CN109020201A - One kind is using scrap glass as glass made from raw material and its production technology - Google Patents
One kind is using scrap glass as glass made from raw material and its production technology Download PDFInfo
- Publication number
- CN109020201A CN109020201A CN201811054920.6A CN201811054920A CN109020201A CN 109020201 A CN109020201 A CN 109020201A CN 201811054920 A CN201811054920 A CN 201811054920A CN 109020201 A CN109020201 A CN 109020201A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- raw material
- scrap
- fluorite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention proposes one kind using scrap glass as glass made from raw material and its production technology, including following raw material: quartz sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, compound clarifier, colorant, fluxing agent, scrap glass, its each component mass ratio are as follows: 300.0-600.0 parts of quartz sand, 20.0-40.0 parts of lime stone, 80.0-150.0 parts of calcite, 100.0-200.0 parts of soda ash, 5.0-10.0 parts of saltcake, 30.0-60.0 parts of fluorite, 1.0-3.0 parts of carbon dust, 0.5-1.0 parts of compound clarifier, 1.0-2.0 parts of fluxing agent, 100.0-200.0 parts of scrap glass, the beneficial effects of the present invention are: first being preheated to raw material when being processed to glass, to The vapor contained in evaporated material, then glass is heated again, pulverization process has been carried out to material by pulverizer simultaneously, to expand the heating surface area of material, the required time for shortening heating thus reduces energy consumption, while joined the scrap glass of recycling in raw material, recycling and reusing has been carried out to resource, has avoided the waste of resource.
Description
Technical field
The present invention relates to field of glass production technology, and specially one kind is using scrap glass as glass made from raw material and its life
Production. art.
Background technique
Glass is to be fused together to be formed by silica and other chemical substances, forms contiguous network knot in melting
Structure, cooling procedure medium viscosity are gradually increased and harden the silicates nonmetallic materials for causing it to crystallize, the chemistry of simple glass
Composition is Na2SiO3, CaSiO3, SiO2 or Na2OCaO6SiO2 etc., and main component is silicate double salt, is a kind of random
The then non-crystalline solids of structure.
Since glass has, good crystalistic sense is good, pollution-free, fashion is strong, moulding is enriched, is widely used, low in cost
The characteristics of be widely used in building, although current has various glass making process on the market, there is add
Longer, the larger problem of power consumption the time required to when hot, and recycling and reusing can not be carried out to scrap glass, to cause
The waste of resource.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the existing defects, provides one kind using scrap glass as made from raw material
Glass and its production technology, the time required to shortening heating, so that energy consumption needed for reducing heating, can return cullet
It receives and recycles, avoid the waste of resource, can effectively solve the problems in background technique.
To achieve the above object, the present invention proposes: using scrap glass as glass made from raw material, including following raw material: stone
Sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, compound clarifier, colorant, fluxing agent, scrap glass, it is each
Constituent mass ratio are as follows: 300.0-600.0 parts of quartz sand, 20.0-40.0 parts of lime stone, 80.0-150.0 parts of calcite, soda ash
100.0-200.0 parts, 5.0-10.0 parts of saltcake, 30.0-60.0 parts of fluorite, 1.0-3.0 parts of carbon dust, compound clarifier 0.5-1.0
Part, 1.0-2.0 parts of fluxing agent, 100.0-200.0 parts of scrap glass.
As a preferred technical solution of the present invention: described quartz sand 350.0-550.0 parts, lime stone 25.0-35.0
Part, 100.0-140.0 parts of calcite, 120.0-180.0 parts of soda ash, 6.0-9.0 parts of saltcake, 35.0-55.0 parts of fluorite, carbon dust
1.5-2.5 parts, 0.6-0.9 parts of compound clarifier, 1.2-1.8 parts of fluxing agent, 120.0-180.0 parts of scrap glass.
As a preferred technical solution of the present invention: described quartz sand 400.0-500.0 parts, lime stone 28.0-32.0
Part, 120.0-140.0 parts of calcite, 140.0-160.0 parts of soda ash, 7.0-8.0 parts of saltcake, 40.0-50.0 parts of fluorite, carbon dust
1.8-2.2 parts, 0.7-0.8 parts of compound clarifier, 1.4-1.6 parts of fluxing agent, 140.0-160.0 parts of scrap glass.
