CN108997930A - A kind of processing technology of polychrome colorful noctilucence wheel - Google Patents
A kind of processing technology of polychrome colorful noctilucence wheel Download PDFInfo
- Publication number
- CN108997930A CN108997930A CN201810858842.9A CN201810858842A CN108997930A CN 108997930 A CN108997930 A CN 108997930A CN 201810858842 A CN201810858842 A CN 201810858842A CN 108997930 A CN108997930 A CN 108997930A
- Authority
- CN
- China
- Prior art keywords
- colorful
- polychrome
- processing technology
- paint
- spray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of processing technology of polychrome colorful noctilucence wheel, is related to wheel processing technology field, it is characterised in that include the following steps: pretreatment cleaning;Spray bottom powder;Diameter is added in priming paint and/or set colored paint after mixing in the photo-induced energy storage luminescent powder of 50-500nm and protection sealer and is uniformly mixed;Primer spray;Spray set colored paint;Spray transparent powder.Present invention process is simple, low in cost, in the insufficient environment of light can self-luminescence, colorful effect do not influenced by light intensity, and has alarm function.
Description
Technical field
The present invention relates to wheel processing technology field, elaborating is a kind of simple process and low cost, inadequate in light
Environment in can self-luminescence, colorful effect do not influenced by light intensity, and the polychrome colorful noctilucence vehicle with alarm function
The processing technology of wheel.
Background technique
It is known that existing aluminum-alloy wheel processing technology includes full coating process, the bright technique of vehicle, polychrome full coat dress work
Skill and polychrome smart car technique etc., it includes: that (degrease pretreatment cleaning oxide skin, using chromium-free deactivation that full coat, which fills processing step,
Technique) → spray bottom powder (170-180 DEG C of baking-curing temperature, curing time 20-25 minute) → color spray paint, varnish (paints and wet touches
Wet spray, 140-150 DEG C of baking-curing temperature, curing time 15-20 minute) → spray transparent powder (spraying crylic acid resin powder
End, 170-180 DEG C of baking-curing temperature, curing time 20-25 minute) or the colored varnish (spraying crylic acid resin paint, baking
140-150 DEG C of solidification temperature, curing time 15-20 minute) and etc..
The step of vehicle bright technique be in full coat dress processing step spray transparent powder or colored varnish step before CNC finishing is added
Work step finishes (revolving speed 1000-1500s/min, amount of feeding 0.15- to wheel surface turning using numerically controlled lathe suddenly
0.25mm/r), make the gloss and texture that show metal at CNC finishing.
Polychrome full coat dress processing step include: pretreatment cleaning (degrease oxide skin, using non-chromium inactivating technique) →
Spray bottom powder (170-180 DEG C of baking-curing temperature, curing time 20-25 minute) → color spray paint, varnish (definition wheel domain color,
140-150 DEG C of baking-curing temperature, curing time 15-20 minute) → spray set colored paint (according to spoke number can choose spray
Red, orange, yellow, green, blue, blue, purple, white, multiple color paint, the increase a variety of different colours of wheel, baking-curing temperature 140-150
DEG C, curing time 15-20 minute) → spray transparent powder (spraying crylic acid resin powder, 170-180 DEG C of baking-curing temperature, Gu
Change time 20-25 minutes).
The step of polychrome smart car technique is that CNC finishing is added before the spray transparent powder step in polychrome full coat dress processing step
Work step is rapid, i.e., finishes (revolving speed 1000-1500s/min, amount of feeding 0.15- to wheel surface turning using numerically controlled lathe
0.25mm/r), make the gloss and texture that show metal at CNC finishing.
The polychrome wheel of existing wheel processing technology manufacture only adapts to use in bright and clear environment, in night or light
When in inadequate environment (the at dusk, bad weather such as rainy day or greasy weather), the colorful effect of polychrome wheel substantially reduces, even disappears.
