straw powders, 3~8 parts of ammonium hydrogen carbonate, 2~4 parts of surfactants, 1~3 part of dispersing agent, 1~3 part
Auxiliary agent;
(4) water, filter residue, frerrous chloride, ammonium hydrogen carbonate are put into reactor first, microwave heating places into surface to 80 DEG C
Activating agent, dispersing agent, auxiliary agent adjust pH to 8.0~8.5 using ammonium hydroxide, stir 60~80min, and pretreatment straw is added
Powder stirs 30~35min, and sodium metasilicate is added, is stirred 1h, collects mixture, spray drying, collect dried object to get
Compound grass-planting brick raw material.
The preparation method for changing waste residue material in advance is to be stirred dregs, blast furnace slag, iron filings by quality 9:4:1, is squeezed with 3MPa
10min is pressed, is crushed, 200 meshes are crossed, sieving particle is put into 0.3mol/L hydrogen peroxide and impregnates 40min, is filtered, filter residue is collected,
Drying is to get pre- modified waste material.
Additive is to mix maleic anhydride, polyethyleneimine 1:5 in mass ratio.
Pre-process plant straw powder preparation method be by wheat stalk, corn stover by etc. mass mixings, crush, mistake
200 meshes mix sieving particle with water 1:2 in mass ratio, and steam blasting, pressure 2.6MPa maintains pressure 130s, collects
Explosion object, filtering, by filter residue and drying to get pretreatment plant straw powder.
Surfactant is lauryl sodium sulfate.
Dispersing agent is magnesium stearate.
Auxiliary agent is sodium tartrate.
A kind of preparation method of compound grass-planting brick raw material, the preparation method include the following steps:
(1) ooze, aluminium ash 6:3 in mass ratio are put into ball mill, ball milling 30min are carried out with 500r/min, collects ball milling object,
By ball milling object, water, change waste residue material 9:10:5 in mass ratio progress ultrasonic vibration 15min in advance, stands 70min, filter, it is dry, it obtains
Base-material;
(2) base-material, 0.5mol/L hydrochloric acid 3:9 in mass ratio are stirred 1h, add the additive of base-material 10%, is surpassed
50min is swung in acoustic shock, stands 3h, and filter residue is collected in filtering;
(3) according to parts by weight, 95 parts of water, 32 parts of filter residues, 15 parts of frerrous chlorides, 15 parts of sodium metasilicate, 13 parts of pretreatment plants are taken
Stalk powder, 8 parts of ammonium hydrogen carbonate, 4 parts of surfactants, 3 parts of dispersing agents, 3 parts of auxiliary agents;
(4) water, filter residue, frerrous chloride, ammonium hydrogen carbonate are put into reactor first, microwave heating places into surface to 80 DEG C
Activating agent, dispersing agent, auxiliary agent adjust pH to 8.5 using ammonium hydroxide, stir 80min, and pretreatment plant straw powder, stirring is added
Sodium metasilicate is added in 33min, is stirred 1h, collects mixture, and it is former to get compound grass-planting brick to collect dried object for spray drying
Material.
The preparation method for changing waste residue material in advance is to be stirred dregs, blast furnace slag, iron filings by quality 8:4:1, is squeezed with 3MPa
10min is pressed, is crushed, 200 meshes are crossed, sieving particle is put into 0.3mol/L hydrogen peroxide and impregnates 40min, is filtered, filter residue is collected,
Drying is to get pre- modified waste material.
Additive is to mix maleic anhydride, polyethyleneimine 1:4 in mass ratio.
Pre-process plant straw powder preparation method be by wheat stalk, corn stover by etc. mass mixings, crush, mistake
200 meshes mix sieving particle with water 1:2 in mass ratio, and steam blasting, pressure 2.6MPa maintains pressure 125s, collects
Explosion object, filtering, by filter residue and drying to get pretreatment plant straw powder.
Surfactant is lauryl sodium sulfate.
Dispersing agent is magnesium stearate.
Auxiliary agent is sodium gluconate.
