CN108943934A - A kind of manufacturing method of the decorating film using water-based ink - Google Patents
A kind of manufacturing method of the decorating film using water-based ink Download PDFInfo
- Publication number
- CN108943934A CN108943934A CN201810546420.8A CN201810546420A CN108943934A CN 108943934 A CN108943934 A CN 108943934A CN 201810546420 A CN201810546420 A CN 201810546420A CN 108943934 A CN108943934 A CN 108943934A
- Authority
- CN
- China
- Prior art keywords
- water
- based ink
- substrate
- parts
- decorating film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of manufacturing method of decorating film using water-based ink, the decorating film includes substrate, printing layer and facial mask, which is characterized in that the printing layer uses water-based ink；The manufacturing method includes pretreatment, printing and laminating step, specific as follows: (1) to pre-process: need to print the coated on one side water treatment agent of water-based ink in substrate；(2) print: being printed to pretreated substrate has been carried out using water-based ink；Be bonded: first pass through preheating wheel by after printing substrate and facial mask in 130 ~ 150 DEG C of preheating certain times, then by facial mask fit to print after substrate on；Then it hot mastication and embosses, then with 30m/min long response time certain time with cooling and shaping, and solidifies to obtain finished product through 48h.It uses water-based ink to the present invention, solves using solvent-based ink and the problem of environmental pollution present in decorating film production and use process.
Description
Technical field
The invention belongs to surface decorative film manufacturing technology fields, more particularly to a kind of decorating film using water-based ink
Manufacturing method.
Background technique
Since the 21th century, the research and application of surface decoration material are fast-developing, and wherein thin-film material such as PVC is thin
Film, PET film and laminated film etc. are various with its simple production process, incrustation pattern and effect, application method is simple,
Cost performance is high and occupies the leading position in novel surface ornament materials market, and application is more and more extensive.Incrustation
The primary structure of film is substrate, printing layer and facial mask, and it is successively pattern printed layers and table above that substrate, which is the core layer of decorating film,
Face wearing layer, that is, facial mask.Pattern printed layers generally use reverse-printed or direct intaglio printing to realize, for the matter for guaranteeing pattern printed layers
Amount, it is very high to the performance requirement of ink, and also used ink is all solvent-based ink.Solvent-based ink is in printing process
Environment is caused greatly to pollute, seriously affects the health of direct labor, and there are inflammable and explosive security risks；Another party
Face in the application process of decorating film, and applies in the use process of material of decorating film, equally exists to environment
Pollution problem.
Summary of the invention
The present invention in view of the deficiency of the prior art, proposes a kind of manufacture of decorating film using water-based ink
Method.It uses water-based ink, solves using solvent-based ink and the environment present in decorating film production and use process
Pollution problem.
The technical solution adopted for solving the technical problem of the present invention is a kind of manufacturer of the decorating film using water-based ink
Method, the decorating film include substrate, printing layer and facial mask, which is characterized in that the printing layer uses water-based ink；The system
It makes method and includes pretreatment, printing and laminating step, specific as follows:
(1) pre-process: the coated on one side water treatment agent of water-based ink need to be printed in substrate；
(2) print: being printed to pretreated substrate has been carried out using water-based ink；
(3) be bonded: first pass through preheating wheel by after printing substrate and facial mask in 130 ~ 150 DEG C of preheating certain times, then by mask sheet
On substrate after closing printing；Then it hot mastication and embosses, then with 30m/min long response time certain time with cooling and shaping, and
Solidify to obtain finished product through 48h.
Preferably, the time of the preheating is 10 ~ 20min, the time of the long response time is 20 ~ 30min, described
Hot mastication temperature be 160 ~ 200 DEG C.
Preferably, formula of the water-based ink in terms of mass parts are as follows:
43 ~ 47 parts of PUD,
2 ~ 3 parts of amine thickener,
2 ~ 4 parts of Silica,
7 ~ 35 parts of pigment,
1 ~ 2 part of amino modified silicone antifoams agent,
1 ~ 2 part of amino modified silicone levelling agent,
20 ~ 30 parts of distilled water,
20 ~ 30 parts of alcohol.
Preferably, the water treatment agent is 3% alum solution.
In the present invention, PVC film, PE film or PP film, coated water treatment agent and drying is usually can be selected in substrate
It is printed again with water-based ink afterwards, then carries out the fitting of facial mask after drying again.The usual PE film of facial mask, pvdf membrane or
PMMA film.
The present invention uses water-based ink printing layer, before printing water-based ink, is first coated with water treatment agent, the water in substrate surface
Inorganic agent can with substrate good combination but also with water-based ink good combination, thus make using water-based ink carry out printing become
It may；In facial mask fitting, certain time the pre-heat treatment first is carried out to substrate and facial mask and is bonded again, and using certain after embossing
Time long response time cooling and shaping and 48 hours cured modes, so that facial mask and water-based ink printing layer be made to be firmly combined.
