CN108943265A - Cucurbit lacquer method modelled after an antique - Google Patents
Cucurbit lacquer method modelled after an antique Download PDFInfo
- Publication number
- CN108943265A CN108943265A CN201810866351.9A CN201810866351A CN108943265A CN 108943265 A CN108943265 A CN 108943265A CN 201810866351 A CN201810866351 A CN 201810866351A CN 108943265 A CN108943265 A CN 108943265A
- Authority
- CN
- China
- Prior art keywords
- cucurbit
- liquid
- lacquer
- oil
- boiled wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the technical fields of cucurbit colouring can improve rate of drying during colouring, reduce the influence to operator, and the retention of cucurbit can be improved more particularly to a kind of cucurbit lacquer method modelled after an antique；The following steps are included: (1) boils boiled wood oil；(2) big paint ingredients is adjusted；(3) viscosity is adjusted；(4) coloration is adjusted；(5) it filters: (6) cucurbit pre-treatment: (7) colouring；(8) it dries.
Description
Technical field
The present invention relates to the technical fields of cucurbit colouring, more particularly to a kind of cucurbit lacquer method modelled after an antique.
Background technique
Cucurbit is a kind of annual herb plant, and vines are raw, leaf be it is heart-shaped, flower is white；Have all over China
Cultivation, thin among fruit, as two balls connect together, surface is smooth, can eat when tender, has good edible value and medicinal
Value, can be used for antidiarrheal draw spit, diuresis, detumescence, dissipating bind at the same can be used for assisting in the treatment of abdominal distension in water, dysphoria with smothery sensation, it is thirsty,
The symptoms such as jaundice, sore and ephritis, cirrhotic ascites；Fruit maturation rear casing lignifying, it is hollow, after certain processing
Various containers, such as wine pot, daily necessity, such as water ladle, singing insect toy, such as katydid cucurbit and various ornamental articles can be done.
In ancients, the big shape of the small tripe of cucurbit mouth can be very good to absorb the excellent gas field between staying in, and to not
Good gas field can effectively be inhibited, be checked, to build a suitable domestic environment, people like cucurbit, because
It like growth, can spread, more fruits, this characteristic, exactly with the original mother worship of the mankind and wish descendants multiply hope
Combine, express one's emotion by means of object, then produce people's doting on and worshipping to cucurbit, thus also derive it is many corresponding mythical and
The auspicious story of lucky good fortune, is mutually rushed from generation to generation, cucurbit just at it is trustworthy in people mind, increase the longevity, the auspicious, evil removing of drop, protect good fortune, help
The mascot of descendants, therefore, the people for liking now and buying cucurbit are more and more.To cater to consumer demand, existing calabash
Through the mode frequently with the lacquer on cucurbit surface cucurbit do old when Lu Shangse, improves the aesthetic measure of cucurbit, into
And meet the various consumption demands of consumer.
Lacquer also known as lacquer, raw lacquer, soil paint, state's paint, general term Chinese lacquer are a kind of natural resin coating, acquisition side
Method is after cutting open sumac bark, and from a kind of white sticky lotion of tough intradermal outflow, processed and manufactured coating makes a kind of pure
Natural prodcuts mainly contain macromolecule laccol, laccase, gumminess and moisture etc. in paint solution, are known as China " three is big precious " reputation name,
With the excellent performance such as anticorrosion, resistance to strong acid, resistance to highly basic, moisture-proof, insulation, high temperature resistant, resistance to soil resistance.
When being painted using lacquer to cucurbit, the rate of drying of lacquer is slower, and the ingredient in lacquer easily draws
Play the skin allergy of staff, and lacquer paint to cucurbit after the paint film color depth, the property that are formed be crisp, resistance to sunlight irradiation property
Difference, therefore use the retention of the cucurbit of lacquer colouring poor.
Summary of the invention
In order to solve the above technical problems, the present invention, which provides one kind, can improve rate of drying, reduction pair during colouring
The influence of operator, and the cucurbit lacquer method modelled after an antique of the retention of cucurbit can be improved.
