CN108950782A - A kind of cladding process of polyamide fibre FDY and spandex - Google Patents
A kind of cladding process of polyamide fibre FDY and spandex Download PDFInfo
- Publication number
- CN108950782A CN108950782A CN201811091908.2A CN201811091908A CN108950782A CN 108950782 A CN108950782 A CN 108950782A CN 201811091908 A CN201811091908 A CN 201811091908A CN 108950782 A CN108950782 A CN 108950782A
- Authority
- CN
- China
- Prior art keywords
- strand
- roller
- fdy
- sent
- spandex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to synthetic fiber technologies, and in particular to a kind of cladding process of polyamide fibre FDY and spandex.The following steps are included: FDY strand is sent to wire leading pipe, it is transported in yarn cutter;Again into roller W1, it is sent to twist arrester, strand is fixed at the top of hot tank by twist arrester, the strand after upper step process carries out on-line tension on tensioner and checks in real time;Spandex is drawn by roller G1, is incorporated to drawing-off together in roller W2 by traveller and FDY, further and enters network nozzle progress interlacing;It is sent into roller W2X through network nozzle treated strand, and the roller W2X strand exported is sent in yarn probe, is then oiled, is wound.The cladding process of polyamide fibre FDY and spandex of the present invention, production cost is low, and high production efficiency has broad application prospects.
Description
Technical field
The invention belongs to synthetic fiber technologies, and in particular to a kind of cladding process of polyamide fibre FDY and spandex.
Background technique
FDY product F ULLY DRAWN YARN, fully drawn yarn belong to chemical-fibres filaments.Polyamide fibre FDY fabric hand feel is smooth soft
It is soft, it is often used in weaving silk-like fabric.The characteristic of its ultimate strength with higher, generally by covering machine by FDY with
More elastomeric performance can be obtained after spandex is compound.But the speed of production of be limited to covering machine influences to cause production cost high.It is logical
Production cost can be greatly reduced in the process program for crossing this patent.
Summary of the invention
The purpose of the present invention is to provide the cladding process of a kind of polyamide fibre FDY and spandex.
To achieve the above object, the present invention adopts the following technical scheme:
The cladding process of a kind of the polyamide fibre FDY and spandex comprising following steps:
(1) FDY strand is sent to wire leading pipe, then is transported in yarn cutter by wire leading pipe transmitting effect;
(2) the FDY strand after yarn cutter incudes is sent in roller W1, is held strand together by apron and roller, is made silk
Item is stretched;
(3) through roller, treated that strand is sent to twist arrester, strand is fixed at the top of hot tank by twist arrester, playing prevents
The effect of strand yarn twist unevenness;
(4) strand after being heat-treated enters coldplate and scroll tube, and the effect of coldplate be to fiber strand silk false twisting with
The fixation of coiled structure afterwards;
(5) strand after upper step process carries out on-line tension on tensioner and checks in real time;
(6) spandex is drawn by roller G1, is incorporated to drawing-off together in roller W2 by traveller and FDY, further and enter network
Nozzle carries out interlacing;
(7) it is sent into roller W2X through network nozzle treated strand, and the roller W2X strand exported is sent in yarn probe,
Yarn probe is then when silk breaks end, and yarn probe can be in time by information feedback to yarn cutter, and yarn cutter cuts off silk, and roller is no longer for silk
There is no strand processes in entire the Silk Road;
(8) strand after yarn probe detection is oiled operation by oil tanker, and the effect of oil tanker mainly adds to elastic filament appropriate
Finish, effect are the convergences for improving fiber, increase the flatness of fiber, improve the antistatic property of fiber;
(9) volume that the strand after oiling makes strand uniformly be coiled into certain shapes and capacity regularly finally by operation is wound
Dress completes cladding processing operation process.
The linear velocity wherein produced: 720m/min;
FDY draw ratio: 1.02;
Spandex draws high ratio: 3.5;
Heater temperature: 0 DEG C;
Network nozzle specification: 1.4mm;
Network pressure Mpa:0.45.
Remarkable advantage of the invention is:
The cladding process of polyamide fibre FDY and spandex of the invention, production cost is low, and high production efficiency has broad application prospects.
