CN108914654A - It is a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile - Google Patents
It is a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile Download PDFInfo
- Publication number
- CN108914654A CN108914654A CN201810828914.5A CN201810828914A CN108914654A CN 108914654 A CN108914654 A CN 108914654A CN 201810828914 A CN201810828914 A CN 201810828914A CN 108914654 A CN108914654 A CN 108914654A
- Authority
- CN
- China
- Prior art keywords
- color pond
- aramid fiber
- polyamide fibre
- fiber blended
- blended textile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, includes the following steps：Dye liquor needed for being formulated into dye；Polyamide fibre, aramid fiber blended textile after removal of impurities, washing and drying is put into color pond；Dye liquor in color pond is carried out continuing heating and keeps keeping temperature constant in color pond；Cool down after constant temperature to color pond, and to keep constant in the case where 80 degrees Celsius inside color pond；Direct-cooled cooling is carried out to color pond after temperature is constant, and makes the temperature constant state in color pond at 60 degrees Celsius after deoxyenzyme is added；Polyamide fibre, the aramid fiber blended textile in color pond are taken out in temperature constant end, and polyamide fibre, aramid fiber blended textile after finally being dyed, the polyamide fibre after dyeing, aramid fiber blended textile is enabled effectively to avoid the occurrence of color difference for this method and color fastness is high, that is, is conducive to the dyeing quality for improving high polyamide fibre, aramid fiber blended textile.
Description
Technical field
The present invention relates to textile dyeing technical fields more particularly to a kind of suitable for polyamide fibre, aramid fiber blended textile
Colouring method.
Background technique
It, can be blended using polyamide fibre is carried out with aramid fiber for polyamide fibre and aramid fiber during the manufacturing of textile
Polyamide fibre, aramid fiber blended textile are made in method, spinning, and spinning the polyamide fibre made, aramid fiber blended textile can be by nylon fibre and virtue
Synthetic fibre it is interfibrous combination and generate complex effect and have complementary functions, reach improvement fabric hygroscopicity and dress comfort, with
And the wrinkle resistance of fabric is improved on the basis of guaranteeing cloth abrasion performance and dimensional stability, but it is directed to polyamide fibre, virtue
The dyeing of synthetic fibre blended textile, traditional colouring method waste water source, and the color fastness after dyeing is low and is easy to appear dyeing partially
Difference is unfavorable for improving the dyeing quality of polyamide fibre, aramid fiber blended textile.For this purpose, we have proposed one kind to be suitable for polyamide fibre, aramid fiber
The colouring method of blended textile.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and the one kind proposed is suitable for polyamide fibre, virtue
The colouring method of synthetic fibre blended textile.
To achieve the goals above, present invention employs following technical solutions：
It is a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, include the following steps：
S1:Dye liquor needed for being formulated into dye is passed through the soft water that temperature is 38-42 degrees Celsius in color pond, and will
Lanaset dyestuff and glacial acetic acid are put into color pond；
S2:Polyamide fibre, aramid fiber blended textile after removal of impurities, washing and drying is put into color pond；
S3:Polyamide fibre, aramid fiber blended textile in step s 2 is put into color pond, is carried out to the dye liquor in color pond
Lasting heating, and when temperature is in 98 degrees Celsius, so that keeping temperature constant in entire color pond, and continue 50-70min；
S4:Cool down after step S3 to color pond, and the fall off rate of temperature is made to be maintained at 3 degrees Celsius every point
Clock, and the temperature in color pond be in 80 degrees Celsius when, catalyst is added into color pond, and make inside color pond 80
It is kept constant in the case where degree Celsius, and continues 50-70min；
S5:Direct-cooled cooling is carried out to color pond after step S4, and makes color pond when in 60 degrees Celsius to dye
Deoxyenzyme is added in color pond, and makes to continue 8-12min in color pond under 60 degrees Celsius of temperature constant state after deoxyenzyme is added；
S6:Polyamide fibre, the aramid fiber blended textile in color pond are taken out after step S5, and after finally being dyed
Polyamide fibre, aramid fiber blended textile.
