CN108997796A - A kind of preparation method of architectural latex coating - Google Patents
A kind of preparation method of architectural latex coating Download PDFInfo
- Publication number
- CN108997796A CN108997796A CN201810724045.1A CN201810724045A CN108997796A CN 108997796 A CN108997796 A CN 108997796A CN 201810724045 A CN201810724045 A CN 201810724045A CN 108997796 A CN108997796 A CN 108997796A
- Authority
- CN
- China
- Prior art keywords
- parts
- weighed
- added
- latex coating
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of architectural latex coating, comprise the following steps that (1) weighs following each component: bentonite, titanium dioxide, coarse whiting, cellulose, talcum powder, Kathon CG, butyl titanate, mica powder and zinc oxide respectively;(2) weighed bentonite, titanium dioxide and coarse whiting are added to the water, carry out ultrasonic high speed dispersion, obtains the first mixture;(3) weighed cellulose, talcum powder and Kathon CG are added to the water, after mixing evenly, pour into sand mill and grind, obtain the second mixture;(4) first is mixed to join in the second mixture, stir process obtains mixing;(5) weighed butyl titanate, mica powder and zinc oxide is added to mixing again, continues to stir 4-5h, obtains semi-finished product;(6) semi-finished product are sent into infrared electric-heating dehydration furnace and carry out dehydration concentration, heating time, 5min was to get architectural latex coating.The emulsion paint has effectively purified indoor air, improves environmental quality, is beneficial to the health of human body.
Description
Technical field
The present invention relates to the field of building materials, and in particular to a kind of preparation method of architectural latex coating.
Background technique
With the improvement of people's life quality, house decoration increasingly obtains the attention of people, emulsion paint is house decoration
In indispensable material, existing emulsion paint moisture-proof function is poor, in south China especially Guangxi annual March to April
Between it is overcast and rainy constantly air humidity is big, often will appear the droplet or flowing water of cohesion on the family brush wall of emulsion paint, not only make
The mouldy damage of the not pleasant Damage by Short Circuit for also causing household electrical appliance and household supplies, furniture of adult body, therefore one kind is provided
The problem of nontoxic, caking ability is by force and the emulsion paint of environment protection damp-proof is those skilled in the art's urgent need to resolve.
Summary of the invention
In conclusion in order to overcome the deficiencies of the prior art, technical problem to be solved by the invention is to provide a kind of buildings
The preparation method of emulsion paint.
The technical scheme to solve the above technical problems is that a kind of preparation method of architectural latex coating, including such as
Under step:
(1) each component of following parts by weight is weighed respectively: 5-11 parts of bentonite, 2-7 parts of titanium dioxide, 6-9 parts of coarse whiting, fine
1-3 parts of element of dimension, 4-8 parts of talcum powder, 3-5 parts of Kathon CG, 7-12 parts of butyl titanate, 6-9 parts and zinc oxide 2-4 parts of mica powder;
(2) weighed bentonite, titanium dioxide and coarse whiting are added to the water, carry out ultrasonic high speed dispersion, obtains the first mixing
Object;
(3) weighed cellulose, talcum powder and Kathon CG are added to the water, after mixing evenly, pour into sand mill and grind, obtains
To the second mixture;
(4) first is mixed to join in the second mixture, stir process obtains mixing;
(5) weighed butyl titanate, mica powder and zinc oxide is added to mixing again, continues to stir 4-5h, obtains semi-finished product;
(6) semi-finished product are sent into infrared electric-heating dehydration furnace and carry out dehydration concentration, heating time 5min is to get building
Build emulsion paint.
The beneficial effects of the present invention are: the emulsion paint not only can solve, existing emulsion paint moisture-proof function is poor to be asked
Topic, moreover it is possible to make wall keep drying, effectively purify indoor air, improved environmental quality, be beneficial to the health of human body.
Based on the above technical solution, the present invention can also be improved as follows:
Further, ultrasonic frequency is 20-40KHz, rate of dispersion 4000-4500r/min, jitter time in step (2)
For 30-45min.
Further, grinding temperature is 30-35 DEG C, revolving speed 1300-1500rpm in step (3), is discharged after grinding 3-4h.
Further, stir process 2-3h in step (4), controlling whipping temp in bucket is 45-50 DEG C.
Specific embodiment
Principles and features of the present invention are described below in conjunction with specific implementation, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
Embodiment one
A kind of preparation method of architectural latex coating, comprises the following steps that
(1) each component of following parts by weight is weighed respectively: 5 parts of bentonite, 2 parts of titanium dioxide, 6 parts of coarse whiting, cellulose 1
Part, 4 parts of talcum powder, 3 parts of Kathon CG, 7 parts of butyl titanate, 6 parts and 2 parts of zinc oxide of mica powder;
(2) weighed bentonite, titanium dioxide and coarse whiting are added to the water, carry out ultrasonic high speed dispersion, ultrasonic frequency is
20KHz, rate of dispersion 4000r/min, jitter time 30min obtain the first mixture;
(3) weighed cellulose, talcum powder and Kathon CG are added to the water, after mixing evenly, pour into sand mill and grind, grinds
Grinding temperature is 30 DEG C, revolving speed 1300rpm, discharges after grinding 3h, obtains the second mixture;
(4) first is mixed to join in the second mixture, stir process 2h, controlling whipping temp in bucket is 45 DEG C, is obtained
To mixing;
(5) weighed butyl titanate, mica powder and zinc oxide is added to mixing again, continues to stir 4h, obtains semi-finished product;
(6) semi-finished product are sent into infrared electric-heating dehydration furnace and carry out dehydration concentration, heating time 5min is to get building
Build emulsion paint.
