CN108944107A - The transfer printing adhesive paper and glassware of transfer film and the application transfer film - Google Patents
The transfer printing adhesive paper and glassware of transfer film and the application transfer film Download PDFInfo
- Publication number
- CN108944107A CN108944107A CN201710354608.8A CN201710354608A CN108944107A CN 108944107 A CN108944107 A CN 108944107A CN 201710354608 A CN201710354608 A CN 201710354608A CN 108944107 A CN108944107 A CN 108944107A
- Authority
- CN
- China
- Prior art keywords
- incorporated
- solid grain
- transfer film
- grain layer
- colored ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of transfer film comprising colored ink layers arc, the solid grain layer for being incorporated into one surface of colored ink layers arc, be incorporated into the solid grain layer separate colored ink layers arc surface metal layer and be incorporated into the metal layer separate solid grain layer surface adhesion coating.The transfer film has solid grain layer, and the surface of glass substrate can directly be arranged in by transfer modes, so that the glassware with solid grain and metallic luster be made, enriches the appearance of glassware.In addition, the present invention also provides a kind of transfer printing adhesive papers and glassware using above-mentioned transfer film.
Description
Technical field
The present invention relates to a kind of transfer films, using the transfer printing adhesive paper of the transfer film, and using the glassware of the transfer film.
Background technique
Glassware is widely used in various fields.The incrustation of existing glassware is generally using spraying, print
Brush etc. carries out incrustation, and the glassware that this kind of incrustation obtains is mostly single tone, and decorates without lines.Though existing
Also have in technology and glass is decorated using transfer film, but the performances such as existing transfer film adhesive force, hardness, endurance exist
Defect, tone is single, and decorates without lines.
Summary of the invention
In view of this, it is necessary to provide a kind of new transfer films, to solve the above problems.
In addition, there is a need to provide a kind of transfer printing adhesive paper using above-mentioned transfer film.
In addition, there is a need to provide a kind of glassware using above-mentioned transfer film.
A kind of transfer film comprising colored ink layers arc, combines the solid grain layer for being incorporated into one surface of colored ink layers arc
In the surface of the separate colored ink layers arc of the solid grain layer metal layer and be incorporated into the separate solid grain layer of the metal layer
Surface adhesion coating.
A kind of transfer printing adhesive paper comprising release paper and the transfer film for being incorporated into one surface of release paper, the transfer film include
Be incorporated into the colored ink layers arc on one surface of release paper, the separate release paper for being incorporated into the colored ink layers arc surface solid
Lines layer, be incorporated into the solid grain layer separate colored ink layers arc surface metal layer and be incorporated into the remote of the metal layer
The adhesion coating on the surface from solid grain layer.
A kind of glassware comprising glass substrate and the transfer film for being incorporated into a glass substrate at least surface, this turn
Die includes the adhesion coating for being incorporated into one surface of glass substrate, the gold for being incorporated into surface of the adhesion coating far from glass substrate
Belong to layer, the separate adhesion coating for being incorporated into the metal layer solid grain layer and be incorporated into the separate metal layer of the solid grain layer
Colored ink layers arc.
The transfer film has excellent performance, and has solid grain layer, can be directly arranged by transfer modes
The surface of glass substrate enriches the appearance of glassware so that the glassware with solid grain and metallic luster be made,
And simplify the processing procedure of the glassware with solid grain.
Detailed description of the invention
Fig. 1 is the schematic cross-section of the transfer film of present pre-ferred embodiments.
Fig. 2 is the schematic cross-section of the transfer printing adhesive paper of present pre-ferred embodiments.
Fig. 3 is the schematic cross-section of the glassware of present pre-ferred embodiments.
Main element symbol description
Transfer film 100
Colored ink layers arc 10
Solid grain layer 20
Metal layer 30
Adhesion coating 40
Transfer printing adhesive paper 200
Release paper 201
Glassware 300
Glass substrate 301
The present invention that the following detailed description will be further explained with reference to the above drawings.
Specific embodiment
Fig. 1 is please referred to, better embodiment of the present invention provides a kind of transfer film 100, is mainly used for being attached to glass
The surface of glass substrate 301 (ginseng Fig. 3), to be decorated to glass substrate 301.
The transfer film 100 includes colored ink layers arc 10, the solid grain layer for being incorporated into 10 1 surface of colored ink layers arc
20, it is incorporated into the metal layer 30 on the surface of the separate colored ink layers arc 10 of the solid grain layer 20 and is incorporated into metal layer 30
The adhesion coating 40 on the surface far from solid grain layer 20.
The colored ink layers arc 10 is used to provide color abundant for transfer film 100 and glass substrate 301.The colored ink
Layer 10 can be formed by way of printing or spraying.
The material of the solid grain layer 20 is ultraviolet hardening resin.The ultraviolet hardening resin can be total for acrylic acid
The conventional use of ultraviolet hardening resin such as polymers.The acrylic copolymer under the irradiation of ultraviolet light can be with rapid curing.It should
Solid grain layer 20 is formed in the surface of the colored ink layers arc 10 by the method imprinted.
