CN108978182A - A kind of composite plant fiber for mattress processing - Google Patents
A kind of composite plant fiber for mattress processing Download PDFInfo
- Publication number
- CN108978182A CN108978182A CN201810912330.6A CN201810912330A CN108978182A CN 108978182 A CN108978182 A CN 108978182A CN 201810912330 A CN201810912330 A CN 201810912330A CN 108978182 A CN108978182 A CN 108978182A
- Authority
- CN
- China
- Prior art keywords
- plant fiber
- parts
- mattress
- fiber
- mattress processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to high-performance fiber and technical field of composite materials, disclose a kind of composite plant fiber for mattress processing, form is uniform, fiber softening, mechanical strength has surmounted existing plant fiber, and anti-mould and anti-moth effect is good, ventilative and hygroscopicity is excellent, it can degrade, regeneration, it is pollution-free, with excellent physics, chemical characteristic, it is expected to become a new generation's environmental protection, energy conservation, the emerging mattress material of high-performance, the present invention efficiently solves the problems, such as that existing plant fiber utility in mattress processing is general, comfortable effect and fine fiber performance are taken into account, improve the development and utilization of natural plant fiber material, it can be realized the realistic meaning of the sustainable development and the feature of environmental protection that improve mattress material, it is a kind of technical solution being extremely worth of widely use.
Description
Technical field
The invention belongs to high-performance fiber and technical field of composite materials, and in particular to a kind of for the compound of mattress processing
Plant fiber.
Background technique
Mattress be in order to guarantee consumer secure good health and comfortably sleep and use it is a kind of between human body and bed it
Between article, mattress material is various, different materials production mattress different sleeper effects can be brought to people.With material progress
With being constantly progressive for technical matters, the mattress type that modern people use gradually tends to diversification, mainly has: sping mattress, palm fibre
Palmitic acid mattress, latex bed mattress, water bed mattress, pneumatic mattress, magnetic mattress etc..
As to advocate natural cry higher and higher by people, and environmental problem is increasingly paid attention to, staple fibre exists
Occurs a series of problems in preparation process, for example energy consumption is excessively high, and more serious pollution, product cost are caused to environment
It is more expensive, not pro-skin etc..So that natural plant fibre occupies certain market again.But due to plant fiber function list
One, and the problems such as textile performance is bad is combined, it causes it to utilize and also rests on most foundation phase.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of composite plant fiber for mattress processing, shape are provided
State is uniform, fiber softening, and mechanical strength has surmounted existing plant fiber, and anti-mould and anti-moth effect is good, and ventilative and hygroscopicity is excellent
It is different.
The present invention is achieved by the following technical solutions:
A kind of composite plant fiber for mattress processing, is made of following component: 45-48 parts of moso bamboo, coconut palm in parts by weight
25-35 parts of shell, 15-20 parts of sponge gourd, 10-15 parts of broom grass, active 5-8 parts of breeze, 0.5-0.7 parts of sulphur；Preparation method packet
Include following steps:
(1) moso bamboo, coconut husk, sponge gourd, the broken shearing of broom grass, in 1-2 cm range, are put into digesting apparatus, are added to length
The sodium hydroxide solution that mass concentration is 1.5-1.8% submerges material, solid-liquid ratio 1:3.5-4.0, and setting boiling temperature is 150-
160 DEG C, digestion time is 2.0-2.5 hours；
(2) well-done material is taken out, is rinsed using clear water and removes remaining lye, with roller to the object after boiling softening
Material carries out preliminary working, and cleaning air-dries and obtains pencil crude fibre after combing, and crude fibre and active breeze are sent into fiber unlatching
Decomposition is broken up in machine, sulphur is added, is then heated by hot press, and hot pressing temperature is 110-120 DEG C, pressing time 15-20
Minute, steam pressure 0.16-0.18MPa, to obtain cross-linked network composite fibre.
It is further described as to above scheme, the moso bamboo is 2-3 breeder mother bamboo.
It is further described as to above scheme, the coconut husk is using the preceding carbon for the use of mass concentration being 2.5-3.0%
Acid sodium aqueous solution impregnates 3-4 hours, is then rinsed using clear water, is dried under sunlight.
