CN108948812A - A kind of building shell mold plate thermal insulation fire-proof coating - Google Patents
A kind of building shell mold plate thermal insulation fire-proof coating Download PDFInfo
- Publication number
- CN108948812A CN108948812A CN201810492165.3A CN201810492165A CN108948812A CN 108948812 A CN108948812 A CN 108948812A CN 201810492165 A CN201810492165 A CN 201810492165A CN 108948812 A CN108948812 A CN 108948812A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid sodium
- thermal insulation
- mold plate
- shell mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of building shell mold plate thermal insulation fire-proof coating, it is made of according to parts by weight following raw material: 0.1-0.6 parts of polyisocyanates, 0.5-0.9 parts of magnesia, 0.6-1.2 parts of aluminium oxide, 0.4-0.8 parts of titanium dioxide, 0.3-0.7 parts of cetyl benzenesulfonic acid sodium, 6-11 parts of starch, 0.3-0.8 parts of ammonium metaborate, 9-13 parts of bentonite, 4-9 parts of rubber powder, 0.5-1.2 parts of boric acid, 4-9 parts of chlorinated paraffin, 0.3-0.6 parts of stearic acid sodium, 3-7 parts of cellulose acetate, 0.3-0.7 parts of ethyl acrylate, poly- isobutyl ester 0.2-0.8 parts, 0.4-0.9 parts of aluminium hydroxide, 0.2-0.5 parts of tributyl phosphate, 3-8 parts of pulullan, 4-9 parts of rosin, propylene glycol first 0.3-0.8 parts of ether, 4-9 parts of Aloe Vera Gel, 6-9 parts of mountain flour, 4-9 parts of silane coupling agent, 4-9 parts of lithium dihydrogen phosphate aerosol and 3-9 parts of dibutyl phthalate.The present invention has many advantages, such as heat-insulating, fire-preventing, environment-protecting and non-poisonous pollution-free.
Description
Technical field
The present invention relates to shell mold plate correlative technology field more particularly to a kind of building shell mold plate thermal insulation fire-proof coating.
Background technique
Recently as the rapid development of building trade, the prevention and control of fire also face huge challenge, fireproof importance
Self-evident, fireproof coating, can be effective to intensity of a fire progress fire-retardant as effective fire proofing material, prevents from further spreading,
Fire threat caused by people's life and property can effectively be reduced.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of building shell mold plate proposed is with absolutely
Hot fireproof coating.
To achieve the goals above, present invention employs following technical solutions:
A kind of building shell mold plate thermal insulation fire-proof coating is made of according to parts by weight following raw material: polyisocyanates 0.1-0.6
Part, 0.5-0.9 parts of magnesia, 0.6-1.2 parts of aluminium oxide, 0.4-0.8 parts of titanium dioxide, cetyl benzenesulfonic acid sodium 0.3-0.7
Part, 6-11 parts of starch, 0.3-0.8 parts of ammonium metaborate, 9-13 parts of bentonite, 0.4-1.2 parts of ethylene glycol monohexylether, Chinese honey locust glue 5-10
Part, 0.3-0.7 parts of nano silica, 3-8 parts of methylcellulose, 6-9 parts of coal tar pitch, 0.7-1.2 parts of graphene, dimethyl
0.4-0.9 parts of ethanol amine, 4-9 parts of rubber powder, 0.2-0.6 parts of cobaltous sulfate calcium carbonate, 0.5-1.2 parts of boric acid, 4-9 parts of chlorinated paraffin,
0.3-0.6 parts of stearic acid sodium, 3-7 parts of cellulose acetate, 0.3-0.7 parts of ethyl acrylate, isobutyl ester 0.2-0.8 parts poly-, hydrogen-oxygen
Change aluminium 0.4-0.9 parts, 0.2-0.5 parts of tributyl phosphate, 3-8 parts of pulullan, 4-9 parts of rosin, propylene glycol monomethyl ether 0.3-0.8
Part, 4-9 parts of Aloe Vera Gel, 6-9 parts of mountain flour, 4-9 parts of silane coupling agent, 4-9 parts of lithium dihydrogen phosphate aerosol and phthalic acid two
3-9 parts of butyl ester.