Cucurbit lacquer method modelled after an antique of the invention, comprising the following steps:
(1) it boils boiled wood oil: raw tung oil heat temperature raising being brewed into boiled wood oil, is cooled to room temperature spare；
(2) it adjusts big paint ingredients: boiled wood oil is mixed with lacquer, and lead naphthenate liquid, manganese naphthenate liquid and naphthalene are added thereto
Sour cobalt liquid, being stirred continuously makes each component mixing that mixed liquor be made；
(3) it adjusts viscosity: a small amount of rosin being added into mixed liquor, adjusts the viscosity of mixed liquor；
(4) it adjusts coloration: can be adjusted in the mixed liquor after red water or pigment filtering and after addition to adjusting viscosity
Save the color of mixed liquor；
(5) filter: mixed liquor is filtered after the completion of adjusting coloration using terylene filter cloth, obtains colouring liquid；
(6) cucurbit pre-treatment: cleaning cucurbit using suds, removes the greasy dirt on cucurbit surface, and use clear water
Cucurbit is cleaned up, is dried spare；
(7) it paints: the cucurbit after drying being completely immersed in colouring liquid, cucurbit surface is made uniformly to paint；
(8) it dries: the cucurbit after colouring is put into drying unit, dried under certain drying temperature and drying wind speed
It is dry.
Cucurbit lacquer method modelled after an antique of the invention, boiled wood oil boiling method in the step (1) the following steps are included:
A, it boils for the first time: measuring the raw tung oil of 100kg, and raw tung oil is heated, raw tung oil is made to heat up in 30min
To 260 DEG C, stop heating immediately when raw tung oil is warming up to 260 DEG C, and be cooled to room temperature using cooling water and prepare mature paulownia
Oil；
B, it boils for second: measuring the raw tung oil of 50kg, and raw tung oil is heated, raw tung oil is made to heat up in 30min
To 260 DEG C, stops heating immediately when raw tung oil is warming up to 260 DEG C, measure the boiled wood oil after the completion of 50kg is boiled for the first time and be added
In boiled wood oil after the completion of boiling to second, and cooperate cooling water temperature, keeps the boiled wood oil of second of tanning near normal rapidly
Warm standby is used.
Cucurbit lacquer method modelled after an antique of the invention, the boiled wood oil, lacquer, lead naphthenate liquid, manganese naphthenate liquid, naphthoic acid cobalt liquid,
The additive amount of rosin and red water is respectively as follows:
Cucurbit lacquer method modelled after an antique of the invention, the boiled wood oil, lacquer, lead naphthenate liquid, manganese naphthenate liquid, naphthoic acid cobalt liquid,
The additive amount of rosin and pigment is respectively as follows:
Cucurbit lacquer method modelled after an antique of the invention, the preparation process of the cleaning solution in the step (6) the following steps are included:
A, soap is thinly sliced, and weighs 50g soap thin slice and is put into mixing vessel；
B, the water 2500ml-3000ml for measuring 100 DEG C, is poured into mixing vessel；
C, it is sufficiently stirred, soap thin slice is made to be dissolved in the water；
D, so that water is down to room temperature after dissolution spare.
Cucurbit lacquer method modelled after an antique of the invention, the drying temperature in the step (8) are 25 DEG C ± 2 DEG C.
Cucurbit lacquer method modelled after an antique of the invention, the drying wind speed in the step (8) are 15m/s.
Compared with prior art the invention has the benefit that cucurbit lacquer method modelled after an antique of the invention and existing method
Compared to having the advantage that
1, the component ratio that lacquer can be adjusted by adding boiled wood oil into lacquer, and can be by adding thereto
Lead naphthenate liquid, manganese naphthenate liquid and naphthoic acid cobalt liquid improve the rate of drying when painting to cucurbit, reduce the ingredient in lacquer
Volatilization, so as to avoid the allergic phenomena of operator；
2, the thick degree of lacquer can be adjusted, is painted to cucurbit according to requires to add rosin into lacquer
When more uniform, the phenomenon that reducing thick agglomeration；
3, cucurbit can be allow to have to adjust the final colour generation of lacquer by adding red water or pigment into lacquer
There is the different old styles that does, the cucurbit produced can more be made to meet the requirement of consumer；
4, the iron oxide in red water in conjunction with the laccol in lacquer show color reaction, can be made it is pitch-dark, wipe light be it is black
Beautiful effect, matting are ebony effect, and cucurbit can be made to do old effect with good when the method paints to cucurbit.