A kind of preparation method of compound grass-planting brick raw material, the preparation method include the following steps:
(1) ooze, aluminium ash 5:3 in mass ratio are put into ball mill, ball milling 30min are carried out with 500r/min, collects ball milling object,
By ball milling object, water, change waste residue material 8:10:4 in mass ratio progress ultrasonic vibration 15min in advance, stands 70min, filter, it is dry, it obtains
Base-material;
(2) base-material, 0.5mol/L hydrochloric acid 3:8 in mass ratio are stirred 1h, add the additive of base-material 9%, is surpassed
50min is swung in acoustic shock, stands 3h, and filter residue is collected in filtering;
(3) according to parts by weight, 93 parts of water, 30 parts of filter residues, 14 parts of frerrous chlorides, 12 parts of sodium metasilicate, 11 parts of pretreatment plants are taken
Stalk powder, 5 parts of ammonium hydrogen carbonate, 3 parts of surfactants, 2 parts of dispersing agents, 2 parts of auxiliary agents;
(4) water, filter residue, frerrous chloride, ammonium hydrogen carbonate are put into reactor first, microwave heating places into surface to 80 DEG C
Activating agent, dispersing agent, auxiliary agent adjust pH to 8.5 using ammonium hydroxide, stir 70min, and pretreatment plant straw powder, stirring is added
Sodium metasilicate is added in 33min, is stirred 1h, collects mixture, and it is former to get compound grass-planting brick to collect dried object for spray drying
Material.
The preparation method for changing waste residue material in advance is to be stirred dregs, blast furnace slag, iron filings by quality 7:4:1, is squeezed with 3MPa
10min is pressed, is crushed, 200 meshes are crossed, sieving particle is put into 0.3mol/L hydrogen peroxide and impregnates 40min, is filtered, filter residue is collected,
Drying is to get pre- modified waste material.
Additive is to mix maleic anhydride, polyethyleneimine 1:3 in mass ratio.
Pre-process plant straw powder preparation method be by wheat stalk, corn stover by etc. mass mixings, crush, mistake
200 meshes mix sieving particle with water 1:2 in mass ratio, and steam blasting, pressure 2.6MPa maintains pressure 120s, collects
Explosion object, filtering, by filter residue and drying to get pretreatment plant straw powder.
Surfactant is neopelex.
Dispersing agent is odium stearate.
Auxiliary agent is sodium gluconate.
A kind of preparation method of compound grass-planting brick raw material, the preparation method include the following steps:
(1) ooze, aluminium ash 4:3 in mass ratio are put into ball mill, ball milling 30min are carried out with 500r/min, collects ball milling object,
By ball milling object, water, change waste residue material 7:10:3 in mass ratio progress ultrasonic vibration 15min in advance, stands 70min, filter, it is dry, it obtains
Base-material;
(2) base-material, 0.5mol/L hydrochloric acid 3:7 in mass ratio are stirred 1h, add the additive of base-material 8~10%, into
Row ultrasonic vibration 50min, stands 3h, and filter residue is collected in filtering;
(3) according to parts by weight, 90 parts of water, 26 parts of filter residues, 13 parts of frerrous chlorides, 9 parts of sodium metasilicate, 8 parts of pretreatment plant straw are taken
Stalk powder, 3 parts of ammonium hydrogen carbonate, 2 parts of surfactants, 1 part of dispersing agent, 1 part of auxiliary agent;
(4) water, filter residue, frerrous chloride, ammonium hydrogen carbonate are put into reactor first, microwave heating places into surface to 80 DEG C
Activating agent, dispersing agent, auxiliary agent adjust pH to 8.0 using ammonium hydroxide, stir 60min, and pretreatment plant straw powder, stirring is added
Sodium metasilicate is added in 30min, is stirred 1h, collects mixture, and it is former to get compound grass-planting brick to collect dried object for spray drying
Material.
The commercially available grass-planting brick of comparative example.
By the compound grass-planting brick raw material of Examples 1 to 3 preparation and water 7:1~3 in mass ratio, mixing is put into grass planting stock mould
In tool, idiosome is pressed into the case where temperature is 24~27 DEG C, pressure is 10~15MPa, outdoor room temperature conserves 7~8 days, during maintenance
Idiosome surface wettability is kept every fetching water for 24 hours, maintenance finishes, then places 28~30 days naturally, and grass-planting brick is made.
