CN108930157A - A kind of uvioresistant and the resistance to composite finishing technique soaped of fabric - Google Patents
A kind of uvioresistant and the resistance to composite finishing technique soaped of fabric Download PDFInfo
- Publication number
- CN108930157A CN108930157A CN201810646094.8A CN201810646094A CN108930157A CN 108930157 A CN108930157 A CN 108930157A CN 201810646094 A CN201810646094 A CN 201810646094A CN 108930157 A CN108930157 A CN 108930157A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistance
- fabric
- finishing
- soaped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of uvioresistants of fabric and the resistance to composite finishing technique soaped, comprising the following steps: (1) anti-ultraviolet finishing;(2) resistance to arrangement of soaping;(3) it washes;(4) it dries.Compared with prior art, the invention has the benefit that composite finishing technique of the invention makes fabric be provided simultaneously with uvioresistant and resistance to performance of soaping, anti-ultraviolet finishing of the invention makes fabric have water-fastness and dry-cleaning, and to light, thermally and chemically product stability, arrangement process safety are environmentally friendly;Resistance to arrangement of soaping of the invention makes fabric have excellent fungicidal properties, and has good corrosion resistance, wrinkle resistance and antibacterial flame-retardant, to extend the service life of fabric.
Description
Technical field
The present invention relates to fabric final finishing field, the uvioresistant of especially a kind of fabric and the resistance to composite finishing work soaped
Skill.
Background technique
With the quickening of human civilization process, the change of the progress of science and technology and consumption idea, people are to influence quality of life
Food, clothing, housing and transportation etc. requirement it is higher and higher.Requirement to clothes is real from initial screening body, warming, protection etc.
With property, diversion functionality, both effectiveness, comfort.The textile fabric of Multifunctional finishing is just concerned by people and likes.It is existing
Anti-ultraviolet finishing be primarily present ultraviolet light finishing fluid and face liber binding force difference defect, fabric is after washing several times
Afterwards, anti-uv-ray weakens rapidly, i.e., the fabric arranged using existing anti-ultraviolet finishing liquid, and ultraviolet-resistent property is resistance to
Long property is poor.
Fabric is in afterfinish, it is generally the case that the resistance to performance of soaping of fabric is all poor, after long-term soap
Leading to fabric, fungicidal properties is poor in use, service life is short, so that the antibacterial bacteriostatic performance of fabric is poor.
Summary of the invention
It is existing to solve the object of the present invention is to provide a kind of uvioresistant of fabric and the resistance to composite finishing technique soaped
Deficiency in technology, it enables to fabric to be provided simultaneously with excellent anti-ultraviolet property and resistance to performance of soaping, improves fabric
Safety.
The present invention provides a kind of uvioresistants of fabric and the resistance to composite finishing technique soaped, comprising the following steps:
(1) anti-ultraviolet finishing: fabric being impregnated into anti-ultraviolet finishing liquid, is handled using second dipping and rolling, described anti-
Ultraviolet light finishing fluid includes the component of following parts by weight: 6-9 parts of 5-aminosalicylic acids, 5-7 parts of nano particles, 1-3 parts of dispersions
Agent, 11-16 parts of ethyl alcohol, 4-7 parts of fatty alcohol polyoxyethylene ether, 5-10 parts of sodium lactates, 2-4 parts of sodium pyrophosphates, 7-12 parts of Plant Powders
End, 3-5 parts of urea, 5-7 parts of glycerol and 22-28 parts of deionized waters;
(2) resistance to arrangement of soaping: the fabric after anti-ultraviolet finishing being added in resistance to finishing fluid of soaping and is handled, described resistance to
Finishing fluid of soaping includes the component of following parts by weight: 80-120 parts of distilled water, 45-50 parts of butyl acetates, 23-28 parts of fillings
Agent, 0.2-0.8 parts of lead acetates, 6-10 parts of ethylene glycol, 16-28 parts of polyvinyl alcohol, 18-28 parts of seven polyglycol ethers of dodecyl,
15-17 parts of alanine, 8-10 parts of Sodium Polyacrylates, 7-12 parts of zinc sulfate and 4-8 parts of aloe fibres;
(3) it washes: the fabric Jing Guo resistance to arrangement of soaping being cleaned multiple times using clear water;
(4) dry: by the fabric after washing at 82-88 DEG C preliminary drying 3-5min, then heat at 100-115 DEG C and bake 5-
8min is dried at 78-82 DEG C after then washing fabric again, completes the composite finishing of fabric.