Specific embodiment
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not intended to limit the scope of the invention.
Embodiment 1
The raw tung oil of 100kg is measured, and raw tung oil is heated, so that raw tung oil is warming up to 260 DEG C in 30min, works as life
Tung oil is warming up to 260 DEG C and stops heating immediately, and is cooled to room temperature using cooling water and is prepared into boiled wood oil；It is raw to measure 50kg
Tung oil, and raw tung oil is heated, so that raw tung oil is warming up to 260 DEG C in 30min, when raw tung oil is warming up to 260 DEG C immediately
Stop heating, measures the boiled wood oil after the completion of 50kg is boiled for the first time and be added to second in the boiled wood oil after the completion of boiling, and
Cooperate cooling water temperature, making the boiled wood oil of second of tanning, near room temperature is spare rapidly.
Soap is thinly sliced, and weighs 50g soap thin slice and is put into mixing vessel, measures 100 DEG C of water 2500ml-
3000ml is poured into mixing vessel, is sufficiently stirred, and so that soap thin slice is dissolved in the water obtained suds, is down to room temperature after dissolution
It is spare.
Measure 10kg boiled wood oil mixed with 30kg lacquer, and thereto addition 5kg lead naphthenate liquid, 0.17kg manganese naphthenate liquid and
0.12kg naphthoic acid cobalt liquid, being stirred continuously makes each component mixing that mixed liquor be made, and the rate of drying of mixed liquor can be improved；To mixing
3kg rosin is added in liquid, adjusts the viscosity of mixed liquor；And by after 18kg red water or 5kg pigment filtering and be added to adjust
In mixed liquor after saving viscosity, the color of mixed liquor is adjusted；Finally use terylene filter cloth that will adjust mixed liquor after the completion of coloration
It is filtered, it is spare to obtain colouring liquid.
Cucurbit is cleaned using suds, removes the greasy dirt on cucurbit surface, and is cleaned up cucurbit using clear water,
It dries, the cucurbit after drying is completely immersed in colouring liquid, so that cucurbit surface is uniformly painted, is finally put into the cucurbit after colouring
In drying unit, adjusting the drying temperature in drying unit is 25 DEG C, and drying wind speed is 15m/s, is dried to cucurbit.
When using red water, the laccol in iron oxide and lacquer in red water shows color reaction, is made pitch-dark, uses face
It, can be according to the color for the color different adjustment colouring liquid that pigment is added when material.
Drying time of this method after the completion of painting to cucurbit is 300s, is operated during painting to cucurbit
Person is without allergic phenomena, and the cucurbit color after the completion of japanning is good, and paint film is secured, it is not easy to fall, and use fluorescent lamp
48h is irradiated to it, fast light irradiation property is good.
Embodiment 2
The raw tung oil of 100kg is measured, and raw tung oil is heated, so that raw tung oil is warming up to 260 DEG C in 30min, works as life
Tung oil is warming up to 260 DEG C and stops heating immediately, and is cooled to room temperature using cooling water and is prepared into boiled wood oil；It is raw to measure 50kg
Tung oil, and raw tung oil is heated, so that raw tung oil is warming up to 260 DEG C in 30min, when raw tung oil is warming up to 260 DEG C immediately
Stop heating, measures the boiled wood oil after the completion of 50kg is boiled for the first time and be added to second in the boiled wood oil after the completion of boiling, and
Cooperate cooling water temperature, making the boiled wood oil of second of tanning, near room temperature is spare rapidly.
Soap is thinly sliced, and weighs 50g soap thin slice and is put into mixing vessel, measures 100 DEG C of water 2500ml-
3000ml is poured into mixing vessel, is sufficiently stirred, and so that soap thin slice is dissolved in the water obtained suds, is down to room temperature after dissolution
It is spare.
Measure 10kg boiled wood oil mixed with 30kg lacquer, and thereto addition 4kg lead naphthenate liquid, 0.15kg manganese naphthenate liquid and
0.10kg naphthoic acid cobalt liquid, being stirred continuously makes each component mixing that mixed liquor be made, and the rate of drying of mixed liquor can be improved；To mixing
3kg rosin is added in liquid, adjusts the viscosity of mixed liquor；And by after 18kg red water or 5kg pigment filtering and be added to adjust
In mixed liquor after saving viscosity, the color of mixed liquor is adjusted；Finally use terylene filter cloth that will adjust mixed liquor after the completion of coloration
It is filtered, it is spare to obtain colouring liquid.
