CN109011842A - A kind of filter cotton and preparation method thereof for high-speed EMUs PM2.5 air cleaning - Google Patents
A kind of filter cotton and preparation method thereof for high-speed EMUs PM2.5 air cleaning Download PDFInfo
- Publication number
- CN109011842A CN109011842A CN201810974930.5A CN201810974930A CN109011842A CN 109011842 A CN109011842 A CN 109011842A CN 201810974930 A CN201810974930 A CN 201810974930A CN 109011842 A CN109011842 A CN 109011842A
- Authority
- CN
- China
- Prior art keywords
- fibre
- fibre web
- acrylic fibers
- base fabric
- filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of filter cottons and preparation method thereof for high-speed EMUs PM2.5 air cleaning, it includes filter layer and PTFE film under composite fibre base fabric, acrylic fibers fibre web antimicrobial filtering layer, acrylic fibers fibre web, composite fibre base fabric is combined by antistatic cotton and polypropylene fibre, the upper surface of composite fibre base fabric is equipped with acrylic fibers fibre web antimicrobial filtering layer, and the lower surface of composite fibre base fabric is equipped with filter layer under acrylic fibers fibre web；The upper surface of the acrylic fibers fibre web antimicrobial filtering layer is covered with PTFE film；Specific preparation method is the material requirements bonding preparation according to each layer, and then naturally dry, cuts and product is made；The filtering material filter effect is good, can not only cross the dust and impurities in air filtering, and have and inhibit bacterial reproduction and deodorization, gas defence antibacterial functions.
Description
Technical field
The invention belongs to air filting material technical fields, and in particular to one kind is net for high-speed EMUs PM2.5 air
Filter cotton of change and preparation method thereof.
Background technique
In daily life and industrial production, haze mask application is very extensive, and people ensure incoming call gas using mask
The quality of body, human health is closely related with environmental quality, and the whole world has half population just by the threat of anaphylactogen, people at present
Live in rapid industrial development, the decline of air quality Japanese TV play, especially industry prosperity area air pollution level is usually than other
Area is higher by 2-5 times, and with the appearance and implementation of PM2.5 standard, people also increase to the understanding of fine particle, it is necessary to logical
It crosses effective filtering and removes these particles, could guarantee Green Travel, the physical and mental health of people.
Summary of the invention
It is provided the purpose of the present invention is overcome the deficiencies in the prior art a kind of for high-speed EMUs PM2.5 air cleaning
Filter cotton and preparation method thereof, which can not only cross the dust and impurities in air filtering, and has and inhibit bacterium numerous
It grows and deodorization, gas defence antibacterial functions.
In order to achieve the above object, the present invention adopts the following technical scheme:
The present invention provides a kind of filter cottons for high-speed EMUs PM2.5 air cleaning, it includes composite fibre base fabric, nitrile
Filter layer and PTFE film under synthetic fibre fibre web antimicrobial filtering layer, acrylic fibers fibre web, composite fibre base fabric are fine by antistatic cotton and polypropylene
Dimension is combined, and the upper surface of composite fibre base fabric is equipped with acrylic fibers fibre web antimicrobial filtering layer, and the lower surface of composite fibre base fabric is set
There is filter layer under acrylic fibers fibre web；The upper surface of the acrylic fibers fibre web antimicrobial filtering layer is covered with PTFE film.
According to the above-mentioned filter cotton for high-speed EMUs PM2.5 air cleaning, the antistatic cotton is anti-to be adsorbed with
The cotton fiber of electrostatic agent.
Filter cotton according to claim 1 for high-speed EMUs PM2.5 air cleaning, it is characterised in that described
Filter layer is fibre web made of being reinforced by way of spun lacing as the acrylic fiber Jing Guo graft modification under acrylic fibers fibre web.
According to the above-mentioned filter cotton for high-speed EMUs PM2.5 air cleaning, the acrylic fibers fibre web antimicrobial filtering layer
Using acrylic fiber as raw material, by pretreatment so that polyamines is reacted with the cyano on acrylic fiber, in grafting polyamino and its
He reacts the azacyclo- of generation.
According to the above-mentioned filter cotton for high-speed EMUs PM2.5 air cleaning, the fiber of the polypropylene fibre is straight
Diameter is 5-40nm.
According to the preparation method of the above-mentioned filter cotton for high-speed EMUs PM2.5 air cleaning, it includes following step
It is rapid:
(1), the preparation of composite fibre base fabric: first preparing antistatic cotton, then logical using antistatic cotton and polypropylene fibre fiber
The base fabric that the mode of spun lacing is woven into fibre web as composite filtering material is crossed,
(2), acrylic fibers fibre web antimicrobial filtering layer then is bonded in the upper surface of above-mentioned composite fibre base fabric, then in composite fibre base
Filter layer under the lower surface bonding acrylic fibers fibre web of cloth；Finally PTFE film is covered in the upper surface of acrylic fibers fibre web antimicrobial filtering layer；
(3), naturally dry cuts and product is made.
Compared with prior art, the present invention obtain the utility model has the advantages that
1, the composite fibre base fabric compression strength in material of the present invention is high, good corrosion resistance, and filtration resistance is small；Acrylic fibers in material
Fibre web antimicrobial filtering layer is, by special pre-treatment, the cyano on polyamines and acrylic fiber to occur using acrylic fiber as raw material
It reacts, polyamino reacts the functional groups such as the azacyclo- generated with other in grafting, these functional groups are to common Gram-positive
Bacterium, negative bacterium, fungi, anaerobic bacteria, pneumobacillus, staphylococcus aureus, Candida albicans etc. have stronger inhibitory or killing effect,
Modified acrylic fiber is fabricated to antimicrobial filtering layer, is entirely free of metal ion, safe to the human body harmless, antibacterial effect is held
Long, broad-spectrum high efficacy, it is environmentally protective and washable；PTFE film in the material can effectively filter dust.