Grass-planting brick in the grass-planting brick and comparative example of the preparation of above-described embodiment 1~3 is detected.
Frost resistance: being tested according to GB/T4111 " concrete segment and brick test method ", and 25 freeze thawing are passed through in measurement
(resistance to compression) loss of strength rate of test specimen after circulation;
1, it compression strength: is measured according to GB/T4111 standard;
2, it water retention: is measured according to NY/T1253-2006 " grass-planting brick " standard.
The results are shown in Table 1.
Table 1
Frost resistance/25 time Frozen-thawed cycled, loss of strength rate (%) | Compression strength/MPa | Water retention/% | |
Embodiment 1 | 6.3 | 43.8 | 34.6 |
Embodiment 2 | 5.9 | 48.9 | 35.2 |
Embodiment 3 | 6.2 | 46.2 | 33.8 |
Comparative example | 18.6 | 26.3 | 24.6 |
Compound grass-planting brick raw material prepared by the present invention has preferable water retention and preferable frost resistance in summary.
Claims (7)
1. a kind of preparation method of compound grass-planting brick raw material, which is characterized in that the preparation method includes the following steps:
(1) ooze, aluminium ash 4~6:3 in mass ratio are put into ball mill and carry out ball milling, collect ball milling object, by ball milling object, water,
Change waste residue material 7~9:10:3 in mass ratio~5 in advance and carry out ultrasonic vibration, stand, filters, it is dry, obtain base-material;
(2) base-material, hydrochloric acid 3:7~9 in mass ratio are stirred, add the additive of base-material 8~10%, carry out ultrasonic shake
It swings, stands, filter residue is collected in filtering;
(3) according to parts by weight, take 90~95 parts of water, 26~32 parts of filter residues, 13~15 parts of frerrous chlorides, 9~15 parts of sodium metasilicate,
8~13 parts of pretreatment plant straw powders, 3~8 parts of ammonium hydrogen carbonate, 2~4 parts of surfactants, 1~3 part of dispersing agent, 1~3 part
Auxiliary agent;
(4) water, filter residue, frerrous chloride, ammonium hydrogen carbonate are put into reactor first, microwave heating, place into surfactant,
Dispersing agent, auxiliary agent adjust pH to 8.0~8.5 using ammonium hydroxide, stir 60~80min, and pretreatment plant straw powder is added, stirs
30~35min is mixed, sodium metasilicate is added, is stirred, collects mixture, spray drying collects dried object to get compound grass-planting brick
Raw material.
2. the preparation method of compound grass-planting brick raw material according to claim 1, which is characterized in that change in advance in the step (1)
The preparation method of waste residue material is to be stirred dregs, blast furnace slag, iron filings by 7~9:4:1 of quality, is squeezed, and is crushed, and is sieved, will
Sieving particle, which is put into hydrogen peroxide, to be impregnated, and is filtered, and filter residue is collected, dry to get pre- modified waste material.
3. the preparation method of compound grass-planting brick raw material according to claim 1, which is characterized in that addition in the step (2)
Agent is to mix maleic anhydride, polyethyleneimine 1:3~5 in mass ratio.
4. the preparation method of compound grass-planting brick raw material according to claim 1, which is characterized in that the pretreatment straw
The preparation method of powder be by wheat stalk, corn stover by etc. mass mixings, crush, cross 200 meshes, by sieving particle and water
The mixing of 1:2 in mass ratio, steam blasting collect explosion object, filtering, by filter residue and drying to get pretreatment plant straw powder.
5. the preparation method of compound grass-planting brick raw material according to claim 1, which is characterized in that the surfactant is ten
Any one in dialkyl benzene sulfonic acids sodium, lauryl sodium sulfate.
6. the preparation method of compound grass-planting brick raw material according to claim 1, which is characterized in that the dispersing agent is stearic acid
Any one in sodium, magnesium stearate.
7. the preparation method of compound grass-planting brick raw material according to claim 1, which is characterized in that the auxiliary agent is gluconic acid
Any one in sodium, sodium tartrate.