Cucurbit is cleaned using suds, removes the greasy dirt on cucurbit surface, and is cleaned up cucurbit using clear water,
It dries, the cucurbit after drying is completely immersed in colouring liquid, so that cucurbit surface is uniformly painted, is finally put into the cucurbit after colouring
In drying unit, adjusting the drying temperature in drying unit is 25 DEG C, and drying wind speed is 15m/s, is dried to cucurbit.
When using red water, the laccol in iron oxide and lacquer in red water shows color reaction, is made pitch-dark, uses face
It, can be according to the color for the color different adjustment colouring liquid that pigment is added when material.
Drying time of this method after the completion of painting to cucurbit is 410s, is operated during painting to cucurbit
Person is without allergic phenomena, and the cucurbit color after the completion of japanning is good, and paint film is secured, it is not easy to fall, and use fluorescent lamp
48h is irradiated to it, fast light irradiation property is good.
Embodiment 3
The raw tung oil of 100kg is measured, and raw tung oil is heated, so that raw tung oil is warming up to 260 DEG C in 30min, works as life
Tung oil is warming up to 260 DEG C and stops heating immediately, and is cooled to room temperature using cooling water and is prepared into boiled wood oil；It is raw to measure 50kg
Tung oil, and raw tung oil is heated, so that raw tung oil is warming up to 260 DEG C in 30min, when raw tung oil is warming up to 260 DEG C immediately
Stop heating, measures the boiled wood oil after the completion of 50kg is boiled for the first time and be added to second in the boiled wood oil after the completion of boiling, and
Cooperate cooling water temperature, making the boiled wood oil of second of tanning, near room temperature is spare rapidly.
Soap is thinly sliced, and weighs 50g soap thin slice and is put into mixing vessel, measures 100 DEG C of water 2500ml-
3000ml is poured into mixing vessel, is sufficiently stirred, and so that soap thin slice is dissolved in the water obtained suds, is down to room temperature after dissolution
It is spare.
Measure 10kg boiled wood oil mixed with 30kg lacquer, and thereto addition 6kg lead naphthenate liquid, 0.20kg manganese naphthenate liquid and
0.15kg naphthoic acid cobalt liquid, being stirred continuously makes each component mixing that mixed liquor be made, and the rate of drying of mixed liquor can be improved；To mixing
3kg rosin is added in liquid, adjusts the viscosity of mixed liquor；And by after 18kg red water or 5kg pigment filtering and be added to adjust
In mixed liquor after saving viscosity, the color of mixed liquor is adjusted；Finally use terylene filter cloth that will adjust mixed liquor after the completion of coloration
It is filtered, it is spare to obtain colouring liquid.
Cucurbit is cleaned using suds, removes the greasy dirt on cucurbit surface, and is cleaned up cucurbit using clear water,
It dries, the cucurbit after drying is completely immersed in colouring liquid, so that cucurbit surface is uniformly painted, is finally put into the cucurbit after colouring
In drying unit, adjusting the drying temperature in drying unit is 25 DEG C, and drying wind speed is 15m/s, is dried to cucurbit.
When using red water, the laccol in iron oxide and lacquer in red water shows color reaction, is made pitch-dark, uses face
It, can be according to the color for the color different adjustment colouring liquid that pigment is added when material.
Drying time of this method after the completion of painting to cucurbit is 350s, is operated during painting to cucurbit
Person is without allergic phenomena, and the cucurbit color after the completion of japanning is good, and paint film is secured, it is not easy to fall, and use fluorescent lamp
48h is irradiated to it, fast light irradiation property is good.
In conjunction with the above results, it is added when by 5kg lead naphthenate liquid, 0.17kg manganese naphthenate liquid and 0.12kg naphthoic acid cobalt liquid to 10kg
When in the mixed liquor of boiled wood oil and 30kg lacquer, colouring liquid obtained is when painting to cucurbit, the rate of drying for liquid of painting
Comparatively fast, and influence of the ingredient in lacquer to operator can be reduced, while daylight can be reduced by the way that boiled wood oil is added
Influence to lacquer, improves the performance of lacquer, and the retention of the cucurbit after lacquer colouring can be improved.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications, these improvements and modifications can also be made
Also it should be regarded as protection scope of the present invention.