2, material of the present invention can filter blocking haze, effective stealthy killer -- bacterial virus, automobile crossed in air filtering
Tail gas, secondhand smoke, formaldehyde, dust mite, haze, Volatile chemical, air pollution poison gas, barrier droplet, Fluids and secretions make
It is influenced with, the pellet as brought by vehicle exhaust, absorbs and filters pollution poison gas etc., be widely used in medical treatment and defend
Raw industry, public arena；The mask either filter efficiency, gas permeability, antibiotic property, safety etc. for changing material production are all big
Surmount common mask greatly.
Specific embodiment
Lower embodiment is to carry out detailed specific description to the content of present invention, but the contents of the present invention do not limit so.
Embodiment 1:
The present invention provides a kind of filter cottons for high-speed EMUs PM2.5 air cleaning, it includes composite fibre base fabric, nitrile
Filter layer and PTFE film under synthetic fibre fibre web antimicrobial filtering layer, acrylic fibers fibre web, composite fibre base fabric are fine by antistatic cotton and polypropylene
Dimension is combined, and the upper surface of composite fibre base fabric is equipped with acrylic fibers fibre web antimicrobial filtering layer, and the lower surface of composite fibre base fabric is set
There is filter layer under acrylic fibers fibre web；The upper surface of the acrylic fibers fibre web antimicrobial filtering layer is covered with PTFE film；The acrylic fibers fibre web is anti-
Bacterium filter layer makes polyamines react with the cyano on acrylic fiber using acrylic fiber as raw material, by pretreatment, more in grafting
Amino reacts the azacyclo- generated with other.
The preparation method of the above-mentioned filter cotton for high-speed EMUs PM2.5 air cleaning, it the following steps are included:
(1), the preparation of composite fibre base fabric: first preparing antistatic cotton, then logical using antistatic cotton and polypropylene fibre fiber
The base fabric that the mode of spun lacing is woven into fibre web as composite filtering material is crossed,
(2), acrylic fibers fibre web antimicrobial filtering layer then is bonded in the upper surface of above-mentioned composite fibre base fabric, then in composite fibre base
Filter layer under the lower surface bonding acrylic fibers fibre web of cloth；Finally PTFE film is covered in the upper surface of acrylic fibers fibre web antimicrobial filtering layer；
(3), naturally dry cuts and product is made.
Embodiment 2:
The present embodiment part same as Example 1 is no longer repeated, difference be the above-mentioned antistatic cotton be adsorbed with resist it is quiet
The cotton fiber of electric agent.
Embodiment 3:
The present embodiment part same as Example 1 is no longer repeated, and difference is under above-mentioned acrylic fibers fibre web that filter layer is by passing through
Fibre web made of the acrylic fiber of graft modification is reinforced by way of spun lacing.
Embodiment 3:
The present embodiment part same as Example 1 is no longer repeated, and difference is that the fibre diameter of above-mentioned polypropylene fibre is 5-
40nm。
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of filter cotton for high-speed EMUs PM2.5 air cleaning, it is characterised in that it includes composite fibre base fabric, nitrile
Filter layer and PTFE film under synthetic fibre fibre web antimicrobial filtering layer, acrylic fibers fibre web, composite fibre base fabric are fine by antistatic cotton and polypropylene
Dimension is combined, and the upper surface of composite fibre base fabric is equipped with acrylic fibers fibre web antimicrobial filtering layer, and the lower surface of composite fibre base fabric is set
There is filter layer under acrylic fibers fibre web；The upper surface of the acrylic fibers fibre web antimicrobial filtering layer is covered with PTFE film.
2. the filter cotton according to claim 1 for high-speed EMUs PM2.5 air cleaning, it is characterised in that described anti-
Electrostatic cotton is the cotton fiber for being adsorbed with antistatic agent.
3. the filter cotton according to claim 1 for high-speed EMUs PM2.5 air cleaning, it is characterised in that the nitrile
Filter layer is fibre web made of being reinforced by way of spun lacing as the acrylic fiber Jing Guo graft modification under synthetic fibre fibre web.
4. the filter cotton according to claim 1 for high-speed EMUs PM2.5 air cleaning, it is characterised in that the nitrile
Synthetic fibre fibre web antimicrobial filtering layer makes polyamines react with the cyano on acrylic fiber using acrylic fiber as raw material, by pretreatment,
Polyamino reacts the azacyclo- generated with other in grafting.
5. the filter cotton according to claim 2 for high-speed EMUs PM2.5 air cleaning, it is characterised in that described poly-
The fibre diameter of tacryl is 5-40nm.
6. the preparation method of the filter cotton according to claim 2 for high-speed EMUs PM2.5 air cleaning, feature
Be it the following steps are included:
(1) preparation of composite fibre base fabric: first preparing antistatic cotton, is then passed through using antistatic cotton and polypropylene fibre fiber
The mode of spun lacing is woven into base fabric of the fibre web as composite filtering material,
(2), acrylic fibers fibre web antimicrobial filtering layer then is bonded in the upper surface of above-mentioned composite fibre base fabric, then in composite fibre base
Filter layer under the lower surface bonding acrylic fibers fibre web of cloth；Finally PTFE film is covered in the upper surface of acrylic fibers fibre web antimicrobial filtering layer；
(3), naturally dry cuts and product is made.