The present invention also provides a kind of using scrap glass as the production technology of glass made from raw material: the following steps are included:
S1 it) stocks up: choosing quartz sand 400.0-500.0 parts, 28.0-32.0 parts of lime stone, calcite 120.0-140.0
Part, 140.0-160.0 parts of soda ash, 7.0-8.0 parts of saltcake, 40.0-50.0 parts of fluorite, 1.8-2.2 parts of carbon dust, compound clarifier
0.7-0.8 parts, 1.4-1.6 parts of fluxing agent, 140.0-160.0 parts of scrap glass；
S2 it) handles: quartz sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, scrap glass by crushing dress
Carry out pulverization process is set, mixed material is put into reaction kettle, is stirred by agitating device, to keep it sufficiently mixed
It closes, while material is heated to 100 DEG C -200 DEG C by heating equipment, while being stirred using corresponding mixing plant；
S3 it) processes: reaction kettle being heated by corresponding heating equipment, while compound clarifier and fluxing is added
Agent, heating temperature are set as 1300-1600 DEG C, to obtain glass solution；
S4) cooling: mold being heated to 500 DEG C -800 DEG C by heating equipment, glass solution is then poured into mold
In, it is then suppressed, so that glass be made, then carries out natural cooling again；
S5) cut: by corresponding glass cutting equipment by using demand to glass carry out cutting process.
Compared with prior art, the beneficial effects of the present invention are: first being preheated to raw material when being processed to glass,
To the vapor contained in evaporated material, then glass is heated again, while material is carried out by pulverizer
Pulverization process shortens the required time of heating to expand the heating surface area of material, thus reduces energy consumption, while former
The scrap glass that joined recycling in material has carried out recycling and reusing to resource, has avoided the waste of resource.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention the following technical schemes are provided:
Embodiment one: one kind is using scrap glass as glass made from raw material, including following raw material: quartz sand, lime stone, side
Xie Shi, soda ash, saltcake, fluorite, carbon dust, compound clarifier, colorant, fluxing agent, scrap glass, each component mass ratio are as follows:
350.0 parts of quartz sand, 24.0 parts of lime stone, 95.0 parts of calcite, 120.0 parts of soda ash, 6.0 parts of saltcake, 35.0 parts of fluorite, carbon
1.4 parts of powder, 0.6 part of compound clarifier, 1.2 parts of fluxing agent, 120.0 parts of scrap glass.
It is a kind of using scrap glass as the production technology of glass made from raw material, comprising the following steps:
S1 it) stocks up: choosing 350.0 parts of quartz sand, 24.0 parts of lime stone, 95.0 parts of calcite, 120.0 parts of soda ash, saltcake
6.0 parts, 35.0 parts of fluorite, 1.4 parts of carbon dust, 0.6 part of compound clarifier, 1.2 parts of fluxing agent, 120.0 parts of scrap glass；
S2 it) handles: quartz sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, scrap glass by crushing dress
Carry out pulverization process is set, mixed material is put into reaction kettle, is stirred by agitating device, to keep it sufficiently mixed
It closes, while material is heated to 100 DEG C -200 DEG C by heating equipment, while being stirred using corresponding mixing plant；
S3 it) processes: reaction kettle being heated by corresponding heating equipment, while compound clarifier and fluxing is added
Agent, heating temperature are set as 1300-1600 DEG C, to obtain glass solution；
S4) cooling: mold being heated to 500 DEG C -800 DEG C by heating equipment, glass solution is then poured into mold
In, it is then suppressed, so that glass be made, then carries out natural cooling again；
S5) cut: by corresponding glass cutting equipment by using demand to glass carry out cutting process.
Embodiment two: one kind is using scrap glass as glass made from raw material, including following raw material: quartz sand, lime stone, side
Xie Shi, soda ash, saltcake, fluorite, carbon dust, compound clarifier, colorant, fluxing agent, scrap glass, each component mass ratio are as follows:
400.0 parts of quartz sand, 28.0 parts of lime stone, 105.0 parts of calcite, 140.0 parts of soda ash, 7.0 parts of saltcake, 40.0 parts of fluorite, carbon
1.8 parts of powder, 0.7 part of compound clarifier, 1.4 parts of fluxing agent, 140.0 parts of scrap glass.