The material of the metal layer 30 can be the metal conventionally used for film layer such as aluminium, copper, zinc, silver, platinum, titanium.The metal
Layer 30 is formed in the separate colored ink layers arc 10 of solid grain layer 20 by non-conductive electric plating methods such as vapor deposition or sputters
Surface.The surface of solid grain layer 20 is arranged in the metal layer 30, and solid grain is clearly showed.The gold
Belonging to layer 30 can make solid grain layer 20 show metallic luster.
The material of the adhesion coating 40 includes but is not limited to ethylene-acetic ethylene ester copolymer, acrylic resin and list
One or more of methyl ether propylene glycol acetate.In an at least embodiment, the material of the adhesion coating 40 is ethyl vinyl acetate
The composition of vinyl acetate co-polymer and acrylic resin.
Referring to Fig. 2, the present invention also provides a kind of transfer printing adhesive papers 200 comprising release paper 201 and be incorporated into the release paper
The transfer film 100 on 201 1 surfaces.The transfer film 100 include be incorporated into 201 1 surface of release paper colored ink layers arc 10,
It is incorporated into the solid grain layer 20 on the surface of the separate release paper 201 of the colored ink layers arc 10, is incorporated into the solid grain layer 20
Separate colored ink layers arc 10 surface metal layer 30 and be incorporated into the metal layer 30 separate solid grain layer 20 surface
Adhesion coating 40.
The material of the release paper 201 is polyolefin (polyolefine, PO) or polyethylene terephthalate
(polyester,PET)。
It should be understood that the transfer printing adhesive paper 200 can also include the table for being incorporated into the separate metal layer 30 of adhesion coating 40
The base stock (not shown) in face.The base stock is for protecting adhesion coating 40.
A kind of production method of transfer printing adhesive paper 200 comprising following steps:
Step S11 provides a release paper 201.The material of the release paper 201 is polyolefin or poly terephthalic acid second two
Ester.
Step S12 forms a colored ink layers arc 10 on a surface of the release paper 201.
Specifically, a colored ink is provided, by the colored ink by the method for printing or spraying in the release paper 201
A surface formed colored ink layers arc 10.
Step S13 forms a solid grain layer 20 on the surface of the separate release paper 201 of the colored ink layers arc 10.
Specifically, providing a surface has solid grain and transparent lines template (not shown), it is hard to provide a ultraviolet light
Change resin, ultraviolet hardening resin is coated in the surface of the separate release paper 201 of the colored ink layers arc 10, then by the line
The surface with solid grain of road template is placed on the surface with ultraviolet hardening resin of release paper 201, coining, ultraviolet
Photocuring forms a solid grain layer 20 on the surface of the separate release paper 201 of the colored ink layers arc 10.Preferably, should
Ultraviolet hardening resin is acrylic copolymer.
Step S14, in the forming metal layer on surface 30 of the separate colored ink layers arc 10 of the solid grain layer 20.
Specifically, stating the separate colored of solid grain layer 20 described by non-conductive electric plating methods such as vapor deposition or sputters
The forming metal layer on surface 30 of ink layer 10.The material of the metal layer 30 can for aluminium, copper, zinc, silver, platinum, titanium etc. conventionally used for
The metal of film layer.
Step S5 forms adhesion coating 40 on the surface of the separate solid grain layer 20 of the metal layer 30.
Specifically, provide an adhesive, by the adhesive coated the metal layer 30 separate solid grain layer 20
Surface forms adhesion coating 40.The material of the adhesive includes but is not limited to ethylene-acetic ethylene ester copolymer, acrylic acid
One or more of resin and monomethyl ether propylene glycol acetate.In an at least embodiment, the material of the adhesion coating 40 is
The composition of ethylene-acetic ethylene ester copolymer and acrylic resin.
Referring to Fig. 3, a kind of glassware 300 comprising glass substrate 301 and be incorporated into the glass substrate 301 at least
The transfer film 100 on one surface.The transfer film 100 includes the adhesion coating 40 for being incorporated into 301 1 surface of glass substrate, is incorporated into
The metal layer 30 on the surface of the adhesion coating 40 far from glass substrate 301, be incorporated into the metal layer 30 separate adhesion coating 40 it is vertical
Body lines layer 20 and be incorporated into the solid grain layer 20 separate metal layer 30 colored ink layers arc 10.
The glass substrate 301 can be flat glass or bend glass.
A kind of production method of glassware 300 comprising following steps:
Step S21: the glass substrate 301 is provided.
Step S22: the transfer printing adhesive paper 200 is provided.
The adhesion coating 40 of the transfer printing adhesive paper 200: being attached to the surface of the glass substrate 301 by step S23, remove from
Type paper 201 obtains glassware 300.
Adhesive force test, surface hardness test, wearability test, resistance to is carried out to the transfer film 100 of the glassware 300
Imparted test, solvent resistance test, cold-resistant thermal shock and the environmental performance test (Miniloop) of high temperature and humidity and resistance toization
Property test.
The adhesive force is measured using hundred lattice methods of testing of standard, and the adhesive force for measuring transfer film is 5B.
The surface hardness is measured using pencil hardness test method, and the surface hardness for measuring transfer film 100 is H.