Summary of the invention
Present invention aim to address above-mentioned the deficiencies in the prior art, a kind of simple process and low cost are provided, in light
In insufficient environment can self-luminescence, colorful effect do not influenced by light intensity, and the polychrome colorful with alarm function
The processing technology of noctilucence wheel.
The present invention solves technical solution used by above-mentioned the deficiencies in the prior art:
A kind of processing technology of polychrome colorful noctilucence wheel, it is characterised in that include the following steps:
A, pretreatment cleaning;
B, bottom powder is sprayed;
C, diameter is added to priming paint and/or set in the photo-induced energy storage luminescent powder of 50-500nm and protection sealer after mixing
It is uniformly mixed in colored paint;
D, primer spray;
E, spray set colored paint;
F, transparent powder is sprayed.
CNC finishing step is added the in the present invention between step e and f step.That is: using numerically controlled lathe to the table of wheel
Face locally carries out turning finishing, makes to show metallic luster texture at turning finishing;Revolving speed 1000-1500s/min, the amount of feeding
0.15-0.25mm/r。
Heretofore described protection sealer is mixed by the raw material of following proportion by weight: 45-55 parts of silicon tree
Rouge, 15-25 parts of amino resins, 8-15 parts of polyurethane, 1-10 parts of fluotitanate, fluozirconate, the mixture of boric acid, 5-
10 parts of auxiliary agent.Fluotitanate, fluozirconate, boric acid mixture in containing fluotitanate, fluozirconate, boric acid mass ratio
For 1-3:1-3:1-3, preferably 1:1:1.Auxiliary agent by mass ratio be 1-5:1-5:1-5:1-5 prevent precipitating anti-settling agent, prevent
Dispersing agent, inhibitor (also known as retarder) and the antioxidant composition of conglomeration, preferably 1:1:1:1.
Silicone resin selects thermosetting acrylic resin, has certain functional group in structure, passes through and add in painting
Functional group reactions in amino resins, polyurethane for entering etc. form reticular structure, and the general relative molecular weight of thermosetting resin is lower.
Thermosetting acrylic coating have excellent richness, gloss, hardness, solvent resistance, weatherability, in high-temperature baking it is non-discolouring,
Not brightness reversion.Most important application is that amino-acrylonitrile acid baking vanish is made with amino resins cooperation.
Protect sealer under higher baking temperature, zirconium, titanium, etc. compounds polymerization reaction formed siloxanes covalent bond (si-
O-me), completion paint molecules align is discontinuous, make the molecule of photo-induced energy storage luminescent powder with paint it is closer in conjunction with molecule,
More regular when levelling, it is evenly distributed that siloxanes covalent bond orients paint and photo-induced energy storage luminescent powder molecule head and the tail, improves paint
The uniformity of construction.Protect sealer that there is good protective separation, when transparent bisque or chromatography paint layer are partially damaged
When can prevent the further diffusion of corrosive water, rainwater, salt water etc., prevent corrosion from accelerating and aggravation, improve the superposition of overbrushing interlayer
Mutual binding force, increase adhesive force and corrosion resistance;Solve layered coating superposition, repeatedly baking in prior art
Caused by coating adhesion, corrosion resistance is poor, is not suitable for the defect of large quantities of volume productions, the quality requirement for meeting client.
Heretofore described spray covers colored paint step, is then to dry the paint of spraying different colours on different spokes
Roasting solidification.It is several in the multiple colors such as red, orange, yellow, green, ultramarine, purple, white paint according to how much selections of spoke when processing
Or all, after the paint that different colours are sprayed on every spoke, baking-curing.
The color of heretofore described bottom powder and/or priming paint is preferably dark, and black is optimal selection, black absorption luminous energy
Dose-effect fruit is good, and black matrix powder and black backing varnish are optimal combinations, can lay in more luminous energy, when continuing the noctilucent function of wheel
Between be up to ten a few houres.
