CN108943229A - A kind of wicker for braiding does old processing method - Google Patents
A kind of wicker for braiding does old processing method Download PDFInfo
- Publication number
- CN108943229A CN108943229A CN201810899570.7A CN201810899570A CN108943229A CN 108943229 A CN108943229 A CN 108943229A CN 201810899570 A CN201810899570 A CN 201810899570A CN 108943229 A CN108943229 A CN 108943229A
- Authority
- CN
- China
- Prior art keywords
- wicker
- parts
- treatment liquid
- old
- single treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wickers for braiding to do old processing method, belongs to wicker processing technology field, comprising the following steps: (1) wicker pre-processes;(2) old processing is done;(3) curing process.Processing method, which handles finally obtained wicker, through the invention has the function of antibacterial, deinsectization, do old clean mark, uniformly, antique effect is good, and treatment fluid is combined closely with wicker, do it is old effect is lasting, stabilization, great market popularization value.
Description
Technical field
The invention belongs to wicker processing technology fields, and in particular to a kind of wicker for braiding does old processing method.
Background technique
Wicker plaiting article is one of folks of china traditional handicraft product.People are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project for becoming selected areas of China foreign exchange earning gradually.The whole nation has three big
Wicker plaiting article production base, Hubei, Shandong, Anhui (in addition Henan also abounds with wicker plaiting article).Wicker soft pliable, thickness are well-balanced, color is high
It is refined, by novel design, natural, handsome in appearance, Portable durable the practical art product of various honesties can be woven into.Its product
It include: crate (packet), meal basket, food basket (circle, ellipse), bamboo strainer, needlework shallow basket made of wicker or thin bamboo strips, kang mat, reed matting etc..As industry is constantly sent out
Exhibition, product are constantly brought forth new ideas, and the willow for having more Nover practical beauties is presented in face of client.
People gradually increase the interest of wicker products modelled after an antique in recent years, do the side of old processing for wicker products at present
Formula mainly carries out doing old processing modelled after an antique by painting.The variation in style is carried out by simple process of surface treatment, together
When it is this processing need using a large amount of chemicals, processing cost is higher, and treatment effect can not be stablized for a long time, basic nothing
Method meets the high request of present consumer.
Summary of the invention
The purpose of the present invention is being directed to existing problem, provides a kind of wicker for braiding and do old processing method.It is logical
Crossing processing method of the present invention and handling finally obtained wicker has the function of antibacterial, deinsectization, does old clean mark, uniformly, modelled after an antique
Effect is good, and treatment fluid is combined closely with wicker, do it is old effect is lasting, stablize, great market popularization value.
The present invention is achieved by the following technical solutions:
A kind of wicker for braiding does old processing method, comprising the following steps:
(1) wicker pre-processes:
A. it takes the soil of long-term plantation crops to be placed in tap water, clay coating is obtained after stirring and evenly mixing, the wicker of peeling is soaked in
In clay coating, the time of immersion treatment is 55-65min;
B. the wicker taking-up in operation a in clay coating, which is placed under tap water, is rinsed, until clay coating is washed out completely, then sets
It is dried in the environment that temperature is 50-60 DEG C, drying to surface moisture content is 28-32%;
C. it selects carpenter's sand paper of 240 mesh to carry out polishing processing to the surface in operation b, removes the fiber on surface;
(2) old processing is done:
A. it prepares single treatment liquid pretreated wicker in step (1) is soaked in single treatment liquid, keeps primary place
Managing the temperature in liquid is 55-57 DEG C, and the process of single treatment liquid immersion treatment carries out in steady magnetic field environment, single treatment liquid
The time of immersion is 1-2d;
B. a single treatment liquid will be operated treated and be dried in the environment that wicker is put into temperature is 50-56 DEG C, it is dry extremely
Surface moisture content is 18-24%;
C. one layer of secondary treatment liquid is uniformly sprayed in the wicker surface after being dried in operation b;
D. will treated that wicker is placed in infrared drying room for secondary treatment liquid in operation c, the wavelength of infrared ray is 30-40 μ
M, drying to surface moisture content are 8-10%;
(3) curing process:
By treated in step (2), wicker is placed in carries out ultra-violet curing in uv curing machine and guarantee the quality processing, and ultraviolet wavelength is
240-280nm, the time for solidifying processing of guaranteeing the quality is 35-45min.
Further, the intensity of steady magnetic field is 1300-1400Gs in step (2) the operation a.