A kind of above-mentioned building shell mold plate thermal insulation fire-proof coating, is made of according to parts by weight following raw material: polyisocyanic acid
0.1-0.5 parts of ester, 0.5-0.8 parts of magnesia, 0.6-1.1 parts of aluminium oxide, 0.4-0.7 parts of titanium dioxide, cetyl benzenesulfonic acid
0.3-0.6 parts of sodium, 6-10 parts of starch, 0.3-0.7 parts of ammonium metaborate, 9-12 parts of bentonite, 0.4-1.1 parts of ethylene glycol monohexylether,
5-9 parts of Chinese honey locust glue, 0.3-0.6 parts of nano silica, 3-7 parts of methylcellulose, 6-8 parts of coal tar pitch, graphene 0.7-1.1
Part, 0.4-0.8 parts of dimethylethanolamine, 4-8 parts of rubber powder, 0.2-0.5 parts of cobaltous sulfate calcium carbonate, 0.5-1.1 parts of boric acid, chlorination stone
4-8 parts of wax, 0.3-0.5 parts of stearic acid sodium, 3-6 parts of cellulose acetate, 0.3-0.6 parts of ethyl acrylate, poly- isobutyl ester 0.2-0.7
Part, 0.4-0.8 parts of aluminium hydroxide, 0.2-0.4 parts of tributyl phosphate, 3-7 parts of pulullan, 4-8 parts of rosin, propylene glycol monomethyl ether
0.3-0.7 parts, 4-8 parts of Aloe Vera Gel, 6-8 parts of mountain flour, 4-8 parts of silane coupling agent, 4-8 parts of lithium dihydrogen phosphate aerosol and adjacent benzene two
3-8 parts of formic acid dibutyl ester.
A kind of above-mentioned building shell mold plate thermal insulation fire-proof coating, is made of according to parts by weight following raw material: polyisocyanic acid
0.2-0.5 parts of ester, 0.6-0.8 parts of magnesia, 0.7-1.1 parts of aluminium oxide, 0.5-0.7 parts of titanium dioxide, cetyl benzenesulfonic acid
0.4-0.6 parts of sodium, 7-10 parts of starch, 0.4-0.7 parts of ammonium metaborate, 10-12 parts of bentonite, 0.5-1.1 parts of ethylene glycol monohexylether,
6-9 parts of Chinese honey locust glue, 0.4-0.6 parts of nano silica, 4-7 parts of methylcellulose, 7-8 parts of coal tar pitch, graphene 0.8-1.1
Part, 0.5-0.8 parts of dimethylethanolamine, 5-8 parts of rubber powder, 0.3-0.5 parts of cobaltous sulfate calcium carbonate, 0.6-1.1 parts of boric acid, chlorination stone
5-8 parts of wax, 0.4-0.5 parts of stearic acid sodium, 4-6 parts of cellulose acetate, 0.4-0.6 parts of ethyl acrylate, poly- isobutyl ester 0.3-0.7
Part, 0.5-0.8 parts of aluminium hydroxide, 0.3-0.4 parts of tributyl phosphate, 4-7 parts of pulullan, 5-8 parts of rosin, propylene glycol monomethyl ether
0.4-0.7 parts, 5-8 parts of Aloe Vera Gel, 7-8 parts of mountain flour, 5-8 parts of silane coupling agent, 5-8 parts of lithium dihydrogen phosphate aerosol and adjacent benzene two
4-8 parts of formic acid dibutyl ester.