Preferably, second dipping and rolling condition described in step (1) is bath raio 1:18, pick-up rate 77-82%, and padding temperature is
58-66℃。
Preferably, anti-ultraviolet finishing liquid described in step (1) includes the component of following parts by weight: 7 parts of 5- amino
Salicylic acid, 6 parts of nano particles, 2 parts of dispersing agents, 13 parts of ethyl alcohol, 6 parts of fatty alcohol polyoxyethylene ether, 8 parts of sodium lactates, 3 parts of pyrophosphoric acids
Sodium, 10 parts of plant powders, 4 parts of urea, 6 parts of glycerol and 25 parts of deionized waters.
Preferably, the nano particle is one of nano-titanium dioxide, nano zine oxide or a variety of.
Preferably, the dispersing agent is triethanolamine, Tween-80, Tween-60, Span -60, polyethylene glycol, six inclined phosphorus
One or more of sour sodium.
Preferably, the resistance to finishing fluid of soaping includes the component of following parts by weight: 105 parts of distilled water, 48 parts of acetic acid
Butyl ester, 25 parts of fillers, 0.5 part of lead acetate, 7 parts of ethylene glycol, 23 parts of polyvinyl alcohol, 24 parts of seven polyglycol ethers of dodecyl,
16 parts of alanine, 9 parts of Sodium Polyacrylates, 10 parts of zinc sulfate and 6 parts of aloe fibres.
Preferably, the filler is calcium bicarbonate.
Compared with prior art, the invention has the benefit that composite finishing technique of the invention makes fabric while having
Standby uvioresistant and resistance to performance of soaping, anti-ultraviolet finishing of the invention makes fabric have water-fastness and dry-cleaning, to light, heat and change
Product stability arranges process safety environmental protection;Resistance to arrangement of soaping of the invention makes fabric have excellent fungicidal properties, and has
There are good corrosion resistance, wrinkle resistance and antibacterial flame-retardant, to extend the service life of fabric.
Specific embodiment
The embodiment of the present invention: a kind of uvioresistant and the resistance to composite finishing technique soaped of fabric, comprising the following steps:
(1) anti-ultraviolet finishing: fabric being impregnated into anti-ultraviolet finishing liquid, is handled using second dipping and rolling, described anti-
Ultraviolet light finishing fluid includes the component of following parts by weight: 6-9 parts of 5-aminosalicylic acids, 5-7 parts of nano particles, 1-3 parts of dispersions
Agent, 11-16 parts of ethyl alcohol, 4-7 parts of fatty alcohol polyoxyethylene ether, 5-10 parts of sodium lactates, 2-4 parts of sodium pyrophosphates, 7-12 parts of Plant Powders
End, 3-5 parts of urea, 5-7 parts of glycerol and 22-28 parts of deionized waters;
(2) resistance to arrangement of soaping: the fabric after anti-ultraviolet finishing being added in resistance to finishing fluid of soaping and is handled, described resistance to
Finishing fluid of soaping includes the component of following parts by weight: 80-120 parts of distilled water, 45-50 parts of butyl acetates, 23-28 parts of fillings
Agent, 0.2-0.8 parts of lead acetates, 6-10 parts of ethylene glycol, 16-28 parts of polyvinyl alcohol, 18-28 parts of seven polyglycol ethers of dodecyl,
15-17 parts of alanine, 8-10 parts of Sodium Polyacrylates, 7-12 parts of zinc sulfate and 4-8 parts of aloe fibres;
(3) it washes: the fabric Jing Guo resistance to arrangement of soaping being cleaned multiple times using clear water;
(4) dry: by the fabric after washing at 82-88 DEG C preliminary drying 3-5min, then heat at 100-115 DEG C and bake 5-
8min is dried at 78-82 DEG C after then washing fabric again, completes the composite finishing of fabric.
Second dipping and rolling condition described in step (1) is bath raio 1:18, pick-up rate 77-82%, and padding temperature is 58-66 DEG C.
Anti-ultraviolet finishing liquid described in step (1) includes the component of following parts by weight: 7 parts of 5-aminosalicylic acids, 6 parts
Nano particle, 2 parts of dispersing agents, 13 parts of ethyl alcohol, 6 parts of fatty alcohol polyoxyethylene ether, 8 parts of sodium lactates, 3 parts of sodium pyrophosphates, 10 parts of plants
Object powder, 4 parts of urea, 6 parts of glycerol and 25 parts of deionized waters.
The nano particle is one of nano-titanium dioxide, nano zine oxide or a variety of.