Embodiment two
A kind of preparation method of architectural latex coating, comprises the following steps that
(1) each component of following parts by weight is weighed respectively: 8 parts of bentonite, 5 parts of titanium dioxide, 8 parts of coarse whiting, cellulose 2
Part, 6 parts of talcum powder, 4 parts of Kathon CG, 9 parts of butyl titanate, 8 parts and 3 parts of zinc oxide of mica powder;
(2) weighed bentonite, titanium dioxide and coarse whiting are added to the water, carry out ultrasonic high speed dispersion, ultrasonic frequency is
30KHz, rate of dispersion 4200r/min, jitter time 40min obtain the first mixture;
(3) weighed cellulose, talcum powder and Kathon CG are added to the water, after mixing evenly, pour into sand mill and grind, grinds
Grinding temperature is 33 DEG C, revolving speed 1400rpm, discharges after grinding 3.5h, obtains the second mixture;
(4) first is mixed to join in the second mixture, stir process 2.5h, controlling whipping temp in bucket is 48 DEG C,
Obtain mixing;
(5) weighed butyl titanate, mica powder and zinc oxide is added to mixing again, continues to stir 4.5h, obtains semi-finished product;
(6) semi-finished product are sent into infrared electric-heating dehydration furnace and carry out dehydration concentration, heating time 5min is to get building
Build emulsion paint.
Embodiment three
A kind of preparation method of architectural latex coating, comprises the following steps that
(1) each component of following parts by weight is weighed respectively: 11 parts of bentonite, 7 parts of titanium dioxide, 9 parts of coarse whiting, cellulose 3
Part, 8 parts of talcum powder, 5 parts of Kathon CG, 12 parts of butyl titanate, 9 parts and 4 parts of zinc oxide of mica powder;
(2) weighed bentonite, titanium dioxide and coarse whiting are added to the water, carry out ultrasonic high speed dispersion, ultrasonic frequency is
40KHz, rate of dispersion 4500r/min, jitter time 45min obtain the first mixture;
(3) weighed cellulose, talcum powder and Kathon CG are added to the water, after mixing evenly, pour into sand mill and grind, grinds
Grinding temperature is 35 DEG C, revolving speed 1500rpm, discharges after grinding 4h, obtains the second mixture;
(4) first is mixed to join in the second mixture, stir process 3h, controlling whipping temp in bucket is 45-50 DEG C,
Obtain mixing;
(5) weighed butyl titanate, mica powder and zinc oxide is added to mixing again, continues to stir 5h, obtains semi-finished product;
(6) semi-finished product are sent into infrared electric-heating dehydration furnace and carry out dehydration concentration, heating time 5min is to get building
Build emulsion paint.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (4)
1. a kind of preparation method of architectural latex coating, which is characterized in that comprise the following steps that
(1) each component of following parts by weight is weighed respectively: 5-11 parts of bentonite, 2-7 parts of titanium dioxide, 6-9 parts of coarse whiting, cellulose
1-3 parts, 4-8 parts of talcum powder, 3-5 parts of Kathon CG, 7-12 parts of butyl titanate, 6-9 parts and zinc oxide 2-4 parts of mica powder;
(2) weighed bentonite, titanium dioxide and coarse whiting are added to the water, carry out ultrasonic high speed dispersion, obtains the first mixture;
(3) weighed cellulose, talcum powder and Kathon CG are added to the water, after mixing evenly, pour into sand mill and grind, obtain
Two mixtures;
(4) first is mixed to join in the second mixture, stir process obtains mixing;
(5) weighed butyl titanate, mica powder and zinc oxide is added to mixing again, continues to stir 4-5h, obtains semi-finished product;
(6) semi-finished product are sent into infrared electric-heating dehydration furnace and carry out dehydration concentration, heating time 5mi, n was to get building
Emulsion paint.
2. the preparation method of architectural latex coating according to claim 1, which is characterized in that ultrasonic frequency in step (2)
For 20-40KHz, rate of dispersion 4000-4500r/mi n, jitter time is 30-45mi n.
3. the preparation method of architectural latex coating according to claim 1, which is characterized in that grinding temperature is in step (3)
It 30-35 DEG C, revolving speed 1300-1500rpm, discharges after grinding 3-4h.
4. the preparation method of architectural latex coating according to any one of claims 1 to 3, which is characterized in that step is stirred in (4)
Processing 2-3h is mixed, controlling whipping temp in bucket is 45-50 DEG C.