It is further described as to above scheme, the sponge gourd, broom grass are to be dried to after nature elder, xanthochromia to contain
Material of the water between 10-15%.
It is further described as to above scheme, the active carbon slag particle size is between 300-500 nanometers.
The present invention has the advantage that solve existing plant fiber utility one in mattress processing compared with prior art
As the problem of, the present invention provides it is a kind of for mattress processing composite plant fiber, form is uniform, fiber softening, and mechanics is strong
Degree has surmounted existing plant fiber, and anti-mould and anti-moth effect is good, and ventilative and hygroscopicity is excellent, can degrade, regenerate, no dirt
Dye has excellent Wuli-Shili-Renli system approach, is expected to become a new generation's environmental protection, energy conservation, the emerging mattress material of high-performance, the present invention
It efficiently solves the problems, such as that existing plant fiber utility in mattress processing is general, has taken into account comfortable effect and fine fiber
Performance improves the development and utilization of natural plant fiber material, can be realized the sustainable development for improving mattress material and ring
The realistic meaning of guarantor property is a kind of technical solution being extremely worth of widely use.
Specific embodiment
To make the purpose of the present invention, technical solution and effect clearer, clear and definite, combined with specific embodiments below to this hair
It is bright to be described further, it should be understood that the specific embodiments described herein are merely illustrative of the present invention, is not used to limit
Technical solution provided by the present invention.
Embodiment 1
A kind of composite plant fiber for mattress processing, is made of following component: 45 parts of moso bamboo, coconut husk 25 in parts by weight
Part, 15 parts of sponge gourd, 10 parts of broom grass, active 5 parts of breeze, 0.5 part of sulphur；Preparation method includes the following steps:
(1) moso bamboo, coconut husk, sponge gourd, the broken shearing of broom grass, in 1-2 cm range, are put into digesting apparatus, are added to length
The sodium hydroxide solution that mass concentration is 1.5% submerges material, solid-liquid ratio 1:3.5, and setting boiling temperature is 150 DEG C, when boiling
Between be 2.0 hours；
(2) well-done material is taken out, is rinsed using clear water and removes remaining lye, with roller to the object after boiling softening
Material carries out preliminary working, and cleaning air-dries and obtains pencil crude fibre after combing, and crude fibre and active breeze are sent into fiber unlatching
Decomposition is broken up in machine, sulphur is added, is then heated by hot press, and hot pressing temperature is 110 DEG C, and pressing time is 15 minutes, is steamed
Steam pressure is 0.16MPa, to obtain cross-linked network composite fibre.
It is further described as to above scheme, the moso bamboo is 2-3 breeder mother bamboo.
It is further described as to above scheme, the coconut husk is using the preceding sodium carbonate for the use of mass concentration being 2.5%
It aqueous solution soaking 3 hours, is then rinsed using clear water, is dried under sunlight.
It is further described as to above scheme, the sponge gourd, broom grass are to be dried to after nature elder, xanthochromia to contain
Material of the water between 10-15%.
It is further described as to above scheme, the active carbon slag particle size is between 300-500 nanometers.
Embodiment 2
A kind of composite plant fiber for mattress processing, is made of following component: 46 parts of moso bamboo, coconut husk 30 in parts by weight
Part, 18 parts of sponge gourd, 12 parts of broom grass, active 6 parts of breeze, 0.6 part of sulphur；Preparation method includes the following steps:
(1) moso bamboo, coconut husk, sponge gourd, the broken shearing of broom grass, in 1-2 cm range, are put into digesting apparatus, are added to length
The sodium hydroxide solution that mass concentration is 1.6% submerges material, solid-liquid ratio 1:3.8, and setting boiling temperature is 155 DEG C, when boiling
Between be 2.2 hours；
(2) well-done material is taken out, is rinsed using clear water and removes remaining lye, with roller to the object after boiling softening
Material carries out preliminary working, and cleaning air-dries and obtains pencil crude fibre after combing, and crude fibre and active breeze are sent into fiber unlatching
Decomposition is broken up in machine, sulphur is added, is then heated by hot press, and hot pressing temperature is 115 DEG C, and pressing time is 18 minutes, is steamed
Steam pressure is 0.17MPa, to obtain cross-linked network composite fibre.