Colorful wheel prepared by the present invention is in night or light weak environment in use, photo-induced energy storage luminescent powder is by white
The energy storage of its illumination shines, and wheel is made to issue colorful light in night or rather dark environment, during vehicle wheel rotation still
The scene of polychrome illusion-colour can be generated, effect is not influenced by light intensity, and it is sustainable to shine more than ten hour, and do not need to consume
Electric energy and the other components of connection, structure is simple, low in cost.At night or in the weak environment of light, vehicle driving or it is parked in
When roadside, vehicular traffic and passerby can be reminded note that at the first time discovery play a warning role, can also in narrow crossing meeting
Obvious reference, pre- Anti-scratching are provided for two vehicle distances.
Specific embodiment
A kind of processing technology of polychrome colorful noctilucence wheel, it is characterised in that include the following steps:
Pretreatment cleaning: polishing to rough machined wheel semi-finished product, after the refine processing such as finishing, select pickling, alkali cleaning, etc.
The methods of ion washing is thoroughly cleaned and is dried to the greasy dirt and cutting fluid draff of product surface, and pre-treatment medicament is reused
Processing is passivated using non-chromium inactivating technique, one layer of fine and close passivating film is formed in aluminum-alloy wheel body surface, increases aluminium
The binding force of alloy base material and coating;
Spray bottom powder: electrostatic bottom powder coating is uniformly sprayed to the aluminum-alloy wheel surface after passivation using static powder gun, coating exists
Uniform adsorption can according to need selection color in wheel surface, bottom powder coating under electrostatic interaction, and preferably dark or black absorbs
Light energy effect is good;Through 170-180 DEG C baking-curing 20-25 minutes, make bottom powder coating solidification, protection substrate, improve it is anticorrosive
Performance.
Diameter is added to priming paint and set in the photo-induced energy storage luminescent powder of 50-500nm and protection sealer after mixing
It is uniformly mixed in colored paint;
Jet background paint: using style electro static spray gun, sprays to the aluminum-alloy wheel surface with bottom powder coating layer
It is added to photo-induced energy storage luminescent powder and protects the priming paint of sealer, paint nature levelling, the color of priming paint is wheel color
Dominant hue can be grey paint or other dark color paint, and preferably black base coat, black absorption light energy effect are good.140
It is toasted 15-20 minutes at~150 DEG C;After solidification background color lacquer coat with a thickness of 40-80 μm, bonding be adsorbed on bottom bisque protection apply
Layer.
Spray set colored paint: putting after protecting tool set-up blocks spray set colored paint, according to the number of spoke select red, orange, yellow, green, ultramarine,
Several or whole in the multiple colors paint such as purple, white, different colours are sprayed on every spoke is added to photo-induced energy storage night
After the set colored paint of light powder and protection sealer, baking-curing 15-20 minutes at 140-150 DEG C.
It sprays transparent powder: spraying transparent powder in wheel surface, transparent powder uses crylic acid resin powder, at 170-180 DEG C
Lower baking-curing 20-25 minutes
CNC finishing step is added the in the present invention between step e and f step.That is: using numerically controlled lathe to the surface office of wheel
Portion carries out turning finishing, makes to show metallic luster texture at turning finishing;Revolving speed 1000-1500s/min, the amount of feeding
0.15-0.25mm/r。
Heretofore described protection sealer is mixed by the raw material of following proportion by weight: 50 parts of silicone resin,
20 parts of amino resins, 1 part of polyurethane, 6 parts of fluotitanate, fluozirconate, the mixture of boric acid, 8 parts of auxiliary agent.Fluorine
Titanate, fluozirconate, boric acid mixture in the mass ratio containing fluotitanate, fluozirconate, boric acid be 1:1:1.Auxiliary agent by
Mass ratio prevents the anti-settling agent precipitated, dispersing agent, inhibitor (also known as retarder) and the antioxygen for preventing conglomeration for 1:1:1:1's
Agent composition.
Silicone resin selects thermosetting acrylic resin, has certain functional group in structure, passes through and add in painting
Functional group reactions in amino resins, polyurethane for entering etc. form reticular structure, and the general relative molecular weight of thermosetting resin is lower.