Claims (7)
1. a kind of cucurbit lacquer method modelled after an antique, which comprises the following steps:
(1) it boils boiled wood oil: raw tung oil heat temperature raising being brewed into boiled wood oil, is cooled to room temperature spare；
(2) it adjusts big paint ingredients: boiled wood oil is mixed with lacquer, and lead naphthenate liquid, manganese naphthenate liquid and naphthoic acid cobalt are added thereto
Liquid, being stirred continuously makes each component mixing that mixed liquor be made；
(3) it adjusts viscosity: a small amount of rosin being added into mixed liquor, adjusts the viscosity of mixed liquor；
(4) it adjusts coloration: can be adjusted in the mixed liquor after red water or pigment filtering and after addition to adjusting viscosity mixed
Close the color of liquid；
(5) filter: mixed liquor is filtered after the completion of adjusting coloration using terylene filter cloth, obtains colouring liquid:
(6) cucurbit pre-treatment: cleaning cucurbit using suds, removes the greasy dirt on cucurbit surface, and use clear water by calabash
Reed cleans up, and dries spare:
(7) it paints: the cucurbit after drying being completely immersed in colouring liquid, cucurbit surface is made uniformly to paint；
(8) it dries: the cucurbit after colouring is put into drying unit, dried under certain drying temperature and drying wind speed.
2. cucurbit lacquer method modelled after an antique as described in claim 1, which is characterized in that the boiled wood oil tanning in the step (1)
Method the following steps are included:
A, it boils for the first time: measuring the raw tung oil of 100kg, and raw tung oil is heated, be warming up to raw tung oil in 30min
260 DEG C, stop heating immediately when raw tung oil is warming up to 260 DEG C, and be cooled to room temperature using cooling water and be prepared into boiled wood oil；
B, it boils for second: measuring the raw tung oil of 50kg, and raw tung oil is heated, raw tung oil is made to be warming up to 260 in 30min
DEG C, stop heating immediately when raw tung oil is warming up to 260 DEG C, measures the boiled wood oil after the completion of 50kg is boiled for the first time and be added to second
In boiled wood oil after the completion of secondary tanning, and cooperate cooling water temperature, making the boiled wood oil of second of tanning, near room temperature is spare rapidly.
3. cucurbit lacquer method modelled after an antique as described in claim 1, which is characterized in that the boiled wood oil, lacquer, lead naphthenate liquid,
Manganese naphthenate liquid, naphthoic acid cobalt liquid, rosin and red water additive amount be respectively as follows:
Boiled wood oil 10kg；
Lacquer 30kg；
Lead naphthenate liquid 3-6kg；
Manganese naphthenate liquid 0.15-0.20kg；
Naphthoic acid cobalt liquid 0.10-0.15kg；
Rosin 3-4kg；
Red water 14-21kg.
4. cucurbit lacquer method modelled after an antique as described in claim 1, which is characterized in that the boiled wood oil, lacquer, lead naphthenate liquid,
Manganese naphthenate liquid, naphthoic acid cobalt liquid, rosin and pigment additive amount be respectively as follows:
Boiled wood oil 10kg；
Lacquer 30kg；
Lead naphthenate liquid 3-6kg；
Manganese naphthenate liquid 0.15-0.20kg；
Naphthoic acid cobalt liquid 0.10-0.15kg；
Rosin 3-4kg；
Pigment 5-10kg.
5. cucurbit lacquer method modelled after an antique as described in claim 1, which is characterized in that the system of the suds in the step (6)
Standby process the following steps are included:
A, soap is thinly sliced, and weighs 50g soap thin slice and is put into mixing vessel；
B, the water 2500ml-3000ml for measuring 100 DEG C, is poured into mixing vessel；
C, it is sufficiently stirred, soap thin slice is made to be dissolved in the water；
D, so that water is down to room temperature after dissolution spare.
6. cucurbit lacquer method modelled after an antique as described in claim 1, which is characterized in that the drying temperature in the step (8) is
25℃±2℃。
7. cucurbit lacquer method modelled after an antique as described in claim 1, which is characterized in that the drying wind speed in the step (8) is
15m/s。