CN108968169A - 一种具有抗菌助剂的丝袜 - Google Patents

一种具有抗菌助剂的丝袜 Download PDF

Info

Publication number
CN108968169A
CN108968169A CN201810788220.3A CN201810788220A CN108968169A CN 108968169 A CN108968169 A CN 108968169A CN 201810788220 A CN201810788220 A CN 201810788220A CN 108968169 A CN108968169 A CN 108968169A
Authority
CN
China
Prior art keywords
parts
accessory ingredient
antibacterial accessory
stretch yarn
silk stocking
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810788220.3A
Other languages
English (en)
Inventor
成勇斌
黄旭敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG BAONASI HOSIERY INDUSTRY Co Ltd
Original Assignee
ZHEJIANG BAONASI HOSIERY INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG BAONASI HOSIERY INDUSTRY Co Ltd filed Critical ZHEJIANG BAONASI HOSIERY INDUSTRY Co Ltd
Priority to CN201810788220.3A priority Critical patent/CN108968169A/zh
Publication of CN108968169A publication Critical patent/CN108968169A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种具有抗菌助剂的丝袜，由复合弹力丝编织而成，所述复合弹力丝包括按照2：1～4的条数比设置的高弹丝以及牵引丝，所述高弹丝以及牵引丝的横截面为“十”字形，在所述高弹丝与牵引丝的外侧壁上包覆有抗菌助剂的浆料干燥后所形成的助剂层；所述牵引丝与所述高弹丝形成加捻丝束；所述抗菌助剂按照质量份数包括以下成分：去离子水60～90份、三元共聚聚二甲基硅氧烷20～50份、乳化剂3～6份、羟基改性聚二甲基硅氧烷3～6份、增溶剂3～8份、防腐剂0.001～0.003份。采用上述技术方案，本发明的具有抗菌助剂的丝袜，在女性穿着时能够达到抗菌抑菌的效果，同时延伸部能够起到阻挡作用，在缠绕过程中能够将部分助剂层挡住，避免其过快流失。