Detailed description of the invention
Fig. 1 present invention process flow diagram.
Specific embodiment
Further to disclose rather than the present invention is limited, the present invention is described in further detail below in conjunction with example.
Embodiment 1
The cladding process of a kind of the polyamide fibre FDY and spandex comprising following steps:
(1) FDY strand is sent to wire leading pipe, then is transported in yarn cutter by wire leading pipe transmitting effect;
(2) the FDY strand after yarn cutter incudes is sent in roller W1, is held strand together by apron and roller, is made silk
Item is stretched;
(3) through roller, treated that strand is sent to twist arrester, strand is fixed at the top of hot tank by twist arrester, playing prevents
The effect of strand yarn twist unevenness;
(4) strand after being heat-treated enters coldplate and scroll tube, and the effect of coldplate be to fiber strand silk false twisting with
The fixation of coiled structure afterwards;
(5) strand after upper step process carries out on-line tension on tensioner and checks in real time;
(6) spandex is drawn by roller G1, is incorporated to drawing-off together in roller W2 by traveller and FDY, further and enter network
Nozzle carries out interlacing;
(7) it is sent into roller W2X through network nozzle treated strand, and the roller W2X strand exported is sent in yarn probe,
Yarn probe is then when silk breaks end, and yarn probe can be in time by information feedback to yarn cutter, and yarn cutter cuts off silk, and roller is no longer for silk
There is no strand processes in entire the Silk Road;
(8) strand after yarn probe detection is oiled operation by oil tanker, and the effect of oil tanker mainly adds to elastic filament appropriate
Finish, effect are the convergences for improving fiber, increase the flatness of fiber, improve the antistatic property of fiber;
(9) volume that the strand after oiling makes strand uniformly be coiled into certain shapes and capacity regularly finally by operation is wound
Dress completes cladding processing operation process.
The linear velocity wherein produced: 720m/min;
FDY draw ratio: 1.02;
Spandex draws high ratio: 3.5;
Heater temperature: 0 DEG C;
Network nozzle specification: 1.4mm;
Network pressure Mpa:0.45.
1 FDY cladding wire product quality indicator of embodiment
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with repair
Decorations, are all covered by the present invention.
Claims (2)
1. the cladding process of a kind of the polyamide fibre FDY and spandex, it is characterised in that: the following steps are included:
(1) FDY strand is sent to wire leading pipe, then is transported in yarn cutter by wire leading pipe transmitting effect;
(2) the FDY strand after yarn cutter incudes is sent in roller W1, is held strand together by apron and roller, is made silk
Item is stretched;
(3) through roller, treated that strand is sent to twist arrester, strand is fixed at the top of hot tank by twist arrester, playing prevents
The effect of strand yarn twist unevenness;
(4) strand after being heat-treated enters coldplate and scroll tube, and the effect of coldplate be to fiber strand silk false twisting with
The fixation of coiled structure afterwards;
(5) strand after upper step process carries out on-line tension on tensioner and checks in real time;
(6) spandex is drawn by roller G1, is incorporated to drawing-off together in roller W2 by traveller and FDY, further and enter network
Nozzle carries out interlacing;
(7) it is sent into roller W2X through network nozzle treated strand, and the roller W2X strand exported is sent in yarn probe,
Yarn probe is then when silk breaks end, and yarn probe can be in time by information feedback to yarn cutter, and yarn cutter cuts off silk, and roller is no longer for silk
There is no strand processes in entire the Silk Road;
(8) strand after yarn probe detection is oiled operation by oil tanker, and the effect of oil tanker mainly adds to elastic filament appropriate
Finish, effect are the convergences for improving fiber, increase the flatness of fiber, improve the antistatic property of fiber;
(9) volume that the strand after oiling makes strand uniformly be coiled into certain shapes and capacity regularly finally by operation is wound
Dress completes cladding processing operation process.
2. the cladding process of polyamide fibre FDY and spandex according to claim 1, it is characterised in that:
Wherein line speed controls are as follows: 720m/min;
FDY draw ratio: 1.02;
Spandex draws high ratio: 3.5;
Heater temperature: 0 DEG C;
Network nozzle specification: 1.4mm;
Network pressure: 0.45Mpa.