Further, single treatment liquid in step (2) the operation a, is made of: copper sulphate 10- following parts by weight of component
14 parts, 15-17 parts of sodium chloride, 8-10 parts of isoamyl alcohol, 7-9 parts of cineole, 4-8 parts of citronellal, 13-15 parts of light-coloured vinegar, sterile water
500-600 parts.
Further, secondary treatment liquid in step (2) the operation c, is made of: detergent alkylate following parts by weight of component
4-5 parts of sodium sulfonate, 3-4 parts of Tween 80,1-2 parts of beta -mercaptoethanol, 4-6 parts of chamazulene, 3-5 parts of tea polyphenols, sodium hydroxide 5-6
Part, 180-240 parts of sterile water.
The present invention provides a kind of wickers for braiding to do old processing method, pre-processes first to wicker, specifically
To decompose wicker surface using substances such as microorganisms in soil, softening, and it is conducive to improve the uniformity on surface, to do
Certain basis is established in old processing.Old processing will be done in subsequent operation and drying process combines, and drying process is divided into three
A stage is first placed in the environment that temperature is 50-60 DEG C and is dried, and drying to surface moisture content is 28-32%, dry journey
Spend lower, degree of drying is excessive, and wicker surface is easily cracked, and and then carries out surface grinding processing, keeps wicker surface smooth clean
Only, it then places it in single treatment liquid and is impregnated, copper sulphate, sodium chloride, isoamyl alcohol, eucalyptus are added in single treatment liquid
Brain, citronellal, light-coloured vinegar make single treatment liquid that faintly acid be presented, and faintly acid can have slight corrosiveness to wicker, play certain
Do old effect, cineole, citronellal, light-coloured vinegar are black to play the role of sterilization, deinsectization, kill the germ and worm on wicker surface
The microorganism that may be carried after ovum, and pretreatment, the process of single treatment liquid processing are the steady magnetic field rings in certain strength
It is carried out in border, steady magnetic field environment, can not only promote doing for single treatment liquid old efficiency and to do old effect, can also eliminate willow
The side effect of drawing stress on surface, treated that wicker is put into the environment that temperature is 50-56 DEG C is dried for single treatment liquid,
Drying to surface moisture content is 18-24%, and degree of drying is slightly stronger than for the first time at this time, then sprays secondary treatment liquid on its surface, again
The stress rupture that is dried and may cause can be further eliminated, neopelex is added in secondary treatment liquid, is spat
Warm 80, beta -mercaptoethanol, chamazulene, tea polyphenols, sodium hydroxide, secondary treatment liquid are presented alkalescence environment, have to wicker surface
Slight corrosiveness, and react to each other with single treatment liquid on wicker surface, increase the uniformity of wicker texture and do old effect
Ingredient in fruit and secondary treatment liquid also has the function of sterilization, deinsectization, promotes the quality of wicker, and secondary treatment liquid handles it
Afterwards, wicker is placed in infrared drying room, the wavelength of infrared ray is 30-40 μm, it is dry to surface moisture content be 8-10%, three
Secondary degree of drying is incremental, can not only make to do old effect more obvious, moreover it is possible to effectively prevent wicker surface stress from acting on
The phenomenon that causing wicker to crack.Wicker is finally placed in progress ultra-violet curing processing in uv curing machine, promotes to do old line
Reason is more clear, uniformly, moreover it is possible to be effectively promoted that treatment fluid is long-lasting to wicker to work, be kept the stabilization for doing old performance
Property, promote the application value of wicker.
The present invention has the advantage that compared with prior art
Processing method, which handles finally obtained wicker, through the invention has the function of antibacterial, deinsectization, do old clean mark,
Even, antique effect is good, and treatment fluid is combined closely with wicker, do it is old effect is lasting, stablize, great market popularization value.
Specific embodiment
Embodiment 1
A kind of wicker for braiding does old processing method, comprising the following steps:
(1) wicker pre-processes:
A. it takes the soil of long-term plantation crops to be placed in tap water, clay coating is obtained after stirring and evenly mixing, the wicker of peeling is soaked in
In clay coating, the time of immersion treatment is 55min;
B. the wicker taking-up in operation a in clay coating, which is placed under tap water, is rinsed, until clay coating is washed out completely, then sets
It is dried in the environment that temperature is 50 DEG C, drying to surface moisture content is 28%;
C. it selects carpenter's sand paper of 240 mesh to carry out polishing processing to the surface in operation b, removes the fiber on surface;
(2) old processing is done:
A. it prepares single treatment liquid pretreated wicker in step (1) is soaked in single treatment liquid, keeps primary place
Managing the temperature in liquid is 55 DEG C, and the process of single treatment liquid immersion treatment carries out in steady magnetic field environment, the leaching of single treatment liquid
The time of bubble is 1d;
B. a single treatment liquid will be operated treated and be dried in the environment that wicker is put into temperature is 50 DEG C, it is dry to surface
Moisture content is 18%;
C. one layer of secondary treatment liquid is uniformly sprayed in the wicker surface after being dried in operation b;
D. will treated that wicker is placed in infrared drying room for secondary treatment liquid in operation c, the wavelength of infrared ray is 30 μm,
Drying to surface moisture content is 8%;
(3) curing process:
By treated in step (2), wicker is placed in carries out ultra-violet curing in uv curing machine and guarantee the quality processing, and ultraviolet wavelength is
240nm, the time for solidifying processing of guaranteeing the quality is 35min.