It is further described as to above scheme, the moso bamboo is 2-3 breeder mother bamboo.
It is further described as to above scheme, the coconut husk is using the preceding sodium carbonate for the use of mass concentration being 2.8%
It aqueous solution soaking 3.5 hours, is then rinsed using clear water, is dried under sunlight.
It is further described as to above scheme, the sponge gourd, broom grass are to be dried to after nature elder, xanthochromia to contain
Material of the water between 10-15%.
It is further described as to above scheme, the active carbon slag particle size is between 300-500 nanometers.
Embodiment 3
A kind of composite plant fiber for mattress processing, is made of following component: 48 parts of moso bamboo, coconut husk 35 in parts by weight
Part, 20 parts of sponge gourd, 15 parts of broom grass, active 8 parts of breeze, 0.7 part of sulphur；Preparation method includes the following steps:
(1) moso bamboo, coconut husk, sponge gourd, the broken shearing of broom grass, in 1-2 cm range, are put into digesting apparatus, are added to length
The sodium hydroxide solution that mass concentration is 1.8% submerges material, solid-liquid ratio 1:4.0, and setting boiling temperature is 160 DEG C, when boiling
Between be 2.5 hours；
(2) well-done material is taken out, is rinsed using clear water and removes remaining lye, with roller to the object after boiling softening
Material carries out preliminary working, and cleaning air-dries and obtains pencil crude fibre after combing, and crude fibre and active breeze are sent into fiber unlatching
Decomposition is broken up in machine, sulphur is added, is then heated by hot press, and hot pressing temperature is 120 DEG C, and pressing time is 20 minutes, is steamed
Steam pressure is 0.18MPa, to obtain cross-linked network composite fibre.
It is further described as to above scheme, the moso bamboo is 2-3 breeder mother bamboo.
It is further described as to above scheme, the coconut husk is using the preceding sodium carbonate for the use of mass concentration being 3.0%
It aqueous solution soaking 4 hours, is then rinsed using clear water, is dried under sunlight.
It is further described as to above scheme, the sponge gourd, broom grass are to be dried to after nature elder, xanthochromia to contain
Material of the water between 10-15%.
It is further described as to above scheme, the active carbon slag particle size is between 300-500 nanometers.
Claims (5)
1. a kind of composite plant fiber for mattress processing, which is characterized in that be made in parts by weight of following component: hair
45-48 parts of bamboo, 25-35 parts of coconut husk, 15-20 parts of sponge gourd, 10-15 parts of broom grass, active 5-8 parts of breeze, 0.5-0.7 parts of sulphur；
Preparation method includes the following steps:
(1) moso bamboo, coconut husk, sponge gourd, the broken shearing of broom grass, in 1-2 cm range, are put into digesting apparatus, are added to length
The sodium hydroxide solution that mass concentration is 1.5-1.8% submerges material, solid-liquid ratio 1:3.5-4.0, and setting boiling temperature is 150-
160 DEG C, digestion time is 2.0-2.5 hours；
(2) well-done material is taken out, is rinsed using clear water and removes remaining lye, with roller to the object after boiling softening
Material carries out preliminary working, and cleaning air-dries and obtains pencil crude fibre after combing, and crude fibre and active breeze are sent into fiber unlatching
Decomposition is broken up in machine, sulphur is added, is then heated by hot press, and hot pressing temperature is 110-120 DEG C, pressing time 15-20
Minute, steam pressure 0.16-0.18MPa, to obtain cross-linked network composite fibre.
2. a kind of composite plant fiber for mattress processing as described in claim 1, which is characterized in that the moso bamboo is 2-3
Year breeder mother bamboo.
3. a kind of composite plant fiber for mattress processing as described in claim 1, which is characterized in that the coconut husk is using
It is preceding to be impregnated 3-4 hours using the aqueous sodium carbonate that mass concentration is 2.5-3.0%, it is then rinsed using clear water, sunlight
Under dry.
4. a kind of composite plant fiber for mattress processing as described in claim 1, which is characterized in that the sponge gourd, broom
Grass is to be dried to material of the water content between 10-15% after nature elder, xanthochromia.
5. a kind of composite plant fiber for mattress processing as described in claim 1, which is characterized in that the active carbon slag particle
Diameter size is between 300-500 nanometers.