It is a kind of using scrap glass as the production technology of glass made from raw material, comprising the following steps:
S1 it) stocks up: choosing 400.0 parts of quartz sand, 28.0 parts of lime stone, 105.0 parts of calcite, 140.0 parts of soda ash, awns
7.0 parts of nitre, 40.0 parts of fluorite, 1.8 parts of carbon dust, 0.7 part of compound clarifier, 1.4 parts of fluxing agent, 140.0 parts of scrap glass；
S2 it) handles: quartz sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, scrap glass by crushing dress
Carry out pulverization process is set, mixed material is put into reaction kettle, is stirred by agitating device, to keep it sufficiently mixed
It closes, while material is heated to 100 DEG C -200 DEG C by heating equipment, while being stirred using corresponding mixing plant；
S3 it) processes: reaction kettle being heated by corresponding heating equipment, while compound clarifier and fluxing is added
Agent, heating temperature are set as 1300-1600 DEG C, to obtain glass solution；
S4) cooling: mold being heated to 500 DEG C -800 DEG C by heating equipment, glass solution is then poured into mold
In, it is then suppressed, so that glass be made, then carries out natural cooling again；
S5) cut: by corresponding glass cutting equipment by using demand to glass carry out cutting process.
Embodiment three: one kind is using scrap glass as glass made from raw material, including following raw material: quartz sand, lime stone, side
Xie Shi, soda ash, saltcake, fluorite, carbon dust, compound clarifier, colorant, fluxing agent, scrap glass, each component mass ratio are as follows:
450.0 parts of quartz sand, 32.0 parts of lime stone, 125.0 parts of calcite, 160.0 parts of soda ash, 8.0 parts of saltcake, 45.0 parts of fluorite, carbon
2.2 parts of powder, 0.8 part of compound clarifier, 1.6 parts of fluxing agent, 160.0 parts of scrap glass.
It is a kind of using scrap glass as the production technology of glass made from raw material, comprising the following steps:
S1 it) stocks up: choosing 450.0 parts of quartz sand, 32.0 parts of lime stone, 125.0 parts of calcite, 160.0 parts of soda ash, awns
8.0 parts of nitre, 45.0 parts of fluorite, 2.2 parts of carbon dust, 0.8 part of compound clarifier, 1.6 parts of fluxing agent, 160.0 parts of scrap glass；
S2 it) handles: quartz sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, scrap glass by crushing dress
Carry out pulverization process is set, mixed material is put into reaction kettle, is stirred by agitating device, to keep it sufficiently mixed
It closes, while material is heated to 100 DEG C -200 DEG C by heating equipment, while being stirred using corresponding mixing plant；
S3 it) processes: reaction kettle being heated by corresponding heating equipment, while compound clarifier and fluxing is added
Agent, heating temperature are set as 1300-1600 DEG C, to obtain glass solution；
S4) cooling: mold being heated to 500 DEG C -800 DEG C by heating equipment, glass solution is then poured into mold
In, it is then suppressed, so that glass be made, then carries out natural cooling again；
S5) cut: by corresponding glass cutting equipment by using demand to glass carry out cutting process.
Example IV: one kind is using scrap glass as glass made from raw material, including following raw material: quartz sand, lime stone, side
Xie Shi, soda ash, saltcake, fluorite, carbon dust, compound clarifier, colorant, fluxing agent, scrap glass, each component mass ratio are as follows:
500.0 parts of quartz sand, 36.0 parts of lime stone, 145.0 parts of calcite, 180.0 parts of soda ash, 9.0 parts of saltcake, 50.0 parts of fluorite, carbon
2.6 parts of powder, 0.9 part of compound clarifier, 1.9 parts of fluxing agent, 180.0 parts of scrap glass.