Preferably, the Lanaset dyestuff that color pond is added in step S1 is specially Lanaset Red 2B, Lanaset
One or more of Yellow 4GN, Lanaset Blue 2R and Lanaset Gray G, and put into glacial acetic acid to dyeing
After in pond, the PH in color pond is tested, and PH is made to be 5-6.
Preferably, the Lanaset dye dosage that color pond is added in step S1 is to polyamide fibre, the virtue put into step S2
Synthetic fibre blended textile weight 1.5-2.5%owf.
Preferably, by weight polyamide fibre, the aramid fiber blended textile put into the dye liquor and step S2 prepared in step S1
Bath raio between is 3:1.
Preferably, the temperature rate-of-rise in step S3 in color pond is specifically maintained at 1 centigrade per minute.
Preferably, before deoxyenzyme is added in S4 end step S5, hydrogen peroxide is added into color pond, and to dyeing
PH in pond is tested, so that PH is specially 7.
Preferably, when testing the pH value in color pond, GB/T 6920-1986 is specifically used《Water pH value
Measure glass electrode method》It is tested.
Proposed by the present invention a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, beneficial effect is：We
Method for water resource using less, and to dye heel row dye polyamide fibre, aramid fiber blended textile during
The waste liquid put is easily handled, and the process in dyeing course is succinct, is convenient for operation and is implemented, the polyamide fibre, aramid fiber after dyeing are blended
Textile can effectively avoid the occurrence of color difference and color fastness is high, that is, be conducive to the dyeing for improving high polyamide fibre, aramid fiber blended textile
Quality.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, all other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment 1
It is a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, include the following steps：
S1:Dye liquor needed for being formulated into dye, it is 38 degrees Celsius of soft water that temperature is passed through in color pond, and by Lanaset
Dyestuff and glacial acetic acid are put into color pond；
S2:Polyamide fibre, aramid fiber blended textile after removal of impurities, washing and drying is put into color pond；
S3:Polyamide fibre, aramid fiber blended textile in step s 2 is put into color pond, is carried out to the dye liquor in color pond
Lasting heating, and when temperature is in 98 degrees Celsius, so that keeping temperature constant in entire color pond, and continue 50min；
S4:Cool down after step S3 to color pond, and the fall off rate of temperature is made to be maintained at 3 degrees Celsius every point
Clock, and the temperature in color pond be in 80 degrees Celsius when, catalyst is added into color pond, and make inside color pond 80
It is kept constant in the case where degree Celsius, and continues 50min；
S5:Direct-cooled cooling is carried out to color pond after step S4, and makes color pond when in 60 degrees Celsius to dye
Deoxyenzyme is added in color pond, and makes to continue 8min in color pond under 60 degrees Celsius of temperature constant state after deoxyenzyme is added；
S6:Polyamide fibre, the aramid fiber blended textile in color pond are taken out after step S5, and after finally being dyed
Polyamide fibre, aramid fiber blended textile.
The Lanaset dyestuff that color pond is added in step S1 is specially Lanaset Red 2B, Lanaset Yellow
One or more of 4GN, Lanaset Blue 2R and Lanaset Gray G, and after glacial acetic acid is put into color pond,
PH in color pond is tested, and PH is made to be 5.
The Lanaset dye dosage that color pond is added in step S1 is blended to the polyamide fibre, the aramid fiber that put into step S2
Textile weight 1.5%owf.
By weight put into the dye liquor prepared in step S1 and step S2 polyamide fibre, aramid fiber blended textile and between
Bath raio is 3:1.
Temperature rate-of-rise in step S3 in color pond is specifically maintained at 1 centigrade per minute.
Before deoxyenzyme is added in S4 end step S5, hydrogen peroxide is added into color pond, and in color pond
PH is tested, so that PH is specially 7.
When testing the pH value in color pond, GB/T 6920-1986 is specifically used《The measurement glass of water pH value
Glass electrode method》It is tested.