A kind of above-mentioned building shell mold plate thermal insulation fire-proof coating, is made of according to parts by weight following raw material: polyisocyanic acid
0.35 part of ester, 0.7 part of magnesia, 0.9 part of aluminium oxide, 0.6 part of titanium dioxide, 0.5 part of cetyl benzenesulfonic acid sodium, starch 8.5
Part, 0.55 part of ammonium metaborate, 11 parts of bentonite, 0.8 part of ethylene glycol monohexylether, 7.5 parts of Chinese honey locust glue, 0.5 part of nano silica,
5.5 parts of methylcellulose, 7.5 parts of coal tar pitch, 0.9 part of graphene, 0.65 part of dimethylethanolamine, 6.5 parts of rubber powder, cobaltous sulfate
0.4 part of calcium carbonate, 0.85 part of boric acid, 6.5 parts of chlorinated paraffin, 0.45 part of stearic acid sodium, 5 parts of cellulose acetate, ethyl acrylate
0.5 part, 0.5 part of poly- isobutyl ester, 0.65 part of aluminium hydroxide, 0.35 part of tributyl phosphate, 5.5 parts of pulullan, 6.5 parts of rosin,
0.55 part of propylene glycol monomethyl ether, 6.5 parts of Aloe Vera Gel, 7.5 parts of mountain flour, 6.5 parts of silane coupling agent, 6.5 parts of lithium dihydrogen phosphate aerosol
With 6 parts of dibutyl phthalate.
Compared with prior art, the invention has the benefit that
Inventing a kind of building shell mold plate provided has good general row with thermal insulation fire-proof coating, harmless, and has
There are the beneficial effects such as splendid heat-insulating, fire-preventing.
Specific embodiment
Embodiment 1
A kind of building shell mold plate thermal insulation fire-proof coating is made of according to parts by weight following raw material: 0.1 part of polyisocyanates, oxygen
Change 0.5 part of magnesium, 0.6 part of aluminium oxide, 0.4 part of titanium dioxide, 0.3 part of cetyl benzenesulfonic acid sodium, 6 parts of starch, ammonium metaborate 0.3
Part, 9 parts of bentonite, 0.4 part of ethylene glycol monohexylether, 5 parts of Chinese honey locust glue, 0.3 part of nano silica, 3 parts of methylcellulose, coal tar
6 parts of pitch, 0.7 part of graphene, 0.4 part of dimethylethanolamine, 4 parts of rubber powder, 0.2 part of cobaltous sulfate calcium carbonate, 0.5 part of boric acid, chlorine
4 parts of fossil waxes, 0.3 part of stearic acid sodium, 3 parts of cellulose acetate, 0.3 part of ethyl acrylate, 0.2 part of poly- isobutyl ester, aluminium hydroxide
0.4 part, 0.2 part of tributyl phosphate, 3 parts of pulullan, 4 parts of rosin, 0.3 part of propylene glycol monomethyl ether, 4 parts of Aloe Vera Gel, 6 parts of mountain flour,
4 parts of silane coupling agent, 4 parts of lithium dihydrogen phosphate aerosol and 3 parts of dibutyl phthalate.
Embodiment 2
A kind of above-mentioned building shell mold plate thermal insulation fire-proof coating, is made of according to parts by weight following raw material: polyisocyanates 0.6
Part, 0.9 part of magnesia, 1.2 parts of aluminium oxide, 0.8 part of titanium dioxide, 0.7 part of cetyl benzenesulfonic acid sodium, 11 parts of starch, inclined boron
0.8 part of sour ammonium, 13 parts of bentonite, 1.2 parts of ethylene glycol monohexylether, 10 parts of Chinese honey locust glue, 0.7 part of nano silica, Methyl cellulose
Plain 8 parts, 9 parts of coal tar pitch, 1.2 parts of graphene, 0.9 part of dimethylethanolamine, 9 parts of rubber powder, 0.6 part of cobaltous sulfate calcium carbonate, boron
Sour 1.2 parts, 9 parts of chlorinated paraffin, 0.6 part of stearic acid sodium, 7 parts of cellulose acetate, 0.7 part of ethyl acrylate, poly- isobutyl ester 0.8
Part, 0.9 part of aluminium hydroxide, 0.5 part of tributyl phosphate, 8 parts of pulullan, 9 parts of rosin, 0.8 part of propylene glycol monomethyl ether, Aloe Vera Gel 9
Part, 9 parts of mountain flour, 9 parts of silane coupling agent, 9 parts of lithium dihydrogen phosphate aerosol and 9 parts of dibutyl phthalate.
