CN109008092A - A kind of preparation method of Resisting fractre zipper - Google Patents
A kind of preparation method of Resisting fractre zipper Download PDFInfo
- Publication number
- CN109008092A CN109008092A CN201810561472.2A CN201810561472A CN109008092A CN 109008092 A CN109008092 A CN 109008092A CN 201810561472 A CN201810561472 A CN 201810561472A CN 109008092 A CN109008092 A CN 109008092A
- Authority
- CN
- China
- Prior art keywords
- chain
- preparation
- zipper
- resisting fractre
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of Resisting fractre zipper, which includes the following steps: a) selection ingredient, b) fuse process, c) cooling dilution processing, d) prepare chain, e) and finished product post-processing, f) finished product.By the above-mentioned means, preparation method process advantages of simple of the present invention, prepared composition is unique, cheap, and chain has high strong hardness, impact resistance, and Resisting fractre effectively extends the service life of zipper.
Description
Technical field
The present invention relates to zipper technology fields, more particularly to a kind of preparation method of Resisting fractre zipper.
Background technique
As the improvement of people's living standards, science and technology makes constant progress, zipper is initially from metal material to nonmetallic
Material, single variety simple function develop to the more specification comprehensive functions of multi items, beautiful by the exquisiteness of simple structure to today, and five
Yan Liuse, according to the common used material point of zipper, zipper can be divided into nylon zipper, resin teeth zipper and metal zip fastener three categories, metal
Zipper largely uses, and aluminium, copper, zinc is commonly copper zipper, but copper is at high cost, is eliminated therewith, and aluminium zipper is easy
Impaired fracture, processing technology is complicated, and intensity is also lower than copper, makes zipper using zinc alloy material currently on the market, but pulling force
It is not still very by force, without enough hardness, so that zipper is easily broken off under long-time use, to be unable to satisfy people to drawing
The use demand of chain.
Summary of the invention
The invention mainly solves the technical problem of providing a kind of preparation method of Resisting fractre zipper, the preparation method processes
Advantages of simple, prepared composition is unique, cheap, and chain has high strong hardness, impact resistance, and Resisting fractre effectively extends
The service life of zipper
In order to solve the above technical problems, one technical scheme adopted by the invention is that: a kind of preparation side of Resisting fractre zipper is provided
Method, the preparation method include the following steps: a) selection ingredient, b) fuse process, c) cooling dilution processing, d) prepare chain, e)
Finished product post-processing, f) finished product.
In a preferred embodiment of the present invention, the b) in step, first by high-carbon steel, composite fibre, albumen rubber
High melt synthesis is added in glue, hardening agent, auxiliary agent mixing, and for temperature at 120-220 DEG C, stirring speed per hour is 60~100 turns/min.
In a preferred embodiment of the present invention, the c) in step, stone is added in the chain solution of high melt synthesis
Wax powder, ethyl carbonate fine powder mixture are strengthened, and are diluted cooling 10 minutes addition auxiliary agents in the water that 1:2 is added and are solidified into
Type.
In a preferred embodiment of the present invention, the d) in step, the chain of injection molding cools down at normal temperature
40-50min。
In a preferred embodiment of the present invention, the e) in step, obtained molding chain be put into 40-50 DEG C again into
Row is reinforced, and 10min, taking-up removes undesired impurities with cold water wash, is put into drying box and dried, and carries out installation process.
The beneficial effects of the present invention are: a kind of preparation method of Resisting fractre zipper of the present invention, the preparation method process are simple
Rationally, prepared composition is unique, cheap, and chain has high strong hardness, and impact resistance effectively avoids zipper and uses long
The phenomenon that being easily broken off in the process.
Detailed description of the invention
The present invention will be further described in detail below with reference to the accompanying drawings and specific embodiments:
Fig. 1 is the preparation method process step diagram of Resisting fractre zipper of the embodiment of the present invention.
Specific embodiment
The preferred embodiments of the present invention will be described in detail with reference to the accompanying drawing, so that advantages and features of the invention energy
It is easier to be readily appreciated by one skilled in the art, so as to make a clearer definition of the protection scope of the present invention.
Fig. 1 is the preparation method block diagram of Resisting fractre zipper of the embodiment of the present invention: the preparation method includes the following steps: a)
Selection ingredient, b) fuse process, c) cooling dilution processing, d) prepare chain, e) and finished product post-processing, f) finished product.
Embodiment 1:
A kind of preparation method of Resisting fractre zipper of the present invention: a) selection ingredient, b) fuse process, c) cooling dilution processing, d) system
Standby chain, e) finished product post-processing, f) finished product, in the step a), the chain of zipper, pull head, base band, chain and pull head are adopted
With alloy material, base band is anti-fracture synthetic fibres, the main component of chain are as follows: high-carbon steel, composite fibre, and albumen rubber,
Hardening agent, auxiliary agent；Composite fibre is polystyrene fiber and glass fibre is mixed and made into fiber, and hardening agent is paraffin powder, carbonic acid
Ethyl ester fine powder mixture, auxiliary agent are formed by release agent nitrogen peroxide, paraffin oil, polystyrene sodium carbonate or by curing agent reinforcing,
The b) in step, first by high-carbon steel, composite fibre, albumen rubber, hardening agent, auxiliary agent mixing is added high melt and closes
At temperature is at 120 DEG C, and stirring speed per hour is in 60 turns/min, the c) step, stone is added in the chain solution of high melt synthesis
Wax powder, ethyl carbonate fine powder mixture are strengthened, and are diluted cooling 10 minutes addition auxiliary agents in the water that 1:2 is added and are solidified into
Type, the d) in step, the chain of injection molding cools down 40min, the e at normal temperature) and in step, obtained molding
Chain is put into 40 DEG C and is reinforced again, and 10min, taking-up removes undesired impurities with cold water wash, is put into drying box and is dried, and carries out
Installation process.
