CN108977911A - A kind of polyester fiber fabric of UV resistant - Google Patents
A kind of polyester fiber fabric of UV resistant Download PDFInfo
- Publication number
- CN108977911A CN108977911A CN201810809328.6A CN201810809328A CN108977911A CN 108977911 A CN108977911 A CN 108977911A CN 201810809328 A CN201810809328 A CN 201810809328A CN 108977911 A CN108977911 A CN 108977911A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- attapulgite
- resistant
- fiber fabric
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polyester fiber fabrics of UV resistant, are related to clothing fabric technical field, the active nano attapulgite soil containing its quality 3.5-4.2% in the polyester fiber fabric of the UV resistant；The polyester fiber for the UV resistant that the present invention obtains has excellent resistance to UV aging, passes through 1000h xenon lamp accelerated aging tests, and the rupture strength retention of the polyester fiber based on UV resistant is 93-95%；The polyester fiber of the UV resistant is by 20 washings, weight retention rate 96-99%.
Description
Technical field
The invention belongs to clothing fabric technical fields, and in particular to a kind of polyester fiber fabric of UV resistant.
Background technique
The specific chemical structure of polyester fiber determines it with excellent performance, such as high intensity, lower shrinkage, dimensionally stable
The good property of property is good etc., thus is widely used in taking and takes field with non-.For outdoor umbrella cloth, shelter cloth, advertising lamp box
The polyester fiber that the specific occasions such as cloth, rope use especially relates to what the higher outdoor application field of security level used
Polyester fiber is exposed under sunlight for a long time, therefore it is required that uvioresistant performance must be guaranteed within certain time,
Therefore developing a kind of polyester fiber good with efficient uvioresistant has far-reaching significance.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of polyester fiber fabric of UV resistant is provided.
The present invention is achieved by the following technical solutions:
A kind of polyester fiber fabric of UV resistant contains its quality 3.5-4.2% in the polyester fiber fabric of the UV resistant
Active nano attapulgite soil.
Further, active nano attapulgite soil the preparation method comprises the following steps:
(1) attapulgite is added in aqueous solution of urea, is heated to 90 DEG C, with 3000r/min revolving speed stirring 2 hours, then
Physical grinding obtains nano-attapulgite after 3 hours, be then filtered, and is cleaned using deionized water to neutrality, is dried to perseverance
Weight；
(2) nano-attapulgite in (1) is evenly spread in deionized water, obtains nano-attapulgite dispersion liquid, Xiang Na
The sodium peroxydisulfate that its quality 0.8% is added in rice attapulgite dispersion liquid, is heated to 60 DEG C, small with the stirring 2 of 200r/min revolving speed
When, obtain mixed dispersion liquid；
(3) mixed dispersion liquid pH obtained in (2) is adjusted to 10.0, keeps the temperature 2 hours at 40 DEG C, is then filtered, i.e.,
Obtain active nano attapulgite soil.
Further, the Ou Xing nano-attapulgite soil granularity is 90nm.
Further, the aqueous solution of urea mass fraction is 10%.
Further, the mixed dispersion liquid pH adjusting uses mass fraction to be adjusted for 5% sodium hydroxide solution.
It is excellent that the present invention has the advantage that the polyester fiber for the UV resistant that the present invention obtains has compared with prior art
Resistance to UV aging, pass through 1000h xenon lamp accelerated aging tests, the breaking strength of the polyester fiber based on UV resistant
Conservation rate is 93-95%；The polyester fiber of the UV resistant is by 20 washings, weight retention rate 96-99%.
Specific embodiment
Embodiment 1
A kind of polyester fiber fabric of UV resistant, the work containing its quality 3.5% in the polyester fiber fabric of the UV resistant
Property nano-attapulgite.
Further, active nano attapulgite soil the preparation method comprises the following steps:
(1) attapulgite is added in aqueous solution of urea, is heated to 90 DEG C, with 3000r/min revolving speed stirring 2 hours, then
Physical grinding obtains nano-attapulgite after 3 hours, be then filtered, and is cleaned using deionized water to neutrality, is dried to perseverance
Weight；
(2) nano-attapulgite in (1) is evenly spread in deionized water, obtains nano-attapulgite dispersion liquid, Xiang Na
The sodium peroxydisulfate that its quality 0.8% is added in rice attapulgite dispersion liquid, is heated to 60 DEG C, small with the stirring 2 of 200r/min revolving speed
When, obtain mixed dispersion liquid；
(3) mixed dispersion liquid pH obtained in (2) is adjusted to 10.0, keeps the temperature 2 hours at 40 DEG C, is then filtered, i.e.,
Obtain active nano attapulgite soil.
Further, the Ou Xing nano-attapulgite soil granularity is 90nm.
Further, the aqueous solution of urea mass fraction is 10%.