Embodiment 3
A kind of above-mentioned building shell mold plate thermal insulation fire-proof coating, is made of according to parts by weight following raw material: polyisocyanates
0.35 part, 0.7 part of magnesia, 0.9 part of aluminium oxide, 0.6 part of titanium dioxide, 0.5 part of cetyl benzenesulfonic acid sodium, 8.5 parts of starch,
0.55 part of ammonium metaborate, 11 parts of bentonite, 0.8 part of ethylene glycol monohexylether, 7.5 parts of Chinese honey locust glue, 0.5 part of nano silica, first
5.5 parts of base cellulose, 7.5 parts of coal tar pitch, 0.9 part of graphene, 0.65 part of dimethylethanolamine, 6.5 parts of rubber powder, cobaltous sulfate carbon
0.4 part of sour calcium, 0.85 part of boric acid, 6.5 parts of chlorinated paraffin, 0.45 part of stearic acid sodium, 5 parts of cellulose acetate, ethyl acrylate 0.5
Part, 0.5 part of poly- isobutyl ester, 0.65 part of aluminium hydroxide, 0.35 part of tributyl phosphate, 5.5 parts of pulullan, 6.5 parts of rosin, the third two
0.55 part of alcohol methyl ether, 6.5 parts of Aloe Vera Gel, 7.5 parts of mountain flour, 6.5 parts of silane coupling agent, 6.5 parts of lithium dihydrogen phosphate aerosol and neighbour
6 parts of dibatyl phithalate.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of building shell mold plate thermal insulation fire-proof coating, which is characterized in that be made of according to parts by weight following raw material: polyisocyanate cyanogen
0.1-0.6 parts of acid esters, 0.5-0.9 parts of magnesia, 0.6-1.2 parts of aluminium oxide, 0.4-0.8 parts of titanium dioxide, cetyl benzene sulphur
Sour sodium 0.3-0.7 parts, 6-11 parts of starch, 0.3-0.8 parts of ammonium metaborate, 9-13 parts of bentonite, ethylene glycol monohexylether 0.4-1.2
Part, 5-10 parts of Chinese honey locust glue, 0.3-0.7 parts of nano silica, 3-8 parts of methylcellulose, 6-9 parts of coal tar pitch, graphene
0.7-1.2 parts, 0.4-0.9 parts of dimethylethanolamine, 4-9 parts of rubber powder, 0.2-0.6 parts of cobaltous sulfate calcium carbonate, boric acid 0.5-1.2
Part, 4-9 parts of chlorinated paraffin, 0.3-0.6 parts of stearic acid sodium, 3-7 parts of cellulose acetate, 0.3-0.7 parts of ethyl acrylate, poly- isobutyl
0.2-0.8 parts of ester, 0.4-0.9 parts of aluminium hydroxide, 0.2-0.5 parts of tributyl phosphate, 3-8 parts of pulullan, 4-9 parts of rosin, third
0.3-0.8 parts of glycol methyl ether, 4-9 parts of Aloe Vera Gel, 6-9 parts of mountain flour, 4-9 parts of silane coupling agent, 4-9 parts of lithium dihydrogen phosphate aerosol
With 3-9 parts of dibutyl phthalate.
2. a kind of building shell mold plate thermal insulation fire-proof coating according to claim 1, which is characterized in that have according to parts by weight
Following raw material composition: 0.1-0.5 parts of polyisocyanates, 0.5-0.8 parts of magnesia, 0.6-1.1 parts of aluminium oxide, titanium dioxide 0.4-
0.7 part, 0.3-0.6 parts of cetyl benzenesulfonic acid sodium, 6-10 parts of starch, 0.3-0.7 parts of ammonium metaborate, 9-12 parts of bentonite, second
0.4-1.1 parts of glycol monohexyl ether, 5-9 parts of Chinese honey locust glue, 0.3-0.6 parts of nano silica, 3-7 parts of methylcellulose, coal tar drip
6-8 parts green, 0.7-1.1 parts of graphene, 0.4-0.8 parts of dimethylethanolamine, 4-8 parts of rubber powder, cobaltous sulfate calcium carbonate 0.2-0.5
Part, 0.5-1.1 parts of boric acid, 4-8 parts of chlorinated paraffin, 0.3-0.5 parts of stearic acid sodium, 3-6 parts of cellulose acetate, ethyl acrylate
0.3-0.6 parts, isobutyl ester 0.2-0.7 parts poly-, 0.4-0.8 parts of aluminium hydroxide, 0.2-0.4 parts of tributyl phosphate, pulullan 3-7
Part, 4-8 parts of rosin, 0.3-0.7 parts of propylene glycol monomethyl ether, 4-8 parts of Aloe Vera Gel, 6-8 parts of mountain flour, 4-8 parts of silane coupling agent, di(2-ethylhexyl)phosphate
4-8 parts and dibutyl phthalate 3-8 parts of hydrogen lithium aerosol.