Embodiment 2:
A kind of preparation method of Resisting fractre zipper of the present invention: a) selection ingredient, b) fuse process, c) cooling dilution processing, d) system
Standby chain, e) finished product post-processing, f) finished product, in the step a), the chain of zipper, pull head, base band, chain and pull head are adopted
With alloy material, base band is anti-fracture synthetic fibres, the main component of chain are as follows: high-carbon steel, composite fibre, and albumen rubber,
Hardening agent, auxiliary agent；Composite fibre is polystyrene fiber and glass fibre is mixed and made into fiber, and hardening agent is paraffin powder, carbonic acid
Ethyl ester fine powder mixture, auxiliary agent are formed by release agent nitrogen peroxide, paraffin oil, polystyrene sodium carbonate or by curing agent reinforcing,
The b) in step, first by high-carbon steel, composite fibre, albumen rubber, hardening agent, auxiliary agent mixing is added high melt and closes
At temperature is at 220 DEG C, and stirring speed per hour is in 100 turns/min, the c) step, the chain solution of high melt synthesis is added
Paraffin powder, ethyl carbonate fine powder mixture are strengthened, and it is solid to be diluted cooling 10 minutes addition auxiliary agents in the water that 1::2 is added
Chemical conversion type, the d) in step, the chain of injection molding cools down 50min, the e at normal temperature) in step, obtain
Molding chain is put into 50 DEG C and is reinforced again, and 10min, taking-up removes undesired impurities with cold water wash, is put into drying box and is dried,
Carry out installation process.
Embodiment 3:
A kind of preparation method of Resisting fractre zipper of the present invention: a) selection ingredient, b) fuse process, c) cooling dilution processing, d) system
Standby chain, e) finished product post-processing, f) finished product, in the step a), the chain of zipper, pull head, base band, chain and pull head are adopted
With alloy material, base band is anti-fracture synthetic fibres, the main component of chain are as follows: high-carbon steel, composite fibre, and albumen rubber,
Hardening agent, auxiliary agent；Composite fibre is polystyrene fiber and glass fibre is mixed and made into fiber, and hardening agent is paraffin powder, carbonic acid
Ethyl ester fine powder mixture, auxiliary agent are formed by release agent nitrogen peroxide, paraffin oil, polystyrene sodium carbonate or by curing agent reinforcing,
The b) in step, first by high-carbon steel, composite fibre, albumen rubber, hardening agent, auxiliary agent mixing is added high melt and closes
At temperature is at 160 DEG C, and stirring speed per hour is in 80 turns/min, the c) step, stone is added in the chain solution of high melt synthesis
Wax powder, ethyl carbonate fine powder mixture are strengthened, and are diluted addition auxiliary agent solidification in cooling 10 minutes in the water that 1::2 is added
Molding, the d) in step, the chain of injection molding cools down 45min, the e at normal temperature) in step, obtain at
Type chain is put into 46 DEG C and is reinforced again, and 10min, taking-up removes undesired impurities with cold water wash, is put into drying box and is dried, into
Row installation process.
It is different from the prior art, preparation method process advantages of simple of the present invention, prepared composition is unique, cheap, chain
With high strong hardness, impact resistance, Resisting fractre effectively extends the service life of zipper.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification and accompanying drawing content is applied directly or indirectly in other relevant skills
Art field, is included within the scope of the present invention.
Claims (6)
1. a kind of preparation method of Resisting fractre zipper, which is characterized in that the preparation method includes the following steps: a) selection ingredient,
B) fuse process, c) cooling dilution processing, d) prepare chain, e) and finished product post-processing, f) finished product.
2. the preparation method of Resisting fractre zipper according to claim 1, which is characterized in that in the step a), zipper
Chain, pull head, base band, chain and pull head be all made of alloy material, and base band is anti-fracture synthetic fibres, chain it is main at
It is divided into: high-carbon steel, composite fibre, albumen rubber, hardening agent, auxiliary agent；Composite fibre is that polystyrene fiber and glass fibre are mixed
Fiber is made in conjunction, and hardening agent is paraffin powder, and ethyl carbonate fine powder mixture, auxiliary agent is by release agent nitrogen peroxide, paraffin oil, polyphenyl
Ethylene sodium carbonate is made of curing agent reinforcing.
3. the preparation method of Resisting fractre zipper according to claim 1, which is characterized in that the b) in step, first
By high-carbon steel, composite fibre, albumen rubber, hardening agent, auxiliary agent, which mixes, is added high melt synthesis, and temperature is stirred at 120-220 DEG C
Mixing speed per hour is 60~100 turns/min.
4. the preparation method of Resisting fractre zipper according to claim 1, which is characterized in that the c) in step, high temperature
Paraffin powder is added in the chain solution of melting synthesis, and ethyl carbonate fine powder mixture is strengthened, and is diluted in the water that 1:2 is added
Cooling 10 minutes addition auxiliary agent curing moldings.
5. the preparation method of Resisting fractre zipper according to claim 1, which is characterized in that the d) in step, injection molding
Molding chain cools down 40-50min at normal temperature.
6. the preparation method of Resisting fractre zipper according to claim 1, which is characterized in that the e) in step, obtain
Molding chain be put into 40-50 DEG C and reinforced again, 10min, taking-up removes undesired impurities with cold water wash, is put into drying box progress
Drying carries out installation process.