Embodiment 2
It is a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, include the following steps：
S1:Dye liquor needed for being formulated into dye, it is 40 degrees Celsius of soft water that temperature is passed through in color pond, and by Lanaset
Dyestuff and glacial acetic acid are put into color pond；
S2:Polyamide fibre, aramid fiber blended textile after removal of impurities, washing and drying is put into color pond；
S3:Polyamide fibre, aramid fiber blended textile in step s 2 is put into color pond, is carried out to the dye liquor in color pond
Lasting heating, and when temperature is in 98 degrees Celsius, so that keeping temperature constant in entire color pond, and continue 60min；
S4:Cool down after step S3 to color pond, and the fall off rate of temperature is made to be maintained at 3 degrees Celsius every point
Clock, and the temperature in color pond be in 80 degrees Celsius when, catalyst is added into color pond, and make inside color pond 80
It is kept constant in the case where degree Celsius, and continues 60min；
S5:Direct-cooled cooling is carried out to color pond after step S4, and makes color pond when in 60 degrees Celsius to dye
Deoxyenzyme is added in color pond, and makes to continue 10min in color pond under 60 degrees Celsius of temperature constant state after deoxyenzyme is added；
S6:Polyamide fibre, the aramid fiber blended textile in color pond are taken out after step S5, and after finally being dyed
Polyamide fibre, aramid fiber blended textile.
The Lanaset dyestuff that color pond is added in step S1 is specially Lanaset Red 2B, Lanaset Yellow
One or more of 4GN, Lanaset Blue 2R and Lanaset Gray G, and after glacial acetic acid is put into color pond,
PH in color pond is tested, and PH is made to be 5.5.
The Lanaset dye dosage that color pond is added in step S1 is blended to the polyamide fibre, the aramid fiber that put into step S2
Textile weight 2%owf.
By weight put into the dye liquor prepared in step S1 and step S2 polyamide fibre, aramid fiber blended textile and between
Bath raio is 3:1.
Temperature rate-of-rise in step S3 in color pond is specifically maintained at 1 centigrade per minute.
Before deoxyenzyme is added in S4 end step S5, hydrogen peroxide is added into color pond, and in color pond
PH is tested, so that PH is specially 7.
When testing the pH value in color pond, GB/T 6920-1986 is specifically used《The measurement glass of water pH value
Glass electrode method》It is tested.
Embodiment 3
It is a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, include the following steps：
S1:Dye liquor needed for being formulated into dye, it is 42 degrees Celsius of soft water that temperature is passed through in color pond, and by Lanaset
Dyestuff and glacial acetic acid are put into color pond；
S2:Polyamide fibre, aramid fiber blended textile after removal of impurities, washing and drying is put into color pond；
S3:Polyamide fibre, aramid fiber blended textile in step s 2 is put into color pond, is carried out to the dye liquor in color pond
Lasting heating, and when temperature is in 98 degrees Celsius, so that keeping temperature constant in entire color pond, and continue 70min；
S4:Cool down after step S3 to color pond, and the fall off rate of temperature is made to be maintained at 3 degrees Celsius every point
Clock, and the temperature in color pond be in 80 degrees Celsius when, catalyst is added into color pond, and make inside color pond 80
It is kept constant in the case where degree Celsius, and continues 70min；
S5:Direct-cooled cooling is carried out to color pond after step S4, and makes color pond when in 60 degrees Celsius to dye
Deoxyenzyme is added in color pond, and makes to continue 12min in color pond under 60 degrees Celsius of temperature constant state after deoxyenzyme is added；
S6:Polyamide fibre, the aramid fiber blended textile in color pond are taken out after step S5, and after finally being dyed
Polyamide fibre, aramid fiber blended textile.
The Lanaset dyestuff that color pond is added in step S1 is specially Lanaset Red 2B, Lanaset Yellow
One or more of 4GN, Lanaset Blue 2R and Lanaset Gray G, and after glacial acetic acid is put into color pond,
PH in color pond is tested, and PH is made to be 6.
The Lanaset dye dosage that color pond is added in step S1 is blended to the polyamide fibre, the aramid fiber that put into step S2
Textile weight 2.5%owf.