Further, the intensity of steady magnetic field is 1300Gs in step (2) the operation a.
Further, single treatment liquid in step (2) the operation a, is made of: copper sulphate 10 following parts by weight of component
Part, 15 parts of sodium chloride, 8 parts of isoamyl alcohol, 7 parts of cineole, 4 parts of citronellal, 13 parts of light-coloured vinegar, 500 parts of sterile water.
Further, secondary treatment liquid in step (2) the operation c, is made of: detergent alkylate following parts by weight of component
4 parts of sodium sulfonate, 3 parts of Tween 80,1 part of beta -mercaptoethanol, 4 parts of chamazulene, 3 parts of tea polyphenols, 5 parts of sodium hydroxide, sterile water 180
Part.
Embodiment 2
A kind of wicker for braiding does old processing method, comprising the following steps:
(1) wicker pre-processes:
A. it takes the soil of long-term plantation crops to be placed in tap water, clay coating is obtained after stirring and evenly mixing, the wicker of peeling is soaked in
In clay coating, the time of immersion treatment is 60min;
B. the wicker taking-up in operation a in clay coating, which is placed under tap water, is rinsed, until clay coating is washed out completely, then sets
It is dried in the environment that temperature is 55 DEG C, drying to surface moisture content is 30%;
C. it selects carpenter's sand paper of 240 mesh to carry out polishing processing to the surface in operation b, removes the fiber on surface;
(2) old processing is done:
A. it prepares single treatment liquid pretreated wicker in step (1) is soaked in single treatment liquid, keeps primary place
Managing the temperature in liquid is 56 DEG C, and the process of single treatment liquid immersion treatment carries out in steady magnetic field environment, the leaching of single treatment liquid
The time of bubble is 1.5d;
B. a single treatment liquid will be operated treated and be dried in the environment that wicker is put into temperature is 53 DEG C, it is dry to surface
Moisture content is 21%;
C. one layer of secondary treatment liquid is uniformly sprayed in the wicker surface after being dried in operation b;
D. will treated that wicker is placed in infrared drying room for secondary treatment liquid in operation c, the wavelength of infrared ray is 35 μm,
Drying to surface moisture content is 9%;
(3) curing process:
By treated in step (2), wicker is placed in carries out ultra-violet curing in uv curing machine and guarantee the quality processing, and ultraviolet wavelength is
260nm, the time for solidifying processing of guaranteeing the quality is 40min.
Further, the intensity of steady magnetic field is 1350Gs in step (2) the operation a.
Further, single treatment liquid in step (2) the operation a, is made of: copper sulphate 12 following parts by weight of component
Part, 16 parts of sodium chloride, 9 parts of isoamyl alcohol, 8 parts of cineole, 6 parts of citronellal, 14 parts of light-coloured vinegar, 550 parts of sterile water.
Further, secondary treatment liquid in step (2) the operation c, is made of: detergent alkylate following parts by weight of component
4-5 parts of sodium sulfonate, 3.5 parts of Tween 80,1.5 parts of beta -mercaptoethanol, 5 parts of chamazulene, 4 parts of tea polyphenols, 5.5 parts of sodium hydroxide, nothing
210 parts of bacterium water.