Application of the present invention by water-based ink, surface preparation i.e. coating water treatment agent, optimization attaching process are successfully made
The standby decorating film using water-based ink, solve using solvent-based ink and present in the decorating film production and use process
Problem of environmental pollution.This uses the decorating film of water-based ink, meets the requirement of building materials and ornaments, is the important of entire industry
Breakthrough.
Detailed description of the invention
Fig. 1 is a kind of specific implementation method process flow diagram of the present invention.
Specific embodiment
Embodiment 1:
As shown in Figure 1, first being pre-processed using PVC film as substrate, it is coated with water treatment agent in substrate surface, is adopted after drying
It is printed to form printing layer with water-based ink, then is bonded facial mask after drying.Facial mask selects PVDF hyaline membrane.It is first passed through when fitting pre-
Heat wheel carries out 10min preheating to substrate and facial mask at 145 DEG C, then facial mask is fitted on substrate；With 160 DEG C of high temperature after fitting
Soften and emboss, then with 30m/min long response time 25min cooling and shaping, and solidifies to obtain finished product through 48h.
Water treatment agent used by preprocessing process is 3% alum solution.The composition of water-based ink in terms of mass parts as
Under:
45 parts of PUD,
2.5 parts of amine thickener,
3 parts of Silica,
20 parts of pigment,
1 part of modified silicone defoaming agent,
2 parts of modified silicone levelling agent,
25 parts of distilled water,
25 parts of alcohol.
Embodiment 2:
It using PVC film as substrate, is first pre-processed, is coated with water treatment agent in substrate surface, uses water-based ink after drying
Printing forms printing layer, then is bonded facial mask after drying.Facial mask selects PVDF hyaline membrane.Preheating wheel is first passed through when fitting to substrate
10min preheating is carried out at 140 DEG C with facial mask, then facial mask is fitted on substrate；It with 170 DEG C of hot mastications and is pressed after fitting
Line then with 30m/min long response time 30min cooling and shaping, and solidifies to obtain finished product through 48h.The water treatment agent of use and aqueous oil
Ink is the same as embodiment 1.
Embodiment 3:
It using PVC film as substrate, is first pre-processed, is coated with water treatment agent in substrate surface, uses water-based ink after drying
Printing forms printing layer, then is bonded facial mask after drying.Facial mask selects PMMA hyaline membrane.Preheating wheel is first passed through when fitting to substrate
15min preheating is carried out at 135 DEG C with facial mask, then facial mask is fitted on substrate；It with 190 DEG C of hot mastications and is pressed after fitting
Line then with 30m/min long response time 20min cooling and shaping, and solidifies to obtain finished product through 48h.The water treatment agent of use and aqueous oil
Ink is the same as embodiment 1.
Embodiment 4
The composition of water-based ink is as follows in terms of mass parts:
43 parts of PUD,
3 parts of amine thickener,
3 parts of Silica,
15 parts of pigment,
2 parts of modified silicone defoaming agent,
1 part of modified silicone levelling agent,
30 parts of distilled water,
20 parts of alcohol.
Remaining is same as Example 1.
Embodiment 5
The composition of water-based ink is as follows in terms of mass parts:
47 parts of PUD,
2 parts of amine thickener,
2 parts of Silica,
25 parts of pigment,
2 parts of modified silicone defoaming agent,
2 parts of modified silicone levelling agent,
30 parts of distilled water,
25 parts of alcohol.
Remaining is same as Example 1.
Claims (4)
1. a kind of manufacturing method of the decorating film using water-based ink, the decorating film includes substrate, printing layer and facial mask, spy
Sign is that the printing layer uses water-based ink；The manufacturing method includes pretreatment, printing and laminating step, specifically such as
Under:
(1) pre-process: the coated on one side water treatment agent of water-based ink need to be printed in substrate；
(2) print: being printed to pretreated substrate has been carried out using water-based ink；
(3) be bonded: first pass through preheating wheel by after printing substrate and facial mask in 130 ~ 150 DEG C of preheating certain times, then by mask sheet
On substrate after closing printing；Then it hot mastication and embosses, then with 30m/min long response time certain time with cooling and shaping, and
Solidify to obtain finished product through 48h.
2. the manufacturing method of the decorating film according to claim 1 using water-based ink, which is characterized in that the preheating
Time be 10 ~ 20min, time of the long response time is 20 ~ 30min, and the temperature of the hot mastication is 160 ~ 200
℃。
3. the manufacturing method of the decorating film according to claim 1 using water-based ink, which is characterized in that described is aqueous
Formula of the ink in terms of mass parts are as follows:
43 ~ 47 parts of PUD,
2 ~ 3 parts of amine thickener,
2 ~ 4 parts of Silica,
7 ~ 35 parts of pigment,
1 ~ 2 part of amino modified silicone antifoams agent,
1 ~ 2 part of amino modified silicone levelling agent,
20 ~ 30 parts of distilled water,
20 ~ 30 parts of alcohol.
4. the manufacturing method of the decorating film according to claim 1 using water-based ink, which is characterized in that at the water
Reason agent is 3% alum solution.