It is a kind of using scrap glass as the production technology of glass made from raw material, comprising the following steps:
S1 it) stocks up: choosing 500.0 parts of quartz sand, 36.0 parts of lime stone, 145.0 parts of calcite, 180.0 parts of soda ash, awns
9.0 parts of nitre, 50.0 parts of fluorite, 2.6 parts of carbon dust, 0.9 part of compound clarifier, 1.9 parts of fluxing agent, 180.0 parts of scrap glass；
S2 it) handles: quartz sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, scrap glass by crushing dress
Carry out pulverization process is set, mixed material is put into reaction kettle, is stirred by agitating device, to keep it sufficiently mixed
It closes, while material is heated to 100 DEG C -200 DEG C by heating equipment, while being stirred using corresponding mixing plant；
S3 it) processes: reaction kettle being heated by corresponding heating equipment, while compound clarifier and fluxing is added
Agent, heating temperature are set as 1300-1600 DEG C, to obtain glass solution；
S4) cooling: mold being heated to 500 DEG C -800 DEG C by heating equipment, glass solution is then poured into mold
In, it is then suppressed, so that glass be made, then carries out natural cooling again；
S5) cut: by corresponding glass cutting equipment by using demand to glass carry out cutting process.
Benefit of the present invention: it first carries out crushing when processing material and pre-add is heat-treated, to not only expand object
The heating surface area of material, while the moisture in material can be effectively removed, consequently facilitating the working process in later period, while addition has
Cosolvent, consequently facilitating the thawing of material, while recycling and reusing has been carried out to cullet, so as to avoid the waste of resource.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (4)
1. one kind is using scrap glass as glass made from raw material, including following raw material: quartz sand, lime stone, calcite, soda ash,
Saltcake, fluorite, carbon dust, compound clarifier, colorant, fluxing agent, scrap glass, it is characterised in that: its each component mass ratio are as follows:
300.0-600.0 parts of quartz sand, 20.0-40.0 parts of lime stone, 80.0-150.0 parts of calcite, 100.0-200.0 parts of soda ash, awns
5.0-10.0 parts of nitre, 30.0-60.0 parts of fluorite, 1.0-3.0 parts of carbon dust, 0.5-1.0 parts of compound clarifier, fluxing agent 1.0-2.0
Part, 100.0-200.0 parts of scrap glass.
2. one kind is using scrap glass as glass made from raw material, it is characterised in that: described quartz sand 350.0-550.0 parts, lime
25.0-35.0 parts of stone, 100.0-140.0 parts of calcite, 120.0-180.0 parts of soda ash, 6.0-9.0 parts of saltcake, fluorite 35.0-
55.0 parts, 1.5-2.5 parts of carbon dust, 0.6-0.9 parts of compound clarifier, 1.2-1.8 parts of fluxing agent, scrap glass 120.0-180.0
Part.
3. one kind is using scrap glass as glass made from raw material, it is characterised in that: described quartz sand 400.0-500.0 parts, lime
28.0-32.0 parts of stone, 120.0-140.0 parts of calcite, 140.0-160.0 parts of soda ash, 7.0-8.0 parts of saltcake, fluorite 40.0-
50.0 parts, 1.8-2.2 parts of carbon dust, 0.7-0.8 parts of compound clarifier, 1.4-1.6 parts of fluxing agent, scrap glass 140.0-160.0
Part.
4. a kind of using scrap glass as the production technology of glass made from raw material, it is characterised in that: the following steps are included:
S1) stock up: choose quartz sand 400.0-500.0 parts, it is 28.0-32.0 parts of lime stone, 120.0-140.0 parts of calcite, pure
140.0-160.0 parts of alkali, 7.0-8.0 parts of saltcake, 40.0-50.0 parts of fluorite, 1.8-2.2 parts of carbon dust, compound clarifier 0.7-0.8
Part, 1.4-1.6 parts of fluxing agent, 140.0-160.0 parts of scrap glass；
S2) handle: quartz sand, lime stone, calcite, soda ash, saltcake, fluorite, carbon dust, scrap glass pass through grinding device into
Row pulverization process is put into mixed material in reaction kettle, is stirred by agitating device, thus mix them thoroughly,
Material is heated to 100 DEG C -200 DEG C by heating equipment simultaneously, while being stirred using corresponding mixing plant；
S3 it) processes: reaction kettle being heated by corresponding heating equipment, while compound clarifier and fluxing agent is added,
Heating temperature is set as 1300-1600 DEG C, to obtain glass solution；
S4) cooling: mold being heated to 500 DEG C -800 DEG C by heating equipment, then glass solution is poured into mold, so
After suppressed, thus be made glass, then carry out natural cooling again；
S5) cut: by corresponding glass cutting equipment by using demand to glass carry out cutting process.