Embodiment 3
A kind of wicker for braiding does old processing method, comprising the following steps:
(1) wicker pre-processes:
A. it takes the soil of long-term plantation crops to be placed in tap water, clay coating is obtained after stirring and evenly mixing, the wicker of peeling is soaked in
In clay coating, the time of immersion treatment is 65min;
B. the wicker taking-up in operation a in clay coating, which is placed under tap water, is rinsed, until clay coating is washed out completely, then sets
It is dried in the environment that temperature is 60 DEG C, drying to surface moisture content is 32%;
C. it selects carpenter's sand paper of 240 mesh to carry out polishing processing to the surface in operation b, removes the fiber on surface;
(2) old processing is done:
A. it prepares single treatment liquid pretreated wicker in step (1) is soaked in single treatment liquid, keeps primary place
Managing the temperature in liquid is 57 DEG C, and the process of single treatment liquid immersion treatment carries out in steady magnetic field environment, the leaching of single treatment liquid
The time of bubble is 2d;
B. a single treatment liquid will be operated treated and be dried in the environment that wicker is put into temperature is 56 DEG C, it is dry to surface
Moisture content is 24%;
C. one layer of secondary treatment liquid is uniformly sprayed in the wicker surface after being dried in operation b;
D. will treated that wicker is placed in infrared drying room for secondary treatment liquid in operation c, the wavelength of infrared ray is 40 μm,
Drying to surface moisture content is 10%;
(3) curing process:
By treated in step (2), wicker is placed in carries out ultra-violet curing in uv curing machine and guarantee the quality processing, and ultraviolet wavelength is
280nm, the time for solidifying processing of guaranteeing the quality is 45min.
Further, the intensity of steady magnetic field is 1400Gs in step (2) the operation a.
Further, single treatment liquid in step (2) the operation a, is made of: copper sulphate 14 following parts by weight of component
Part, 17 parts of sodium chloride, 10 parts of isoamyl alcohol, 9 parts of cineole, 8 parts of citronellal, 15 parts of light-coloured vinegar, 600 parts of sterile water.
Further, secondary treatment liquid in step (2) the operation c, is made of: detergent alkylate following parts by weight of component
5 parts of sodium sulfonate, 4 parts of Tween 80,2 parts of beta -mercaptoethanol, 6 parts of chamazulene, 5 parts of tea polyphenols, 6 parts of sodium hydroxide, sterile water 240
Part.
Claims (4)
1. a kind of wicker for braiding does old processing method, which comprises the following steps:
(1) wicker pre-processes:
A. it takes the soil of long-term plantation crops to be placed in tap water, clay coating is obtained after stirring and evenly mixing, the wicker of peeling is soaked in
In clay coating, the time of immersion treatment is 55-65min;
B. the wicker taking-up in operation a in clay coating, which is placed under tap water, is rinsed, until clay coating is washed out completely, then sets
It is dried in the environment that temperature is 50-60 DEG C, drying to surface moisture content is 28-32%;
C. it selects carpenter's sand paper of 240 mesh to carry out polishing processing to the surface in operation b, removes the fiber on surface;
(2) old processing is done:
A. it prepares single treatment liquid pretreated wicker in step (1) is soaked in single treatment liquid, keeps primary place
Managing the temperature in liquid is 55-57 DEG C, and the process of single treatment liquid immersion treatment carries out in steady magnetic field environment, single treatment liquid
The time of immersion is 1-2d;
B. a single treatment liquid will be operated treated and be dried in the environment that wicker is put into temperature is 50-56 DEG C, it is dry extremely
Surface moisture content is 18-24%;
C. one layer of secondary treatment liquid is uniformly sprayed in the wicker surface after being dried in operation b;
D. will treated that wicker is placed in infrared drying room for secondary treatment liquid in operation c, the wavelength of infrared ray is 30-40 μ
M, drying to surface moisture content are 8-10%;
(3) curing process:
By treated in step (2), wicker is placed in carries out ultra-violet curing in uv curing machine and guarantee the quality processing, and ultraviolet wavelength is
240-280nm, the time for solidifying processing of guaranteeing the quality is 35-45min.
2. a kind of wicker for braiding does old processing method according to claim 1, which is characterized in that the step (2)
The intensity for operating steady magnetic field in a is 1300-1400Gs.
3. a kind of wicker for braiding does old processing method according to claim 1, which is characterized in that the step (2)
Single treatment liquid in a is operated, is made of following parts by weight of component: 10-14 parts of copper sulphate, 15-17 parts of sodium chloride, isoamyl alcohol 8-10
Part, 7-9 parts of cineole, 4-8 parts of citronellal, 13-15 parts of light-coloured vinegar, 500-600 parts of sterile water.
4. a kind of wicker for braiding does old processing method according to claim 1, which is characterized in that the step (2)
Secondary treatment liquid in c is operated, is made of following parts by weight of component: 4-5 parts of neopelex, 3-4 parts of Tween 80, β-
1-2 parts of mercaptoethanol, 4-6 parts of chamazulene, 3-5 parts of tea polyphenols, 5-6 parts of sodium hydroxide, 180-240 parts of sterile water.