Description

一种具有抗菌助剂的丝袜
技术领域
本发明涉及丝织品领域，尤其涉及一种具有抗菌助剂的丝袜。
背景技术
丝袜一般是指尼龙薄袜，俗称女人的第二层皮肤，也是每个女性必备的单品，无论年轻女孩的彩色丝袜，还是成熟女性的性感丝袜，在每个女孩的衣橱里都可以找到她的身影。由于丝袜的修饰性好，流行程度较高，使得女性穿着丝袜的人数不断增长，丝袜的市场需求量逐年上升。为了追求丝袜的高品质，通常还会针对丝袜在各个方面的用户体验进行改进，例如厂家已经设计的高弹丝袜、防脱丝丝袜、面膜丝袜等，但目前丝袜在添加功能型助剂时是在丝袜成型后使用各类助剂浆料浸泡再风干，助剂附着再丝袜上，但随着丝袜的几次清洗，助剂就会逐渐消失，从而丧失相应的功能。
发明内容
本发明要解决的技术问题在于克服现有技术中的缺陷，从而提供一种不易使抗菌助剂丧失的丝袜。
为了实现上述目的，本发明的一种具有抗菌助剂的丝袜，由复合弹力丝编织而成，所述复合弹力丝包括按照2：1～4的条数比设置的高弹丝以及牵引丝，所述高弹丝以及牵引丝的横截面为“十”字形，在所述高弹丝与牵引丝的外侧壁上包覆有抗菌助剂的浆料干燥后所形成的助剂层；所述牵引丝与所述高弹丝形成加捻丝束；所述抗菌助剂按照质量份数包括以下成分：去离子水60～90份、三元共聚聚二甲基硅氧烷20～50份、乳化剂3～6份、羟基改性聚二甲基硅氧烷3～6份、增溶剂3～8份、防腐剂0.001～0.003份。
所述抗菌助剂按照质量份数包括以下成分：去离子水75份、三元共聚聚二甲基硅氧烷35份、乳化剂4份、羟基改性聚二甲基硅氧烷5份、增溶剂5份、防腐剂0.002份。
所述乳化剂为异构十三醇聚氧乙烯醚-7-环氧乙烷。
所述防腐剂为异噻唑啉酮。
所述增溶剂为丙三醇
所述高弹丝为聚氨酯高弹丝。
所述牵引丝包括涤纶低弹丝和/或丙纶低弹丝。
所述复合弹力丝，包括按照2：2～3的条数比设置的多条高弹丝以及多条牵引丝。
所述聚氨酯高弹丝，其包含含量为重量百分比10%～12%的苯酚磺酸以及包含含量为重量百分比12%～18%的二羟基苯基砜。
所述聚氨酯高弹丝的成分包括聚合物二醇以及二异氰酸酯。
采用上述技术方案，本发明的具有抗菌助剂的丝袜，在女性穿着时能够达到抗菌抑菌的效果，其中复合弹力丝由高弹丝、牵引丝作为原丝，由于每一条原丝的横截面为“十”字形的结构，那么能够在“十”字形的中心点位置向外侧形成四个延伸部，通过将原丝放入抗菌助剂浆料内浸泡，再经干燥处理后，助剂层形成于原丝外表面，当牵引丝与所述高弹丝加捻后，延伸部能够起到阻挡作用，在缠绕过程中能够将部分助剂层挡住，避免其过快流失。
附图说明
图1为本发明的复合弹力丝的结构示意图。
图2为复合弹力丝的截面示意图。
具体实施方式
以下通过附图和具体实施方式对本发明作进一步的详细说明。
如图所示，本实施例提供一种具有抗菌助剂的丝袜，由复合弹力丝编织而成，所述复合弹力丝包括按照2：1～4的条数比设置的高弹丝以及牵引丝，所述高弹丝以及牵引丝的横截面为“十”字形，如图1、2所示。在所述高弹丝与牵引丝的外侧壁上包覆有抗菌助剂的浆料干燥后所形成的助剂层；所述牵引丝与所述高弹丝形成加捻丝束。
所述抗菌助剂按照质量份数包括以下成分：去离子水60～90份、三元共聚聚二甲基硅氧烷20～50份、乳化剂3～6份、羟基改性聚二甲基硅氧烷3～6份、增溶剂3～8份、防腐剂0.001～0.003份。
所述抗菌助剂按照质量份数包括以下成分：去离子水75份、三元共聚聚二甲基硅氧烷35份、乳化剂4份、羟基改性聚二甲基硅氧烷5份、增溶剂5份、防腐剂0.002份。
所述乳化剂为异构十三醇聚氧乙烯醚-7-环氧乙烷。
所述防腐剂为异噻唑啉酮。
所述增溶剂为丙三醇
所述高弹丝为聚氨酯高弹丝。
所述牵引丝包括涤纶低弹丝和/或丙纶低弹丝。
所述复合弹力丝，包括按照2：2～3的条数比设置的多条高弹丝以及多条牵引丝。
所述聚氨酯高弹丝，其包含含量为重量百分比10%～12%的苯酚磺酸以及包含含量为重量百分比12%～18%的二羟基苯基砜。
所述聚氨酯高弹丝的成分包括聚合物二醇以及二异氰酸酯。
采用上述技术方案，本发明的具有抗菌助剂的丝袜，在女性穿着时能够达到抗菌抑菌的效果，其中复合弹力丝由高弹丝1、牵引丝2作为原丝，由于每一条原丝的横截面为“十”字形的结构，那么能够在“十”字形的中心点位置向外侧形成四个延伸部100，通过将原丝放入抗菌助剂浆料内浸泡，再经干燥处理后，助剂层200形成于原丝外表面，当牵引丝与所述高弹丝加捻后，延伸部能够起到阻挡作用，在缠绕过程中能够将部分助剂层挡住，避免其过快流失。

Claims (10)

1.一种具有抗菌助剂的丝袜，其特征在于：由复合弹力丝编织而成，所述复合弹力丝包括按照2：1～4的条数比设置的高弹丝以及牵引丝，所述高弹丝以及牵引丝的横截面为“十”字形，在所述高弹丝与牵引丝的外侧壁上包覆有抗菌助剂的浆料干燥后所形成的助剂层；所述牵引丝与所述高弹丝形成加捻丝束；所述抗菌助剂按照质量份数包括以下成分：去离子水60～90份、三元共聚聚二甲基硅氧烷20～50份、乳化剂3～6份、羟基改性聚二甲基硅氧烷3～6份、增溶剂3～8份、防腐剂0.001～0.003份。
2.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述抗菌助剂按照质量份数包括以下成分：去离子水75份、三元共聚聚二甲基硅氧烷35份、乳化剂4份、羟基改性聚二甲基硅氧烷5份、增溶剂5份、防腐剂0.002份。
3.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述乳化剂为异构十三醇聚氧乙烯醚-7-环氧乙烷。
4.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述防腐剂为异噻唑啉酮。
5.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述增溶剂为丙三醇。
6.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述非离子表面活性剂为异构醇聚氧乙烯醚。
7.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述高弹丝为聚氨酯高弹丝。
8.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述牵引丝包括涤纶低弹丝和/或丙纶低弹丝。
9.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述复合弹力丝，包括按照2：2～3的条数比设置的多条高弹丝以及多条牵引丝。
10.如权利要求1所述的具有抗菌助剂的丝袜，其特征在于：所述聚氨酯高弹丝，其包含含量为重量百分比10%～12%的苯酚磺酸以及包含含量为重量百分比12%～18%的二羟基苯基砜。
CN201810788220.3A 2018-07-18 2018-07-18 一种具有抗菌助剂的丝袜 Pending CN108968169A (zh)