By weight put into the dye liquor prepared in step S1 and step S2 polyamide fibre, aramid fiber blended textile and between
Bath raio is 3:1.
Temperature rate-of-rise in step S3 in color pond is specifically maintained at 1 centigrade per minute.
Before deoxyenzyme is added in S4 end step S5, hydrogen peroxide is added into color pond, and in color pond
PH is tested, so that PH is specially 7.
When testing the pH value in color pond, GB/T 6920-1986 is specifically used《The measurement glass of water pH value
Glass electrode method》It is tested.
In the description of this specification, the description of reference term " one embodiment ", " example ", " specific example " etc. means
Particular features, structures, materials, or characteristics described in conjunction with this embodiment or example are contained at least one implementation of the invention
In example or example.In the present specification, schematic expression of the above terms may not refer to the same embodiment or example.
Moreover, particular features, structures, materials, or characteristics described can be in any one or more of the embodiments or examples to close
Suitable mode combines.
Present invention disclosed above preferred embodiment is only intended to help to illustrate the present invention.There is no detailed for preferred embodiment
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.These embodiments are chosen and specifically described to this specification, is in order to better explain the present invention
Principle and practical application, so that skilled artisan be enable to better understand and utilize the present invention.The present invention is only
It is limited by claims and its full scope and equivalent.
Claims (7)
1. a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, which is characterized in that include the following steps：
S1:Dye liquor needed for being formulated into dye is passed through temperature in color pond and is 38-42 degrees Celsius of soft water, and Lanaset is contaminated
Material and glacial acetic acid are put into color pond；
S2:Polyamide fibre, aramid fiber blended textile after removal of impurities, washing and drying is put into color pond；
S3:Polyamide fibre, aramid fiber blended textile in step s 2 is put into color pond, is continued to the dye liquor in color pond
Heating, and when temperature is in 98 degrees Celsius, so that keeping temperature constant in entire color pond, and continue 50-70min；
S4:Cool down after step S3 to color pond, and the fall off rate of temperature made to be maintained at 3 centigrade per minutes,
And the temperature in color pond be in 80 degrees Celsius when, catalyst is added into color pond, and to take the photograph inside color pond 80
It is kept constant in the case where family name's degree, and continues 50-70min；
S5:Direct-cooled cooling is carried out to color pond after step S4, and makes color pond when in 60 degrees Celsius to color pond
Interior addition deoxyenzyme, and make to continue 8-12min in color pond under 60 degrees Celsius of temperature constant state after deoxyenzyme is added；
S6:Polyamide fibre, the aramid fiber blended textile in color pond are taken out after step S5, and the brocade after finally being dyed
Synthetic fibre, aramid fiber blended textile.
2. according to claim 1 a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, which is characterized in that
The Lanaset dyestuff that color pond is added in step S1 be specially Lanaset Red 2B, Lanaset Yellow 4GN,
One or more of Lanaset Blue 2R and Lanaset Gray G, and after glacial acetic acid is put into color pond, to dye
PH in color pond is tested, and PH is made to be 5-6.
3. according to claim 1 a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, which is characterized in that
The Lanaset dye dosage that color pond is added in step S1 is to polyamide fibre, the aramid fiber blended textile weight put into step S2
1.5-2.5%owf.
4. according to claim 1 a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, which is characterized in that
By weight put into the dye liquor prepared in step S1 and step S2 polyamide fibre, aramid fiber blended textile and between bath raio be 3:
1。
5. according to claim 1 a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, which is characterized in that
Temperature rate-of-rise in step S3 in color pond is specifically maintained at 1 centigrade per minute.
6. according to claim 1 a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile, which is characterized in that
Before deoxyenzyme is added in S4 end step S5, hydrogen peroxide is added into color pond, and survey to the PH in color pond
Examination, so that PH is specially 7.
7. a kind of suitable for polyamide fibre, the colouring method of aramid fiber blended textile according to claim 2 or 6, feature exists
In when testing the pH value in color pond, specifically using GB/T 6920-1986《The measurement glass electrode of water pH value
Method》It is tested.