Thermosetting acrylic coating have excellent richness, gloss, hardness, solvent resistance, weatherability, in high-temperature baking it is non-discolouring,
Not brightness reversion.Most important application is that amino-acrylonitrile acid baking vanish is made with amino resins cooperation.
Protect sealer under higher baking temperature, zirconium, titanium, etc. compounds polymerization reaction formed siloxanes covalent bond (si-
O-me), completion paint molecules align is discontinuous, make the molecule of photo-induced energy storage luminescent powder with paint it is closer in conjunction with molecule,
More regular when levelling, it is evenly distributed that siloxanes covalent bond orients paint and photo-induced energy storage luminescent powder molecule head and the tail, improves paint
The uniformity of construction.Protect sealer that there is good protective separation, when transparent bisque or chromatography paint layer are partially damaged
When can prevent the further diffusion of corrosive water, rainwater, salt water etc., prevent corrosion from accelerating and aggravation, improve the superposition of overbrushing interlayer
Mutual binding force, increase adhesive force and corrosion resistance;Solve layered coating superposition, repeatedly baking in prior art
Caused by coating adhesion, corrosion resistance is poor, is not suitable for the defect of large quantities of volume productions, the quality requirement for meeting client.
Heretofore described spray covers colored paint step, is then to dry the paint of spraying different colours on different spokes
Roasting solidification.It is several in the multiple colors such as red, orange, yellow, green, ultramarine, purple, white paint according to how much selections of spoke when processing
Or all, after the paint that different colours are sprayed on every spoke, baking-curing.
The color of heretofore described priming paint and/or set colored paint is preferably dark, and black is optimal selection, black absorption light
Energy effect is good, and black matrix powder and black backing varnish are optimal combinations, can lay in more luminous energy, continues the noctilucent function of wheel
Time was up to for ten a few houres.
Colorful wheel prepared by the present invention is in night or light weak environment in use, photo-induced energy storage luminescent powder is by white
The energy storage of its illumination shines, and wheel is made to issue colorful light in night or rather dark environment, during vehicle wheel rotation still
The scene of polychrome illusion-colour can be generated, effect is not influenced by light intensity, and it is sustainable to shine more than ten hour, and do not need to consume
Electric energy and the other components of connection, structure is simple, low in cost.At night or in the weak environment of light, vehicle driving or it is parked in
When roadside, vehicular traffic and passerby can be reminded note that at the first time discovery play a warning role, can also in narrow crossing meeting
Obvious reference, pre- Anti-scratching are provided for two vehicle distances.
Claims (5)
1. a kind of processing technology of polychrome colorful noctilucence wheel, it is characterised in that include the following steps:
A, pretreatment cleaning;
B, bottom powder is sprayed;
C, diameter is added to priming paint and/or set in the photo-induced energy storage luminescent powder of 50-500nm and protection sealer after mixing
It is uniformly mixed in colored paint;
D, primer spray;
E, spray set colored paint;
F, transparent powder is sprayed.
2. the processing technology of polychrome colorful noctilucence wheel according to claim 1, it is characterised in that in step e and f
CNC finishing step is added between step.
3. the processing technology of polychrome colorful noctilucence wheel according to claim 1 or 2, it is characterised in that the protection envelope
It closes agent to be mixed by the raw material of following proportion by weight: 45-55 parts of silicone resin, 15-25 parts of amino resins, 8-15 parts
Polyurethane, 1-10 parts of fluotitanate, fluozirconate, the mixture of boric acid, 5-10 parts of auxiliary agent.
4. the processing technology of polychrome colorful noctilucence wheel according to claim 3, it is characterised in that the spray covers colored paint
Step is that the paint of different colours, then baking-curing will be sprayed on different spokes.
5. the processing technology of polychrome colorful noctilucence wheel according to claim 3, it is characterised in that the face of the priming paint
Color is black.