Embodiment 2
A kind of polyester fiber fabric of UV resistant, the work containing its quality 4.2% in the polyester fiber fabric of the UV resistant
Property nano-attapulgite.
Further, active nano attapulgite soil the preparation method comprises the following steps:
(1) attapulgite is added in aqueous solution of urea, is heated to 90 DEG C, with 3000r/min revolving speed stirring 2 hours, then
Physical grinding obtains nano-attapulgite after 3 hours, be then filtered, and is cleaned using deionized water to neutrality, is dried to perseverance
Weight；
(2) nano-attapulgite in (1) is evenly spread in deionized water, obtains nano-attapulgite dispersion liquid, Xiang Na
The sodium peroxydisulfate that its quality 0.8% is added in rice attapulgite dispersion liquid, is heated to 60 DEG C, small with the stirring 2 of 200r/min revolving speed
When, obtain mixed dispersion liquid；
(3) mixed dispersion liquid pH obtained in (2) is adjusted to 10.0, keeps the temperature 2 hours at 40 DEG C, is then filtered, i.e.,
Obtain active nano attapulgite soil.
Further, the Ou Xing nano-attapulgite soil granularity is 90nm.
Further, the aqueous solution of urea mass fraction is 10%.
Embodiment 3
A kind of polyester fiber fabric of UV resistant, the work containing its quality 3.8% in the polyester fiber fabric of the UV resistant
Property nano-attapulgite.
Further, active nano attapulgite soil the preparation method comprises the following steps:
(1) attapulgite is added in aqueous solution of urea, is heated to 90 DEG C, with 3000r/min revolving speed stirring 2 hours, then
Physical grinding obtains nano-attapulgite after 3 hours, be then filtered, and is cleaned using deionized water to neutrality, is dried to perseverance
Weight；
(2) nano-attapulgite in (1) is evenly spread in deionized water, obtains nano-attapulgite dispersion liquid, Xiang Na
The sodium peroxydisulfate that its quality 0.8% is added in rice attapulgite dispersion liquid, is heated to 60 DEG C, small with the stirring 2 of 200r/min revolving speed
When, obtain mixed dispersion liquid；
(3) mixed dispersion liquid pH obtained in (2) is adjusted to 10.0, keeps the temperature 2 hours at 40 DEG C, is then filtered, i.e.,
Obtain active nano attapulgite soil.
Further, the Ou Xing nano-attapulgite soil granularity is 90nm.
Further, the aqueous solution of urea mass fraction is 10%.
The polyester fiber for the UV resistant that the present invention obtains has excellent resistance to UV aging, passes through 1000h xenon
The rupture strength retention of lamp accelerated aging tests, the polyester fiber based on UV resistant is 93-95%, does not add active nano
The polyester fiber of attapulgite passes through 1000h xenon lamp accelerated aging tests, the breaking strength of the polyester fiber based on UV resistant
Conservation rate is 80%, adds the polyester fiber of untreated nano-attapulgite by 1000h xenon lamp accelerated aging tests, is based on
The rupture strength retention of the polyester fiber of UV resistant is 83.5%.
Claims (5)
1. a kind of polyester fiber fabric of UV resistant, which is characterized in that contain in the polyester fiber fabric of the UV resistant
The active nano attapulgite soil of its quality 3.5-4.2%.
2. a kind of polyester fiber fabric of UV resistant according to claim 1, which is characterized in that the active nano is recessed
Convex stick soil the preparation method comprises the following steps:
(1) attapulgite is added in aqueous solution of urea, is heated to 90 DEG C, with 3000r/min revolving speed stirring 2 hours, then
Physical grinding obtains nano-attapulgite after 3 hours, be then filtered, and is cleaned using deionized water to neutrality, is dried to perseverance
Weight；
(2) nano-attapulgite in (1) is evenly spread in deionized water, obtains nano-attapulgite dispersion liquid, Xiang Na
The sodium peroxydisulfate that its quality 0.8% is added in rice attapulgite dispersion liquid, is heated to 60 DEG C, small with the stirring 2 of 200r/min revolving speed
When, obtain mixed dispersion liquid；
(3) mixed dispersion liquid pH obtained in (2) is adjusted to 10.0, keeps the temperature 2 hours at 40 DEG C, is then filtered, i.e.,
Obtain active nano attapulgite soil.
3. a kind of polyester fiber fabric of UV resistant according to claim 2, which is characterized in that described Ou Xing nanometers recessed
Convex stick soil granularity is 90nm.
4. a kind of polyester fiber fabric of UV resistant according to claim 2, which is characterized in that the aqueous solution of urea
Mass fraction is 10%.
5. a kind of polyester fiber fabric of UV resistant according to claim 2, which is characterized in that the mixed dispersion liquid
PH adjusting uses mass fraction to be adjusted for 5% sodium hydroxide solution.