The dispersing agent is triethanolamine, in Tween-80, Tween-60, Span -60, polyethylene glycol, calgon
It is one or more of.
The resistance to finishing fluid of soaping includes the component of following parts by weight: 105 parts of distilled water, 48 parts of butyl acetates, 25 parts
Filler, 0.5 part of lead acetate, 7 parts of ethylene glycol, 23 parts of polyvinyl alcohol, 24 parts of seven polyglycol ethers of dodecyl, 16 part of third ammonia
Acid, 9 parts of Sodium Polyacrylates, 10 parts of zinc sulfate and 6 parts of aloe fibres.
The filler is calcium bicarbonate.
Claims (7)
1. a kind of uvioresistant of fabric and the resistance to composite finishing technique soaped, it is characterised in that: the following steps are included:
(1) anti-ultraviolet finishing: fabric being impregnated into anti-ultraviolet finishing liquid, is handled using second dipping and rolling, described anti-
Ultraviolet light finishing fluid includes the component of following parts by weight: 6-9 parts of 5-aminosalicylic acids, 5-7 parts of nano particles, 1-3 parts of dispersions
Agent, 11-16 parts of ethyl alcohol, 4-7 parts of fatty alcohol polyoxyethylene ether, 5-10 parts of sodium lactates, 2-4 parts of sodium pyrophosphates, 7-12 parts of Plant Powders
End, 3-5 parts of urea, 5-7 parts of glycerol and 22-28 parts of deionized waters;
(2) resistance to arrangement of soaping: the fabric after anti-ultraviolet finishing being added in resistance to finishing fluid of soaping and is handled, described resistance to
Finishing fluid of soaping includes the component of following parts by weight: 80-120 parts of distilled water, 45-50 parts of butyl acetates, 23-28 parts of fillings
Agent, 0.2-0.8 parts of lead acetates, 6-10 parts of ethylene glycol, 16-28 parts of polyvinyl alcohol, 18-28 parts of seven polyglycol ethers of dodecyl,
15-17 parts of alanine, 8-10 parts of Sodium Polyacrylates, 7-12 parts of zinc sulfate and 4-8 parts of aloe fibres;
(3) it washes: the fabric Jing Guo resistance to arrangement of soaping being cleaned multiple times using clear water;
(4) dry: by the fabric after washing at 82-88 DEG C preliminary drying 3-5min, then heat at 100-115 DEG C and bake 5-
8min is dried at 78-82 DEG C after then washing fabric again, completes the composite finishing of fabric.
2. the uvioresistant of fabric according to claim 1 and the resistance to composite finishing technique soaped, it is characterised in that: step
(1) second dipping and rolling condition described in is bath raio 1:18, pick-up rate 77-82%, and padding temperature is 58-66 DEG C.
3. the uvioresistant of fabric according to claim 1 and the resistance to composite finishing technique soaped, it is characterised in that: step
(1) anti-ultraviolet finishing liquid described in includes the component of following parts by weight: 7 parts of 5-aminosalicylic acids, 6 parts of nano particles, 2 parts
Dispersing agent, 13 parts of ethyl alcohol, 6 parts of fatty alcohol polyoxyethylene ether, 8 parts of sodium lactates, 3 parts of sodium pyrophosphates, 10 parts of plant powders, 4 parts of urine
Element, 6 parts of glycerol and 25 parts of deionized waters.
4. the uvioresistant of fabric according to claim 1 or 3 and the resistance to composite finishing technique soaped, it is characterised in that:
The nano particle is one of nano-titanium dioxide, nano zine oxide or a variety of.
5. the uvioresistant of fabric according to claim 1 or 3 and the resistance to composite finishing technique soaped, it is characterised in that:
The dispersing agent is one of triethanolamine, Tween-80, Tween-60, Span -60, polyethylene glycol, calgon or several
Kind.
6. the uvioresistant of fabric according to claim 1 and the resistance to composite finishing technique soaped, it is characterised in that: described
Resistance to finishing fluid of soaping includes the component of following parts by weight: 105 parts of distilled water, 48 parts of butyl acetates, 25 parts of fillers, 0.5 part
Lead acetate, 7 parts of ethylene glycol, 23 parts of polyvinyl alcohol, 24 parts of seven polyglycol ethers of dodecyl, 16 parts of alanine, 9 parts of polyacrylic acid
Sodium, 10 parts of zinc sulfate and 6 parts of aloe fibres.
7. the uvioresistant of fabric according to claim 1 or 6 and the resistance to composite finishing technique soaped, it is characterised in that:
The filler is calcium bicarbonate.