The wearability is measured using paper tape friction testing (abrasion of RCA paper tape), and at attached middle school 175gf (gram force), revolving speed is
Under 16 revs/min~17 revs/min, pivoting friction is carried out to transfer film 100.Test result are as follows: glassware 300 after 100 turns of friction
Glass substrate 301 it is not exposed.
The method of the ultra-violet resistance test are as follows: illumination in 4 hours is carried out to transfer film 100, then under constant temperature and humidity
Storage 4 hours, then repeatedly illumination and constant temperature and humidity store 12 times.Wherein, illumination condition are as follows: a length of 340nm of ultraviolet light wave, spoke
Penetrating illumination is 0.63W/m2, temperature is 60 DEG C.The condition of constant temperature and humidity are as follows: temperature is 50 DEG C, humidity 95%RT.Test knot
Fruit is that 100 appearance of transfer film is unchanged, no damage.
The method of solvent resistance test are as follows: respectively using isopropanol, petroleum ether, synthetic perspiration to transfer film 100 into
Row wiping, wipes 200 times in 2 minutes.Test result is that the appearance of transfer film 100 is unchanged, no damage.
The test method of the Miniloop are as follows: glassware 300 is put into the punching of temperature shock case, adjusts temperature shock case
Ice chest temperature to subzero 40 DEG C, glassware 300 is now put into ice chest 2 hours, then shifts to 70 DEG C by the temperature of hot tank
It into hot tank and places 2 hours, carries out 5 circulations.Test result is that 100 appearance of transfer film is unchanged, no damage.
The test method of the endurance is, by hand lotion, suncream, lipstick, vanishing cream, black whirlwind insecticide, Jin Long
Fish edible oil is coated in the surface of the transfer film 100 of glassware 300 respectively, places 24 hours, observes transfer film 100.Test knot
Fruit is that 100 appearance of transfer film is unchanged, no damage.
By the above test result it is found that transfer film of the invention has stronger adhesive force, surface hardness, wearability, resistance to
The environmental performance and endurance of imparted, solvent resistance, cold-resistant thermal shock and high temperature and humidity.
Transfer film 100 of the invention has excellent performance, and has solid grain layer 20, can directly pass through transfer side
The surface of glass substrate 301 is arranged in formula, so that the glassware 300 with solid grain and metallic luster be made, enriches
The appearance of glassware 300, and simplify the processing procedure of the glassware 300 with solid grain.
In addition, for those of ordinary skill in the art, can make in accordance with the technical idea of the present invention other each
Kind changes and modifications, and all these changes and deformation all should belong to the protection scope of the claims in the present invention.
Claims (10)
1. a kind of transfer film, it is characterised in that: the transfer film includes colored ink layers arc, is incorporated into one surface of colored ink layers arc
Solid grain layer, be incorporated into the solid grain layer separate colored ink layers arc surface metal layer and be incorporated into the metal layer
Separate solid grain layer surface adhesion coating.
2. transfer film as described in claim 1, it is characterised in that: the material of the solid grain layer is UV cured tree
Rouge, the ultraviolet hardening resin are acrylic copolymer.
3. transfer film as described in claim 1, it is characterised in that: the material of the adhesion coating includes ethylene-vinyl acetate
One or more of co-polymer, acrylic resin and monomethyl ether propylene glycol acetate.
4. a kind of transfer printing adhesive paper comprising release paper and the transfer film for being incorporated into one surface of release paper, it is characterised in that: this turn
Die includes the table for being incorporated into the colored ink layers arc on one surface of release paper, being incorporated into the separate release paper of the colored ink layers arc
The solid grain layer in face, be incorporated into the solid grain layer separate colored ink layers arc surface metal layer and be incorporated into the gold
Belong to the adhesion coating on the surface of the separate solid grain layer of layer.
5. transfer printing adhesive paper as claimed in claim 4, it is characterised in that: the material of the solid grain layer is UV cured tree
Rouge, the ultraviolet hardening resin are acrylic copolymer.
6. transfer printing adhesive paper as claimed in claim 4, it is characterised in that: the material of the adhesion coating includes ethene-vinyl acetate
One or more of ester co-polymer, acrylic resin and monomethyl ether propylene glycol acetate.
7. transfer printing adhesive paper as claimed in claim 4, it is characterised in that: the material of the release paper is polyolefin or gathers to benzene two
Formic acid second diester.
8. a kind of glassware comprising glass substrate and the transfer film for being incorporated into a glass substrate at least surface, feature
Be: the transfer film includes the adhesion coating for being incorporated into one surface of glass substrate, is incorporated into the adhesion coating far from glass substrate
Surface metal layer, be incorporated into the metal layer separate adhesion coating solid grain layer and be incorporated into the solid grain layer
Colored ink layers arc far from metal layer.
9. glassware as claimed in claim 8, it is characterised in that: the material of the solid grain layer is UV cured tree
Rouge, the ultraviolet hardening resin are acrylic copolymer.
10. glassware as claimed in claim 8, it is characterised in that: the material of the adhesion coating includes ethene-vinyl acetate
One or more of ester co-polymer, acrylic resin and monomethyl ether propylene glycol acetate.