3. a kind of building shell mold plate thermal insulation fire-proof coating according to claim 1, which is characterized in that have according to parts by weight
Following raw material composition: 0.2-0.5 parts of polyisocyanates, 0.6-0.8 parts of magnesia, 0.7-1.1 parts of aluminium oxide, titanium dioxide 0.5-
0.7 part, 0.4-0.6 parts of cetyl benzenesulfonic acid sodium, 7-10 parts of starch, 0.4-0.7 parts of ammonium metaborate, 10-12 parts of bentonite, second
0.5-1.1 parts of glycol monohexyl ether, 6-9 parts of Chinese honey locust glue, 0.4-0.6 parts of nano silica, 4-7 parts of methylcellulose, coal tar drip
7-8 parts green, 0.8-1.1 parts of graphene, 0.5-0.8 parts of dimethylethanolamine, 5-8 parts of rubber powder, cobaltous sulfate calcium carbonate 0.3-0.5
Part, 0.6-1.1 parts of boric acid, 5-8 parts of chlorinated paraffin, 0.4-0.5 parts of stearic acid sodium, 4-6 parts of cellulose acetate, ethyl acrylate
0.4-0.6 parts, isobutyl ester 0.3-0.7 parts poly-, 0.5-0.8 parts of aluminium hydroxide, 0.3-0.4 parts of tributyl phosphate, pulullan 4-7
Part, 5-8 parts of rosin, 0.4-0.7 parts of propylene glycol monomethyl ether, 5-8 parts of Aloe Vera Gel, 7-8 parts of mountain flour, 5-8 parts of silane coupling agent, di(2-ethylhexyl)phosphate
5-8 parts and dibutyl phthalate 4-8 parts of hydrogen lithium aerosol.
4. a kind of building shell mold plate thermal insulation fire-proof coating according to claim 1, which is characterized in that have according to parts by weight
Following raw material composition: 0.35 part of polyisocyanates, 0.7 part of magnesia, 0.9 part of aluminium oxide, 0.6 part of titanium dioxide, cetyl
0.5 part of benzene sulfonic acid sodium salt, 8.5 parts of starch, 0.55 part of ammonium metaborate, 11 parts of bentonite, 0.8 part of ethylene glycol monohexylether, Chinese honey locust glue 7.5
Part, 0.5 part of nano silica, 5.5 parts of methylcellulose, 7.5 parts of coal tar pitch, 0.9 part of graphene, dimethylethanolamine
0.65 part, 6.5 parts of rubber powder, 0.4 part of cobaltous sulfate calcium carbonate, 0.85 part of boric acid, 6.5 parts of chlorinated paraffin, 0.45 part of stearic acid sodium, vinegar
It is 5 parts of acid cellulose, 0.5 part of ethyl acrylate, 0.5 part of poly- isobutyl ester, 0.65 part of aluminium hydroxide, 0.35 part of tributyl phosphate, general
Blue 5.5 parts of the sugar in Shandong, 6.5 parts of rosin, 0.55 part of propylene glycol monomethyl ether, 6.5 parts of Aloe Vera Gel, 7.5 parts of mountain flour, 6.5 parts of silane coupling agent,
6.5 parts and 6 parts of dibutyl phthalate of lithium dihydrogen phosphate aerosol.